Stable bismuth-antimony alloy cathode with a conversion-dissolution/deposition mechanism for high-performance zinc batteries

Abstract

Although a large number of intercalation cathode materials for aqueous Zn batteries have been reported, limited intercalation capacity precludes achieving a higher energy density. Here, for this work, we develop a high-performance aqueous Zn battery based on BiSb alloy (Bi 0.5 Sb 0.5 ) using a high-concentrated strong-basic polyelectrolyte. We demonstrate that a conversion-dissolution/deposition electrochemical mechanism (BiSb ↔ Bi + SbO 2 – ↔ Bi + SbO 3 – ↔ Bi 2 O 3 ) through in situ X-ray diffraction (XRD), Raman, and ex-situ X-ray photoelectron spectrometry (XPS) characterizations with the help of density functional theory calculations. The BiSb cathode delivers large capacity of 512 mAh g –1 at 0.3 Ag –1 and superior rate capability of 90 mAh g –1 even at 20 Ag –1 , and long-term cyclability with capacity retentions of 184 mAh g –1 after 600 cycles at 0.5 Ag –1 and 130 mAh g –1 after 1300 cycles at 1 Ag –1 . Remarkably, even at temperatures as low as –10 and –20 °C, capacities of 210 and 197 mAh g –1 are reserved at 1 Ag –1 , respectively. Moreover, the prepared pouch Zn//BiSb battery delivers a high energy density of 303 Wh kg –1 BiSb at 0.3 Ag –1 . When coupled with a high concentration polyelectrolyte, the Zn/BiSb battery exhibits an excellent performance over a wide temperature range (–40 to 40 °C). Our research reveals the metal cathode is promising for Zn batteries to achieve a high performance with the unique mechanism and alloys can be an effective approach to stabilize metal electrodes for cycling.