A Dispersion-Strengthened Low-Density Niobium Alloy and Its Elevated Temperature Mechanical Performance

Abstract

In response to the elevated-temperature and weight-reduction demands of modern aerospace applications, a novel oxide-dispersion-strengthened low-density niobium alloy (LDNb-ODS) was fabricated using laser powder bed fusion (L-PBF). To overcome powder procurement barriers, L-PBF feedstock was produced by blending commercial Nb521, Ti64, and Cr powder with Y2O3 nanoparticles via resonant acoustic mixing. Following L-PBF and a 1400°C vacuum heat treatment, the alloy achieved a density of 6.73 g/cc and a fine mean grain size of 4.62 µm stabilized by uniform ~30 nm yttria dispersoids. Microstructural analysis revealed a chemically inhomogeneous build with lack-of-fusion defects and a titanium (Ti) shift from a nominal 31.5 wt% in the starting powder blend to 24.8 wt% in the printed part due to preferential Ti loss during printing. Elevated-temperature tensile testing demonstrated that LDNb-ODS maintained a superior specific yield strength of 60-85 MPa/(g/cc) up to 800°C, outperforming nickel-based alloys Ni625, Ni230, and GRX-810. Between 870°C and 950°C, its specific strength surpassed both Ni718 and Ni625. In rapid stress-rupture testing at 1093°C and 20.7 MPa, uncoated LDNb-ODS survived 21.4 hours (a tenfold increase over legacy C-103) while an R512E silicide coating extended rupture life to 84.8 hours, confirming that oxidation accelerates low-stress failure. These findings demonstrate that additive manufacturing of LDNb-ODS provides a viable, lightweight alternative to nickel-based superalloys for high-temperature (>850°C) aerospace components.