Material and Design Optimization of Printed Melt Wire Arrays

Abstract

Recent work conducted by the Advanced Sensors and Instrumentation (ASI) program at Idaho National Laboratory resulted in the establishment of in-house capabilities for fabricating and testing new advanced manufactured sensors for measuring irradiation temperatures inside a nuclear test reactor. Though current methods of real-time temperature monitoring (e.g., thermocouples) can still be used, the complexity of the feedthroughs and attachments needed for collecting real time measurements greatly increases the experiment-related costs. On the other hand, passive monitoring techniques can be used for collecting post irradiation temperature measurements by inferring reactor temperatures, based on the melting points of well-characterized materials (i.e., standard melt wires). However, challenges have arisen due to the limited space available for including instrumentation in experiments. To resolve this issue, the ASI program expanded its temperature detection capabilities to include advance manufactured melt wires for post-irradiation temperature measurements. These melt wires can determine reactor temperatures while also accommodating space limitations in irradiation experiments. To improve performance reliability and enhance melt wire readability following irradiation, FY-22 efforts have focused on optimizing the materials used in the encapsulation and printed melt wire array. This report details the design and fabrication tasks, along with the subsequent x ray computed tomography (XCT) evaluation process. The melt wire array consisted of indium with a melting point of 157°C, indium/silver (96/4 at%) with a melting point of 219°C, and tin with a melting point of 230°C. The encapsulation disc was made of vanadium due to its low activation properties and radiation resistance when deployed in nuclear reactors. Additionally, the melt wire design consisted of a ceramic sublayer (alumina disc) to further enhance the XCT post melting images of the printed melt wires. However, when sealing the vanadium container, all three melt wires melted, reflecting the temperature limitations that must be considered when employing metal containers in the sealing process.