High Performance Ceramic Interconnect Material for Solid Oxide Fuel Cells (SOFCs): Ca- and Transition Metal-doped Yttrium Chromite

Yoon, Kyung J·Stevenson, Jeffry W·Marina, Olga A
View original source ↗Export metadata ↓

Abstract

The effect of transition metal substitution on thermal and electrical properties of Ca-doped yttrium chromite was investigated in relation to use as a ceramic interconnect in high temperature solid oxide fuel cells (SOFCs). 10 at% Co, 4 at% Ni, and 1 at% Cu substitution on B-site of 20 at% Ca-doped yttrium chromite led to a close match of thermal expansion coefficient (TEC) with that of 8 mol% yttria-stabilized zirconia (YSZ), and a single phase Y0.8Ca0.2Cr0.85Co0.1Ni0.04Cu0.01O3 remained stable between 25 and 1100 degree C over a wide oxygen partial pressure range. Doping with Cu significantly facilitated densification of yttrium chromite. Ni dopant improved both electrical conductivity and dimensional stability in reducing environments, likely through diminishing the oxygen vacancy formation. Substitution with Co substantially enhanced electrical conductivity in oxidizing atmosphere, which was attributed to an increase in charge carrier density and hopping mobility. Electrical conductivity of Y0.8Ca0.2Cr0.85Co0.1Ni0.04Cu0.01O3 at 900 degree C is 57 S/cm in air and 11 S/cm in fuel (pO2=5×10^-17 atm) environments. Chemical compatibility of doped yttrium chromite with other cell components was verified at the processing temperatures. Based on the chemical and dimensional stability, sinterability, and thermal and electrical properties, Y0.8Ca0.2Cr0.85Co0.1Ni0.04Cu0.01O3 is suggested as a promising SOFC ceramic interconnect to potentially overcome technical limitations of conventional acceptor-doped lanthanum chromites.

Explore related subjects

30 DIRECT ENERGY CONVERSIONAIRCERAMICSCHARGE CARRIERSChemical expansionCHROMITESCHROMIUM OXIDESCOMPATIBILITYDoped yttrium chromiteELECTRIC CONDUCTIVITYElectrical conductivityELECTRICAL PROPERTIESLANTHANUM OXIDESOXYGENPARTIAL PRESSUREPERFORMANCEPROCESSINGSinteringSOFC interconnectSOLID OXIDE FUEL CELLSSTABILITYTHERMAL EXPANSIONTRANSITION ELEMENTSYTTRIUM

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Yoon, Kyung J, Stevenson, Jeffry W, Marina, Olga A. 2011-10-15. High Performance Ceramic Interconnect Material for Solid Oxide Fuel Cells (SOFCs): Ca- and Transition Metal-doped Yttrium Chromite. https://doi.org/10.1016/j.jpowsour.2011.06.089

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Engineering Thermally Resilient and Kinetically Active Reversible Protonic Ceramic Cells via Interfacial Design

Achieving concurrent fast electrode kinetics and long-term thermo-mechanical durability remains a critical challenge for reversible protonic ceramic electrochemical cells (R-PCECs). Herein, we report an interfacial engineering strategy that integrates a perovs.kite-type PrBaRu0.1Co1.9O5+δ (PBRC) nanoparticle layer onto a PrBa0.5Sr0.5Co1.5Fe0.5O5+δ (PBSCF) substrate (PBRC-PBSCF), together with a modified pellet-assisted sintering approach to fabricate dense BaZr0.4Ce0.4Y0.1Yb0.1O3-δ (BZCYYb4411) electrolytes. The in situ reconstructed heterointerface enhances oxygen reduction/evolution reaction (ORR/OER) kinetics, promotes H2O adsorption/dissociation, and improves steam tolerance, as verified by electrochemical measurements and interfacial microstructural analyses. Density functional theory reveals that Ru-induced electronic modulation at the PBRC-PBSCF interface lowers the energy of oxygen vacancy formation and optimizes the position of the O 2p band center, thereby accelerating oxygen redox kinetics and stabilizing the interface. The resulting R-PCECs deliver an excellent peak power density of 1.112 W cm−2 and an electrolysis current density of −1.257 A cm−2 at 1.3 V in 3% H2O wet air at 600°C, with a reasonable faradaic efficiency. Furthermore, the cells demonstrate excellent stability, sustaining 100 h of thermal cycling (400–600°C, 200°C h−1) in both fuel cell and electrolysis modes, with 600 h of stability in electrolysis mode (600°C, −0.5 to −2 A cm−2).

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2026

Development of a High-Efficiency Hybrid Dry Cooler System for sCO 2 Power Cycles in CSP Applications

This project addressed a major gap in supercritical CO 2 (sCO 2 ) power cycle research by focusing on the pre-cooler, a component that had received little attention despite its significant impact on cycle efficiency and plant economics. The team developed a compact dry cooler using brazed/diffusion-bonded microchannel passages paired with formed air-side fins, advancing the technology from TRL-2 toward commercial readiness. Compared to conventional fin-tube coolers, the design cuts installation footprint by roughly half for 10+ MWth systems while achieving better heat transfer and lower approach temperatures, translating into a projected LCOE reduction from 6.04 ¢/kWh to between 5.85 and 5.94 ¢/kWh. While fabrication of an aluminum MW-scale prototype revealed brazing and sealing challenges at larger scales, lessons learned informed a subsequent 1 MWth unit that was successfully built and delivered for integration into Sandia's Gen3 Particle Pilot Plant, advancing the technology to TRL-7 with a path toward TRL-8 pending successful testing.

30 DIRECT ENERGY CONVERSION↗
DOE OSTI2026

Pressurized Gas-Driven Elemental Redistribution Enables Ultrastable PtNi Catalysts for Heavy-Duty Vehicles

Gas-driven element redistribution, characterized by the preferential enrichment of one element at the surface relative to the bulk, is frequently observed in multicomponent alloys. Using L1 0 -ordered PtNi as a model system, we reveal that gas pressure plays a critical role in governing adsorption-driven surface composition during annealing in reducing gases: low pressure favors Pt surface segregation, while high pressure facilitates Ni surface enrichment. In this study, we developed a high-pressure nitriding (HPN) strategy that modulates the surface structure and composition of PtNi catalysts. The resulting HPN-PtNi exhibits enhanced performance and durability in membrane electrode assemblies for heavy-duty fuel cell applications, maintaining a high current density of 1.19 A cm −2 at 0.7 V after 90,000 voltage cycles. Through a combination of experimental and theoretical analyses, we reveal that the HPN process forms additional stabilizing Ni−N bonds and induces elemental redistribution with Ni surface enrichment and a Ni-deficient Pt subsurface. These modifications alter the atomic coordination environment of the ordered PtNi phase. This work presents a generalizable strategy to design robust and high-performing Pt-based catalysts by controlling gas-pressure-driven elemental redistribution and dopant incorporation.

30 DIRECT ENERGY CONVERSION↗