Discerning structure sensitivity of Ni-core Pd-shell nanoparticles for enhanced nitrite reduction

Abstract

Denitrification using Pd-based catalysts converts N-oxyanions into harmless products. However, the metal cost and scarcity are barriers to application. In this work, we synthesize water-suspended, structure-controlled Ni-core/Pd-shell nanoparticles (Ni@Pd NPs) that show Pd-catalyzed nitrite (NO 2 − ) reduction catalysis promoted by Ni. The NPs immobilized on Al 2 O 3 (0.47 wt % Pd and 0.74 wt % Ni) have higher NH 4 + selectivity and higher catalytic activity than wet-impregnated Pd/Al 2 O 3 (1.0 wt % Pd), i.e., 315.4 vs. 132.1 Lg surface Pd −1 min −1 . X-ray photoelectron spectroscopy (XPS) and CO-diffuse reflectance infrared Fourier transform spectroscopy (CO-DRIFTS) analyses show that Ni increases Pd electron density, which is proposed to lower the bond dissociation energy barrier for nitric oxide surface intermediate. Low-coordinated Pd atoms correlate to high activity and low NH 4 + selectivity. Using CatCost software, we estimate Ni@Pd/Al 2 O 3 to have a ∼40% lower manufacturing cost compared to wet-impregnated Pd/Al 2 O 3 . This rationally designed catalyst illustrates how nickel promotes Pd catalysis and how Pd usage can be lowered for denitrification and other hydrogenation reactions.