NASA NTRS2018

Update - Body of Knowledge (BOK) for Copper Wire Bonds

Copper wire bond technology developments continue to be a subject of technical interest to the NASA (National Aeronautics and Space Administration) NEPP (NASA Electronic Parts and Packaging Program) which funded this update. Based on this new research, additional copper bond wire vulnerabilities were found in the literature - Crevice corrosion, intrinsic degradation of palladium coated copper wire, congregation of palladium near ball bond interface leading to failure, residual aluminum pad metallization impact on device lifetimes, stitch cracking phenomena, package delamination's that have resulted in wire bond failures and device failure due to elemental sulfur. A search of the U.S.A. patent web site found 3 noteworthy patents on the following developments: claim of a certain IMC (Intermetallic Compound) thickness as a mitigation solution to chlorine corrosion; claim of using materials with different pHs to neutralize contaminants in a package containing copper wire bonds; and a discussion on ball shear test threshold values for different applications. In addition, an aerospace contractor of military hardware had a presentation on copper bond wires where it was reported that there was a parametric shift and noise susceptibility of devices with copper bond wires which affected legacy design performance. A review of silver bond wire (another emerging technology) technical papers found that an electromigration failure mechanism was evident in device applications that operate under high current conditions. More studies may need to be performed on a comprehensive basis. Research areas for consideration are suggested, however, these research and or qualification/standard test areas are not all inclusive and should not be construed as the element (s) that delivers any potential copper wire bond solution. A false sense of security may occur, whenever there is a reliance on passing any particular qualification, standard, or test protocol.

Rutkowski, E.↗
NASA NTRS2018

Residual Stress Mapping of As-Built and Hot Isostatic Pressure Treated GRCop-84 as Fabricated by Selective Laser Melting

GRCop-84, a copper alloy developed by NASA Glenn Research Center (GRC) with the starting At% (atomic percent) Cu-8 Cr-4 Nb, has a copper matrix with a fine intermetallic dispersion of Cr2Nb (cubic Laves phase C15). The alloy is being developed for high-heat-flux applications and has excellent high temperature properties including retention of tensile strength at high temperatures, high thermal conductivity, and excellent creep resistance. GRCop-84 has shown higher survivability rates than other metal additive alloys, good surface finish, and requires less operator tweaking for builds, and this is not fully understood. Neutron diffraction provides an accurate, non-destructive method of measuring the thermal stresses accumulated during production; the primary source of failure before annealing. The unstressed lattice spacing (d (sub 0)), residual stress, and distribution have been characterized for simple shapes in HIP (Hot Isostatic Pressing,) and as-built conditions made with SLM (Selective Laser Melting), a powder bed fusion method, with the HIP samples showing significantly reduced stresses concentrations than the as-built.

Minnecci, Robert↗
NASA NTRS2019

Fatigue Behavior of Coated Titanium Alloys

Advanced multi-component TiAlCrTaSiN-based multilayered coatings were developed and processed onto Ti-6Al-4V (Ti-6-4) and GammaMet PX (GMPX or TiAl) alloys by a magnetron-enhanced physical vapor deposition technique. The coatings have recently been in development with the goal of improving advanced titanium alloy, turbine engine component durability and oxidation-erosion resistance. In this work, the performance of the multi-component coating system (including the outer layer nitride based coating and inner TiAlCrSi oxidation barrier bond coat) was studied, and the coating's influence on the fatigue behavior of the titanium-based alloys were compared. Although the multi-component coating was initially optimized to improve the coating's high temperature oxidation and erosion resistance, the lower ductility nitride-based coating needs further work on microstructure or composition to improve its mechanical stress resistance and strain tolerance for use in cyclically loaded, turbine blade operating conditions. This is particularly true for GMPX and other γ-TiAl alloys because these intermetallic titanium alloys have limited ductility and are very sensitive to defects such as coating cracks. However, the inner layer TiAlCrSi-coating had better adhesion and ductility, and may be a suitable choice to improve the oxidation resistance of titanium alloys.

Oxidation Barrier Coatings↗
NASA NTRS2019

Fabrication and Performance of NiCuCoFeMn High Entropy Alloy Nanopastes for Brazing Inconel 718

Overview: High entropy alloys (HEAs) are a class of metallic alloys consisting of 5 plus elemental components and have four core effects - 1. High mixing entropy - 2. Sluggish diffusion kinetics - 3. High lattice distortion - 4. Cocktail effect; Boron-free, silicon-free brazing materials for nickel superalloys to avoid brittle intermetallic and eutectic phase formation; Size-dependent melting point depression can eliminate the need for boron, silicon and other melting point depressants; A Ni-Mn-Fe-Co-Cu HEA with low solidus and liquidus temperatures (1080 °C and 1150 °C) was developed; Low solidus and liquidus temperatures of the HEA combined with the nanoscale melting point depression in this study; Bulk HEA fabricated by induction melting of elemental powders; HEA nanoparticles (NPs) fabricated by ball milling of the HEA micropowder; Inconel 718 was laser brazed in air using the HEA and bulk and NP performances are compared.

Bridges, Denzel↗
NASA NTRS2014

Resilient and Corrosion-Proof Rolling Element Bearings Made from Superelastic Ni-Ti Alloys for Aerospace

Mechanical components (bearings, gears, mechanisms) typically utilize hardened construction materials to minimize wear and attain long life. In such components, loaded contact points (e.g., meshing gear teeth, bearing balls-raceway contacts) experience high contact stresses. The combination of high hardness and high elastic modulus often leads to damaging contact stress and denting, particularly during transient overload events such as shock impacts that occur during the launching of space vehicles or the landing of aircraft. In this webinar, Dr. DellaCorte will introduce the results of a research project that employs a superelastic alloy, Ni-Ti for rolling element bearing applications. Bearings and components made from such alloys can alleviate many problems encountered in advanced aerospace applications and may solve many terrestrial applications as well

intermetallics↗
NASA NTRS2016

Hardness and Microstructure of Binary and Ternary Nitinol Compounds

The hardness and microstructure of twenty-six binary and ternary Nitinol (nickel titanium, nickel titanium hafnium, nickel titanium zirconium and nickel titanium tantalum) compounds were studied. A small (50g) ingot of each compound was produced by vacuum arc remelting. Each ingot was homogenized in vacuum for 48 hr followed by furnace cooling. Specimens from the ingots were then heat treated at 800, 900, 1000 or 1100 degree C for 2 hr followed by water quenching. The hardness and microstructure of each specimen was compared to the baseline material (55-Nitinol, 55 at.% nickel - 45 at.% titanium, after heat treatment at 900 degC). The results show that eleven of the studied compounds had higher hardness values than the baseline material. Moreover, twelve of the studied compounds had measured hardness values greater 600HV at heat treatments from 800 to 900 degree C.

intermetallics↗
NASA NTRS2017

NiTi Alloys: New Materials that enable Shockproof, Corrosion Immune Bearings

Though steel is the dominant material of choice for mechanical components (bearings and gears) it has intrinsic limitations related to corrosion and plastic deformation. In contrast, dimensionally stable nickel-rich Ni-Ti alloys, such as Nitinol 60, are intrinsically rustproof and can withstand high contact loads without damage (denting). Over the last decade, focused RD to exploit these alloys for new applications has revealed the science behind NiTi's remarkable properties. In this presentation, the state-of-the-art of nickel-rich NiTi alloys will be introduced along with a discussion of how NASA is adopting this new technology inside the space station water recycling system as a pathfinder for more down-to-earth tribological challenges.

bearings↗
NASA NTRS2018

Friction and Wear of Unlubricated NiTiHf with Nitriding Surface Treatments

The unlubricated friction and wear properties of the superelastic materials NiTi and NiTiHf, treated by either gas nitriding or plasma nitriding, have been investigated. Pin on disk testing of the studied materials was performed at sliding speeds from 0.01 to 1m/s at normal loads of 1, 5 or 10N. For all of the studied friction pairs (NiTiHf pins vs. NiTi and NiTiHf disks) over the given parameters, the steady-state coefficients of friction varied from 0.22 to 1.6. Pin wear factors ranged from approximately 1E-6 against the NiTiHf and plasma nitrided disks to approximately 1E-4 for the gas nitrided disks. The plasma nitrided disks provided wear protection in several cases and tended to wear by adhesion. The gas nitrided treatment generated the most pin wear but had essentially no disk wear except at the most severe of the studied conditions (1N load and 1m/s sliding speed). The results of this study are expected to provide guidance for design of components such as gears and fasteners.

friction↗
NASA NTRS2018

Fractographic Analysis of 60-Nitinol Bearing Races

Fracture surfaces on a failed bearing race made from 60-Nitinol (60 wt% Ni - 40 wt% Ti) were analyzed. The bearing had experienced excessive localized heat due to an issue during machining that may have resulted in dimensional distortion. However, the classical fracture features that were identified by scanning electron microscopy and the fracture origins coincided with high concentrations of TiC-based contamination. Lessons learned for processing and quality control are discussed. An attempt to use x-ray diffraction to directly measure residual stresses imparted from the required heat treatment is also discussed.

intermetallics↗
NASA NTRS2024

Metallurgical and Thermal Properties of 57Ni–40Ti–3Hf (wt%)

Selected properties of 57Ni-40Ti-3Hf (wt%) were measured to further develop this material for use in aerospace rolling-element bearings. The average grain size and microindentation hardness of the material at room temperature were 90 μm and 549 HV, respectively. From room temperature to 500 °C, electrical resistivity increased from 8.9×10 –7 to 11.3×10 –7 Ω⋅m, thermal expansion coefficients varied from 1.1×10 –5 to 1.2×10 –5 mm/mm⋅°C, specific heat increased from 0.44 to 0.53 W⋅sec/g⋅K, thermal diffusivity rose from approximately 0.003 to 0.005 cm 2 /sec and thermal conductivity increased from approximately 0.09 to 0.19 W/cm⋅K. The behavior of the material can be explained by well-known metallurgical theory. These results are expected to provide a basis for design and modeling of future aerospace components.

intermetallics↗
NASA NTRS2025

Metallurgical and Thermal Properties of 57Ni-40Ti-3Hf (wt%)

Selected properties of 57Ni-40Ti-3Hf (wt%) were measured to further develop this material for use in aerospace rolling-element bearings. The average grain size and microindentation hardness of the material at room temperature were 90 μm and 549 HV, respectively. From room temperature to 500 °C, electrical resistivity increased from 8.9×10–7 to 11.3×10–7 Ω⋅m, thermal expansion coefficients varied from 1.1×10–5 to 1.2×10–5 mm/mm⋅°C, specific heat increased from 0.44 to 0.53 W⋅sec/g⋅K, thermal diffusivity rose from approximately 0.003 to 0.005 cm2/sec and thermal conductivity increased from approximately 0.09 to 0.19 W/cm⋅K. The behavior of the material can be explained by well-known metallurgical theory. These results are expected to provide a basis for design and modeling of future aerospace components.

rule of mixtures↗