Application of Energy-efficient Electromagnetic Melt-Processing for the Upcycling of Recycled Polyphenylene Sulfide into Multifunctional Segregated Nanocomposites

Abstract

Polyphenylene sulfide (PPS) is widely used in structural and functional composites because of its thermal stability, chemical resistance, and mechanical strength. As circular manufacturing becomes increasingly important, extending the service life of recycled PPS (rPPS) is essential. However, conventional high-temperature reprocessing accelerates thermo-oxidative degradation, reducing recycled composite performance. This study proposes a rapid and potentially energy-saving upcycling strategy for rPPS using electromagnetic (EM) melt-processing to form segregated carbon nanotube (CNT) networks and produce EM-responsive nanocomposites. The aim was to determine whether CNT-assisted EM heating could reduce polymer degradation while improving multifunctional properties at ultralow filler loadings. rPPS micropellets were coated with CNTs by ball milling to create conductive shells, then compacted into green bodies (GBs) and selectively melted by rapid EM irradiation. Structural, electrical, mechanical, rheological, and electromagnetic interference (EMI) shielding properties were evaluated. Electrical percolation occurred at an ultralow CNT loading of 0.08 wt%, with conductivity reaching (1.24 ± 0.74) × 10 -5 S⋅m -1 at 0.1 wt%. At this concentration, tensile strength and modulus increased by 72% and 99%, respectively. At ~ 0.7 mm thickness, X-band EMI shielding effectiveness reached 6 dB for GBs and 3 dB after EM processing. This shows that EM melt-processing upcycles rPPS into high-performance multifunctional nanocomposites with minimum thermal degradation.