Solid Oxide Based Electrolysis and Stack Technology with Ultra-High Electrolysis Current Density (>3A/cm 2 ) and Efficiency

Tang, Eric·Wood, Tony·Brown, Casey·Casteel, Micah·Pastula, Michael·Richards, Mark·Petri, Randy
View original source ↗Read source document ↗Export metadata ↓

Abstract

Hydrogen, a valuable commodity gas, is increasingly recognized as an important fuel and energy storage pathway of the future. This project aims to develop an innovative solid oxide based electrolysis cell and stack technology with ultra-high steam electrolysis current (>3A/cm 2 ) for potentially ultra-low-cost, highly efficient hydrogen production from diverse renewable sources. In this project, solid oxide based high power density cells (HiPoD cells) were developed. Those cells demonstrated capability of operating at ultra-high electrolysis current density of 6 A/cm 2 at 1.67V. During a long term steady state electrolysis test, a HiPoD cell was operated for more than 1000 hours at 3 A/cm 2 with a low degradation rate of 1.8% per 1000 hours. A 20-cell electrolysis stack was built using HiPoD cells and an ultra-compact, low-cost stack design platform. This stack was used to explore the boundaries of high current density electrolysis operation and achieved an incredible stack current density of 3 A/cm 2 with an average cell voltage of only 1.493 V. The stack was further operated in steady-state electrolysis at 2 A/cm 2 for more than 1000 hours with an overall degradation of 0.57% per 1000 hours. With an improved understanding of electrolysis operation at ultra-high current density, a new compact stack architecture (CSA) design with scalability up to 55 kW (or 38 kg H 2 per day) was tested. A number of 45-cell CSA stack was built and demonstrated 10 kW and 245 g/hr hydrogen production at 1.8 A/cm 2 electrolysis current density. In addition to cell and stack development, a preliminary system design was developed by integrating the inputs from electrochemistry, cell/stack performance data, and system level implications of configuration and operational parameters. A module design was created based on a circular array of six stacks surrounded in a cool pressure vessel. Further architectural and controls strategies such as stack power control and instrumentation were determined through the development of the module. A comprehensive techno-economic study of an ultra-high current density SOEC system integrated with renewable energy sources has been conducted. To determine the estimated cost of hydrogen for the system, the H2A Current Distributed Hydrogen Production Model version 3.101 was applied. Annual system production cases at both commercial and industrial electricity rates as per the H2A model was analyzed. The option of meeting DOE 2020 Advanced Electrolysis Technologies targets were discussed. Feedstock electricity represents the bulk of projected hydrogen cost with either electricity rate. At an annual production volume of 250 units, H2A hydrogen cost of $2.3/kg can be achieved at electricity cost around 3.5¢/kWh.

Explore related subjects

08 HYDROGENefficiencyelectrolysishydrogenproductionSOECsolid oxidestacksteamwater

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Tang, Eric, Wood, Tony, Brown, Casey, Casteel, Micah, Pastula, Michael, Richards, Mark, Petri, Randy. 2018-03-31. Solid Oxide Based Electrolysis and Stack Technology with Ultra-High Electrolysis Current Density (>3A/cm 2 ) and Efficiency. https://doi.org/10.2172/1513461

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Elucidating key reducing species beyond ions in hydrogen plasma smelting reduction of iron ore

Hydrogen plasma smelting reduction (HPSR) of iron ore has attracted significant attention over the past decade due to its high-temperature operation, rapid plasma mediated reduction kinetics, and simpler density-based separation of molten iron product, compared to H2-based solid-state reduction. All of these attributes enable processing of low-grade ores for downstream use in electric-arc furnaces, as virgin iron with low gangue content is required for high quality steel and improved furnace operation. While positive ions exist within the plasma arc, this work demonstrates that near the anodic ore surface, hydrogen radicals and vibrationally excited hydrogen species dominate and their densities correlate well with observed reduction rates. Species concentrations in the transferred plasma arc and at the plasma-ore interface are evaluated using coupled thermal plasma and near-wall non-equilibrium plasma models. The thermal plasma model is validated against experimental voltage data and spectroscopic measurements of plasma temperature and density for varying current inputs. Modeling of the near surface thermochemical non-equilibrium and micrometer scale anode sheath layer reveals, in addition to the expected H + , significant concentrations of ArH + and H$^+_3$ ions, typically not observed in thermal plasmas under thermodynamic equilibrium. Our results show that the inverted sheath structure at the anodic ore surface strongly suppresses reactive positive ion fluxes, while non-equilibrium electron-impact processes generate abundant hydrogen radicals and vibrationally excited species. These findings highlight the critical role of non-equilibrium effects in hydrogen arc-driven iron ore reduction and advance understanding beyond prevailing hypotheses centered on hydrogen ion-driven mechanisms.

08 HYDROGEN↗
DOE OSTI2026

SimH 2 : an integrated techno-economic modeling framework for hydrogen pipeline infrastructure and network optimization

Large-scale hydrogen (H 2 ) pipeline transport design and network optimization have seldom been reported due to the lack of a cost model accounting for the relationship between transport cost and hydrogen mass flow rate. Here, this work introduced a system-level cost model for hydrogen pipeline transport at supercritical state and integrated it with an existing CO 2 pipeline network tool, SimCCS, for hydrogen-specific pipeline design and optimization. The Intermountain West (I-West) region of the U.S., historically dependent on fossil fuel-based economies, is chosen to demonstrate the capabilities of our H 2 pipeline cost model and transport network optimization platform called SimH 2 . Two scenarios are examined: one where the pipeline is not allowed to pass through disadvantaged communities and the other where it is permitted. The results highlight that incorporating disadvantaged-community constraints lead to longer pipeline routes and increased transport costs, reflecting the trade-offs involved in equitable infrastructure development. It is demonstrated that the newly developed SimH 2 tool not only enables the efficient design of H 2 transportation pipelines but also optimizes the network by accounting for local terrain and the presence of disadvantaged areas.

08 HYDROGEN↗
DOE OSTI2026

Disordered hydrogen adsorption at the three-fold site of W(110)

Hydrogen often forms disordered phases on metals; however, deciphering the atomic-scale behavior requires experimental and modeling techniques that directly probe the short-range order between neighboring hydrogen adsorbates. Here, to address this challenge, we applied direct recoil spectroscopy (DRS) to investigate hydrogen adsorption on the W(110) surface. We show that the recoiled hydrogen flux measured during DRS is sensitive to the short range order of the adsorbed hydrogen. Ordered hydrogen neighbors are much more efficient at dechanneling incident ions along low-index surface channels, strongly suppressing the recoiled hydrogen flux along these directions. By modeling the DRS measurements with molecular dynamics for ordered and disordered hydrogen phases, we find that at a hydrogen surface coverage of approximately Θ = 0.6, the hydrogen adsorbates are bound to three-fold sites in a disordered phase at room temperature. This finding is consistent with transfer-matrix scaling model calculations that suggest the transition to an ordered hydrogen phase occurs at a greater surface coverage of Θ = 0.83.

08 HYDROGEN↗