Initial ASME code rule analysis on Simple and Full assessment

Abstract

ASME & ASTM codes present simple and full assessment methodologies to qualify nuclear grade graphite components. This report explains the theory behind the statistical portion of the codes and describes the issues discussed in a 2020 workshop in the simple assessment, as well as the full assessment. The methodology for the full assessment was developed by Hindley []. He used a validation methodology to match the experimental average failure load of test specimens from several geometries to the calculated 50% POF load to tune the grouping criteria parameters based on an RMSE penalty function. The grouping criteria consists of a minimum volume to satisfy the weakest link theory of the Weibull distribution and a minimum stress range parameter. Hindley’s work found a minimum link volume of 10 times the grain size and a stress range parameter of 7% [satisfy the validation requirements. Several studies found that the link volume of 10 times the grain size was not satisfactory for the volume grouping criteria for graphite grades with fine grains. ASME 2021 code adopted a new volume grouping criteria based on fracture toughness for calculation of the process zone volume. However, errors were found in the ASME 2021 code process zone volume equation and the question is now open as to what volume grouping criteria is satisfactory. This report presents results from sensitivity studies that were done to evaluate the volume grouping criteria effect on the full assessment POF. This report also presents results from sensitivity studies on other aspects of the code that affect the POF, the mesh size and the choice of the Weibull threshold parameter. All three sensitivity studies: the volume grouping criteria, the mesh size, and the threshold parameter choice are found to affect the component qualification decision for components of structural reliability class 1 (SRC-1). The sensitivity analysis results are presented in the body of the report for NBG-18, which is the same grade of graphite as Hindley used in his thesis. Results from NBG-17, IG-110, 2114, and PCEA are presented in the Appendix. For NBG-18, it was found that increasing the threshold increases the POF, finer meshes result in higher POFs, and that smaller link volume requirements lead to higher POFs (which is inconsistent with Hindley’s findings). This report proposes a new validation study similar to Hindley’s []. The purpose of the new validation study is to tune the threshold, mesh size and grouping criteria based on results from multiple grades of graphite, including finer grain graphites T220 (1-3 microns) and NG-CT-50 (5 microns). The test specimens will be broken at 3 labs, such that we can measure between lab measurement variability, with at least 5 test specimens per lab such that the within lab uncertainty can also be measured. Hindley’s validation method tried matching the average experimental load with the median. The future study will attempt to match failures at lower percentiles, which would be closer to the SRC POF limit. We are currently looking into what geometries make sense and the best method to measure multi-axial stress states. These design decisions are still being set.