Tacky Elastomers to Enable Tear-Resistant and Autonomous Self-Healing Semiconductor Composites

Abstract

Mechanical failure of π-conjugated polymer thin films is unavoidable under cyclic loading conditions, due to intrinsic defects and poor resistance to crack propagation. Here, the first tear-resistant and room-temperature self-healable semiconducting composite is presented, consisting of conjugated polymers and butyl rubber elastomers. This new composite displays both a record-low elastic modulus (<1 MPa) and ultrahigh deformability with fracture strain above 800%. More importantly, failure behavior is not sensitive to precut notches under deformation. Autonomous self-healing at room temperature, both mechanical and electronic, is demonstrated through the physical contact of two separate films. The composite film also shows device stability in the ambient environment over 5 months due to much-improved barrier property to both oxygen and water. Butyl rubber is broadly applicable to various p-type and n-type semiconducting polymers for fabricating self-healable electronics to provide new resilient electronics that mimic the tear resistance and healable property of human skin.