Advancements in nanocomposites for enhancing the performance of rechargeable lithium-ion batteries

Pranto, Tawhid·Rappoport, Deborah·Ahmed, Fariha·Kundla, Matthew·Suarez, Sophia
View original source ↗Export metadata ↓

Abstract

The benefits of nanotechnology have been realized in almost every component of lithium-ion batteries. From electrodes to electrolytes, the incorporation of nanoparticles as dopants and coatings has shown marked improvements in cell cycle life, efficiency, mechanical and thermal stabilities, and lithium-ion transport. The improvements realized depends on several factors, from processing methods, nanoparticle type, structure, and concentration, to the material into which the nanoparticulate will be incorporated. Regardless of these many factors, nanotechnology has vastly improved the performance of secondary lithium-ion batteries. Here we will highlight some of the works that demonstrate these improvements and the quantitative benefits of nanotechnology.

Explore related subjects

25 ENERGY STORAGEnanoparticles, lithium-ion battery, electrolyte, capacity, coating

Keep this discovery

BibTeXRIS

Pranto, Tawhid, Rappoport, Deborah, Ahmed, Fariha, Kundla, Matthew, Suarez, Sophia. 2025-01-01. Advancements in nanocomposites for enhancing the performance of rechargeable lithium-ion batteries. https://doi.org/10.1016/b978-0-443-30065-3.00001-6

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Lithium-ion batteries material25 ENERGY STORAGE subjectnanoparticles, lithium-ion battery, electrolyte, capacity, coating subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related reports

DOE OSTI2023

Speciation of Transition Metal Dissolution in Electrolyte from Common Cathode Materials

Significant capacity loss has been observed across extended cycling of lithium-ion batteries cycled to high potential. One of the sources of capacity fade is transition metal dissolution from the cathode active material, ion migration through the electrolyte, and deposition on the solid-electrolyte interphase on the anode. While much research has been conducted on the oxidation state of the transition metal in the cathode active material or deposited on the anode, there have been limited investigations of the oxidation state of the transition metal ions dissolved in the electrolyte. Here, in this work, X-ray absorption spectroscopy has been performed on electrolytes extracted from cells built with four different cathode active materials (LiMn 2 O 4 (LMO), LiNi 0.5 Mn 1.5 O 4 (LNMO), LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811), and (x Li 2 MnO 3 *(1-x) LiNi a Mn b Co c O 2 , with a+b+c=1) (LMRNMC)) that were cycled at either high or standard potentials to determine the oxidation state of Mn and Ni in solution. Inductively coupled plasma-mass spectrometry has been performed on the anodes from these cells to determine the concentration of deposited transition metal ions. While transition metal ions were found dissolved in all electrolytes, the oxidation state(s) of Mn and Ni were determined to be dependent on the cathode material and independent of cycling potential.

25 ENERGY STORAGE↗
DOE OSTI2023

Interface Design for High‐Performance All‐Solid‐State Lithium Batteries

All‐solid‐state batteries suffer from high interface resistance and lithium dendrite growth leading to low Li plating/stripping Coulombic efficiency (CE) of <90% and low critical current density at high capacity. Here, in this work, both challenges are simultaneously addressed and the Li plating/stripping CE is significantly increased to 99.6% at 0.2 mA cm −2 /0.2 mAh cm −2 , and critical current density (CCD) of > 3.0 mA cm −2 /3.0 mAh cm −2 by inserting a mixed ionic‐electronic conductive (MIEC) and lithiophobic LiF‐C‐Li 3 N‐Bi nanocomposite interlayer between Li 6 PS 5 Cl electrolyte and Li anode. The highly lithiophobic LiF‐C‐Li 3 N‐Bi interlayer with high ionic conductivity (10 −5 S cm −1 ) and low electronic conductivity (3.4×10 −7 S cm −1 ) enables Li to plate on the current collector (CC) surface rather than on Li 6 PS 5 Cl surface avoiding Li 6 PS 5 Cl electrolyte reduction. During initial Li plating on CC, Li penetrates into porous LiF‐C‐Li 3 N‐Bi interlayer and lithiates Bi nanoparticles into Li 3 Bi. The lithiophilic Li 3 Bi and Li 3 N nanoparticles in LiF‐C‐Li 3 N‐Li 3 Bi sub‐interlayer will move to CC along with plated Li, forming LiF‐C/Li 3 N‐Li 3 Bi lithiophobic/lithiophilic sublayer during the following Li stripping. This interlayer enables Co 0.1 Fe 0.9 S 2 /Li 6 PS 5 Cl/Li cell with an areal capacity of 1.4 mAh cm −2 to achieve a cycle life of >850 cycles at 150 mA g −1 . The lithiophobic/lithiophilic interlayer enables solid‐state metal batteries to simultaneously achieve high energy and long cycle life.

25 ENERGY STORAGE↗