By employing 3,5-bis(trifluoromethyl) pyrazole (TFMP) as an electrolyte additive in both aqueous and non-aqueous mediums, a versatile interphase strategy is achieved. This facilitates stable Zn anodes with improved efficiency and longer cycling life.
An improved zinc anode for use in a high density rechargeable alkaline battery is disclosed. A process for making the zinc electrode comprises electrolytic loading of the zinc active material from a slightly acidic zinc nitrate solution into a substrate of nickel, copper or silver. The substrate comprises a sintered plaque having very fine pores, a high surface area, and 80-85 percent total initial porosity. The residual porosity after zinc loading is approximately 25-30%. The electrode of the present invention exhibits reduced zinc mobility, shape change and distortion, and demonstrates reduced dendrite buildup cycling of the battery. The disclosed battery is useful for applications requiring high energy density and multiple charge capability.
High temperature battery development - zeolites, anode and cathode couples, and molten salts
One promising method for reducing precious metal usage in proton exchange membrane water electrolysis is lowering iridium (Ir) loading at the anode. However, low-loading Ir catalysts often suffer from poor stability under high current densities. In this study, hydrogen (H2) crossover from the cathode to the anode is identified as a key degradation pathway. Temperature-programmed reduction confirms the reduction of IrO2 at 80 °C in a hydrogen environment, highlighting the vulnerability of IrO2-based catalysts to H2 exposure. To mitigate this effect, palladium (Pd) is introduced as an anode additive, acting as an H2 oxidation catalyst and mitigating IrO2 reduction. This protective role is verified by inductively coupled plasma optical emission spectroscopy and in situ X-ray absorption spectroscopy, showing significantly suppressed Ir dissolution at 80 °C under H2 flow when an O-covered Pd surface is present at oxygen evolution reaction potentials. Results from the current study identify a new strategy in improving activity and durability of catalysts in electrolyzers.
High energy anode and cathode development, electrolyte encapsulation, tape activation, and parasitic operation techniques for dry tape battery concept
High energy anode and cathode for dry tape battery - incapsulation of electrolyte - manufacturing and testing of device
Cell discharge measurements for dry tape battery couple - anode and cathode development in aqueous and nonaqueous electrolytes
Conventional solid electrolyte interphases (SEIs) strongly adhere to micro-silicon (µ-Si) and crack under volume changes, causing poor cycling performance. Nano-silicon improves cycling performance but remains costly with limited calendar life. Here potentiostatic ageing tests demonstrate that both calendar and cycle ageing are governed by SEI cracking and dissolution with different relative contributions. When the system is not dominated by SEI dissolution, the relative calendar life of Si anodes could correlates positively with their cycle life. LiF-rich SEI that enables long cycle life in µ-Si is therefore expected to enhance calendar life as well. Using this framework, we screened electrolytes, SEIs and electrodes and validated them with full-cell storage. LiF-rich SEI minimizes cracking and dissolution, enabling μ-Si to achieve excellent calendar life, whereas nano-silicon suffers from SEI dissolution and needs reduced electrolyte–electrode contact for better calendar life. This work clarifies calendar-ageing behaviour and accelerates electrolytes and SEI development for long-life Si anodes.
The growing demand for sodium-ion batteries (SIBs) in grid storage underscores the need for electrode materials that balance performance and cost, including sustainable and robust carbon sources. The equitable and abundant distribution of materials for SIBs, along with their superior low-temperature performance, safety, and fast-charging capability, further distinguishes them from lithium-ion batteries (LIBs). Hard carbon (HC) is the state-of-the-art anode for SIBs, but current commercial HC production is localized mostly to one region of the world, raising concerns about supply chain vulnerability, critical material dependency, and environmental aspects. Here, the first demonstration of humins, an abundant biorefinery byproduct, as a precursor for HC anodes for sodium-ion storage is reported. Humins were carbonized at 1100 degrees C-1300 degrees C, and the resulting materials were subjected to comprehensive materials and electrochemical characterization. Among the temperatures studied, humins-derived hard carbon synthesized at 1200 degrees C delivers an initial reversible capacity 270mA h g-1 , with stable cycling performance up to 500 cycles and excellent rate capability, representing the optimal performance. This study establishes humins as a promising and low-cost carbon source that provides a route to mitigate supply chain risks and valorizes an underutilized biorefinery waste stream for high-performance SIB anodes.
High energy density primary battery development - anode-electrolyte, cupric fluoride cathode, and chemical stability tests
High energy density primary battery development - electrochemical half-cell screening of anode- electrolyte combinations, cell discharge, and potential studies
Lithium anodes, inorganic and organic cathodes, vacuum-distilled solvents, and methods for sintering cupric fluoride on lightweight metal substrates - development of high energy battery
We report a purely mechanical “cold-compression flow” method for fabricating Zn, Sn, and In substrates with tunable crystallographic textures. Using textured Zn as a model system, we investigate Zn electrocrystallization and demonstrate correlated growth of crystalline films with correlation lengths from tens to hundreds of micrometers. At 5 milliamperes per square centimeter (mA/cm 2 ), capacities between 20 and 82 milliampere hours per square centimeter (mA·hour/cm 2 ) are achieved depending on substrate texture level. At higher currents (40 mA/cm 2 ), capacities reach up to 604 mA·hour/cm 2 . Rotating disk electrode studies show that dominantly (002) textured Zn substrates exhibit enhanced corrosion resistance and reduced interphase passivation. We introduce an effective Damköhler number (Da*) to concisely describe morphological evolution during electrocrystallization across substrates with different textures. High-texture (002) Zn substrates substantially enhance performance in high-capacity (~20 mA·hour/cm 2 ) symmetric Zn||Zn cells and full cells (Zn||δ-MnO 2 and Zn||I 2 ), enabling fast-charging and prolonged energy storage in coin and pouch rechargeable Zn battery formats.
Addressing sustainable energy storage remains crucial for transitioning to renewable sources. While Li‐ion batteries have made significant contributions, enhancing their capacity through alternative materials remains a key challenge. Micro‐sized silicon is a promising anode material due to its tenfold higher theoretical capacity compared to conventional graphite. However, its substantial volumetric expansion during cycling impedes practical application due to mechanical failure and rapid capacity fading. A novel approach is proposed to mitigate this issue by incorporating trace amounts of aluminum into the micro‐sized silicon electrode using ball milling. Density functional theory (DFT) is employed to establish a theoretical framework elucidating how grain boundary sliding, a key mechanism involved in preventing mechanical failure is facilitated by the presence of trace aluminum at grain boundaries. This, in turn, reduces stress accumulation within the material, reducing the likelihood of failure. To validate the theoretical predictions, capacity retention experiments are conducted on undoped and Al‐doped micro‐sized silicon samples. In conclusion, the results demonstrate significantly reduced capacity fading in the doped sample, corroborating the theoretical framework and showcasing the potential of aluminum doping for improved Li‐ion battery performance.
This manuscript contributes a Viewpoint article to ACS Sustainable Resource Management and discusses the graphite supply chain, growing mismatch between graphite demand and global manufacturing capacity, current graphite manufacturing technologies, and different feedstocks.
The redox behavior and speciation of cerium at mesoporous thin films composed of nanoparticles of indium tin-doped oxide (nITO) electrodes were characterized in pH 4.8, 0.1 M acetate buffer and both 0.1 and 1 M HNO 3 using electrochemical techniques and X-ray photoelectron spectroscopy. Anodic deposition of ceria species from Ce(III) to the nITO electrode was achieved under all solvent conditions via spontaneous condensation of electrochemically generated ceric hydroxide species. In 1 M nitric acid, the rate of CeO 2 dissolution is on the same order as CeO 2 deposition, resulting in negligible amounts of CeO 2 electrodeposited at the nITO surface. The cathodic stripping of CeO 2 from the nITO substrate deposited in 0.1 M nitric acid or pH 4.8 acetate buffer follows a 2-step process where Ce(IV)-oxide is initially reduced to an unstable Ce(III)-oxide species that rapidly undergoes acid catalyzed dissolution to yield soluble Ce(III) (aq) . These findings provide a foundation for the pH and anodic potential controlled deposition of CeO 2 thin films to ITO substrates, which can aid in the development of materials composed of ceria. As a result, they can also be used to infer likely analogous actinide redox behavior and speciation at these electrodes.
Solid-polymer electrolytes comprised of polypropylene carbonate (PPC) and varied sodium bis(fluorosulfonyl)imide (NaFSI) salt concentrations are investigated for implementation as a conductive solid polymer electrolyte into solid-state cathode composites utilizing a sodium-layered oxide active material. The ionic conductivity generally increases with NaFSI salt content, reaching ≈1 mS cm −1 at 80 °C at the highest salt concentration (PPC:NaFSI = 0.5:1). Through an all-in-one slurry casting method, Na 2/3 Ni 1/3 Mn 2/3 O 2 cathode composites are fabricated in which the dispersed PPC electrolyte acts as the primary binder. Enabled by a bilayer polymer electrolyte system, cycling performance with the PPC cathode electrolyte is optimized with respect to salt concentration and anode material. The best cyclability is achieved with a moderate salt concentration electrolyte (PPC:NaFSI = 5:1), showcasing an initial capacity of 83 mA h g −1 with a remarkable 80% capacity retention after 150 cycles at C/5 rate and 60 °C. The superior performance of the lower salt concentration electrolyte is attributed to better electrochemical stability, as confirmed by linear sweep voltammetry and online electrochemical mass spectrometry measurements. In conclusion, these results underscore the potential of carbonate-based polymer electrolytes and the importance of balancing electrolyte conductivity and stability in cell design.