High Strength Aluminum Additive Manufacturing

Abstract

High-strength aluminum alloys for elevated temperature applications are desirable to replace heavier and more expensive titanium alloys. However, most aluminum alloys lose a large fraction of their strength at temperatures above approximately 200°C. ORNL has designed DuAlumin-3D, an alloy with nominal composition Al-9Ce-4Ni-0.5Mn-1Zr (wt.%), which utilizes the high cooling rates in additive manufacturing (AM) to achieve a refined microstructure, and thermally stable mechanical properties. DuAlumin-3D was fabricated by laser powder bed fusion and tested for its tensile mechanical properties across a range of temperature, and for its room temperature high-cycle fatigue resistance. The alloy was tested in both the as-printed and heat treated conditions, and both parallel and perpendicular to the AM build direction. The alloy was found to have anisotropic mechanical behavior in the as-printed state, but the anisotropy significantly decreased (both for tensile and fatigue properties) following heat treatment. The tensile properties significantly out-performed benchmark wrought 2219-T61 across a wide temperature range. The room temperature fatigue performance was approximately similar to 2219-T61.