Effect of Oxidizing Impurities on the Corrosion Behavior of Structural Alloys Exposed to MgCl 2 Molten Salt Vapor

The corrosion behavior of structural alloys SS304 and IN617 when exposed to vapors of MgCl 2 molten salt at 764 °C for 100 h in an argon atmosphere was investigated as a function of the level of oxidizing impurities (e.g., NaOH) present in the salt. Increasing the concentration of oxidizing impurities in the salt caused an increase in corrosion in both structural alloys, as measured by Cr depletion layers. A poorly adhered oxide scale layer containing Mg, Al, and Cr was observed on the surface of the metals, and local attack was observed as well. The Ni-based IN617 showed lower Cr depletion and less scale formation than the Fe-based SS304. These results demonstrate that oxidizing impurities in the molten salt will impact the vapor phase corrosion for structural members exposed to the molten salt headspace. This finding is highly relevant for understanding the effects of the vapor phase in molten salt applications, including molten salt thermal energy storage, molten salt nuclear reactors, and molten salt electrochemistry.

25 ENERGY STORAGE↗

NASA NTRSDate not supplied

Bosch Carbon Catalyst Regeneration in Water II: Analysis of Bosch Catalyst Beads Throughout the Initial Regeneration Process

Catalyst integrity is an important factor in reactor longevity since it changes the effectiveness of a reaction. A Carbon Formation Reactor (CFR), used within Series Bosch (S-Bosch), utilizes an iron alloy catalyst to convert carbon monoxide and hydrogen into water and solid carbon. The catalyst promotes the formation of carbon to such an extent that pressure-causing clogs form within the reactor and reaction sites on the catalyst become limited. To remove carbon from both the reactor and the surface of the iron alloy catalyst, a technique was developed that utilizes water, an In-Situ Resource Utilization (ISRU) Resource, and agitation to regenerate the reactor. To ascertain catalyst integrity throughout this regenerative process, sample catalyst beads were taken before and after the carbon formation reaction, and then after the regeneration process. Additionally, wastewater from the regeneration process was sampled. The sampled beads and wastewater were observed under a Scanning Electron Microscopy (SEM) microscope and the beads were chemically etched to determine if the catalyst had degraded at any point during this process, and if catalyst was lost. Minimal catalyst degradation was observed after carbon formation in the CFR.

regeneration↗

NASA NTRSDate not supplied

Bosch Carbon Catalyst Regeneration in Water II: Analysis of Bosch Catalyst Beads Throughout the Initial Regeneration Process

Catalyst integrity is an important factor in reactor longevity since it changes the effectiveness of a reaction. A Carbon Formation Reactor (CFR), used within Series Bosch (S-Bosch), utilizes an iron alloy catalyst to convert carbon monoxide and hydrogen into water and solid carbon. The catalyst promotes the formation of carbon to such an extent that pressure-causing clogs form within the reactor and reaction sites on the catalyst become limited. To remove carbon from both the reactor and the surface of the iron alloy catalyst, a technique was developed that utilizes water, an In-Situ Resource Utilization (ISRU) Resource, and agitation to regenerate the reactor. To ascertain catalyst integrity throughout this regenerative process, sample catalyst beads were taken before and after the carbon formation reaction, and then after the regeneration process. Additionally, wastewater from the regeneration process was sampled. The sampled beads and wastewater were observed under a Scanning Electron Microscopy (SEM) microscope and the beads were chemically etched to determine if the catalyst had degraded at any point during this process, and if catalyst was lost. Minimal catalyst degradation was observed after carbon formation in the CFR.

Series Bosch↗