DOE OSTI2023

Irradiation-assisted Stress Corrosion Cracking of PWRirradiated Type 347 Stainless Steel (NSUF CINR 19-16567)

This document serves as the final report for NSUF Project 19-16567 (Reference 1) and its supporting contracts (References 2 and 3). It documents completion of testing of specimens fabricated as previously described in Reference 4. At a high level, the purpose of the testing is to generate data to support continued operation of light water reactors (LWR) and provide further understanding of irradiation-assisted stress corrosion crack (IASCC) initiation in baffle-former bolt materials. Baffle-former bolts that had been extracted from commercial pressurized water reactors (PWRs) were machined into miniature 4-point bend specimens and TEM samples at the Westinghouse Churchill Site hot cell facility. These samples were then shipped to the University of Michigan to undergo IASCC initiation testing in simulated PWR primary coolant containing either LiOH or KOH additions. Overall, 15 samples were tested, 8 in water with KOH additions and 7 in water with LiOH additions, until indications of cracking were observed. Crack initiation stress was similar in both water environments at 50-60% of the irradiated yield stress. Post-test examination of the cracking sites, including scanning electron microscopy and transmission electron microscopy, demonstrated that the crack initiation mechanism and crack initiation rates were similar between the two different water chemistries. A grain boundary oxidation and oxide fracture mechanism was observed to be responsible for crack initiation.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2022

A Critical Review of Radiolysis Issues in Water-Cooled Fission and Fusion Reactors: Part I, Assessment of Radiolysis Models

A critical review is presented on modeling of the radiolysis of the coolant water in nuclear power reactors with emphasis on ITER. The review is presented in two parts: In Part I, we assess previous work in terms of compliance with important chemical principles and conclude that no model proposed to date is completely satisfactory, in this regard. Thus, some reactions that have been proposed in various radiolysis models are not elementary in nature and can be decomposed into two or more elementary reactions, some of which are already included in the models. These reactions must be removed in formulating a viable model. Furthermore, elementary reactions between species of like charge are also commonly included, but they can be discounted upon the basis of Coulombic repulsion under the prevailing conditions (T < 350 °C) and must also be removed. Likewise, it is concluded that the current state of knowledge with respect to radiolytic yields (i.e., G-values) is also unsatisfactory. More work is required to ensure that the yields used in radiolysis models are truly “primary” yields corresponding to a time scale of nanoseconds or less. This is necessary to ensure that the impact of the reactions that occur outside of the spurs (ionizing particle tracks in the medium) are not counted twice. In Part II, the authors review the use of the radiolysis models coupled with electrochemical models to predict the water chemistry, corrosion potential, crack growth rate in Type 304 SS, and accumulated damage in the coolant circuits of boiling water reactors, pressurized water reactors, and the test fusion reactor, ITER. Based on experience with fission reactors, the emphasis should be placed on the control of the electrochemical corrosion potential because it is the parameter that best describes the state of corrosion in coolant circuits.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

Investigation of the irradiation effects in additively manufactured 316L steel resulting in decreased irradiation assisted stress corrosion cracking susceptibility

While additive manufacturing (AM) is an area of increasing interest to the nuclear industry, there are significant research and development needs prior to successful implementation of additively manufactured components into reactors. AM steel behaves differently than traditional wrought material, as has been observed in numerous mechanical testing studies. The nuclear industry must also understand the material response to irradiation. This work examines the irradiation damage and the irradiation assisted stress corrosion cracking behavior (IASCC) of both proton irradiated AM and wrought 316L steel. For IASCC testing, specimens were strained to 4% plastic strain in a simulated boiling water reactor environment (288°C, 0.2 µS/cm). Transmission and scanning electron microscopy, confocal microscopy, and X-ray computed tomography were used to examine coupons of the material as well as tensile bars used in the IASCC testing. This work found that the wrought 316L was more susceptible to IASCC than the AM steel, however, some IASCC was observed in the AM steel when tested with the tensile axis parallel to the build direction. Electron microscopy has shown significantly fewer radiation induced voids formed in the AM steel. While the pre-existing pore network in the AM steel may act as a sink to point defects, this is not expected to be the major factor in the reduced swelling observed in the AM steel. The lower density of radiation induced voids was expected to contribute to the IASCC resistance by decreasing the localization of deformation in the irradiated specimens, however, severity of localized deformation in AM steel, measured in dislocation channel spacing and height, was similar or more severe to that found in wrought. In conclusion, the presence of severe cracking in the wrought specimens did not allow for a direct comparison of localized deformation severities between the AM and wrought steel.

Additive manufacturing↗
DOE OSTI2020

Fluorine Limits and Impacts in High-Level Waste Glass Compositions

The impact of elevated fluorine (F) content on Hanford high-level waste (HLW) glasses has not previously been studied in detail. This effort represents the first systematic study to determine what F concentration limits should be used for the design of alkali-borosilicate-based Hanford Waste Treatment and Immobilization Plant (WTP) HLW glasses, and to document the technical basis for that limit. If alkali borosilicate glass made from Hanford HLW can accommodate a large amount of F, the large capital costs for complex sludge washing facilities may be avoided, as would much of the operational costs and negative schedule impacts associated with handling the large volumes of water required to dissolve these salts. In order to determine a limit for F in likely HLW glass compositions, an evaluation was conducted on glasses with F ≤ 0.90 mass% from previous nuclear waste glass studies. The collected dataset contains 239 glasses (232 HLW glasses and 7 LAW glasses) including 109 glasses with 0.9 ≤ F mass% ≤ 2.5, 116 with 2.5 < F mass% ≤ 8.0, and 14 with F mass% ≥ 8 (max. F mass% = 17.42). The collected composition and property data were analyzed to determine the basis for the F tolerance, i.e. the maximum F concentration that can be processed without potential issues. Fluorine volatility, product consistency test (PCT) response, liquidus temperature (T L ), glass melt viscosity, and crystallinity have been investigated. No limits for F concentration can be made based on F volatility, T L , or glass melt viscosity, because the data show that high F in glasses do not indicate, with high probability, being restricted by those property constrains. However, crystallinity and PCT response were used to estimate the F tolerance. The results show that glasses with high F (≥ 0.90 mass%) are more likely to form large fractions of F-containing crystal phases which may increase PCT responses, i.e. decrease the glass durability. Based on the results of crystallinity and PCT data, the F tolerance of 4.5 mass% is estimated. There is no evidence of other glass components, such as calcium oxides and alkali metal oxides have combined impacts with F on the glass properties. Overall, the available high-F glass data is limited, especially in the designed HLW glass composition regions. Future work on formulation and testing of HLW glasses with F ≥ 0.9 mass% will close the data gaps and expand operational flexibility with respect to the fluoride tolerances. Volatility of F from melters and corrosion of materials in contact with glass melts are important for processing of high-F wastes; yet no test data are currently available. It is recommended tests be conducted to address these two potential issues.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2022

Subcomponent Validation of Composite Joints for Marine Energy Structures

The Marine Energy Advanced Materials project addresses the barriers and uncertainties facing marine renewable energy developers in using composite materials for load-bearing structures. Sponsored by the U.S. Department of Energy's Water Power Technologies Office, the multiyear project comprises of collaborators from the National Renewable Energy Laboratory (NREL), Sandia National Laboratories, Pacific Northwest National Laboratory (PNNL), Montana State University (MSU), Florida Atlantic University (FAU), and industry stakeholders. As part of the Marine Energy Advanced Materials project, marine renewable energy industry surveys and assessments were conducted to identify key materials and knowledge gaps that hinder the adoption of composite materials in marine renewable energy structures. Specific knowledge gaps highlighted for composite materials were environmental effects, fatigue strengths, and bonded and bolted interconnects (composite/composite and composite/metal). It was concluded that many of these gaps could be addressed through subcomponent validation; consequently, a program was developed at NREL with the goals of developing subcomponent validation methods for appropriate marine energy materials, which would improve the understanding of design allowables for full-scale structural components and joints. Ultimately, the aim is to reduce timelines and costs associated with full-scale structural validation efforts while also providing near-net-scale static and fatigue data of composite/metal subcomponents for marine renewable energy systems. To approach these goals, a testing program was developed at NREL to investigate a variety of materials and structural design details at the subcomponent scale to understand (a) the effects of harsh and corrosive marine energy environments and (b) the static and fatigue strengths of the complex geometries. The recent study from this testing program is perhaps the largest that has ever been conducted with respect to specimen scale and geographic diversity of underwater environmental conditions that the specimens were subjected to. A variety of specimen geometries were designed by NREL to highlight key features of multimaterial (composite/composite or metal/composite) interconnects that may be used in marine renewable energy structural designs. The designs used several different composite matrices, adhesives, and marine-grade steels, which were highlighted in the surveys as being the most appropriate for harsh marine environments. Composite panels were then manufactured at MSU, and were subsequently manufactured into test specimens by NREL. The specimens were shipped to FAU and PNNL for conditioning in ocean water tanks at various temperatures for an extended period. The specimens were then returned to NREL for structural validation. This presentation will provide an overview of recent advances within the testing program in terms of specimen design and test methods, and will discuss results and key findings of the subcomponent testing program to date at NREL.

adhesives↗
DOE OSTI2024

Dynamic Binary Complexes (DBC) as Super-Adjustable Viscosity Modifiers for Hydraulic Fracturing Fluids

In the preceding project year two, we refined three DBC formulations from a selection of over 50 different chemistries. The optimization study primarily encompassed testing for (i) reversibility extent, (ii) performance in the presence of chemical additives, (iii) adhesion and friction behavior during displacement in wellbores and pipelines, (iv) corrosion protection performance, and (v) injection performance with model fracture systems at the laboratory scale. Highly promising results obtained from all these tests signify the significant potential of DBCs in enhancing hydrocarbon recovery from unconventional reservoirs. The primary activities in the third project year included publishing experimental findings across multiple articles and conducting outreach initiatives. Throughout the year, we undertook tasks such as replicating experimental results, further optimizing various formulations and their associated experimental sets, and conducting additional tests to address missing components based on reviewer feedback and suggestions. We also explored the surfactant and friction-reduction aspects of selected formulations through drag reduction tests. In addition, we constructed an improved fracturing performance setup and performed flow injection tests. The specific DBC formulations focused on during this project period were A8/B1, A12/B5, and A10/B12. We also obtained results for additional DBC formulations and a select few commercial fracturing fluids for the purpose of comparison. Within the project's scope, we aim to enhance the experimental findings with the development of various models. The first two years focused on two key aspects: (i) the creation of a high-fidelity hydraulic fracturing model for non-Newtonian fluids to gain insights into the implementation of DBC fluids in fracking environments, and (ii) the development of a multiphase flow simulator for estimating total production, fluid saturation in the reservoir, and the creation of a fracture propagation model and kinetic Monte Carlo (kMC) models for diverse applications. In the third year, we delved into the fundamental nanostructural properties of DBCs, exploring aspects such as material chemistry, pH tunability, and control of DBC formation and stability. Subsequently, in the extension year, we conducted a systematic investigation of various building blocks containing primary, secondary, and tertiary amine functional groups to understand their impact on rheological and viscoelastic properties. Furthermore, we explored a Dissipative Particle Dynamics (DPD) model to simulate self-assembly processes with precision, creating a high-fidelity representation of relevant nanostructures. The tasks performed this year with the significant results obtained have been discussed in Section 2.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2020

High-throughput synthesis and corrosion behavior of sputter-deposited nanocrystalline Al x (CoCrFeNi) 100-x combinatorial high-entropy alloys

High-entropy alloys (HEAs) are inherently complex and potentially span a vast composition space, making their research and discovery challenging. In the present study, high-throughput synthesis of an Al x (CoCrFeNi) 100-x combinatorial material library covering x = 4.5–40 atomic percent Al is achieved, using magnetron cosputtering. The effects of Al on the microstructure and corrosion behavior are investigated. With the increased amount of Al, crystal-structures of thin films transform from face-centered cubic (FCC) to body-centered cubic (BCC). Both the FCC and BCC thin films demonstrate a uniform elemental distribution. Corrosion characteristics of combinatorial samples immersed in the 3.5 wt% (wt%) NaCl solution are evaluated via electrochemical tests. Complementary X-ray photoelectron spectroscopy analysis reveals the compositional variation of passivated films formed on the sample surface after immersion. The results show that the Al x (CoCrFeNi) 100-x HEA thin films possess outstanding corrosion-resistant properties, but the resistance diminishes with the increasing Al content. The decreased corrosion resistance is revealed to be directly related to the constituents of passivated films.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Localized Corrosion of Chromium-Containing Conventional and Multiprincipal Element Alloys in Methanol and Aqueous Chloride Environments

The localized corrosion behavior of Type 304L stainless steel (UNS S30400), Alloy 625 (UNS N06625), and three experimental NiCoCrMo multiprincipal element alloys (MPEA), exposed to methanol/lithium chloride solutions with different water contents, is examined in this paper. Cyclic potentiodynamic polarization tests indicated that water increased the pitting and repassivation potentials and the critical temperature at which localized corrosion occurred in chloride solutions. The effect of water on repassivation potential in methanol-chloride solution depended on the chloride concentration and alloy content. At lower chloride concentration and higher alloy content, water had a greater inhibiting effect on repassivation potential, suggesting a competitive reaction between chloride and water on the metal surface in the pit. The localized corrosion resistance of the MPEAs followed the same trend as that of commercial stainless steels and Ni-base alloys in terms of the effect of alloying elements. The implications of these results on the mechanisms of localized corrosion are discussed.

Materials Science↗
DOE OSTI2020

Vitrification of High-Cr Glass in Research-Scale Melter

This test report describes the experimental results from a small-scale test using the research-scale melter (RSM) at Pacific Northwest National Laboratory to demonstrate processing of a high-Cr simulated feed stream, designated HLW-HCr-16. The RSM is a small, joule-heated melter capable of processing melter feed continuously. The melter is equipped with Inconel ® 693 electrodes, Monofrax ® K-3 refractory, and an Inconel 690 pour spout. An electric kiln surrounds the melter body and minimizes heat loss from the melter body during operation. The RSM is equipped with an offgas treatment system that employs quenching, wet scrubbing, and high-efficiency mist elimination. The glass-discharge section is heated to facilitate pouring of the glass. The melter is fitted with a melt cavity that is ~25 cm (10 in.) in diameter with a nominal glass depth of 8.9 cm (3.5 in.). The melter was operated with a target glass temperature of 1150°C and target plenum temperature between 550°C and 700°C for this test. The air bubbling rate was 4.2 L/min. Overall, during the continuous operation of the melter for ~ 103 hours, ~ 141 kg of glass was produced. At the conclusion of the test, the melter and exhaust lines were visually inspected for particulate deposition and corrosion. Entrained material had adhered to the underside of the melter lid and to the exhaust piping. Enrichments in elements such as Cl, F, B, K, Li, P, Na, and S were measured in these deposits through inductively coupled plasma–optical emission spectroscopy and X-ray fluorescence analysis. When the melter electrodes and air bubbler tube were removed from the glass in the RSM, the electrodes appeared discolored, but no significant loss of metal was observed. The processing of a high-Cr simulant, HLW-HCr-16, in the RSM produced glass at an average rate of 1.36 kg/h, equaling a melter-surface-area normalized glass generation rate of 654 kg/day/m 2 . The resulting glass met the toxicity characteristic leaching procedure requirement. Test results of crystallinity, electrical conductivity, and viscosity showed good processing properties of this high-Cr high-level waste glass. RSM offgas was also sampled and analyzed at periodic intervals during steady-state operating conditions. The total decontamination factor averaged by four sampling periods was 134. The concentrations of CO and NO x in emissions were 237 to 422 and 69 to 94 parts per million by volume, respectively.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2026

Impact of nitrogen on lithium-induced corrosion and cracking of RAFM steel

The emergence of private fusion enterprises, combined with advancements in U.S. and EU ITER-TBM as well as EU DEMO liquid breeder blanket concepts, has renewed focus on the materials challenges. This study examines the compatibility of reduced activation ferritic/martensitic (RAFM) steel in liquid Lithium (Li) containing various Nitrogen (N) concentrations, tested at 600 and 700 °C for 500 and 1000 h under static conditions. Microstructural characterization revealed the corrosion-induced dissolution and precipitation in Li containing 0.082 and 0.17 wt.% N at 600 °C, while limited dissolution and precipitation were observed in N-gettered Li using zirconium (Zr) and titanium (Ti) foils at 600 °C. Tensile testing at room temperature after Li exposure revealed a decrease in strength and ductility of the RAFM steel as a function of N content in Li. Severe embrittlement was observed after 500 h in Li containing 0.17 wt.% N at 600 °C and after 500 h in hot-gettered Li at 700 °C. Chromium (Cr) depletion from the steel matrix was observed, leading to the formation of M6C-type carbides on the surface identified by electron microscopy (SEM), X-ray diffraction (XRD), in agreement with thermodynamic calculations. These findings highlight the critical materials challenges posed by liquid Li breeder blanket concepts, emphasizing the need for improved strategies to address Li-induced dissolution, precipitation, and steel embrittlement due to N contamination of the coolant.

Romedenne, Marie [ORNL] (ORCID:0000000317936561)↗
DOE OSTI2024

Promoting the regulatory acceptance of combined ion and neutron irradiation for material degradation in nuclear reactors

The Advanced Materials and Manufacturing Technologies (AMMT) program within the Department of Energy (DOE) Office of Nuclear Energy has developed its current recommendation for promoting the use of combined ion irradiation and neutron irradiation for the accelerated qualification of materials to be deployed in nuclear reactors. This plan is intended to provide a collaborative path forward that can be adopted by academia, national laboratories, and industry, and has been developed with input from the regulatory research arm of the U.S. Nuclear Regulatory Commission (NRC). To deploy new materials or materials manufactured with new technologies, such as additive manufacturing, materials must be evaluated for reactor-induced degradation from the combination of harsh temperatures, corrosive environments, and radiation fields. However, rapid deployment of materials necessitates accelerated testing methods rather than relying on years of neutron irradiation in a material test reactor. Ion irradiation has demonstrated success in reproducing material microstructure and select property evolution resulting from neutron irradiation with three to four orders of magnitude reduction in time and cost, making it an ideal candidate for accelerated irradiation testing. This presentation provides context governing both the scientific and regulatory aspects of the proposed goal. The discussion is aimed at a broad audience including researchers from industry, national laboratories, and academia. The recommended path forward is presented as a conceptual framework of specific steps. In brief, the strategy entails developing an integrated ion and neutron irradiation test plan for the material property of interest based on the fundamental tenet of the linkage of microstructure and properties in materials. Physics-based modeling interprets ion irradiation data and predicts neutron irradiation microstructure and properties with uncertainty bounds. The first round of testing is sufficient for an initial licensing application using a risk-informed approach, while a minimum required neutron irradiation test plan reduces cost and time requirements. A surveillance program with witness specimens in-reactor provides additional data over time to improve model predictions to higher damage levels and further reduce uncertainty bounds, which can be used for license extensions or longer lifetimes in new license applications.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2025

In-service corrosion and grain boundary oxidation in neutron-irradiated 316 stainless steel baffle-former bolts

Reactor core internal components such as baffle-former bolts (BFBs) are subjected to significant mechanical stress, corrosive environment, and neutron irradiation from the reactor core during the plant operation. Over the long operation period, these conditions lead to potential degradation and of the bolts. In this work, characterization was performed on the oxidized surface of stainless steel BFBs harvested from a commercial pressurized water reactor (PWR) after 40 years of operation. The analysis shows that a complex multilayered surface oxide with six identified layers formed that is different from 2-layer structure commonly observed in model experiments. The oxide varies by composition – predominantly Fe, Cr, and Ni, grain size, and phase, and has features resembling both unirradiated and radiation/ corrosion experiments likely due to the low radiation flux compared to ion-irradiation or the test reactor radiation. In addition, grain boundary oxidative attack featured a pathway for Fe and other elements to move from the metal matrix to the outermost oxide. In conclusion, the results help assess PWR lifetime extension, put into context previous experimental studies, and provide input for designing experiments combining radiation and corrosion effects.

Baffle-former bolt↗
DOE OSTI2020

Wide Area 3D Measurement System for Analysis of 3013 Inner Container Closure Weld Region

One of the main focus areas of the 3013 Surveillance Program is a thorough evaluation of the inner container closure weld region (ICCWR) opened for destructive examination (DE). As part of the protocol to investigate the corrosion in the ICCWR, a laser confocal microscope (LCM) is used to perform close visual examination of the surface and to measure corrosion features on the surface. However, in FY20, the introduction of the Wide Area 3D Measurement System (WAMS) was tested as a method for faster inspection of the ICCWR. Optimization of the WAMS parameters for data collection was carried out using a generic tear-drop type sample containing large and fine Stress Corrosion Cracking (SCC) fractures and high resolution images were compared to the image obtained with the LCM. Although the image with the LCM shows higher resolution than the WAMS images, the small features can be still identified in the WAMS images. The advantage of collecting data for the full circumference using the WAMS is that it can take about a week to complete, which represents 1/16 of the time needed with the LCM. Nonetheless, both systems offer capabilities that combined can be utilized to expedite the examination of the ICCWR. The WAMS can be utilized to obtain images for faster screening or identification of corrosion features on the surface while the LCM can be utilized to obtain higher resolution images of those areas identified by the WAMS.

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2022

Status of Eddy Current Developments at INL

Both standard and advanced Light Water Reactor (LWR) fuel systems are composed of fuel pellets enclosed in a metallic cladding. The fuel cladding represents the first containment of the fission products and the first safety barrier. Upon progression of irradiation, the cladding properties deteriorate, mainly due to the pick-up of hydrogen, which causes embrittlement, and the consequence corrosion that reduced the metallic substrate. Those changes in the properties combined with the harsh environment, e.g., fatigue and fretting occurring during operation, might eventually lead to loss of hermeticity. Therefore, it is important to be able to quantify the amount of corrosion taking place and to detect and size structural discontinuity that can promote cladding failure. Eddy current testing is one of the non-destructive methods employed for this purpose. Inspections are carried out using special probes, which are designed and optimized to inspect a tube with well-defined geometrical and physical characteristics, i.e. external diameter, wall thickness, material electric conductivity and magnetic permeability. The inspection goals are mainly twofold: first, the determination of the amount of corrosion by measurement of the external oxide thickness; second, the detection of flaws in the tube wall, ether on the external or the internal surface of the tube. This report summarizes the available capabilities for eddy current testing of LWR fuel claddings, identifies needs and are of developments for testing of ATF claddings.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2020

GPR Robotic Assisted Non-Destructive Evaluation of Concrete Structures - 20196

Reinforced concrete structures are always under exposure of internal or external deteriorations due to many factors such as environmental, nuclear radiation or even construction deficiencies. The use of nondestructive test is one of the reliable methods to inspect structural members. In this case, GPR has a good capability to detect inside deteriorations of concrete structures. However, in many cases it is hard to inspect structural members by hand due to safety issues or inaccessibility. Thus, an alternative way to reduce such risks is to employ robot to carry nondestructive equipment. In this research, twelve reinforced concrete RC beams (8 x 16 x 96, width, height and length) are cast in the lab. Three RC beams have no defect and nine others various defects such as corrosion, de-bonded bars, void, delamination and honeycombing. The one-point load is applied at the center of the RC beam. The loading level is carried out at three levels: 50%, 75% and 100% of maximum load and total load-displacement diagram are performed. The load is held at each level and the robotic GPR is used to scan the side of RC beams. Then, RADAN software is employed to find out any defects at different loading conditions and visualize the crack propagation. The RADAN results show that the pattern of crack propagation for corrosion and debonding are same. Also, the load-displacement results present that inside defect cause reduction of load-capacity of RC beam. (authors)

12 MANAGEMENT OF RADIOACTIVE AND NON-RADIOACTIVE W↗
DOE OSTI2022

The Electrochemical Behavior of As-Prepared Aluminum Alloy A360 Produced by Selective Laser Melting Fabrication with and without a Trivalent Chromium Process Conversion Coating

In this paper, we report on the electrochemical behavior and corrosion resistance of as-prepared aluminum alloy, A360 (AlSi10Mg), fabricated by additive manufacturing, with and without a trivalent chromium process conversion coating. Selective laser melting was the 3D printing process used for the alloy build. The corrosion suppression provided by the coating system was assessed through electrochemical measurements and accelerated degradation testing during a 14-day continuous neutral salt-spray exposure. The results indicate that the conversion coating can be formed by solution pretreating (degreasing and deoxidation) the alloy (X-Z plane perpendicular to the build plane) with its native surface roughness (as-prepared) followed by immersion for 10, 15 or 20 min in the coating bath. All three immersion times provide an equivalent level of corrosion protection to the alloy. The conversion coating suppresses both anodic and cathodic currents, increases the polarization resistance, and provides both anodic and cathodic corrosion protection to the as-prepared alloy. The conversion-coated specimens exhibit good stand-alone corrosion resistance during a 14-day neutral salt-spray exposure with corrosion intensity values (g/m 2 -year) ~10x lower than values for the uncoated, as-prepared alloy specimens.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Experimental Methods for the Performance Test of Environment-Assisted Cracking (EAC) in Nuclear Industry and Examples through NSUF

Environmentally assisted cracking (EAC) is a critical failure mode in nuclear reactor environments, where materials are exposed to high temperatures, radiation, and corrosive media. Specific EAC studies in nuclear environments include stress corrosion cracking in primary water chemistry, irradiation-assisted stress corrosion cracking (IASCC) under neutron exposure, and hydrogen induced cracking (HIC) in reactor pressure vessels. The experimental methodologies of EAC include slow strain rate testing (SSRT), constant load, and cyclic loading techniques, conducted in autoclaves designed to simulate the reactor’s operational environments. This paper highlights several experimental case studies, especially on IASCC, conducted within the Nuclear Science User Facilities (NSUF).

36 - MATERIALS SCIENCE↗