Microstructure prediction for Ti-22Al-25Nb in laser powder bed fusion

Abstract

This work presents a physics-informed framework for predicting solidification morphology and defect susceptibility in additively manufactured Ti–22Al–25Nb across a broad processing space. The framework integrates solidification microstructure selection (SMS) analysis with a single-track defect-based printability map to establish a unified methodology linking processing parameters to both interfacial morphology and manufacturability. Thermal gradients G and solidification rates R are first computed using the Thermo-Calc Additive Manufacturing (TC-AM) module, a finite-interface-dissipation (FID) phase-field (PF) model coupled with CALPHAD method is then employed to systematically distinguish planar and dendritic regimes as functions of $G$ and $R$. By superimposing the printability map onto the morphology projections, a comprehensive process–structure framework is obtained. Across most processing conditions, the predicted microstructure is predominantly dendritic, while planar growth emerges only under selected laser power $P$ and scan speed $v$ combinations. In addition to morphology classification, the framework quantifies the dendritic area fraction and introduces a width-based morphology descriptor to characterize the spatial extent of planar/dendritic regions within the melt pool. It provides mechanistic insight into the interplay between solidification physics and defect formation, offering practical guidance for parameter selection and microstructural control in Ti–22Al–25Nb additive manufacturing (AM).