Li 15 P 4 S 16 Cl 3 , a Lithium Chlorothiophosphate as a Solid-State Ionic Conductor

Abstract

Tremendous efforts have been devoted to the design of solid Li + electrolytes and the development of all-solid-state batteries. Compared with conventional Li-ion batteries, which use flammable liquid organic electrolytes, all-solid-state batteries show significant advantages in safety. In this work, a novel lithium chlorothiophosphate compound, Li 15 P 4 S 16 Cl 3 , is discovered. The crystal structure and electrochemical properties are investigated. Li 15 P 4 S 16 Cl 3 can be synthesized as a pure phase via a facile solid-state reaction by heating a ball-milled mixture of Li 2 S, P 2 S 5 , and LiCl at 360 °C. The crystal structure of Li 15 P 4 S 16 Cl 3 was refined against neutron and synchrotron powder X-ray diffraction data, revealing that it crystallizes in the space group $I\bar{4}3d$. Furthermore, the Li + transport in Li 15 P 4 S 16 Cl 3 was also investigated by multiple solid-state NMR methods, including variable-temperature NMR line-shape analysis, NMR relaxometry, and pulsed-field-gradient NMR. Li 15 P 4 S 16 Cl 3 shows good thermodynamic stability and can be synthesized at relatively low temperature. Although it exhibits a low ionic conductivity at room temperature, it can serve as a new motif crystal structure for the design and development of new solid-state electrolytes.