Nickel-base superalloy has a strength of 20,000 psi at 2,200 degrees F, approximately double the strength of the strongest available cast nickel-base alloys. It is not subject to the formation of embrittling phases upon long time exposure at intermediate temperatures.
Tensile and stress-rupture tests were conducted on wires of W-Hf-C, W-Re-Hf-C, ASTAR 811C (a tantalum alloy), and B-88 (a columbium alloy) at room temperature, 1093 C (2000 F), and 1204 C (2200 F). Metallographic examinations were also made of the wire microstructure after testing. Ultimate tensile strength values up to 2170 meganewtons per square meter (314000 psi) at 1093 C (2000 F) and 1940 meganewtons per square meter (281 000 psi) at 1204 C (2200 F) were obtained for W-Re-Hf-C wire. The best strength values obtained for a 100-hour rupture life were, 1410 meganewtons per square meter (205 000 psi) at 1093 C (2000 F) and 910 meganewtons per square meter (132 000 psi) at 1240 C (2200 F) for W-Re-Hf-C wire. The properties obtained suggested that the wires studied showed promise as potential fiber reinforcement in the 1093 to 1204 C (2000 to 2200 F) temperature range.
Under NAS 8-27435, the Convair Aerospace Division of General Dynamics and their subcontractor, Hercules Incorporated, have conducted studies on the effects of moisture on the properties of fiber-reinforced resin composites and on the epoxy resins presently used in advanced composites. Data are presented on the resins and composites subjected to varying time/temperature/humidity or time/temperature/water-boil exposures. The effects of moisture on matrix, reinforcement, and fiber/resin interface are discussed and supported by experimental test data.
Si3N4 specimens having the composition 88.7 wt pct Si3N4-4.9 wt pct SiO2-6.4 wt pct Y2O3 were sintered at 2140 C under 25 atm N2 for 1 h and then subjected to a 5 h anneal at 1500 C. Crystallization of an amorphous grain-boundary phase resulted in the formation of Y2Si2O7. The short-time 1370 C strength of this material was compared with that of material of the same composition having no annealing treatment. No change in strength was noted. This is attributed to the refractory nature of the yttrium-rich grain-boundary phase (apparently identical in both glassy and crystalline phases) and the subsequent domination of the failure process by common processing flaws.
Explore the source record for details and available documents.
Explore the source record for details and available documents.
Current Ni-based alloys used in turbine blade applications are operating at 1100°C which is approximately 90% of the solidus of Ni-based alloys. Further increases in temperature can be achieved only through the use of alloys with higher solidus temperatures such as refractory alloys which include Mo, Nb, W, Ta alloys. Niobium has a unique combination of physical properties that include a high melting point (2468°C), lowest density (8.57 g/cc), and the lowest modulus amongst refractory alloys, a good thermal conductivity that increases from 45 W/mK at room temperature to 62 W/mK at 1093°C, good ductility with fabricability using traditional techniques, high strength, good creep resistance, and general chemical inactivity. Hence niobium alloys offer many advantages for use at the desired temperature of 1300°C. One of the major deterrents to the use of niobium and its alloys at high temperatures is achieving good oxidation resistance. In addition, achieving balanced properties of room temperature strength, ductility, fracture toughness, high temperature strength, and creep resistance required for 1300°C operation at a density of 9 g/cm 3 is extremely challenging since the addition of W which is a potent strengthener increases the density of the alloy. This project seeks to enable the development of a tri-layered turbine blade that can operate continuously at 1300°C with the core of the turbine blade providing good creep resistance, the second layer providing improved oxidation resistance over the core layer, and the third layer being an environmental barrier providing oxidation resistance. The objective of this Phase 1 project was to use computational modeling and advanced characterization tools to develop two classes of Nb alloys which could be used as the core layer and the transition layer. The first class of alloys developed in this project was a Nb-alloy designed to serve as the turbine blade core with excellent room temperature strength, ductility, and high temperature strength and creep resistance required for 1300°C operation. These alloys were designed to contain sufficient solute solution strengthening elements (W, Mo) but constrained by the density of alloy, along with the addition of elements such as Zr, Hf, Ta, C, and N to achieve a combination of primary and secondary carbide precipitation. A total of 38 “creep-resistant” alloys were designed and cast during the duration of the project. Processing techniques were developed to keep the oxygen contents as low as possible with typical oxygen contents less than 250 ppm. One alloy with a density of < 9.5 g/cc was successful in meeting the Phase 2 intermediate project mechanical property milestone requirements of room temperature ductility greater than 1.0%, 1200°C creep strain of less than 3% at 150 MPa and 100 hours in vacuum, and with solidus temperature greater than 1500ᵒC. The second class of alloys was designed to be a Nb-rich alloy with improved oxidation resistance when compared to the core layer and was designed specifically to be compatible with the core layer and the outer environmental barrier coating. This Nb- alloy will be specifically designed to be microstructurally stable at these temperatures when in contact with the core alloy and provide protection against catastrophic failure of the barrier coating. Two alloys were cast and processed but further development was discontinued to focus on the development of the creep resistant alloy.
Modern engineered ceramics offer high temperature capabilities not found in even the best superalloy metals. The high temperature properties of several selected ceramics including aluminum oxide, silicon carbide, and silicon nitride are reviewed as they apply to hypersonic engine seal design. A ranking procedure is employed to objectively differentiate among four different monolithic ceramic materials considered, including: a cold-pressed and sintered aluminum oxide; a sintered alpha-phase silicon carbide; a hot-isostatically pressed silicon nitride; and a cold-pressed and sintered silicon nitride. This procedure is used to narrow the wide range of potential ceramics considered to an acceptable number for future detailed and costly analyses and tests. The materials are numerically scored according to their high temperature flexural strength; high temperature thermal conductivity; resistance to crack growth; resistance to high heating rates; fracture toughness; Weibull modulus; and finally according to their resistance to leakage flow, where materials having coefficients of thermal expansion closely matching the engine panel material resist leakage flow best. The cold-pressed and sintered material (Kyocera SN-251) ranked the highest in the overall ranking especially when implemented in engine panels made of low expansion rate materials being considered for the engine, including Incoloy and titanium alloys.
High-temperature resistant eutectic Al alloys are crucial materials for lightweight and energy efficient design in the automotive and aviation industries. Additive manufacturing offers a pathway to refine eutectic microstructures and develop novel alloys with superior high-temperature strength. High-volume fraction intermetallic Al-Cu-Ce alloys have been developed to deliver high-temperature strength in combination with reduced hot-tearing susceptibility. Zr is added to provide additional strengthening via nanoscale Al 3 Zr precipitation, and to stabilize and avoid coarsening of the Al 8 Cu 3 Ce phase. However, the detailed interaction between Zr and Al 8 Cu 3 Ce remains unexplored. In this work, we show with synchrotron X-ray diffraction that laser powder bed fusion fabricated Al-Cu-Ce and Al-Cu-Ce-Zr alloys contain predominantly the Al 8 Cu 3 Ce intermetallic in the as-fabricated condition. Heat treatment of the Al-Cu-Ce alloy results in the Al 8 Cu 3 Ce → Al 8 Cu 4 Ce phase transformation. In the Al-Cu-Ce-Zr alloy, minor fractions of (Al,Cu,Si) 4 Ce and Al 2 Cu-θ are found in the as-fabricated condition, while Al 8 Cu 3 Ce remains stable during heat treatment. Atom probe microscopy quantifies intermetallic stoichiometries and reveals how Zr is enriched at the Al-matrix/Al 8 Cu 3 Ce interface acting as a diffusion barrier against solute exchange. Calibrated thermodynamic modeling underpins this as a kinetic effect. Here, a qualitative microstructural model summarizes, how Zr stabilizes Al 8 Cu 3 Ce against phase transformations and coarsening.
Current Ni-based alloys used in turbine blade applications are operating at 1100°C which is approximately 90% of the solidus of Ni-based alloys. Further increases in temperature can be achieved only through the use of alloys with higher solidus temperatures such as refractory alloys which include Mo, Nb, W, Ta alloys. Niobium has a unique combination of physical properties that include a high melting point (2468°C), lowest density (8.57 g/cc), and the lowest modulus amongst refractory alloys, a good thermal conductivity that increases from 45 W/mK at room temperature to 62 W/mK at 1093°C, good ductility with fabricability using traditional techniques, high strength, good creep resistance, and general chemical inactivity. Hence niobium alloys offer many advantages for use at the desired temperature of 1300°C. One of the major deterrents to the use of niobium and its alloys at high temperatures is achieving good oxidation resistance. In addition, achieving balanced properties of room temperature strength, ductility, fracture toughness, high temperature strength, and creep resistance required for 1300°C operation at a density of 9 g/cm 3 is extremely challenging since the addition of W which is a potent strengthener increases the density of the alloy. This project seeks to enable the development of a tri-layered turbine blade that can operate continuously at 1300°C with the core of the turbine blade providing good creep resistance, the second layer providing improved oxidation resistance over the core layer, and the third layer being an environmental barrier providing oxidation resistance. The objective of this Phase 1 project was to use computational modeling and advanced characterization tools to develop two classes of Nb alloys which could be used as the core layer and the transition layer.
The poor machinability and extensive work hardening of Ni-based superalloys makes additive manufacturing an attractive option for producing geometrically complex components with distinct microstructures. Although previous studies show recovery of high strength at room temperature, very few studies demonstrate successful properties at elevated temperatures required for industrial applications. Here, the objectives of this study are to present a post-build heat treatment for high strength across a wide temperature range, determine the strength contribution of nanoscale precipitating phases to the overall mechanical properties of superalloy 718, and from these, provide a comprehensive microstructure-property relationship for wrought and AM 718 to guide efforts to simulate the properties of AM components. Laser powder bed fusion–produced superalloy 718 was characterized at multiple length scales using scanning electron microscopy and transmission electron microscopy in the as-built condition and with multiple heat treatments designed to form combinations of γ', γ", and δ precipitates. Uniaxial tensile tests performed from room temperature to 600 °C on subsize specimens determined the yield strength, elastic modulus, ultimate tensile strength, fracture stress, and uniform elongation. Precipitates in this work proved to be weak barriers to dislocation motion through a dispersed barrier model, but they provided strength to the alloy through their consistent high density. The relative contribution to the yield strength from γ" remained consistent between 48% and 57% of the total strength up to 600 °C, the primary influence on the high temperature strength of superalloy 718. The strength factors for γ" and δ precipitates were found to trend inversely with tensile test temperature and may be attributable to the differences in precipitate coherency. A post-build heat treatment is recommended to maintain high strength at elevated temperatures. A quantitative microstructure-property relationship, dependent on precipitate size, density, and morphology, was derived and can estimate the yield strength across a wide temperature range applicable to the operational regimes for superalloy 718.
The elevated temperature properties (tensile and creep) of NiCrALY, a nickel base alloy containing nominally 16% chromium, 4% aluminum, and 2 to 3% yttria (Y2O3) were evaluated and the optimal combination of thermomechanical treatments for maximum creep resistance was determined. Stored strain energy in as-extruded bars (14:1 extrusion ratio) permitted the development of a large grain size in the material when it was annealed at the maximum safe temperature 2450 F (1343 C). With a one-hour anneal at this temperature, the relatively fine grain size of the as-extruded material was changed to one in which the average grain diameter approached 1 mm, and the aspect ratio was about 10. The material was capable of being cold worked (by rolling) in amounts greater than 30% reduction in area. When the cold worked material was given a relaxation treatment, consisting of heating one hour at 1600 F(871 C), and then a high temperature anneal at 2450 F (1343 C) for one hour, both the high temperature strength and the high temperature creep resistance of the material was further enhanced.
Nickel-based alloys are known for their excellent corrosion resistance and high-temperature strength. However, at high temperatures, polycrystals experience grain boundary-stress-driven vacancy diffusion leading to diffusion-driven creep. Understanding the fundamentals of defect migration is essential to predict diffusion creep behavior. In this talk, we explore the Nabarro-Herring diffusion creep and the associated solute segregation that is likely to result from the different diffusivities of the solute and solvent elements. Density functional theory calculations are performed to determine the formation, migration and binding energies of the solute and vacancy defects in stress-free and stressed states. The dilute-limit transport coefficients are then calculated using the self-consistent mean field theory as implemented in the Kinetic Cluster Expansion (KineCluE) code. Predictions of diffusion creep strain rates and solute segregation are then presented for various solutes, stress and temperatures. This work opens research avenues for exploration of diffusion creep via characterization of elemental segregation to grain boundaries.
Thermomechanical processing (TMP) of ferritic–martensitic (FM) steels, such as HT9 (Fe–12Cr–1MoWV) steels, involves normalizing, quenching, and tempering to create a microstructure of fine ferritic/martensitic laths with carbide precipitates. HT9 steels are used in fast reactor core components due to their high-temperature strength and resistance to irradiation damage. However, traditional TMP methods for these steels often result in performance limitations under irradiation, including embrittlement at low temperatures (<~430 °C), insufficient strength and toughness at higher temperatures (>500 °C), and void swelling after high-dose irradiation (>200 dpa). This research aimed to enhance both fracture toughness and strength at high temperatures by creating a quenched and tempered martensitic structure with ultrafine laths and precipitates through rapid quenching and unconventional tempering. Mechanical testing revealed significant variations in strength and fracture toughness depending on the processing route, particularly the tempering conditions. Tailored TMP approaches, combining rapid quenching with limited tempering, elevated strength to levels comparable to nano-oxide strengthened ferritic alloys while preserving fracture toughness. For optimal properties in high-Cr steels for future reactor applications, this study recommends a modified tempering treatment, i.e., post-quench annealing at 500 °C or 600 °C for 1 h, possibly followed by a brief tempering at a slightly higher temperature.
Lightweight, strong, tough high-temperature materials are required to complement efficiency improvements for next-generation gas turbine engines that can operate with minimum cooling. Because of their low density, high-temperature strength, and high thermal conductivity, ceramics are being investigated as materials to replace the nickelbase superalloys that are currently used for engine hot-section components. Ceramic structures can withstand higher operating temperatures and a harsh combustion environment. In addition, their low densities relative to metals help reduce component mass (ref. 1). To complement the effectiveness of the ceramics and their applicability for turbine engine applications, a parametric study using the finite element method is being carried out. The NASA Glenn Research Center remains very active in conducting and supporting a variety of research activities related to ceramic matrix composites through both experimental and analytical efforts (ref. 1). The objectives of this work are to develop manufacturing technology, develop a thermal and environmental barrier coating (TBC/EBC), develop an analytical modeling capability to predict thermomechanical stresses, and perform a minimal burner rig test on silicon nitride (Si3N4) and SiC/SiC turbine nozzle vanes under simulated engine conditions. Moreover, we intend to generate a detailed database of the material s property characteristics and their effects on structural response. We expect to offer a wide range of data since the modeling will account for other variables, such as cooling channel geometry and spacing. Comprehensive analyses have begun on a plate specimen with Si3N4 cooling holes.
A new high-temperature-strength, high-conductivity Cu-Cr-Nb alloy with a CrNb ratio of 2:1 was developed to achieve improved performance and durability. The Cu-8 Cr4 Nb alloy studied has demonstrated remarkable thermal and microstructural stability after long exposures at temperatures up to 0.98 T(sub m). This stability was mainly attributed to the slow coarsening kinetics of the Cr2Nb precipitates present in the alloy. At all temperatures, the microstructure consists of a bimodal and sometimes trimodal distribution of strengthening Cr2Nb precipitates, depending on precipitation condition, i.e. from liquid or solid solution, and cooling rates. These precipitates remain in the same size range, i.e. large precipitates of approximately I pm, and small precipitates less dm 300 nm, and effectively pin the grain boundaries thus retaining a fine grain size of 2.7 micro-m after 100 h at 1323 K. (A relatively small number of Cr-rich and Nb-rich particles were also present.) This grain boundary pinning and sluggish coarsening of Cr2Nb particles explain the retention of good mechanical properties after prolonged holding at very high temperatures, e.g., 75% of the original hardness after aging for 100 h at 1273 K. Application of LSW-based coarsening models indicated that the coarsening kinetics of the large precipitates are most likely governed by grain boundary diffsion and, to a lesser extent, volume diffusion mechanisms.
Particle production targets and accelerator beam windows receive millions of high-energy/intensity beam pulses throughout their service lifetime. For next-generation multi-MW accelerators, it is necessary for beam windows to be able to withstand higher levels of thermal shock and radiation damage, while also having good high-temperature mechanical properties. Novel High-Entropy Alloys (HEAs) that form a single-phase microstructure, have nanoscale precipitates, and are made from low-Z elements are good candidates for beam window materials. This is due to their high-temperature strength and high resistance to radiation-induced swelling and hardening, as well as their beam transparency, allowing for maximized particle production and a longer service lifetime.
Efforts to improve the performance of modern gas turbine engines have imposed increasing service temperature demands on structural materials. Through active cooling, the useful temperature range of nickel-base superalloys in current gas turbine engines has been extended, but the margin for further improvement appears modest. Because of their low density, high-temperature strength, and high thermal conductivity, in situ toughened silicon nitride ceramics have received a great deal of attention for cooled structures. However, high processing costs have proven to be a major obstacle to their widespread application. Advanced rapid prototyping technology, which is developing rapidly, offers the possibility of an affordable manufacturing approach.