Microstructure-dependent particulate populations in ODS steels revealed by single-particle ICP-TOF-MS

Brubaker, Zach E. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000256293119)·Szakas, Sarah E. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000241332197)·Hewitt, Josh [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0009000751413189)·Moseley, Duncan H. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000343518347)·Hoelzer, David T. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000193669958)·Manard, Benjamin T. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000207400627)
View original source ↗Read source document ↗Export metadata ↓

Abstract

In this work, we evaluated the ability of single-particle inductively coupled plasma time-of-flight mass spectrometry (SP-ICP-TOF-MS) to characterize particulates generated from 300 series stainless steels and oxide dispersion–strengthened (ODS) steels. Particulates were produced using two different rotary tools (cutting disk and grinding bit) to assess the influence of particle generation on effluent particulates. Across all materials and preparation techniques, SP-ICP-TOF-MS detected a substantial population of particles containing the expected constituent elements, with average compositions closely matching the nominal alloy values. A secondary population of Y-bearing particles was evident in ODS steels; their formation is strongly favored in particulates generated using the grinding bit. Specifically, in PM2000, Y-bearing particles were predominantly colocated with Al, whereas in 14YWT, Y-bearing particles were less frequently Fe-free but showed stronger colocation with Ti. These trends are consistent with the known microstructural differences between Y–Al–O oxide particles in PM2000 and finer Y–Ti–O nanoclusters in 14YWT. Together, these results demonstrate that SP-ICP-TOF-MS can resolve distinct particulate populations in complex, multicomponent steels at the femtogram mass scale, enabling particle-resolved insight into microstructure-driven phase separation and preparation-dependent particle generation.

Keep this discovery

BibTeXRIS

Brubaker, Zach E. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000256293119), Szakas, Sarah E. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000241332197), Hewitt, Josh [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0009000751413189), Moseley, Duncan H. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000343518347), Hoelzer, David T. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000193669958), Manard, Benjamin T. [Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)] (ORCID:0000000207400627). 2026-06-15. Microstructure-dependent particulate populations in ODS steels revealed by single-particle ICP-TOF-MS. https://doi.org/10.1039/d6ja00117c

Cite the original work for its findings. Save a collection to share your selection of sources.

KEEP EXPLORING

Related discoveries

DOE OSTI2025

A Review of the Influence of Processing Parameters on ODS Steels Produced via Additive Manufacturing Techniques

Abstract This paper reviews current observations regarding processing conditions for oxide dispersion-strengthened steels consolidated through additive manufacturing techniques. Variations in ODS steels observed across process parameters include changes in grain size, grain texture, oxide size, density of oxides, porosity, melt pool characteristics, and mechanical properties. These properties were then compared across techniques to understand which techniques and processing conditions lead to the highest strength, ductility, and oxide density. Current literature suggests that a mix of grain types, in the form of either morphology or phase, can significantly increase the strength of printed ODS steels. Meanwhile, the most ductile samples, regardless of consolidation technique or matrix material, were made from feedstock with oxide additions located on the powder surface. Reported grain and oxide sizes were plotted against the ratio of laser power to scan speed, volumetric energy density, and normalized enthalpy. No strong correlation between these values and microstructural features was observed. The plots that were made suggest that a larger data set, more in-depth representative equations, and more defined material properties as a function of specific feedstock used are necessary to determine a value that can be correlated to the printed ODS steel microstructure.

deJong, Matthew↗
DOE OSTI2026

Process control-enabled mitigation of microstructural and plastic heterogeneities in additively manufactured Grade 91 steel

Synergizing wire arc-directed energy deposition (WA-DED) additive manufacturing (AM) with particle-strengthened creep strength-enhanced ferritic (CSEF) steels enables fabrication and repair of critical power-plant components. Investigations focused on fusion-welded particle-strengthened CSEF steels, such as Grade 91 steel, have linked microstructurally heterogeneous regions—forming due to heat affected zones (HAZ)—with premature failure during elevated temperature service. Fusion-based AM, including WA-DED, likewise generates microstructurally and plastically heterogeneous regions due to spatiotemporally varying thermokinetics during deposition. However, works investigating such microstructural heterogeneities, their implications for mechanical behavior, and strategies to mitigate their formation remain scarce. This work identifies microstructurally and plastically heterogeneous regions within the WA-DED-processed Grade 91 steel. Spatial microhardness variations in the as-fabricated specimen correlate with the variation in the attributes of grain, martensitic microstructure, and precipitates across the fusion zone and HAZ. Digital image correlation-enabled tensile tests performed at 500 °C revealed pronounced deformation localization and a wave-like strain distribution, with wavelength close to the melt pool depth, indicating susceptibility of the as-fabricated components to premature creep failure. Such heterogeneity in microstructural and mechanical behavior was attributed to recurring solid-state phase transformations. Subsequently, an interlayer temperature control strategy was implemented, wherein maintaining interlayer temperature above the martensitic start temperature mitigated the heterogeneous microstructural and plastic response in the as-fabricated condition. Findings open pathways to achieving deformation-localization- and creep-resistant microstructures in WA-DED fabricated particle-strengthened CSEF steel components, reducing reliance on post-welding heat treatments—conventionally required to enhance creep resistance—and enabling on-demand, short lead-time fabrication of next-generation power-plant components.

Heat affected zones↗
NASA NTRS2026

Influences of Introduced Yttrium Oxide Particles on Superalloy 718

Additive manufacturing has proven useful for introducing oxide particles into superalloys, to provide oxide dispersion strengthening (ODS) at high temperatures. This study screened how such an approach can influence microstructure and failure modes for superalloy 718. The objective of this study was to compare tensile and creep failure modes for additively manufactured superalloy 718 having introduced oxide particles. Fine yttrium-oxide (yttria) particles were introduced into 718 powder using two different powder mixing methods. Additive manufacturing by laser powder bed fusion was then used to prepare specimen blanks for each case, oriented parallel and transverse to the building direction. These were subsequently given consistent stress relief, hot isostatic pressurization, and final heat treatments, then subjected to tensile and creep tests at varied temperatures. Additively manufactured 718 without ODS (“no-ODS”) had nearly equiaxed grains at 50 μm in width. Roll-mixed ODS material had a bimodal grain size distribution, with fine grains at 9 μm and coarse grains at 66 μm in average width. The fine grains were elongated about 5x in the building direction. Acoustic-mixed ODS materials had grains at 10 μm in width that were elongated about 10x in the build direction. Compared to no-ODS, roll-mixed and acoustic mixed ODS materials did not show improved tensile strengths at room temperature, 760 °C, and 1093 °C. The tensile failure strains parallel to the building direction of roll-mixed ODS material were lowest in these tests. Flattened clumps of yttria had formed transverse to the building direction in roll-mixed material, which were easily cracked. Creep rupture response at 760 °C in the building direction was highest for acoustic-mixed material test. Creep tests at 1093 °C showed varied results, with low rupture lives associated with enhanced cavitation at grain boundaries and surface oxidation. Transverse to the building direction, all three materials had low failure strains in tests at 760 °C. The elongated grain boundaries failed readily in all transverse specimens tested at 760 °C and 1093 °C.

oxide dispersion strengthening↗