Results for “Chemical Compatibility Examination” — Page 2

DOE OSTI2023

Robust highly durable solid oxide fuel cell cathodes – Improved materials compatibility & self-regulating surface chemistry

Solid oxide fuel cells (SOFCs) are electrochemical conversion devices that directly transform hydrogen or hydrocarbon fuels to electricity, with energy efficiencies as high as 90%, coupled with reduced emissions. Several factors, however, remain to be addressed when considering scale-up of SOFC technology, including the need to overcome decreased performance due to sluggish rates of the oxygen reduction reaction (ORR) at the cathode under reduced temperatures and susceptibility to degradation in performance from surface poisoning e.g. from chromia, while limiting the use of critical raw materials (lanthanides and transition metals) present in high performing mixed ionic electronic conducting electrodes like (La,Sr)CoO 3 (LSC). In this project we explored the key descriptors for determining ORR activity in SOFC electrodes and tried to recover performance degradation by applying them to SOFC electrodes. In order to do this, we first selected a model mixed ionic electronic conducting (MIEC) oxide, Pr-doped CeO 2 (Pr 0.1 Ce 0.9 O 2-δ , PCO), which is a chemically stable fluorite and free of inherent poison sources (e.g. Sr segregation in LSC) that potentially react with external impurities such as Cr-species vaporized from the interconnect. The three approaches originally planned in this project are as follows: 1) evaluation of scavenger exsolution characteristics, 2) study of scavengers gettering efficacy following Cr and Si poisoning and 3) integration of new compositions into porous electrodes. Among them, exceptional progress has been made in 2) and 3), especially understanding the role of surface infiltrants in impacting electrode performance and degradation of PCO materials. We found that the Smith acidity scale for binary oxides serves as a powerful descriptor for tuning and predicting the oxygen exchange kinetics on MIEC PCO surfaces. As a result, with infiltration with binary oxides, ranging from strongly basic (Li 2 O) to strongly acidic (SiO 2 ) onto the surface of porous PCO, it was possible to systematically vary the chemical surface exchange coefficient (k chem ) by 6 orders of magnitude! L i2 O increased k chem by nearly 1,000 times over that of pristine PCO, while SiO 2 decreased k chem by nearly the same factor. Strikingly, although the pre-exponential of k chem scales linearly with the acidity of the infiltrated binary oxide, there is nearly no change in the activation energy. With this insight, we attributed the origin of these dramatic changes in k chem values to the systematic increase and decrease in the surface electron density induced by infiltrated binary oxides. More interestingly, although both Cr 2 O 3 and SiO 2 were determined to be acidic by Smith, suggesting that this feature could likely be the primary reason that these compounds serve to poison the ORR on SOFC cathodes, the effect of poisoning could be subsequently tuned by adding multiple infiltrants and controlling their relative surface acidities. We also systematically examined the effect of serial infiltration of basic and acidic oxides. It turned out that serial infiltration of Li not only recovers approximately 20-fold degraded k chem of PCO by acidic Cr 2 O 3 but its k chem is enhanced even beyond that of the non-infiltrated PCO by more than three orders of magnitude. This was further verified with a screen-printing PCO symmetric cell in terms of the electrode performance (area-specific resistance, ASR) related to approach 3). These observations point to acidity as a key descriptor not only in tuning and predicting the ORR activity of SOFC cathodes that largely determines the overall performance of SOFC, but in mitigating and reactivating poisoned electrode performance. This work provides novel guidelines for making the electrode performance much more active and robust in SOFCs, which can further be applied to all applications requiring oxygen exchange reaction, such as electrolyzers, permeation membranes and gas sensors.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2024

Examining Graphite Degradation in Molten Salt Environments: A Chemical, Physical, and Material Analysis

Molten-salt reactors (MSRs) are Generation IV nuclear reactors that use liquid salt as a coolant and/or fuel. In several MSR designs, graphite serves as a moderator and/or reflector. However, due to limited experimental data and operational experience, our understanding of graphite behavior in molten salt environments remains incomplete. This report aims to identify the degradation mechanisms of nuclear graphite in MSRs, detail the mechanisms of each factor, and provide an initial assessment of their impact on the structural integrity of graphite components. This assessment is based on an extensive literature review and insights from subject matter experts. Furthermore, given the limited data, a modeling strategy using existing Grizzly software is proposed for a more thorough analysis where appropriate. Additionally, it presents mitigation strategies where applicable. The report covers physical degradation mechanisms such as infiltration, erosion, and abrasion, as well as chemical degradation mechanisms including fluorination, intercalation, corrosion, and oxidation. Molten salt can infiltrate the porous structure of graphite, leading to several detrimental effects. Entrapment of fissile products within the graphite pores can cause radiation damage and could pose challenges in the handling and disposal of contaminated components. The differential thermal expansion between the infiltrated salt and graphite, along with internal stress from pressurized molten salt and volumetric heating, can compromise the structural integrity of graphite. To mitigate these effects, employing ultra-fine graphite grades and applying sealants and coatings are effective strategies. A computational model based on coupled solid mechanics and heat transfer phenomena could be used to predict the internal stresses using Grizzly software. In pebble-bed MSRs, graphite fuel pebbles can cause abrasion against reactor components due to friction and wear. The severity of wear is influenced by various factors such as temperature, environment, and the presence of lubricants. Tribological studies reveal that higher temperatures and molten salt environments, such as FLiBe, significantly reduce wear rates compared to dry conditions. Additionally, the chemical composition of the salt can further optimize graphite's tribological performance. Long-term wear effects can be modeled by incorporating surface defects into the geometry and predict stresses under thermal and radiation effects using Grizzly software. Chemical degradation of graphite in a molten salt environment can occur through fluorination and intercalation. Fluorination can occur via replacement of hydrogen or oxygen atoms, or at the active sites, but does not cause structural degradation. Intercalation, on the other hand, can lead to exfoliation, where layers of graphite separate and peel away, damaging the graphite. Protective coatings can enhance graphite's resistance to intercalation. Graphite generally exhibits good chemical stability in molten salt environments, though it can corrode under specific conditions, particularly in the presence of impurities or oxidants. Studies have shown that protective coatings, such as plasma-sprayed partially stabilized zirconia (PSZ), can effectively prevent such degradation. Corrosion behavior varies significantly with different graphite grades and coating applications, underscoring the need for detailed studies on uncoated and coated graphite to understand and mitigate corrosion mechanisms in MSRs. Research indicates that the presence of oxidants and impurities can accelerate graphite degradation in molten salts, making it essential to explore acceptable impurity limits. Oxidation is another critical degradation mechanism, leading to weight loss and structural damage due to the formation of CO and CO 2 from the reaction of carbon atoms with oxygen. This process creates new porosity and compromises graphite's integrity. While extensive research on graphite oxidation has been conducted for gas-cooled reactors, studies specific to MSRs are limited. Findings from the coal industry suggest that molten alkali metal salts can significantly accelerate graphite oxidation, a hypothesis worth exploring for fluoride salts in MSRs. Understanding oxidation behavior in MSRs is vital for developing protective measures. The analysis of post-irradiated graphite from the MSRE experiment demonstrated exceptional chemical compatibility with molten fluoride salt, suggesting that the extent of chemical attack on graphite largely depends on the salt's infiltration capability. Therefore, the use of ultra-fine grade graphite could help mitigate chemical degradation effects. Existing oxidation modeling capabilities in Grizzly, which use reaction-diffusion equations to model graphite-air interactions, could be adapted to simulate the chemical degradation effects of graphite in molten salt environments.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗