Interfacial stabilization for epitaxial CuCrO 2 delafossites

Abstract

AB O 2 delafossites are fascinating materials that exhibit a wide range of physical properties, including giant Rashba spin splitting and anomalous Hall effects, because of their characteristic layered structures composed of noble metal A and strongly correlated B O 2 sublayers. However, thin film synthesis is known to be extremely challenging owing to their low symmetry rhombohedral structures, which limit the selection of substrates for thin film epitaxy. Hexagonal lattices, such as those provided by Al 2 O 3 (0001) and (111) oriented cubic perovskites, are promising candidates for epitaxy of delafossites. However, the formation of twin domains and impurity phases is hard to suppress, and the nucleation and growth mechanisms thereon have not been studied for the growth of epitaxial delafossites. In this study, we report the epitaxial stabilization of a new interfacial phase formed during pulsed-laser epitaxy of (0001)-oriented CuCrO 2 epitaxial thin films on Al 2 O 3 substrates. Through a combined study using scanning transmission electron microscopy/electron-energy loss spectroscopy and density functional theory calculations, we report that the nucleation of a thermodynamically stable, atomically thick CuCr 1-x Al x O 2 interfacial layer is the critical element for the epitaxy of CuCrO 2 delafossites on Al 2 O 3 substrates. This finding provides key insights into the thermodynamic mechanism for the nucleation of intermixing-induced buffer layers that can be used for the growth of other noble-metal-based delafossites, which are known to be challenging due to the difficulty in initial nucleation.