Evolution of the structural transition in Mo 1–x W x Te 2

Abstract

The composition dependence of the structural transition between the monoclinic 1T' and orthorhombic Td phases in the Mo 1–x W x Te 2 Weyl semimetal was investigated by elastic neutron scattering on single crystals up to x ≈ 0.54. First observed in MoTe 2 , the transition from T d to 1T' is accompanied by an intermediate pseudo-orthorhombic phase, T d *. Upon doping with W, the T d * phase vanishes by x ≈ 0.34. Above this concentration, a phase coexistence behavior with both T d and 1T' is observed instead. The interlayer in-plane positioning parameter δ, which relates to the 1T' β angle, decreases with temperature as well as with W substitution, likely due to strong anharmonicity in the interlayer interactions. As a result, the temperature width of the phase coexistence remains almost constant up to x ≈ 0.54, in contrast to the broadening reported under pressure.