Computational modeling of coupled mechanical damage and electrochemistry in ternary oxide composite electrodes

Abstract

Performance degradation of ternary layered oxide cathodes largely originates from their loss of structural integrity in cyclic usage. Mechanical damage, such as intergranular fracture of the active particles, is not only a mechanical cleavage process but also interferes with electrochemical kinetics such as infiltration of liquid electrolyte, surface corrosion of the constituent primary particles, and may eventually isolate the primary grains from the electron conducting network. Here, in this work, we develop a computational framework that integrates electrochemistry of a LiNi x Mn y Co 1−x−y O 2 (NMC) composite cathode with mechanical damage of the active particles. To fully examine the intricate chemomechanical behavior of the electrode, we evaluate the effects of the anisotropic material properties, the influence of mechanical potential on Li transport, and the concurrent intergranular fracture and electrolyte penetration along the grain boundaries upon multiple cycles. Electrolyte infiltration benefits capacity retention but aggravates further mechanical damage by corrosion. Structural failure mostly occurs in the first charging due to the anisotropic mechanical strain between the primary grains, while the resulting damage remains stable in the later few cycles. The results are consistent with experimental observations and the integration of electrochemistry and mechanical failure enables a step further understanding of the complex mechanism of battery degradation.

Explore related subjects

Keep this discovery

BibTeXRIS

Han, Jiaxiu [Purdue Univ., West Lafayette, IN (United States)], Sharma, Nikhil [Purdue Univ., West Lafayette, IN (United States)], Zhao, Kejie [Purdue Univ., West Lafayette, IN (United States)] (ORCID:0000000150307412). 2024-01-14. Computational modeling of coupled mechanical damage and electrochemistry in ternary oxide composite electrodes. https://doi.org/10.1016/j.jpowsour.2023.234034

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

Factors Influencing Gas Evolution from High‐Nickel Layered Oxide Cathodes in Lithium‐Based Batteries

Abstract Gas evolution from high‐nickel layered oxide cathodes (>90% Ni) remains a major issue for their practical application. Gaseous species, such as CO 2 , O 2 , and CO, that are evolved at high states of charge (SOC) worsen the overall safety of batteries, as pressure build‐up within the cell may lead to cell rupture. Since these gasses are produced during cathode degradation, tracking the formation of gasses is also important in diagnosing cathode failure. Online electrochemical mass spectrometry (OEMS) is a powerful in situ technique to study gas evolution from the cathode during high‐voltage charge. However, the differences in the OEMS experimental setups between different groups make it challenging to compare results between groups. In this perspective, the various factors that influence gas evolution based on the OEMS results collected in this group are presented. The focus is on the conditions that lead to gas release, with a particular emphasis on reactive oxygen formation and subsequent chemical reactions with the electrolyte. Promising strategies, such as electrolytes, compositional tuning, and surface coatings that are effective at suppressing gas evolution from the cathode are highlighted. Critical insights into mitigating cathode degradation and gas evolution are provided to guide the development of safer, high‐energy batteries.

Chemistry

Understanding Discharge‐Driven Growth of Cathode Impedance in Ni‐Rich NMC Cathodes

Degradation of LiNi x Mn y Co 1-x-y O 2 (NMC)-based lithium-ion batteries depends strongly on cut-off voltage ranges. In addition to the high upper cut-off voltage, a high depth of discharge (i.e., lower cut-off voltage) significantly worsens cathode impedance growth and capacity fade during long-term cycling. However, there is currently no consensus on the mechanism behind the negative role of a deep discharge. Here, this phenomenon was investigated in graphite||NMC cells with single-crystal cathodes (LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NMC622) or LiNi 0.76 Co 0.14 Mn 0.10 O 2 (NMC76)) using targeted aging protocols (constant high-voltage holds vs. charge–discharge cycling), while monitoring transition-metal (TM) dissolution, cathode-electrolyte interface (CEI) impedance, and NMC surface composition. We demonstrate a correlation between discharge-driven CEI impedance growth and increased TM dissolution. Furthermore, this degradation pathway is more pronounced in lower-Ni NMC622 than in higher-Ni (NMC76) under comparable delithiation states at charge, with both compositions undergoing the H2→H3 phase transition. X-ray photoelectron spectroscopy (XPS) reveals NMC composition-dependent evolution of surface lattice oxygen and restructured surface layer composition between charged and discharged states. These findings add mechanistic depth to the role of discharge as an active driver of interfacial degradation and provide new insights into its composition dependence.

25 ENERGY STORAGE

Electrostatic‐Attraction‐Driven Self‐Assembled Graphene‐Disordered Rocksalt Composite Cathode for Lithium‐Ion Batteries

Disordered rocksalt cathodes hold promise for achieving high-capacity lithium-ion batteries while using low-cost, earth-abundant elements. However, their electrochemical performance remains critically limited by their poor electronic conductivity. Conventional strategies such as high-energy ball milling with excess carbon additives can improve conductivity but remain challenging to scale and often produce defects and increase surface area, thereby accelerating capacity degradation. Herein, we report an alternative approach of electrostatic-attraction-driven self-assembly to fabricate Li 1.2 Mn 0.6 Ti 0.2 O 1.8 F 0.2 (LMTOF) particles uniformly wrapped with electronically conductive graphene sheets without associated materials degradation. The graphene-wrapped LMTOF demonstrates significantly improved cycling stability (89% capacity retention after 100 cycles) and superior rate capability compared with an LMTOF-carbon composite electrode fabricated using the conventional high-energy ball-milling process. Post-cycling analysis reveals reduced oxygen evolution, suppressed unwanted side reactions, and improved structural integrity for the graphene-LMTOF composite. This work highlights the advantages of solution-based carbon wrapping and offers a scalable strategy to prepare high-performance DRX cathodes for lithium-ion batteries.

carbon composite