DOE OSTI2019

Selective laser melting of 304L stainless steel: Role of volumetric energy density on the microstructure, texture and mechanical properties

The role of volumetric energy density on the microstructural evolution, texture and mechanical properties of 304L stainless steel parts additively manufactured via selective laser melting process is investigated. 304L is chosen because it is a potential candidate to be used as a matrix in a metal matrix composite with nanoparticles dispersion for energy and high temperature applications. The highest relative density of 99 %±0.5 was achieved using a volumetric energy density of 1400 J/mm 3 . Both XRD analysis and Scheil simulation revealed the presence of a small trace of the delta ferrite phase, due to rapid solidification within the austenitic matrix of 304L. Here, a fine cellular substructure ranged between 0.4–1.8 μm, was detected across different energy density values. At the highest energy density value, a strong texture in the direction of [100] was identified. At lower energy density values, multicomponent texture was found due to high nucleation rate and the existing defects. Yield strength, ultimate tensile strength, and microhardness of samples with a relative density of 99 % were measured to be 540 ± 15 MPa, 660 ± 20 MPa and 254 ± 7 HV, respectively and higher than mechanical properties of conventionally manufactured 304L stainless steel. Heat treatment of the laser melted 304L at 1200 °C for 2 h, resulted in the nucleation of recrystallized equiaxed grains followed by a decrease in microhardness value from 233 ± 3 HV to 208 ± 8 HV due to disappearance of cellular substructure.

304L stainless steel↗
DOE OSTI2022

Pitting Corrosion in 316L Stainless Steel Fabricated by Laser Powder Bed Fusion Additive Manufacturing: A Review and Perspective

Abstract 316L stainless steel (316L SS) is a flagship material for structural applications in corrosive environments, having been extensively studied for decades for its favorable balance between mechanical and corrosion properties. More recently, 316L SS has also proven to have excellent printability when parts are produced with additive manufacturing techniques, notably laser powder bed fusion (LPBF). Because of the harsh thermo-mechanical cycles experienced during rapid solidification and cooling, LPBF processing tends to generate unique microstructures. Strong heterogeneities can be found inside grains, including trapped elements, nano-inclusions, and a high density of dislocations that form the so-called cellular structure. Interestingly, LPBF 316L SS not only exhibits better mechanical properties than its conventionally processed counterpart, but it also usually offers much higher resistance to pitting in chloride solutions. Unfortunately, the complexity of the LPBF microstructures, in addition to process-induced defects, such as porosity and surface roughness, have slowed progress toward linking specific microstructural features to corrosion susceptibility and complicated the development of calibrated simulations of pitting phenomena. The first part of this article is dedicated to an in-depth review of the microstructures found in LPBF 316L SS and their potential effects on the corrosion properties, with an emphasis on pitting resistance. The second part offers a perspective of some relevant modeling techniques available to simulate the corrosion of LPBF 316L SS, including current challenges that should be overcome.

Voisin, T. (ORCID:0000000287462659)↗
DOE OSTI2026

Exploring the tempering behaviour of additively manufactured high-alloy tool steel using synchrotron X-ray and neutron techniques

Post-processing heat treatment provides a critical pathway toward the commercialisation of additively manufactured (AM) S390 high-speed steel, which is a representative high-alloy tool steel employed in precision manufacturing, offering up to 1.5 times longer tool life and over 20% higher cutting speeds compared to conventional grades. In this study, the phase evolution of AM S390 steel during heat treatment, with particular emphasis on carbide precipitation behaviour, was systematically investigated using a combination of synchrotron X-ray and neutron techniques. The metastable M2C carbides were found to dissolve during austenitisation, while the stable primary carbides MC and M6C experienced coarsening with an average size increase of about 60 nm after just 2 min of tempering. Moreover, the austenite lattice parameters reduced from 3.618 to 3.608 Å within the first 10 min of tempering, suggesting carbon depletion in the steel matrix was likely associated with the formation of secondary carbides. This interpretation was substantiated by small-angle scattering results, which revealed the presence of nanoscale precipitates with a volume fraction of 3.1% after 60 min of tempering. These microstructural evolutions collectively accounted for the observed peak hardness of 921 HV. Furthermore, a comparative analysis of synchrotron and neutron small-angle scattering data highlighted the complementary strengths of each technique, offering critical insight into their suitability for characterising nanoscale features in AM high-alloy steels.

Synchrotron X-ray diffraction↗
NASA NTRSDate not supplied

Effect of Heat Treatments on the Tensile Properties of Additively Manufactured 15-5 Ph Stainless Steel

This study investigated the effect of post-manufacture heat treatments on the microstructure and mechanical properties of 15-5 PH stainless steel (SS) fabricated by laser powder-directed energy deposition (LP-DED). Various heat treatment procedures (CA-H900 and CA-H1150) were conducted to evaluate their effects on the tensile behavior of LP-DED 15-5 PH SS. Scanning electron microscopy was used to characterize the microstructural features and the fracture surfaces. Tensile tests were performed to evaluate the mechanical properties at cryogenic and room temperatures. Reduction in area of CA-H1150 treated specimens after tensile tests was significantly higher than CA-H900 ones, while the ultimate tensile and yield strengths of CA-H900 specimens were higher compared to the CA-H1150 ones. The mechanical behavior of the LP-DED 15-5 PH SS in various heat treatment conditions is discussed based on their microstructures and fracture surfaces.

Laser powder directed energy deposition (LP-DED)↗
DOE OSTI2024

Manufacturing Oxide Dispersion Strengthened (ODS) steel plate via cold spray and friction stir processing

Oxide dispersion strengthened (ODS) steels, traditionally fabricated by ball milling and conventional powder metallurgy techniques to achieve bulk form, followed by intricate rolling and thermal treatment steps to achieve plate or sheet form. Here, we present a novel processing route that combines cold spray (CS) with friction stir processing (FSP) to manufacture ODS steel plate directly from gas atomization reaction synthesis (GARS)-prepared powder, thus no rolling steps involved. Microstructural and mechanical characterizations were performed to assess the quality and properties of the resulting ODS steel plate. Our findings demonstrate that the slightly porous CS deposited layer was fully consolidated after FSP, yielding a fully dense ODS steel plate that exhibited a favorable tradeoff between strength and ductility upon extraction from the substrate. Furthermore, through microstructural analysis, we revealed the presence of an appreciable density (∼10 22 /m 3 ) of nano-sized oxide particles, with the majority being smaller than 5 nm via the combined CS + FSP fabrication route. This work serves as a first proof-of-concept demonstration of the manufacturing approach described herein, offering a possible alternative route for producing ODS steel plates.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Two-step deformation-induced martensitic transformation in additively manufactured High-Si stainless steel

Deformation-induced phase transformation in the additively manufactured (AM) Fe–18Cr–8Ni-5.5Si (in wt.%) alloy was analyzed using the in-situ electron backscattered diffraction (EBSD) record during uniaxial tensile testing in a scanning electron microscope (SEM). Analysis of EBSD data was focused to investigate phase transformation behavior during deformation with consideration of mechanical interactions among phases and grains in the ultrafine AM microstructure. The initial EBSD phase map illustrated that the as-built microstructure was a duplex structure consisting of major austenite (γ) and minor ferrite phases, some of which showed non-traditional orientation relationship since the rapid solidification in the AM process has produced non-equilibrium state in phase formation. In the deformed as-built AM alloy, the two-step martensitic transformation (γ→ε→α´) was identified as the main deformation-induced transformation mechanism. Martensitic transformation steps were found to be associated with glides of Shockley partial dislocations on closed packed (111) planes under the influence of atomic disturbance in the γ and ε phases, respectively. Using the closed-packed plane pole figures and unit cell orientations, their evolutions and mechanisms accompanying with the transformation were analyzed. Finally, the results indicate that one variant of ε-martensite forms from their parent γ phase, while two variants of α´ form from their parent ε phase.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Mechanical Performance of Additively Manufactured ODS 316L and 316H Stainless Steels

This work package within the Advanced Materials and Manufacturing Technologies (AMMT) program focused on the mechanical and microstructural characterization of oxide dispersion strengthened (ODS) stainless steels produced using advanced manufacturing techniques. The research aimed to identify an accelerated development path for ODS alloys by integrating additive manufacturing (AM) technologies with recent advancements in ODS materials and traditional manufacturing methods. For FY 24, the research specifically targeted exploring an accelerated development path for ODS alloys by combining AM technologies with these advancements. Novel AM and post-build processing routes were developed for ODS austenitic alloys, including Fe-Cr-Ni alloys such as 316L and 316H. Electron microscopy and mechanical characterizations were conducted to evaluate the impact of process variables on microstructure and properties, with the goal of optimizing these properties economically. Traditionally, producing ODS alloys involves multi-day, high-energy mechanical milling of alloy powder with yttria powder, followed by milled-powder consolidation through extrusion or other methods, and additional thermomechanical processing (TMP) for property control. To overcome the challenges associated with this complex and costly approach, we propose exploring alternative, cost-effective processing routes that emphasize AM and traditional TMP methods. The new processing routes for ODS alloys have achieved significantly higher strengths—several times greater than those of wrought stainless steels—while maintaining substantial ductility and fracture toughness. This report outlines the novel and economical AM-based processing routes for ODS austenitic alloys, combined with post-build TMPs, and discusses the mechanical and microstructural characteristics of the developed materials.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Tailoring additive manufacturing to optimize dynamic properties in 316L stainless steel

With the advent of additive manufacturing, manipulation of typical microstructural elements such as grain size, texture, and defect densities is now possible at a faster time scale. While the processing–structure–property relationship in additive manufactured metals has been well studied over the past decade, little work has been done in understanding how this process affects the dynamic behavior of materials. We postulate that additive manufacturing can be used to alter the material microstructure and used to enhance its dynamic strength. In this work, 316L stainless steel (SS) was manufactured via selected laser melting and its microstructure was altered through changing build parameters like laser power, speed, and hatch spacing systematically. These samples were then subjected to spall recovery experiments to measure the spall strength and quantify the amount of damage as a function of build parameters. By mapping the spall strength as a function of build parameters, this work demonstrated that indeed additive manufacturing can be used to tailor the spall strength of 316L SS. This work also determined the optimum build parameters (laser power=195W; scanning speed=1083mm/s; hatch spacing=0.09mm; layer thickness=0.02mm) to obtain the highest spall strength and the least amount of total damage in 316L SS. Microstructural characterization of the pre- and post-mortem samples revealed that increased grain average misorientation and textural index were the main driving force behind this higher spall strength. This work aims to enhance microstructural engineering techniques to design materials with greater resistance to dynamic shock loading.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Influence of microstructure and temperature on impact toughness of H13 steel produced by binder jet additive manufacturing

Binder Jet Additive Manufacturing (BJAM) is a promising manufacturing pathway to produce H13 steel dies and tooling with complex geometries for applications in high pressure aluminum die casting, hot stamping, and injection molding. While fully dense H13 coupons produced using BJAM have been subjected to detailed microstructure characterization, properties which are critical and relevant to the aforementioned applications, such as impact toughness, have not been reported. Here, this work evaluated the influence of microstructural characteristics and test temperature on the impact toughness of H13 produced by BJAM. Coupons were produced from three different powder size distributions (PSDs), with nominal powder size ranges of −22 μm, 10-32 μm, and 15-53 μm. Coupons were printed, sintered, hot isostatically pressed (HIPed), and heat treated by quenching and tempering. After HIPing, the measured porosities of the different PSDs were all less than 0.015 vol%. The −22 μm PSD BJAM material exhibited the best impact toughness of all three PSDs across the entire test temperature range from 25 to 400 °C, and also exhibited an ambient temperature impact toughness of 10.9 J at a hardness of 46 HRC, equivalent to minimum threshold requirements for premium grade H13. However, all three BJAM PSDs exhibited moderately lower impact toughness than premium grade wrought H13 from RT to 400 °C. We attribute this in part due to the very large prior-austenite grain (PAG) sizes near 400 μm and segregation from former liquid channels leading to greater amounts of carbide precipitation on PAG boundaries. Technical pathways for optimizing processing and chemistry of BJAM H13 to further improve impact toughness are discussed.

Binder jet additive manufacturing↗
DOE OSTI2025

High temperature tensile properties of H13 tool steel fabricated via binder jet additive manufacturing

H13 is one of the most used steels for hot work tooling applications like die casting. Binder jet additive manufacturing (BJAM) offers a cost-effective solution to fabricate tools with performance enhancing features like internal cooling channels. While full densification of BJAM H13 has been demonstrated in the literature, the room and high temperature tensile properties of the material, and the effect of post-process treatments like hot isostatic pressing (HIP), and heat treatment (HT) are unknown. Here we use HIP+HT to obtain a combination of ultimate tensile strength (UTS) and elongation to failure that is superior to H13 fabricated via laser powder bed fusion and wire arc additive manufacturing. HIP+HT BJAM H13 has a superior UTS (1836 MPa) compared with conventionally processed (1671 MPa) H13 but has lower plastic elongation. We report that as-sintered samples have an extensive network of continuous grain boundary (GB) carbides that contribute to brittle fracture. HIP+HT results in partial dissolution of GB carbides and formation of a fine martensitic microstructure resulting in superior tensile strength and elongation compared with as-sintered H13. We use thermo-kinetic calculations to rationalize the effects of HIP+HT on microstructure and properties.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Comparing the deformation mechanism in 316 L stainless steel fabricated by hybrid and additive manufacturing

This study rationalizes the relatively higher elongation with minimal strength drop of 316L stainless steel (316LSS) manufactured using the hybrid approach in comparison to a fully additive approach followed by machining. It was found that twinning was the dominant deformation mechanism in 316LSS produced by both additive and hybrid approaches. Additionally, the relatively lower fraction of twins in the as-fabricated state of hybrid approach compared to a fully additive approach resulted in delaying the onset of steady-state strain hardening rate to higher strain levels, thereby resulting in an overall increase in elongation to failure.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Dynamic response of 17-4 stainless steel as a function of manufacturing method and heat treatment

We present a series of plate-impact experiments on 17-4 stainless steel to study the effect of manufacturing method and heat treatment on the Hugoniot elastic limit (HEL), Hugoniot, phase transformation stress, and spallation strength. Two traditional manufacturing methods were considered, wrought processing and casting, as well as two additive manufacturing methods, laser powder-bed fusion (LPBF) and wire-fed electron beam (EBAM). For both LPBF and EBAM 17-4 stainless steel variants, two billets were printed, enabling the application of two unique heat treatments. The HEL stress depended heavily on the thermal history, with the HEL increasing after the formation of Cu-rich precipitates via heat treatment. The Hugoniot response both below and above the phase transition was unaffected by the manufacturing method or heat treatment. The phase transition stress depended heavily on the thermal history, with its variation being attributed to the presence of various microstructural features. This is supported by a marked increase in the phase transition stress after precipitation hardening. These results suggest that the notion of the phase transition stress being dictated by bulk composition is an oversimplification and the stress fields generated by the meso-scale structure are a dominant force. The spallation strength was lower in the cast material compared to all other 17-4 stainless steel variants due to the presence of brittle δ-ferrite inclusions. Additionally, a drop in the tensile strain-rate was observed in the spallation response above the phase transition stress, which was hypothesized to stem from the kinetics of the reversion to the low-pressure phase during spall.

Compressive stress↗
DOE OSTI2021

Tailoring plasticity mechanisms in compositionally graded hierarchical steels fabricated using additive manufacturing

Abstract While there exists in nature abundant examples of materials with site-specific gradients in microstructures and properties, engineers and designers have traditionally used monolithic materials with discrete properties. Now, however, additive manufacturing (AM) offers the possibility of creating structures that mimic some aspects of nature. One example that has attracted attention in the recent years is the hierarchical structure in bamboo. The hierarchical architecture in bamboo is characterized by spatial gradients in properties and microstructures and is well suited to accommodate and survive complex stress states, severe mechanical forces, and large deformations. While AM has been used routinely to fabricate functionally graded materials, this study distinguishes itself by leveraging AM and physical metallurgy concepts to trigger cascading deformation in a single sample. Specifically, we have been successful in using AM to fabricate steel with unique spatial hierarchies in structure and property to emulate the structure and deformation mechanisms in natural materials. This study shows an improvement in the strength and ductility of the nature-inspired “hierarchical steel” compared with conventional cast stainless steels. In situ characterization proves that this improvement is due to the sequential activation of multiple deformation mechanisms namely twinning, transformation-induced plasticity, and dislocation-based plasticity. While significantly higher strengths can be achieved by refining the chemical and processing technique, this study sets the stage to achieve the paradigm of using AM to fabricate structures which emulate the flexibility in mechanical properties of natural materials and are able to adapt to in-service conditions.

36 MATERIALS SCIENCE↗
DOE OSTI2021

Mechanical behavior of additively manufactured and wrought 316L stainless steels before and after neutron irradiation

Fabrication of nuclear reactor components using additive manufacturing (AM) methods is now a practical option since the AM technologies have advanced to allow for building of complex parts with high quality materials. To assess the mechanical performance of printed components in reactor-relevant conditions and to build a property database for the AM 316L stainless steel (SS), mechanical testing and characterization were performed before and after neutron irradiation. In this work, miniature tensile specimens were irradiated at the High Flux Isotope Reactor (HFIR) to 0.2 and 2 displacements per atom (dpa) at 300 and 600°C. The AM 316L SS was tested in the as-built, stress-relieved, and solution-annealed conditions, and the wrought (WT) 316L SS in solution-annealed condition as a reference alloy. The baseline test result showed that the AM 316L SS, regardless of the post-build heat treatment, had higher strength than the WT 316L SS, but similar ductility. Post-irradiation tensile testing was conducted at RT, 300°C, and 500°C for selected irradiation conditions. Neutron irradiation induced significant changes in the mechanical behavior of the AM stainless steels, including both hardening and softening. Although the as-built 316L steel after 300°C irradiation showed necking just after yielding, the overall property changes of the as-printed alloy became less significant after 600°C irradiation. Irradiation-induced ductilization was also observed after the higher temperature irradiation. In general, the strength change was smaller in the relatively stronger as-built and stress-relieved AM SSs than in the solution-annealed AM and WT SSs. These relatively lower strength 316L SSs overall retained higher ductility in the irradiation conditions tested, but the stronger 316L SSs demonstrated a similar level of ductility after the higher temperature (600°C) irradiation. It is a positive assessment for the AM 316L materials that no embrittlement was observed within the test and irradiation conditions of the experiment.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Development and Integration of Predictive Models for Manufacturing and Structural Performance of Carbon Fiber Composites in Automotive Applications (Final Report)

The goal of this project is to develop integrated, state-of-the-art, computational modeling tools based on an integrated computational materials engineering (ICME) methodology that are critically needed to enable structural carbon fiber (CF) applications in automobiles. These tools are designed to predict the manufacturing and structural performance of CF composites, including stochastic effects. During the first phase of the project, the manufacturing and structural performance tools, including a stochastic driver, were developed, calibrated, and validated against coupon and component level test results. For this project, from the manufacturing side, the development efforts were focused on high-pressure resin transfer molding (HP-RTM), a potentially game-changing manufacturing technology that is capable of reaching the 3-5-minute cycle time that is necessary for volume manufacturing of composites. On the structural performance side, the crashworthiness of CF structures was studied. Accordingly, computational tools were developed and validated. The resulting differences between the numerical predictions and the experimental results in the first phase of the project were required to be less than 15%. During the second phase of the project, the manufacturing and performance tools were integrated by mapping the manufacturing outcomes (e.g., fiber angles, residual stresses, degree of cure, and defects) into the structural models. Also, using the tools developed in this project, an automotive assembly currently manufactured in steel (2016 GM Malibu) was redesigned to be manufactured using advanced CF composites with the objective of comparing the performance of the CF assembly with the developed ICME model predictions. The weight, performance and cost of the CF assembly were compared with the baseline steel assembly as well. The CF underbody design was shown to be 30% lighter than the corresponding steel design. The CF underbody assembly withstood the side pole impact with less than half the intrusion for the steel assembly. Excellent correlations within 10% for both peak impact load and intrusion were observed between the numerical predictions and experimental results. Based on the cost models developed in the project, the cost increase per Kg saved was determined to be $22. The project team has prepared a total of 28 publications in various journals and conferences and broadly communicated the project results for the benefit of the composite industry. The project team has also prepared a total of 10 patent applications that were submitted to the US Patent and Trademark office.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Characterization and prediction of the electromechanical wear of contact tips during wire arc additive manufacturing of 316L stainless steel

Here, this study seeks to better understand the degradation of the contact tip with respect to WAAM for a 316L wire electrode as well as explore methods of monitoring the contact tip state from process data. The contact tip, a consumable component, positions the wire and serves as the electrical contact surface between the wire electrode and the welding power supply. The wear of the contact tip was characterized in terms of material loss and material contamination for a set of tips worn to discrete levels as measured by the amount of wire fed or arc time. Geometrical characterization found a 49% increase in the bore exit area at 180 meters of wire fed. Machine learning models were developed to predict the relative bore exit area of the contact tip from arc-based process data and a random forest classifier exhibited favorable performance with a cross-validated f1-score of 0.84. The regression architecture implemented a multi-layer perceptron with the ability to predict the relative exit area with an $R^2$ score of 0.75. Key features used in the prediction include the standard deviation of the voltage and the time between shorts.

Contact tip wear↗