DOE OSTI2020

Build orientation, surface roughness, and scan path influence on the microstructure, mechanical properties, and flexural fatigue behavior of Ti–6Al–4V fabricated by electron beam melting

In the present work, microstructure and fatigue behavior of Electron Beam Melted (EBM) Ti–6Al–4V have been systematically studied. Fatigue behavior was investigated using four-point bend tests of rectangular bars with internal features fabricated with different build orientations, scan paths, and surface conditions. Microstructural variations were evaluated by optical microscopy and Vickers micro-hardness indentations, both of which were found to be consistent throughout the build and within ranges reported in the literature. The fatigue performance of the EBM material was comparable to wrought Ti–6Al–4V when the loading direction was parallel to the build direction, but severely limited when loaded perpendicular to the build direction or if surface roughness defects were present. Scanning electron microscopy and interrupted fatigue tests were utilized to characterize fracture surfaces, failure mechanisms, crack initiation, and propagation behavior. Crack initiation sites in the vertically-oriented specimens were identified to be melt-related defects formed by insufficient melting.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Equibiaxial Flexure Strength of a Superfine-Grained Nuclear Graphite

The strength of advanced graphite is reported in accordance with ASTM D7846-16 using a two-parameter Weibull distribution for uniaxial strength testing. The rule of thumb for Weibull distributions is to use a minimum of 30 strength measurements to have a high level of confidence in the Weibull characteristic strength and the Weibull modulus. These large sample sets for statistical confidence are easily obtained for as-manufactured graphite, but determination of the Weibull two-factor parameters on graphite that has been exposed to neutron irradiation is nearly impossible due to irradiation testing restraints on specimen size and space limitations in test reactors for the accommodation of specimens. These restrictions have resulted in irradiation programs that use sub-sized specimens to measure uniaxial strength change, but the specimen geometries still hinder the number of replicate specimens for each irradiation condition. In contrast, this work used an advanced ceramic standard, ASTM C1499-05, as the foundation for equibiaxial strength testing of a superfine-grained nuclear graphite to investigate the irradiation-induced strength change and any changes to the two-parameter Weibull distribution. The goal was to investigate the effect of specimen size on the two-parameter Weibull distribution parameters in support of the small specimens and geometry desired for irradiation. A study of the effect of a reduced sample population was also undertaken to investigate the reliability of using the two-parameter Weibull distribution to study changes to the materials properties caused by neutron irradiation damage. The results of this work suggest that these equibiaxial specimens would be ideal for statistically significant studies of the effects of irradiation on the Weibull characteristic strength (but not the modulus) and for providing a method for surveillance specimen campaigns for future operating commercial reactors.

Campbell, Anne↗
DOE OSTI2021

Flexure Upgrade System Engineering Project

At the National Ignition Facility (NIF), a system of lasers is used to implode and blow-up targets and create temperatures and pressures unlike any other place on earth. There are many target types that are used on experiments, but they can be broadly put in two categories – room temperature targets and cold targets. All targets can be mounted on any of the three target positioners on NIF, and two of these three target positioners can cryogenically cool the targets in the low Kelvin range for the cold targets. To minimize the ice buildup and infrared light exposure to these cold targets, a shroud surrounds the targets and seals the target from the outer environment. By shrouding the target, air, water, and other molecules have a difficult time reaching the target and some particles get cryo trapped into the shrouds themselves.

42 ENGINEERING↗