Large-scale additive manufacturing tooling for extrusion-compression molds

Yeole, Pritesh·Kim, Seokpum·Hassen, Ahmed Arabi·Kumar, Vipin·Kunc, Vlastimil·Vaidya, Uday
View original source ↗Read source document ↗Export metadata ↓

Abstract

Carbon fiber reinforced polymer composites (CFPC) have been used in additive manufacturing (AM) due to both the high-strength-to-weight and superior-stiffness-to-weight ratios. CF AM is being considered for tooling applications. In AM, CFPCs are usually aligned along the deposition direction; however, it results in anisotropic thermal properties which affect the heat transfer and warpage of the final part. In this study, three male molds with different infill patterns were produced via the material extrusion additive manufacturing (EDF-AM) process. These include (a) 0°: infill pattern along the printing direction; (b) 90°: infill pattern perpendicular to the printing direction; and (c) 0°/90°: alternate layers along and perpendicular directions. The effect of the infill pattern on thermal conductivity was analyzed and observed that 0° infill (surface temperature: 79.2°C) had the highest conductivity; and 90° infill (surface temperature: 66.4°C) had the least.

Explore related subjects

36 MATERIALS SCIENCEExtrusion deposition fabrication – additive manufacturingInfill patternThermal conductivity

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Yeole, Pritesh, Kim, Seokpum, Hassen, Ahmed Arabi, Kumar, Vipin, Kunc, Vlastimil, Vaidya, Uday. 2021-09-04. Large-scale additive manufacturing tooling for extrusion-compression molds. https://doi.org/10.1016/j.addlet.2021.100007

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2026

Cyclic moisture reactivation of calcium sorbents for long duration thermochemical energy storage

The transition to a flexible and reliable energy infrastructure, using electro-thermal energy generation technologies such as geothermal, concentrated solar power, and nuclear, usually demands simultaneous advancement of thermal energy storage (TES) to support on-demand electricity generation and industrial applications while mitigating the inherent intermittency of renewable energy sources and power outages from direct energy generation. Among TES technologies, thermochemical energy storage (TCES) based on calcium looping emerges as a compelling high-power energy storage candidate due to its high reaction enthalpy, compatibility with elevated operating temperatures, and abundance of low-cost materials. However, the long-term durability of calcium-based sorbents for TCES is hindered by surface sintering and particle aggregation, leading to performance degradation over repeated thermal cycles. This study explores a moisture hydration-based strategy to regenerate a degraded calcium sorbent and mitigate performance degradation for long duration TCES. The addition of moisture transforms calcium oxide into calcium hydroxide and produces intercalation water layers, associated with a regenerated surface area and reduced calcium oxide crystallite size. Both these effects are beneficial in restoring the sorbents' reactivity for carbonization. Additionally, an optimized hydration-assisted reactivation protocol balances the recovered energy storage capacity with heating penalty required for moisture removal from hydrated samples, resulting in an enhanced energy storage capacity up to 176% compared to benchmark sorbents that undergo cycling without reactivation after 60 cycles. In conclusion, these results highlight the potential of hydration-assisted reactivation to enhance the long-term performance of TCES, providing an effective pathway to advancing electro-thermal storage technologies.

36 MATERIALS SCIENCE↗