Influences of Introduced Yttrium Oxide Particles on Superalloy 718

Timothy P Gabb·Christopher A Kantzos·Timothy M Smith·Henry C Degroh III·Aaron C Thompson
View original source ↗Read source document ↗Export metadata ↓

Abstract

Additive manufacturing has proven useful for introducing oxide particles into superalloys, to provide oxide dispersion strengthening (ODS) at high temperatures. This study screened how such an approach can influence microstructure and failure modes for superalloy 718. The objective of this study was to compare tensile and creep failure modes for additively manufactured superalloy 718 having introduced oxide particles. Fine yttrium-oxide (yttria) particles were introduced into 718 powder using two different powder mixing methods. Additive manufacturing by laser powder bed fusion was then used to prepare specimen blanks for each case, oriented parallel and transverse to the building direction. These were subsequently given consistent stress relief, hot isostatic pressurization, and final heat treatments, then subjected to tensile and creep tests at varied temperatures. Additively manufactured 718 without ODS (“no-ODS”) had nearly equiaxed grains at 50 μm in width. Roll-mixed ODS material had a bimodal grain size distribution, with fine grains at 9 μm and coarse grains at 66 μm in average width. The fine grains were elongated about 5x in the building direction. Acoustic-mixed ODS materials had grains at 10 μm in width that were elongated about 10x in the build direction. Compared to no-ODS, roll-mixed and acoustic mixed ODS materials did not show improved tensile strengths at room temperature, 760 °C, and 1093 °C. The tensile failure strains parallel to the building direction of roll-mixed ODS material were lowest in these tests. Flattened clumps of yttria had formed transverse to the building direction in roll-mixed material, which were easily cracked. Creep rupture response at 760 °C in the building direction was highest for acoustic-mixed material test. Creep tests at 1093 °C showed varied results, with low rupture lives associated with enhanced cavitation at grain boundaries and surface oxidation. Transverse to the building direction, all three materials had low failure strains in tests at 760 °C. The elongated grain boundaries failed readily in all transverse specimens tested at 760 °C and 1093 °C.

Explore related subjects

oxide dispersion strengtheningadditive manufacturingsupper alloys

Keep this discovery

BibTeXRIS

Timothy P Gabb, Christopher A Kantzos, Timothy M Smith, Henry C Degroh III, Aaron C Thompson. 2026-07-01. Influences of Introduced Yttrium Oxide Particles on Superalloy 718. https://ntrs.nasa.gov/citations/20260001480

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

Additive Manufacturing subjectOxide Dispersion Strengthening subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

NASA NTRS2026

A Dispersion-Strengthened Low-Density Niobium Alloy and Its Elevated Temperature Mechanical Performance

In response to the elevated-temperature and weight-reduction demands of modern aerospace applications, a novel oxide-dispersion-strengthened low-density niobium alloy (LDNb-ODS) was fabricated using laser powder bed fusion (L-PBF). To overcome powder procurement barriers, L-PBF feedstock was produced by blending commercial Nb521, Ti64, and Cr powder with Y2O3 nanoparticles via resonant acoustic mixing. Following L-PBF and a 1400°C vacuum heat treatment, the alloy achieved a density of 6.73 g/cc and a fine mean grain size of 4.62 µm stabilized by uniform ~30 nm yttria dispersoids. Microstructural analysis revealed a chemically inhomogeneous build with lack-of-fusion defects and a titanium (Ti) shift from a nominal 31.5 wt% in the starting powder blend to 24.8 wt% in the printed part due to preferential Ti loss during printing. Elevated-temperature tensile testing demonstrated that LDNb-ODS maintained a superior specific yield strength of 60-85 MPa/(g/cc) up to 800°C, outperforming nickel-based alloys Ni625, Ni230, and GRX-810. Between 870°C and 950°C, its specific strength surpassed both Ni718 and Ni625. In rapid stress-rupture testing at 1093°C and 20.7 MPa, uncoated LDNb-ODS survived 21.4 hours (a tenfold increase over legacy C-103) while an R512E silicide coating extended rupture life to 84.8 hours, confirming that oxidation accelerates low-stress failure. These findings demonstrate that additive manufacturing of LDNb-ODS provides a viable, lightweight alternative to nickel-based superalloys for high-temperature (>850°C) aerospace components.

Low Density Niobium Alloy↗
NASA NTRS2026

List of Commercial and Advanced Developmental Niobium-Based Alloys of the Space Age

This report compiles a list of commercial and developmental niobium-based alloys developed during the Space Age (late 1950s through mid-1970s) for extreme-temperature applications, including rocket engine thrust chambers, hypersonic re-entry thermal protection systems, and space fission reactor loops. Niobium (Nb) was widely pursued because it provided the lowest density (~8.6 g/cc) among the primary refractory metals, a high melting temperature (~2470°C), exceptional low-temperature ductility, good formability, and compatibility with liquid alkali metals. An evaluation of physical metallurgy mechanisms, focusing on solid-solution strengthening via heavy refractory solutes (W, Mo, Ta), dual-purpose reactive solutes (Hf, Zr, Ti), and dispersion strengthening using carbides, nitrides, and oxides is presented. Additionally, the report compares Western and Soviet Union metallurgical approaches, explaining how supply chain factors and manufacturing infrastructure influenced element selection, interstitial chemistry, and alloy identification/naming conventions. Cataloging these historical alloy chemical compositions serves as a foundational reference for modern alloy additive manufacturing, thermodynamic CALPHAD modeling, and machine-learning discovery pipelines for next-generation extreme-environment niobium-based alloys.

Physical Metallurgy↗
DOE OSTI2025

A Review of the Influence of Processing Parameters on ODS Steels Produced via Additive Manufacturing Techniques

Abstract This paper reviews current observations regarding processing conditions for oxide dispersion-strengthened steels consolidated through additive manufacturing techniques. Variations in ODS steels observed across process parameters include changes in grain size, grain texture, oxide size, density of oxides, porosity, melt pool characteristics, and mechanical properties. These properties were then compared across techniques to understand which techniques and processing conditions lead to the highest strength, ductility, and oxide density. Current literature suggests that a mix of grain types, in the form of either morphology or phase, can significantly increase the strength of printed ODS steels. Meanwhile, the most ductile samples, regardless of consolidation technique or matrix material, were made from feedstock with oxide additions located on the powder surface. Reported grain and oxide sizes were plotted against the ratio of laser power to scan speed, volumetric energy density, and normalized enthalpy. No strong correlation between these values and microstructural features was observed. The plots that were made suggest that a larger data set, more in-depth representative equations, and more defined material properties as a function of specific feedstock used are necessary to determine a value that can be correlated to the printed ODS steel microstructure.

deJong, Matthew↗