Defect Engineering in Large‐Scale CVD‐Grown Hexagonal Boron Nitride: Formation, Spectroscopy, and Spin Relaxation Dynamics

Vlassiouk, Ivan V. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000254940386)·Wu, Yueh‐Chun [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000292996882)·Puretzky, Alexander [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000299964429)·Liang, Liangbo [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000311990049)·Lasseter, John C. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)]·Dryzhakov, Bogdan [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000221564396)·Gallagher, Ian [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000335045594)·Ghosh, Sujoy [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000328948971)·Lavrik, Nickolay [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000295435634)·Dyck, Ondrej [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000182009874)·Lupini, Andrew R. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000218747925)·Checa Nualart, Marti [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000326076866)·Collins, Liam [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000349469195)·Meyer III, Harry M. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000349941664)·Zhao, Huan [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000249820865)·Likhi, Farzana [Univ. of Houston, TX (United States)]·Xiao, Kai [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000204028276)·Ivanov, Ilia [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000267262502)·Glasgow, David [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000263343639)·Tselev, Alexander [Univ. of Aveiro (Portugal)]·Lawrie, Benjamin [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:000000031431066X)·Smirnov, Sergei N. [New Mexico State Univ., Las Cruces, NM (United States)]·Randolph, Steven J. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)]
View original source ↗Read source document ↗Export metadata ↓

Abstract

Recently, numerous techniques have been reported for generating optically active defects in exfoliated hexagonal boron nitride (hBN), which hold transformative potential for quantum photonic devices. However, achieving on-demand generation of desirable defect types in scalable hBN films remains a significant challenge. Here, it is demonstrated that formation of negative boron vacancy defects, V B − , in suspended, large-area CVD-grown hBN is strongly dependent on the type of bombarding particles (ions, neutrons, and electrons) and irradiation conditions. In contrast to suspended hBN, defect formation in substrate-supported hBN is more complex due to the uncontrollable generation of secondary particles from the substrate, and the outcome strongly depends on the thickness of the hBN. Different defect types are identified by correlating spectroscopic and optically detected magnetic resonance features, distinguishing boron vacancies (formed by light ions and neutrons and emitting at 800 nm) from other optically active defects emitting at 650 nm assigned to anti-site nitrogen vacancy (N B V N ) and reveal the presence of additional “dark” paramagnetic defects that influence spin-lattice relaxation time (T 1 ) and zero-field splitting parameters, all of which strongly depend on the defect density. These results underscore the potential for precisely engineered defect formation in large-scale CVD-grown hBN, paving the way for the scalable fabrication of quantum photonic devices.

Explore related subjects

CVDODMRRamanbombardmentdefectshBNphotoluminescence

Keep this discovery

Explore connections, maps & timelines

BibTeXRIS

Vlassiouk, Ivan V. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000254940386), Wu, Yueh‐Chun [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000292996882), Puretzky, Alexander [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000299964429), Liang, Liangbo [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000311990049), Lasseter, John C. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)], Dryzhakov, Bogdan [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000221564396), Gallagher, Ian [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000335045594), Ghosh, Sujoy [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000328948971), Lavrik, Nickolay [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000295435634), Dyck, Ondrej [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000182009874), Lupini, Andrew R. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000218747925), Checa Nualart, Marti [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000326076866), Collins, Liam [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000349469195), Meyer III, Harry M. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000349941664), Zhao, Huan [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000249820865), Likhi, Farzana [Univ. of Houston, TX (United States)], Xiao, Kai [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000204028276), Ivanov, Ilia [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:0000000267262502), Glasgow, David [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000263343639), Tselev, Alexander [Univ. of Aveiro (Portugal)], Lawrie, Benjamin [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)] (ORCID:000000031431066X), Smirnov, Sergei N. [New Mexico State Univ., Las Cruces, NM (United States)], Randolph, Steven J. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). Center for Nanophase Materials Sciences (CNMS)]. 2025-10-31. Defect Engineering in Large‐Scale CVD‐Grown Hexagonal Boron Nitride: Formation, Spectroscopy, and Spin Relaxation Dynamics. https://doi.org/10.1002/smll.202506874

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related reports

DOE OSTI2025

Comparing approaches for introducing polycyclic aromatic hydrocarbons to Ge(001) to seed graphene nanoribbon synthesis by CH 4 chemical vapor deposition

Here, we evaluate two approaches for introducing polycyclic aromatic hydrocarbons (PAHs) to a graphene catalyst substrate as part of a two-step chemical vapor deposition (CVD) process for growing graphene nanoribbons (GNRs). In this process, PAHs first form graphene-like seeds on Ge, and then GNRs are subsequently evolved from these PAH-derived seeds via substrate-mediated anisotropic growth kinetics during the CVD of CH4. The first seeding approach sublimes controlled doses of PAH thin films into the CVD chamber, while the second delivers PAHs directly from the vapor phase at set concentrations. Using these two approaches, we measure the dependence of GNR density on PAH dose and compare the experimental results with predictions from a rate model of PAH diffusion, desorption, and clustering. We find that PAHs that more strongly adsorb to the catalyst surface (generally larger PAHs) desirably remain more individualized prior to GNR evolution whereas smaller, more weakly bound PAHs aggregate into larger clusters with various sizes on Ge that are undesirable for synthesizing more monodisperse GNRs. As a result, this work is important because it offers a framework that enables the rational selection and design of seed molecules, advancing anisotropic GNR CVD synthesis.

CVD↗
DOE OSTI2025

Tuning transition metal nanoparticles on a non-traditional support via experimental design

The ability to control metal nanoparticle size and morphology on supported catalysts is crucial for optimizing catalytic performance in targeted applications. Here, this work presents a systematic approach for tuning Ni particle and crystallite size on an unconventional, low-porosity silica fume support through select thermal treatments. The catalyst was synthesized via the deposition of nickelocene onto silica fume, resulting in well-dispersed Ni nanoparticles. A face-centered central composite design was employed to systematically assess the effects of time, temperature, and sintering gas environment on metal particle growth. The results demonstrate that the sintering gas environment is the primary factor governing particle and crystallite evolution, with temperature as the next most significant influence. Nickel nanoparticles sintered at temperatures of 650 °C and above under inert conditions exhibited substantial growth and polycrystalline structures, whereas samples treated in oxidative environments formed NiO, restricting particle mobility. Minimally oxidative (500 ppm O₂) environments facilitated rapid sintering while effectively removing residual ligands from the one-step nickelocene deposition process. Extensive structural characterization via a combination of scanning transmission electron microscopy, X-ray diffraction, hydrogen temperature programmed reduction, and small-angle X-ray scattering revealed that oxidative treatments enhanced metal-support interactions, as evidenced by increased reduction temperatures and narrower particle size distributions. These findings establish quantitative relationships between sintering parameters and Ni nanoparticle characteristics, providing a framework for rational catalyst design through controlled thermal treatments. This methodology is broadly applicable to other catalytic systems and provides a quantitative foundation for catalyst design.

CVD↗
DOE OSTI2025

Bottom-up fabrication of scalable room-temperature diamond quantum computing and sensing technologies

The nitrogen-vacancy (NV) centre in diamond is a premier solid-state defect for quantum information processing and metrology. An integrated diamond quantum device harnesses the collective properties of multiple NV centres, enabling room-temperature quantum computing and sensing. While large-scale devices are poised to fill an important gap in the burgeoning quantum technology landscape, their practical realisation has not been achieved using current top-down fabrication techniques such as ion implantation. Consequently, this necessitates the development of a bottom-up fabrication technique, which is scalable, deterministic, and possesses atomic-scale precision. Informed by existing methods for fabricating phosphorous defect qubits in silicon, we envision a hydrogen depassivation lithography technique for atomically-precise manufacturing of nitrogen-vacancy centres in diamond. This perspective article outlines a viable multi-step procedure for realising scalable fabrication of diamond quantum devices and identifies the key challenges in its development.

CVD↗