Switching CO 2 Electroreduction Selectivity Between C 1 and C 2 Hydrocarbons on Cu Gas-Diffusion Electrodes

Abstract

We report that regulating the selectivity toward a target hydrocarbon product is still the focus of CO 2 electroreduction. Here, we discover that the original surface Cu species in Cu gas-diffusion electrodes plays a more important role than the surface roughness, local pH, and facet in governing the selectivity toward C 1 or C 2 hydrocarbons. The selectivity toward C 2 H 4 progressively increases, while CH 4 decreases steadily upon lowering the Cu oxidation species fraction. At a relatively low electrodeposition voltage of 1.5 V, the Cu gas-diffusion electrode with the highest Cu δ+ /Cu 0 ratio favors the pathways of hydrogenation to form CH 4 with maximum Faradaic efficiency of 65.4% and partial current density of 228 mA cm -2 at -0.83 V vs RHE. At 2.0 V, the Cu gas-diffusion electrode with the lowest Cu δ+ /Cu 0 ratio prefers C–C coupling to form C 2+ products with Faradaic efficiency topping 80.1% at -0.75 V vs RHE, where the Faradaic efficiency of C 2 H 4 accounts for 46.4% and the partial current density of C 2 H 4 achieves 279 mA cm -2 . This work demonstrates that the selectivity from CH 4 to C 2 H 4 is switchable by tuning surface Cu species composition of Cu gas-diffusion electrodes.