Comparing Environmental Barrier Surface Temperature Mapping With Either A Y2SiO5:Er or Sc2SiO5:Er Temperature Sensing Layer

Jeffrey I Eldridge·Michael J Presby·Kang N Lee·John A Setlock
View original source ↗Read source document ↗Export metadata ↓

Abstract

The source did not provide an abstract. Follow the original record for more information.

Explore related subjects

environmental barrier coatingstemperature measurementphosphor thermometry

Keep this discovery

BibTeXRIS

Jeffrey I Eldridge, Michael J Presby, Kang N Lee, John A Setlock. Comparing Environmental Barrier Surface Temperature Mapping With Either A Y2SiO5:Er or Sc2SiO5:Er Temperature Sensing Layer. https://ntrs.nasa.gov/citations/20260002346

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

environmental barrier coatings subjectphosphor thermometry subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

NASA NTRS1994

Thermal Testing of High Performance: Thermal Barrier Coatings for Turbine Blades

A 350 micron thick 7 wt.% Y 2 O 3 -ZrO 2 (7YSZ) ceramic Thermal Barrier Coating (TBC) was manufactured in an argon atmosphere and with a strictly controlled substrate temperature on flat IN 600 samples and on IN 100 aircraft turbine blades. This new atmosphere and temperature controlled spraying (ATCS) allows the reduction of the residual stresses and an improvement in the microstructure and in the mechanical properties of the coating. The good performance of these new TBC's was assessed in thermal fatigue and in thermal shock tests carried out in air at 1100°C and at 1280°C respectively. The oxidation rate of the metal-ceramic interface was measured at 1100°C. Failure of the TBC's was induced only by the deterioration (like oxidation, cracking, ...) of the uncoated parts of the samples, as testing temperature was too severe for the base metals. Spalling was thereafter driven by compressive stresses near the aluminum oxide layer at the metal-ceramic interface. The results of these tests underline the good quality of the ceramic coating manufactured by the new ATCS technology.

L Bertamini↗
NASA NTRSDate not supplied

Evaluation of Particle Degradation of a Ytterbium Disilicate Gas Turbine Coating in a Combustion Environment

Ytterbium disilicate (Yb2Si2O7) is a state-of-the-art topcoat material used in environmental barrier coatings (EBCs) to protect SiC-SiC composites from water vapor corrosion in gas turbine engines. However, it’s degradation by thermochemical and thermomechanical particle interactions may limit its use in next generation engine systems. Several static furnace tests have been performed on Yb2Si2O7 to elucidate methods of degradation, although dynamic testing in an engine-relevant environment has not been carried out. Ultimately, testing and evaluation of materials that incorporates all environmental damage modes will allow for an accurate assessment of long-term durability and operating lifetime. This work details the investigation of particle-induced erosion and corrosion of Yb2Si2O7 in NASA Glenn’s Erosion Burner Rig Facility. Coating durability was investigated as a function of test temperature, particle size, and deposition rate. Thermal cycling was also incorporated into testing to determine the interplay of heating/cooling cycles with particle degradation. Overall, these analyses will be used to determine coating robustness in an engine relevant environment.

Jamesa L Stokes↗