Atmospheric Plasma for Cathode Relithiation & Up Cycling: Cooperative Research and Development (Final Report)

Brow, Ryan [National Laboratory of the Rockies (NLR), Golden, CO (United States)] (ORCID:0000000159842446)
View original source ↗Read source document ↗Export metadata ↓

Abstract

The Parties are working together to utilize a one-step atmospheric microplasma reaction for the elimination of electrolyte degradation products and the relithiation of end-of-life cathode materials. This project aims to streamline the direct recycling process of battery components by reducing the required steps and time.

Explore related subjects

25 ENERGY STORAGEargon ionscathode electrolyte interphase (CEI)cathode recyclingCRADAelectrochemical propertiesmicroplasma reactionnickel manganese cobalt (NMC)plasmapouch cellsrelithiationx-ray photoelectron spectroscopy (XPS)

Keep this discovery

BibTeXRIS

Brow, Ryan [National Laboratory of the Rockies (NLR), Golden, CO (United States)] (ORCID:0000000159842446). 2026-07-28. Atmospheric Plasma for Cathode Relithiation & Up Cycling: Cooperative Research and Development (Final Report). https://doi.org/10.66816/tp3080069

Cite the original work for its findings. Save a collection to share your selection of sources.

Discover connections

25 ENERGY STORAGE subjectCRADA subjectargon ions subjectcathode electrolyte interphase (CEI) subjectcathode recycling subjectelectrochemical properties subjectmicroplasma reaction subjectnickel manganese cobalt (NMC) subjectplasma subjectpouch cells subject

Connections use source metadata and explicit phrase matches, not verified experimental comparisons.

KEEP EXPLORING

Related discoveries

DOE OSTI2026

Liquified SO 2 induced solid/cathode electrolyte interphase for lithium ion batteries

Formation of robust solid/cathode electrolyte interphases (S/CEI) is vital for long-term stability and high-performance operation of lithium-ion batteries (LIBs), particularly under high voltage regimes. However, engineering electrochemically stable S/CEIs that effectively suppress interfacial side reactions remains a key challenge. Herein, we introduce a liquefied sulfur dioxide (SO 2 )– ionic liquid complex as a fluorine-free multifunctional electrolyte additive for the first time that significantly improves the formation of sulfate/sulfite-rich S/CEI layers at both graphite and NMC811 interfaces. The unique SO 2 -N coordination with a 1,2,4-triazolide-based ionic liquid enables homogeneous SO 2 dissolution, resulting in controlled SO 2 decomposition during the initial electrochemical cycle. This decomposition yields sulfur-rich interphase species that stabilize the electrolyte-electrode interface, reduce impedance growth, and lessen electrolyte decomposition. Electrochemical tests show significantly improved cycle life, reduced polarization, and increased Coulombic efficiency for both anodes and cathodes. XPS confirms the presence of SO 2 -derived surface species that contribute to interfacial stability. In conclusion, this approach highlights a new direction for interphase engineering using liquefied gas additives and opens pathways for sulfur-based S/CEI chemistry in advanced battery systems.

Graphite↗
DOE OSTI2023

Speciation of Transition Metal Dissolution in Electrolyte from Common Cathode Materials

Significant capacity loss has been observed across extended cycling of lithium-ion batteries cycled to high potential. One of the sources of capacity fade is transition metal dissolution from the cathode active material, ion migration through the electrolyte, and deposition on the solid-electrolyte interphase on the anode. While much research has been conducted on the oxidation state of the transition metal in the cathode active material or deposited on the anode, there have been limited investigations of the oxidation state of the transition metal ions dissolved in the electrolyte. Here, in this work, X-ray absorption spectroscopy has been performed on electrolytes extracted from cells built with four different cathode active materials (LiMn 2 O 4 (LMO), LiNi 0.5 Mn 1.5 O 4 (LNMO), LiNi 0.8 Mn 0.1 Co 0.1 O 2 (NMC811), and (x Li 2 MnO 3 *(1-x) LiNi a Mn b Co c O 2 , with a+b+c=1) (LMRNMC)) that were cycled at either high or standard potentials to determine the oxidation state of Mn and Ni in solution. Inductively coupled plasma-mass spectrometry has been performed on the anodes from these cells to determine the concentration of deposited transition metal ions. While transition metal ions were found dissolved in all electrolytes, the oxidation state(s) of Mn and Ni were determined to be dependent on the cathode material and independent of cycling potential.

25 ENERGY STORAGE↗