Rapid Assessment of Sulfate Resistance in Mortar and Concrete

Abstract

Extensive research has been conducted on the sulfate attack of concrete structures; however, the need to adopt the use of more sustainable materials is driving a need for a quicker test method to assess sulfate resistance. This work presents accelerated methods that can reduce the time required for assessing the sulfate resistance of mixtures by 70%. Class F fly ash has historically been used in concrete mixtures to improve sulfate resistance. However, environmental considerations and the evolving energy industry have decreased its availability, requiring the identification of economically viable and environmentally friendly alternatives to fly ash. Another challenge in addressing sulfate attack durability issues in concrete is that the standard sulfate attack test (ASTM C1012) is time-consuming and designed for only standard mortars (not concrete mixtures). To expedite the testing process, accelerated testing methods for both mortar and concrete mixtures were adopted from previous work to further the development of the accelerated tests and to assess the feasibility of testing the sulfate resistance of mortar and concrete mixtures rapidly. This study also established criteria for interpreting sulfate resistance for each of the test methods used in this work. A total of 14 mortar mixtures and four concrete mixtures using two types of Portland cement (Type I and Type I/II) and various supplementary cementitious materials (SCMs) were evaluated in this study. The accelerated testing methods significantly reduced the evaluation time from 12 months to 21 days for mortar mixtures and from 6 months to 56 days for concrete mixtures. The proposed interpretation method for mortar accelerated test results showed acceptable consistency with the ACI 318-19 interpretations for ASTM C1012 results. The interpretation methods proposed for the two concrete sulfate attack tests demonstrated excellent consistency with the ASTM C1012 results from mortar mixtures with the same cementitious materials combinations. Metakaolin was shown to improve sulfate resistance for both mortar and concrete mixtures, while silica fume and natural pozzolan had a limited impact. Using 15% metakaolin in mortar or concrete mixtures with Type I/II cement provided the best sulfate resistance.