DOE OSTI2022

Correlating the Morphological Changes to Electrochemical Performance During Carbon Corrosion in Polymer Electrolyte Fuel Cells

A mechanistic understanding of carbon corrosion in polymer electrolyte fuel cells (PEFCs) is required to design durable catalyst layers. Uncontrolled startup and shutdown of PEFCs cause electrochemical oxidation of carbon, which leads to several degradation phenomena, such as loss in electrochemical surface area (ECSA), pore structure collapse or increase in mass transport resistance. In this study, the chronology of morphological changes in the cathode catalyst layer due to carbon corrosion was identified and correlated with electrochemical performance degradation. PEFCs were subjected to the Department of Energy carbon corrosion accelerated stress test (AST) protocol. The study revealed two phases: in the initial phase (~500 AST cycles), amorphous carbon in contact with Pt nanoparticles oxidized fast. Rapid carbon loss and catalyst layer thinning occurred, but pore structure did not change significantly. Pt nanoparticles detached from the support and ECSA decreased drastically. In the second phase (~1500 AST cycles), carbon corrosion slowed down, but severe pore structure collapse was observed. Porosity and pore connectivity within the cathode catalyst layer decreased considerably. Electrochemical diagnostics corroborated this finding by showing significantly higher O2 mass transport resistance. Lastly, no significant change was observed in the concentration of oxides on the carbon surface after AST. But overall water management in the cathode catalyst layer deteriorated as the pore structure collapsed. This study provides an in-depth understanding of morphological changes during PEFC carbon corrosion AST protocol and motivates novel material design strategies to enable durable PEFCs.

catalyst layers↗
NASA NTRS2001

The SHIVA Project: Spaceflight Holography in a Virtual Apparatus

The poster summarizes theoretical and experimental concepts used in the development of the proposed NASA flight experiment SHIVA (Spaceflight Holography in a Virtual Apparatus). SHIVA exploits a unique holography-based, diagnostics tools to understand the behavior of small particles subjected to transient accelerations. Flight experiment protocols and apparatus will test model equations, characterize the acceleration environment and other microgravity phenomena. The primary objective of SHIVA is to enhance the current understanding of complex dynamics of small particles subjected to transient microgravity conditions. Existing theory did not fully describe the movement of particles in fluids in the microgravity environment. Results from recent ground-based experiments and comparison with the model recently developed by Rangel and Coimbra are presented.

Jim Trolinger↗
DOE OSTI2021

High-Current Density Durability of Pt/C and PtCo/C Catalysts at Similar Particle Sizes in PEMFCs

The durability of carbon supported PtCo-alloy based nanoparticle catalysts play a key role in the longevity of proton-exchange membrane fuel cells (PEMFC) in electric vehicle applications. To improve its durability, it is important to understand and mitigate the various factors that cause PtCo-based cathode catalyst layers (CCL) to lose performance over time. These factors include i) electrochemical surface area (ECSA) loss, ii) specific activity loss, iii) H + /O 2 -transport changes and iv) Co 2+ contamination effects. We use a catalyst-specific accelerated stress test (AST) voltage cycling protocol to compare the durability of Pt and PtCo catalysts at similar average nanoparticle size and distribution. Our studies indicate that while Pt and PtCo nanoparticle catalysts suffer from similar magnitudes of electrochemical surface area (ECSA) losses, PtCo catalyst shows a significantly larger cell voltage loss at high current densities upon durability testing. The distinctive factor causing the large cell voltage loss of PtCo catalyst appears to be the secondary effects of the leached Co 2+ cations that contaminate the electrode ionomer. A 1D performance model has been used to quantify the cell voltage losses arising from various factors causing degradation of the membrane electrode assembly (MEA).

08 HYDROGEN↗
DOE OSTI2021

Mitigation of PtCo/C Cathode Catalyst Degradation via Control of Relative Humidity

Maintaining the high performance of proton-exchange membrane fuel cells (PEMFC) over the course of its lifetime is a key enabling factor for its successful commercialization as a primary power source in zero-emission transportation applications. In this context, it is important to mitigate the degradation of PtCo-alloy based cathode catalysts used for oxygen reduction reaction (ORR). PtCo-alloy catalysts exhibit high activity at beginning-of-life (BOL) which tends to decrease during operation due to loss of electrochemical surface area (ECSA) and dissolution-contamination related effects of the Co-alloying component. Here, we demonstrate the use of relative humidity (RH) of the inlet gases as a controllable parameter to mitigate the degradation of PtCo-alloy catalyst degradation. We employ a catalyst-specific voltage cycling accelerated stress test (AST) durability protocol as a function of inlet RH to degrade PtCo catalysts. A series of in situ electrochemical diagnostics and ex situ characterizations have been carried out to investigate the catalyst layer characteristics at end-of-test (EOT). Our results show that at sub-saturated conditions of durability protocol operation, PtCo catalyst sustains higher EOT H 2 /air performance due to better retention of ECSA and smaller impact of Co 2+ dissolution/contamination.

25 ENERGY STORAGE↗
DOE OSTI2021

Investigation of Membrane Chemical Degradation as a Function of Catalyst Platinum Loading

Membrane chemical degradation is one of many factors that can impact fuel cell durability. Additionally, the fuel cell’s lifetime heavily depends on the membrane and its ability to maintain chemical and mechanical integrity. Previous studies indicate that chemical degradation is due to the formation of hydroxyl radicals that attack the polymer structure resulting in membrane thinning, pinhole formation, and the release of fluoride and sulfate ions. Membrane durability was investigated using ultra-low Pt electrode loadings (≤ 0.1 mg Pt cm -2 ). Accelerated stress testing (US-DOE protocols) demonstrated that the degradation rate was found to increase with higher Pt loadings. This is most likely due to more heterogeneous sites for radical formation due to hydrogen crossover to the cathode. We also explored membrane degradation rates while varying catalyst layer thickness, ionomer to carbon ratio, and types of carbon support. All of the aforementioned variables impact the membrane degradation rates.

25 ENERGY STORAGE↗
DOE OSTI2024

Photovoltaic Cable Jackets: A Comparison of Representative Products Using Combined-Accelerated Stress Testing [Slides]

Photovoltaic (PV) cables facilitate the distribution of electricity collected from modules to the energy grid. Durable cabling enables continuous operation of PV installations, whereas cables with a lifetime less than the modules must be replaced - reducing electricity generation and adding to the operating expense. This study primarily focusses on the aging of the key cable types using the combined-accelerated stress testing (C-AST) protocol. Representative cables for utility, building, and control/auxiliary applications were examined. Cable jacket materials examined include: polyolefin, polyethylene, polyamide, poly(vinyl chloride), chlorinated polyethylene, thermoplastic elastomer, and ethylene propylene diene monomer rubber. Specimen characterizations applied include: optical microscopy, mechanical profilometry, instrumented indentation, scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS), Fourier-transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), and differential scanning calorimetry (DSC). A variety of performance and durability characteristics were observed, depending on the base material, polymer formulation, and jacket color. The results from C-AST are analyzed and discussed relative to a recent industry survey on electronic balance of system components in addition to a recent study where similar cables were aged using steady state ultraviolet weathering (International Electrotechnical Commission Technical Specification 62788-7-2). Recommendations are made for the screening, industry qualification, and service life prediction of PV cable jackets.

24 POWER TRANSMISSION AND DISTRIBUTION↗
DOE OSTI2020

Advancing reliability assessments of photovoltaic modules and materials using combined-accelerated stress testing

Previously undiscovered failure modes in photovoltaic (PV) modules continue to emerge in field installations despite passing protocols for design qualification and quality assurance. Failure to detect these modes prior to widespread use could be attributed to the limitations of present-day standard accelerated stress tests (ASTs), which are primarily designed to identify known degradation or failure modes at the time of development by applying simultaneous or sequential stress factors (usually two at most). Here, we introduce an accelerated testing method known as the combined-accelerated stress test (C-AST), which simultaneously combines multiple stress factors of the natural environment. Simultaneous combination of multiple stress factors allows for improved identification of failure modes with better ability to detect modes not known a priori. A demonstration experiment was conducted that reproduced the field-observed cracking of polyamide- (PA-) and polyvinylidene fluoride (PVDF)–based backsheet films, a failure mode that was not detected by current design qualification and quality assurance testing requirements. In this work, a two-phase testing protocol was implemented. The first cycle (“Tropical”) is a predominantly high-humidity and high-temperature test designed to replicate harsh tropical climates. The second cycle (“Multi-season”) was designed to replicate drier and more temperate conditions found in continental or desert climates. Testing was conducted on 2 × 2-cell crystalline-silicon cell miniature modules constructed with both ultraviolet (UV)–transmitting and UV-blocking encapsulants. Cracking failures were observed within a cumulative 120 days of the Tropical condition for one of the PA-based backsheets and after 84 days of Tropical cycle followed by 42 days of the Multi-season cycle for the PVDF-based backsheet, which are both consistent with failures seen in fielded modules. In addition to backsheet cracking, degradation modes were observed including solder/interconnect fatigue, various light-induced degradation modes, backsheet delamination, discoloration, corrosion, and cell cracking. The ability to simultaneously apply multiple stress factors may allow many of the test sequences within the standardized design qualification procedure to be performed using a single test setup.

14 SOLAR ENERGY↗
DOE OSTI2020

Correlation of Advanced Accelerated Stress Testing with Polyamide-Based Photovoltaic Backsheet Field-Failures

Cracking of polyamide (PA)-based photovoltaic (PV) backsheet materials has been widely reported for field-aged modules. Failure was not detected by conventional accelerated stress tests (ASTs), which lacked the necessary combination of stress factors and/or factor sequences. PA-based AAA backsheet cracking has since been reproduced through combined and sequential stress testing. Planar- and cross-sectional-optical microscopy as well as Fourier-transform Infrared Spectroscopy (FTIR), have been used to elucidate the mechanical and chemical changes which lead to failure of the backsheet. Field-aged backsheet samples demonstrating failure in various climates (including locations in China and Italy) are also analyzed. Through the analysis, a comparison is made between the different stress testing protocols and the field-aged samples to validate relevance of the advanced stress tests. It is shown that the changes induced through combined-accelerated stress testing (C-AST) were most representative of changes induced by the field, supporting the relevance of C-AST and providing validity for the test protocol.

14 SOLAR ENERGY↗
DOE OSTI2025

A harmonized protocol to assess the single-cell performance of proton exchange membrane water electrolyzers

The harmonization of testing protocols for proton exchange membrane (PEM) electrolyzers is essential for ensuring accurate and reliable performance assessments and accelerating the development of hydrogen production technologies. This protocol provides a structured approach to PEM electrolyzer setup and testing, incorporating key considerations for test station design and single-cell characterization techniques. Polarization curves and electrochemical impedance spectroscopy (EIS) are detailed, along with best practices from academic and industry research groups to enhance data accuracy and comparability. By addressing material variability and harmonizing testing methodologies, this framework enables more precise evaluations of membrane electrode assemblies and electrolyzer components. Harmonized protocols not only streamline development efforts but also foster collaboration across institutions, ultimately supporting the commercialization of hydrogen solutions through improved stack efficiency and durability.

08 HYDROGEN↗
DOE OSTI2024

Corrosion-Resistant Non-Carbon Electrocatalyst Supports for PEFCS

Insufficient durability of commercial catalysts is a persistent issue for PEFC applications.1 Herein, Pt on Nb-doped-TiO 2 is reported as a highly durable electrocatalyst on which the direct 4-electron reduction of oxygen to water is more facile compared to Pt/C. All performance metrics are reported comparing Pt/Nb-TiO2 with a 15% Pt loading, against a commercial Pt/C catalyst (46.5% Pt loading, Tanaka, K. K.). Nb-doped-TiO 2 with high surface area and high electronic conductivity was synthesized using the supercritical fluid method. Initially, the durability of the catalyst was characterized using accelerated stability tests (ASTs) involving 10,000 high potential cycles (DOE/FCCJ protocol) and the Pt/Nb-TiO 2 was found to retain 78% of its initial electrochemically active surface area (ECSA) compared to the 57.6 % retained by Pt/C. These observations were in excellent agreement with previous reports that the Pt particle size of Pt/C grew from 2nm to 8nm during the AST protocol along with severe corrosion and amorphization of the carbon surface.2, 3 TEM and XPS studies of the Pt-Nb-doped-TiO 2 catalyst showed that the Pt particle size grew from 3nm to 6nm and the Nb(IV) and Ti(III) in the support were oxidized to Nb(V) and Ti(IV) after the durability test. Thus, the improvement in Pt/Nb-TiO 2 ECSA retention was attributed to the lower extent of particle growth and lack of oxidative support loss upon oxidation as compared to Pt/C. The oxygen reduction reaction (ORR) performance was characterized by linear polarization using a rotating disk electrode (RDE). The electrochemical surface areas of Pt/Nb-TiO 2 and Pt/C were found to be 48m2·g -1 and 83m2·g -1 respectively, and the mass activity for the ORR at 0.9V vs. RHE were found to be 150 mA·mg-1Pt and 124 mA·mg-1Pt respectively. The improved mass activity on Pt/Nb-TiO 2 was attributed to strong metal support interaction (SMSI) between the Nb-TiO 2 support and the Pt catalyst based on the 625 meV decrease in the binding energy of the Pt4f x-ray photo-electron spectroscopy (XPS) peaks of Pt/Nb-TiO 2 compared to Pt/C. To quantify the impact of the SMSI, a kinetic model was applied to calculate the elementary reaction rate constants for the various steps of the ORR on both catalysts. The reaction rate constant (k1) for the direct 4-electron transfer pathway to produce H 2 O was significantly larger in Pt/Nb-TiO 2 as compared to Pt/C. Thus, the reduction in the electron binding energy as observed in the XPS was found to aid the facile filling of the higher energy 2p orbitals of O 2 thereby leading to improved 4-electron transfer kinetics and improved overall activity.

08 HYDROGEN↗
DOE OSTI2023

PV Module BOM and Test Data

This dataset contains compiled results from annual PV Module Reliability Scorecards published by PV Evolution Labs – also known as PVEL. These scorecards show summary results of PV module testing performed by PVEL and name specific models of PV modules as "Top Performers" in various tests. Full details on testing, Top Performer status and other criteria for inclusion in Scorecards are documented in reports and online documentation available from https://www.modulescorecard.pvel.com. This dataset is not affiliated with PVEL and is intended only to simplify sorting and filtering Scorecard data and finding specific PV module models and Top Performer results. Note that data included in Scorecards has evolved over time, so not all data is available for all years, and testing protocols and Scorecard criteria have been changed over time.

14 SOLAR ENERGY↗
DOE OSTI2025

Durability of Pt-Alloy Catalyst for Heavy-Duty Polymer Electrolyte Fuel Cell Applications under Realistic Conditions

As an emerging technology, polymer electrolyte fuel cells (PEFCs) powered by clean hydrogen can be a great source of renewable power generation with flexible utilization because of high gravimetric energy density of hydrogen. To be used in real-life applications, PEFCs need to maintain their performance for long-term use under a wide range of conditions. Therefore, it's important to understand the degradation of the PEFC under protocols that are closely related to the catalyst lifetime. Alloying Pt with transitional metal improves catalyst activity. It is also crucial to understand Pt alloys degradation mechanisms to improve their durability. To study durability of Pt alloys, accelerated stress tests (ASTs) are performed on Pt-Co catalyst supported on two types of carbon. Two different AST protocols were being studied: Membrane Electrolyte Assembly (MEA) AST based on the protocol introduced by the Million Mile Fuel Cell Truck consortium in 2023 and Catalyst AST, adopted from the U.S. Department of Energy (DoE).

25 ENERGY STORAGE↗
DOE OSTI2023

(Invited) Fuel Cell Component Durability for Million Mile Fuel Cell Trucks

While significant advances have been made and early commercial fuel cell light-duty vehicles (LDVs) are starting to be produced, fuel cells in the heavy-duty-vehicle (HDV) transportation sector (including trucks, long-haul semitrailers, maritime, trains, etc.) are nascent, despite the fact that advantages of fuel cells compared to both diesel and electric powertrains are very compelling in terms of emissions, charging time, efficiency, power-to-weight ratio, among others. However, the fuel-cell technology for HDVs requires a paradigm shift in fuel-cell research and development compared to LDVs, where the emphasis becomes efficiency and improvements in durability instead of a focus on increased power densities and lower cell costs. Heavy-duty applications require significantly longer vehicle lifetimes (>25,000 hours/1,000,000 miles for heavy-duty trucks), and therefore require improved fuel cell durability compared to light-duty vehicles. In 2020, HFTO formed the Million Mile Fuel Cell Truck Consortium (M2FCT) that includes a core team of five national laboratories to overcome durability and efficiency challenges in PEMFCs for heavy-duty applications with an initial focus on long-haul trucks. While targets and testing protocols have been developed for light-duty vehicles, the same level of targets and testing protocols have not been established for heavy-duty transportation. With operational times of greater than > 25,000 hours required, the need for well-developed accelerated stress tests (ASTs) is amplified. Results from these ASTs demonstrate the need for more durable electrode layers and well-controlled potential variations. Finally, this presentation will provide an overview of the DOE's Fuel Cell R&D approach, highlighting past and current activities, as well as strategies to enable fuel cell competiveness for heavy-duty applications.

25 ENERGY STORAGE↗
NASA NTRS1994

An artifical corrosion protocol for lap-splices in aircraft skin

This paper reviews the progress to date to formulate an artificial corrosion protocol for the Tinker AFB C/KC-135 Corrosion Fatigue Round Robin Test Program. The project has provided new test methods to faithfully reproduce the corrosion damage within a lap-splice by accelerated means, the rationale for a new laboratory test environment, and a means for corrosion damage quantification. The approach is pragmatic and the resulting artificial corrosion protocol lays the foundation for future research in the assessment of aerospace alloys. The general means for quantification of corrosion damage has been presented in a form which can be directly applied to structural integrity calculations.

Shaw, Bevil J.↗
DOE OSTI2022

Lithium-Ion Battery Design for Grid-Scale Energy Storage App

A software that delivers parameters from energy storage system (ESS) to container, rack, module and single cell design, as well as data analysis on arbitrage energy and frequency regulation of ESS in different regions, has been developed. The Lithium-ion Battery Design for Grid-scale Energy Storage App V1.0 has the capability to output the system, module and cell design with the energy, power, capacity, group method, cost of single cell, and single cell test protocol which break down from input energy storage system data in different regions. The default chemistry of the battery is LiFePO4 and graphite. The energy density of the graphite/LiFePO 4 pouch cell ranges from 100 Wh/kg to 200 Wh/Kg in the software. Graphite/LiFePO 4 pouch cell (up to 1Ah in lab) manufacturing line is also built and can be used to evaluate the test protocol, moreover, for electrolyte evaluation in other ESMI seedling projects. The software enables rapid prototyping to accelerate energy storage research, development, and manufacturing.

Liu, Dianying↗
DOE OSTI2022

Feature engineering for machine learning enabled early prediction of battery lifetime

Accurate battery lifetime estimates enable accelerated design of novel battery materials and determination of optimal use protocols for longevity in deployments. Unfortunately, traditional battery testing may take years to reach thousands of cycles. Recent studies have shown that machine learning (ML) tools can predict lithium-ion battery lifetimes from 100 or fewer preliminary cycles, representing only a few weeks of cycling. Until now, conclusions about the efficacy and broad applicability of these predictions across a variety of cathode chemistries have been limited by available experimental information. In this work, we leverage a battery cycling dataset representing six cathode chemistries (NMC111, NMC532, NMC622, NMC811, HE5050, and 5Vspinel), multiple electrolyte/anode compositions, and 300 total carefully prepared pouch batteries to explore feature selection and battery chemistry's role in ML battery lifetime predictions. Here, a mean absolute error (MAE) of 78 cycles in prediction was seen for a chemistry-spanning test set from 100 preliminary cycles. Furthermore, an MAE of 103 cycles was seen when using only the first cycle. This study represents an in-depth investigation of strategies for feature selection for battery lifetime prediction, ML models' generalization across multiple battery chemistries, and predictions beyond the training set in the chemical space.

25 ENERGY STORAGE↗