Ce- and Ni-Codoped Double PrBaMn 2 O 5 Perovskite as a Ceramic SOFC Anode

Abstract

This study explores the efficacy of cerium introduction, both on its own and in combination with nickel, into PrBaMn 2 O 5+δ (PBM) structures to enhance solid oxide fuel cell (SOFC) anodes. We synthesized Pr 1–x Ce x BaMn 2 O 5+δ compositions for x values of 0.05 (PrCe5) and 0.1 (PrCe10), as well as a nickel-doped variant (PrCe5Ni), assessing their performance under H 2 – 3% H 2 O reducing conditions pertinent to SOFC anode operations. Our findings reveal that the PrCe5 composition exhibits a thermal expansion coefficient (TEC) that not only improves upon that of the Ce-free counterpart but also aligns closely with the TEC standards of prevalent SOFC electrolytes. A notable advancement was achieved with the application of a 3.5 μm gadoliniadoped ceria (GDC) buffer layer through physical vapor deposition, effectively mitigating chemical interactions between PBM-based anodes and yttria-stabilized zirconia (YSZ) electrolytes, a concern highlighted by in situ neutron diffraction analyses. Electrochemical impedance spectroscopy, conducted over 220 h in a H 2 –3% H 2 O atmosphere at 750 °C, demonstrated that the optimal 3.5 μm thickness of the GDC buffer layer significantly minimizes the area-specific resistance (ASR) degradation rate to 0.002 Ω cm 2 /h, markedly outperforming both thinner (1 μm) and thicker (8 μm) GDC layers, which showed higher degradation rates of 0.15–0.2 Ω cm 2 /h due to the diffusion of Ba ions or delamination. Moreover, cerium doping fosters superior microstructural stability and obviates barium diffusion, thereby suggesting an enhanced durability of the doped anodes over their lifespan. Integrating nickel into the PrCe5 structure halved the ASR to 0.5 Ω cm 2 at 750 °C, situating it well within the ideal performance range for SOFC anodes. Furthermore, the enhancement brought about by simultaneously doping PBM with cerium and nickel, which fundamentally relies on the critical contributions of defect chemistry and crystal structure, highlights the significance of these fields in creating sophisticated materials for energy related applications.

Explore related subjects

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Managutti, Praveen B., Wen, Yeting, Hansen, Thomas C., Dorcet, Vincent, Paofai, Serge, Briois, Pascal, Huang, Kevin, Bahout, Mona. 2024-04-30. Ce- and Ni-Codoped Double PrBaMn 2 O 5 Perovskite as a Ceramic SOFC Anode. https://doi.org/10.1021/acsaem.4c00111

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

An immersed interface method for microstructure-scale electrochemical battery models: numerical formulation and performance portable implementation

We present the numerical formulation, verification, and performance portable implementation of an immersed interface method for microstructure scale electrochemical modeling of batteries. The innovation in this approach is the resolution of chemical species and electrostatic potential discontinuities at active interfaces without the use of interface conforming unstructured grids. A unified formulation on Cartesian grids for all domains (electrodes and electrolyte) is used with interfacial flux conditions applied using volume fraction or “color” function gradients. We have developed one dimensional and two dimensional test cases with analytic solutions for electrochemical modeling using which we verified the consistency and accuracy of our scheme. Our solver is also validated against solutions from a macroscale model and an unstructured multi-subdomain solver for a full lithium ion cell. We then demonstrated the utility of our solver on an image-based complex battery electrode microstructure at high charging rate. Our technique also exhibits good scalability on distributed memory architectures using central processing units (CPU), with problem sizes up to 1.8 billion degrees of freedom and with 5400 ranks. Initial performance studies of our open-source performance portable solver showed about 70 times speed up using a graphics processing unit (GPU) compared to single compute core for a problem with 4 million cells.

25 ENERGY STORAGE↗

Solvation-guided inhibition of manganese dissolution of lithium- and manganese- rich cathode via cyclic carbonate molecular engineering

Lithium and manganese-rich (LMR) layered oxides represent a leading class of high-energy cathode materials, but their practical realization is fundamentally limited by severe manganese (Mn) dissolution, a process that triggers structural degradation and rapid capacity fade. While mitigation efforts have predominantly focused on interfacial engineering, the intrinsic contribution of bulk electrolyte solvation to this degradation pathway remains largely unexplored, primarily due to the difficulty of deconvolving its effects from concurrent cathode-electrolyte interphase (CEI) formation. Here, we report an experimental design to isolate the role of solvation. We systematically varied the electrolyte solvent solvation power by substituting the strongly coordinating ethylene carbonate (EC) with its weaker coordinating fluorinated derivatives, fluoroethylene carbonate (FEC) and trans-4,5-Difluoro-1,3-dioxolan-2-one (DFEC), while maintaining a consistent interfacial chemistry. Remarkably, the electrolyte formulated with the weakest solvent, DFEC, exhibits superior cycling stability, suppressing Mn dissolution by up to 63% relative to the conventional EC-based system. Post-mortem analysis unequivocally attributes this performance enhancement to the preservation of the LMR cathode's structural integrity, a direct consequence of mitigated Mn dissolution. This work provides conclusive evidence that modulating bulk electrolyte solvation is a potent and direct strategy for stabilizing LMR cathodes, establishing a vital design principle for next-generation battery systems.

25 ENERGY STORAGE↗

Geothermal district energy systems coupled with seasonal underground thermal energy storage: a U.S. techno-economic screening by climate and geology

In the United States, cooling-dominated commercial building loads can cause geothermal heat pump-based district energy systems to accumulate a long-term subsurface thermal imbalance, motivating the incorporation of seasonal underground thermal energy storage. We developed a transferable workflow to evaluate geothermal district systems that pair ground heat exchangers with seasonal underground thermal energy storage. Using standardized hourly loads for seven commercial buildings and a uniform cost framework, we simulated ten U.S. cities with a physics-based ground heat exchanger model, subsurface storage simulations, and economic assessment to isolate the roles of climate and hydrogeology. In cooling-dominated cities, underground thermal energy storage supplied the majority of annual cooling, cutting electricity use and summer peaks substantially while achieving levelized costs comparable to or below conventional chiller-boiler plants. In cooler climates, the storage share shrunk, required borefield size and costs rose, and levelized cost of energy increased nearly linearly with declining underground thermal energy storage fraction, indicating storage fraction as the primary economic lever. Sensitivity analysis showed capital risk dominated by borefield drilling and surface heating, ventilation, and air-conditioning and piping, with underground thermal energy storage costs secondary. This workflow provides a transparent foundation for site-specific design and screening of next-generation geothermal district energy systems.

25 ENERGY STORAGE↗