Sodium-ion batteries offer low-cost energy storage solutions for the grid and electric vehicles, leveraging the established "rocking-chair" Li-ion design and the natural abundance of sodium. However, SIBs face challenges such as relatively lower voltage and capacity than lithium-ion batteries, as well as dependence on nickel resources. Here, in this work, a new nickel-free cathode material, Na 0.75 Li 0.08 Cu 0.25 Mn 0.66 O 2 , was designed and synthesized. This material has a capacity of ~125 mAh/g and an average discharge voltage of 3.5 V. Notably, more than one-third of the capacity arises from lithium substitution of Cu (~8 mol.%) and high voltage activation to 4.6 V. Multimodal synchrotron x-ray characterization combining spectroscopy, microscopy, and scattering reveal the capacity is primarily from the redox of copper and oxygen, with a minor contribution from the manganese redox. Lithium substitution alters the phase transition mechanism from a two-phase transition in P3-Na 2/3 Cu 1/3 Mn 2/3 O 2 to a solid-solution in Na 0.75 Li 0.08 Cu 0.25 Mn 0.66 O 2 , enhancing the reversibility of this material.