Results for “insulation polymers” — Page 2

NASA NTRS2018

Lightweight, Durable, and Multifunctional Electrical Insulation Material Systems for High Voltage Applications

Newly developed multilayer structures of well-known polymer insulation materials significantly improved dielectric breakdown voltage, VB, or dielectric strength, K, if well-bonded, when compared to those of single material insulations or the commercial SOA systems, such as Teflon-Kapton-Teflon (TKT), at the same overall thickness. To date, the greatest improvement of the new structures from a few candidate materials, including various types of Kapton PIs and PFA or PET as bond layer (BL), was about 61% higher than that of the Kapton PI alone films, 40.1 vs. 24.9 kV, which was translated to 86.3% decrease in insulation thickness, thus significant volume and weight reduction of the final system. However, it was of interest to note that most improvements of the multilayer structures occurred at thicker overall thicknesses, above ~ 0.15 mm. Extensive analyses also showed that K of the multilayer structures increased with (i) decreasing individual layer thickness regardless of material type, (ii) increasing total accumulated thickness of PI or overall PI/BL ratio, and (iii) increasing number of interface or total number of layers, but only above the aforementioned overall thickness limit. Increases in VB of the multilayer structures were directly correlated with damage evolution and failure mode. With further material-design-process optimizations of the multilayer structures, it was expected to achieve other multifunctionalities, such as high partial discharge (PD) resistance, improved durability, EMI shielding, and high thermal dissipation in addition to high dielectric strength. These new structures can be used in various high voltage and high temperature applications, such as future hybrid or all electric aircraft wiring and power transmission as well as many other non-aerospace high power cables, electronic parts and components, printed circuit board, and so forth. The multilayer insulation system can be easily processed and manufactured with various conductor types via calendaring, compression-molding, stamping, laminating, vacuum-bagging and autoclaving, or 3D printing, even for complex 3-D components. Based on their unique structural configurations and potential capabilities, the new insulation system was identified as micro-multilayer multifunctional electrical insulation (MMEI). Patent application of the MMEI concept and current design configurations was filed for a 1-year provisional application (OAI-58834, Serial No.: 62/659,234), pending conversion to a U.S. utility application. This paper presents details of the MMEI structures, their dielectric performance analyses, potential mechanisms, and commercial scaleup feasibility assessment.

Electric aircrafts↗

NASA NTRS2018

Lightweight, Durable, and Multifunctional Electrical Insulation Material Systems for High Voltage Applications

Newly developed multilayer structures of well-known polymer insulation materials significantly improved dielectric breakdown voltage, VB, or dielectric strength, K, if well-bonded, when compared to those of single material insulations or the commercial SOA systems, such as Teflon-Kapton-Teflon (TKT), at the same overall thickness. To date, the greatest improvement of the new structures from a few candidate materials, including various types of Kapton PIs and PFA or PET as bond layer (BL), was about 61% higher than that of the Kapton PI alone films, 40.1 vs. 24.9 kV, which was translated to 86.3% decrease in insulation thickness, thus significant volume and weight reduction of the final system. However, it was of interest to note that most improvements of the multilayer structures occurred at thicker overall thicknesses, above ~ 0.15 mm. Extensive analyses also showed that K of the multilayer structures increased with (i) decreasing individual layer thickness regardless of material type, (ii) increasing total accumulated thickness of PI or overall PI/BL ratio, and (iii) increasing number of interface or total number of layers, but only above the aforementioned overall thickness limit. Increases in VB of the multilayer structures were directly correlated with damage evolution and failure mode. With further material-design-process optimizations of the multilayer structures, it was expected to achieve other multifunctionalities, such as high partial discharge (PD) resistance, improved durability, EMI shielding, and high thermal dissipation in addition to high dielectric strength. These new structures can be used in various high voltage and high temperature applications, such as future hybrid or all electric aircraft wiring and power transmission as well as many other non-aerospace high power cables, electronic parts and components, printed circuit board, and so forth. The multilayer insulation system can be easily processed and manufactured with various conductor types via calendaring, compression-molding, stamping, laminating, vacuum-bagging and autoclaving, or 3D printing, even for complex 3-D components. Based on their unique structural configurations and potential capabilities, the new insulation system was identified as micro-multilayer multifunctional electrical insulation (MMEI). Patent application of the MMEI concept and current design configurations was filed for a 1-year provisional application (OAI-58834, Serial No.: 62/659,234), pending conversion to a U.S. utility application. This paper presents details of the MMEI structures, their dielectric performance analyses, potential mechanisms, and commercial scaleup feasibility assessment.

Multifunctional↗

DOE OSTI2020

Sequential versus Simultaneous Aging of XLPE Nuclear Cable Insulation Subjected to Elevated Temperature and Gamma Radiation

Electrical cables constitute a critical component of nuclear power generation. The aging behavior of electrical cable insulation under combined exposure to thermal and radiation stress is not additive, complicating lifetime prediction of cable performance based on sequential accelerated aging. In this work we explore the relative effects of simultaneous and sequential thermal and gamma radiation aging on cross-linked polyethylene (XLPE), which is commonly found in commercial nuclear power plants in the United States. Samples of XLPE were subjected to up to 320 kGy of gamma irradiation at a dose rate of 300 Gy/hr in two heating scenarios. In the first, simultaneously-aged samples were heated at 150°C during irradiation. In the second, sequentially aged samples were heated at 150°C for designated durations followed by corresponding periods of irradiation without heating. The mass, total color difference, and density were characterized to quantify aging of the insulation polymer. Sequential aging is hypothesized to be more damaging to XLPE insulation due to an increased trend in mass gain, total color difference, and density.

Cross-linked polyethylene, XLPE, nuclear cable, ac↗

DOE OSTI2020

Mixed-flow design for microfluidic printing of two-component polymer semiconductor systems

The rational creation of two-component conjugated polymer systems with high levels of phase purity in each component is challenging but crucial for realizing printed soft-matter electronics. Here, we report a mixed-flow microfluidic printing (MFMP) approach for two-component π -polymer systems that significantly elevates phase purity in bulk-heterojunction solar cells and thin-film transistors. MFMP integrates laminar and extensional flows using a specially microstructured shear blade, designed with fluid flow simulation tools to tune the flow patterns and induce shear, stretch, and pushout effects. This optimizes polymer conformation and semiconducting blend order as assessed by atomic force microscopy (AFM), transmission electron microscopy (TEM), grazing incidence wide-angle X-ray scattering (GIWAXS), resonant soft X-ray scattering (R-SoXS), photovoltaic response, and field effect mobility. For printed all-polymer (poly[(5,6-difluoro-2-octyl-2H-benzotriazole-4,7-diyl)-2,5-thiophenediyl[4,8-bis[5-(2-hexyldecyl)-2-thienyl]benzo[1,2-b:4,5-b′]dithiophene-2,6-diyl]-2,5-thiophenediyl]) [J51]:(poly{[N,N′-bis(2-octyldodecyl)naphthalene-1,4,5,8-bis(dicarboximide)-2,6-diyl]-alt-5,5′-(2,2′-bithiophene)}) [N2200]) solar cells, this approach enhances short-circuit currents and fill factors, with power conversion efficiency increasing from 5.20% for conventional blade coating to 7.80% for MFMP. Moreover, the performance of mixed polymer ambipolar [poly(3-hexylthiophene-2,5-diyl) (P3HT):N2200] and semiconducting:insulating polymer unipolar (N2200:polystyrene) transistors is similarly enhanced, underscoring versatility for two-component π -polymer systems. Mixed-flow designs offer modalities for achieving high-performance organic optoelectronics via innovative printing methodologies.

42 ENGINEERING↗

NASA NTRS2005

Ferrocene Containing Copolymers with Improved Electrostatic Dissipation Properties for Advanced Applications

Electrostatic dissipative polymers are used for a variety of functions. Typical methods utilized to transform electrically insulating polymers into either charge dissipative or conductive materials involve incorporating a conductive filler, conductive polymer, oxidizing the surface using plasma, or incorporating surfactants that act as surface wetting agents. Another approach is to synthesize a block copolymer that is expected to result in better electrical properties with minimal impacts to physical, fire, and thermal properties. One such block that can be added into the main chain of polymers is a diol terminated ferrocene oligomer, which is expected to impart electrostatic dissipative properties into the host polymer while concurrently improving the overall fire properties. Previous work with polyurethanes incorporating a ferrocene oligomer into the main chain resulted in much improved fire retardancy. In dealing with electrostatic dissipative materials the important questions are: how easily does the material charge and how quickly can the charge move to ground. One normally describes the materials conductivity, but conductivity only measures the fastest path for an electron not the slowest path. The slowest path is the one of interest, since it is left on the surface and thus can cause discharges. In order to assess ease of charging and decay times corona charge dissipation measurements can accurately assess these properties by introducing a charge on the surface of the material then measuring the surface voltage and the amount of charge deposited. The charge decay curve then will give an indication of a materials electrostatic dissipation properties. Normally, triboelectric testing can be performed, but results vary. Corona charge dissipation results are more repeatable.

Smith, T. M.↗

DOE OSTI2024

Thermodynamic driving forces in contact electrification between polymeric materials

Abstract Contact electrification, or contact charging, refers to the process of static charge accumulation after rubbing, or even simple touching, of two materials. Despite its relevance in static electricity, various natural phenomena, and numerous technologies, contact charging remains poorly understood. For insulating materials, even the species of charge carrier may be unknown, and the direction of charge-transfer lacks firm molecular-level explanation. Here, we use all-atom molecular dynamics simulations to investigate whether thermodynamics can explain contact charging between insulating polymers. Based on prior work suggesting that water-ions, such as hydronium and hydroxide ions, are potential charge carriers, we predict preferred directions of charge-transfer between polymer surfaces according to the free energy of water-ions within water droplets on such surfaces. Broad agreement between our predictions and experimental triboelectric series indicate that thermodynamically driven ion-transfer likely influences contact charging of polymers. Furthermore, simulation analyses reveal how specific interactions of water and water-ions proximate to the polymer-water interface explain observed trends. This study establishes relevance of thermodynamic driving forces in contact charging of insulators with new evidence informed by molecular-level interactions. These insights have direct implications for future mechanistic studies and applications of contact charging involving polymeric materials.

36 MATERIALS SCIENCE↗

NASA NTRS2003

Composite-Based High Performance Electroactive Polymers For Remotely Controlled Mechanical Manipulations in NASA Applications

This program supported investigation of an all-polymer percolative composite which exhibits very high dielectric constant (less than 7,000). The experimental results show that the dielectric behavior of this new class of percolative composites follows the prediction of the percolation theory and the analysis of the conductive percolation phenomena. The very high dielectric constant of the all-polymer composites which are also very flexible and possess elastic modulus not very much different from that of the insulation polymer matrix makes it possible to induce a high electromechanical response under a much reduced electric field (a strain of 2.65% with an elastic energy density of 0.18 J/cu cm can be achieved under a field of 16 MV/m). Data analysis also suggests that in these composites, the non-uniform local field distribution as well as interface effects can significantly enhance the strain responses. Furthermore, the experimental data as well as the data analysis indicate that the conduction loss in these composites will not affect the strain hysteresis.

Zhang, Q. M.↗

DOE OSTI2020

Development of an In-Situ Method for Cable Condition Monitoring in Nuclear Power Plants (SBIR Phase IIB Final Report)

This is the final report of a Small Business Innovation Research (SBIR) project that Analysis and Measurement Services Corporation (AMS) has conducted for the U.S. Department of Energy (DOE) over a seven-and-a-half year period (February 2013 through April 2020 with the awards of Phase I, Phase II and Phase IIB projects). The goal of the project was to design, develop, validate, and demonstrate a technique for in-situ testing of cable insulation polymers that will identify, locate, and provide the degree of aging for cables commonly used in nuclear power plants. During the Phase I project, AMS established that the frequency domain reflectometry (FDR) technique can successfully identify and measure cable insulation degradation that can be trended with aging. In Phase II, AMS performed extensive cable aging studies to correlate FDR measurements with other laboratory condition monitoring techniques and developed aging condition categories to quantify the severity of insulation degradation. In Phase IIB, the project expanded the research to include a wider variety of cable polymers that are used in the commercial nuclear power industry. This work also involved developing acceptance criteria to objectively assess age-related cable degradation while sharing the results of this research with industry, academia, and national laboratories to advance the state of the art in cable aging management technologies. The products developed under this research project provide the nuclear industry with an effective condition monitoring tool to support safe and long-term plant operation. Throughout the project, collaborations and support were received from a variety of industry organizations and individuals including DOE National Laboratories as well as nuclear plant utilities and several other industry experts and cable manufacturers. Contributions from these organizations included the donation of new cables, naturally aged cables, and research collaboration. The validation and commercialization of the products of this project were achieved through opportunities to test and demonstrate the technologies’ capabilities on-site at nuclear power generation and research facilities as well as in the laboratory alongside industry peers and cable testing service companies. The research resulted in a technology that can be used to identify, locate, and quantify age-related degradation in several types of cable polymers. This included developing software and hardware as well as the methodology for using the FDR technique to assess age-related degradation of installed cables. The technology developed under this project can provide nuclear plant management, engineers, and technicians with an in-situ electrical test method to determine if in-service cables need to be replaced, monitored on a periodic basis, or show no evidence of significant age-related degradation that may require action. Near the end of this Phase IIB project, the FDR product was sold to a nuclear power utility in South Korea. This sale of a dedicated aging assessment tool is the beginning of a comprehensive contract with the expectation of twelve (12) units sold to that country. Additionally, the FDR technology has been sold to several industry organizations including a nuclear research institute and the Diablo Canyon nuclear power plant. This technology is also being leased by other nuclear industry service companies for incorporation into aging management programs. The cable testing technology that was developed under this project was also integrated into a comprehensive cable aging assessment service that is being offered to the nuclear industry at the request of U.S. nuclear utilities and is currently part of onsite testing services provided by AMS.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2022

Condition assessment of cable insulation materials in advanced reactor environments

While existing cable insulation materials are sufficient for use in the current reactor fleet, environmental conditions inside some advanced reactors, such as small modular reactors, will be substantially harsher. The work herein was conducted to assess the performance and overall survivability of several high-temperature, radiation resistant insulation polymers in a simulated small modular reactor environment. The materials evaluated under this research include polyether ether ketone, polyimide, and silicone rubber. These polymers were subjected to 1000 h of environmental stress exposure under two different conditions: 1) high temperature (i.e., 250 °C) in atmospheric pressure and 2) high temperature in a low-pressure vacuum (i.e., less than 2 psia). During the environmental exposure process, each insulation was periodically tested using several materials characterization techniques including Fourier transform infrared spectroscopy, oxidation induction time, and oxidation induction temperature. The objective of this testing was to assess and monitor changes that occurred in the thermal and chemical properties of the materials during the environmental exposures. The overall survivability of each insulation was assessed based on these property changes. The results of this research revealed that the polyimide and polyether ether ketone insulations had significantly better thermal and chemical stability than the silicone rubber during both the high-temperature atmospheric and vacuum exposures. Both polyimide and polyether ether ketone experienced minimal reductions in their chemical and thermal properties over the course of 1000 h in the simulated environments. Finally, based on this research, polyimide and polyether ether ketone show promise as potential base materials for small modular reactor cable insulation.

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS↗

DOE OSTI2021

Understanding, quantifying, and controlling the molecular ordering of semiconducting polymers: from novices to experts and amorphous to perfect crystals

Molecular packing and texture of semiconducting polymers are often critical to the performance of devices using these materials. Although frameworks exist to quantify the ordering, interpretations are often just qualitative, resulting in imprecise use of terminology. Here, we reemphasize the significance of quantifying molecular ordering in terms of degree of crystallinity (volume fractions that are ordered) and quality of ordering and their relation to the size scale of an ordered region. We are motivated in part by our own imprecise and inconsistent use of terminology in the past, as well as the need to have a primer or tutorial reference to teach new group members. We strive to develop and use consistent terminology with regards to crystallinity, semicrystallinity, paracrystallinity, and related characteristics. To account for vastly different quality of ordering along different directions, we classify paracrystals into 2D and 3D paracrystals and use paracrystallite to describe the spatial extent of molecular ordering in 1–10 nm. We show that a deeper understanding of molecular ordering can be achieved by combining grazing-incidence wide-angle X-ray scattering and differential scanning calorimetry, even though not all aspects of these measurements are consistent, and some classification appears to be method dependent. We classify a broad range of representative polymers under common processing conditions into five categories based on the quantitative analysis of the paracrystalline disorder parameter (g) and thermal transitions. A small database is presented for 13 representative conjugated and insulating polymers ranging from amorphous to semi-paracrystalline. Lastly, we outline the challenges to rationally design more perfect polymer crystals and propose a new molecular design approach that envisions conceptual molecular grafting that is akin to strained and unstrained hetero-epitaxy in classic (compound) semiconductors thin film growth.

36 MATERIALS SCIENCE↗

NASA NTRS2017

Self-Healable Electrical Insulation for High Voltage Applications

Polymeric aircraft electrical insulation normally degrades by partial discharge with increasing voltage, which causes excessive localized Joule heating in the material and ultimately leads to dielectric failure of the insulator through thermal breakdown. Developing self-healing insulation could be a viable option to mitigate permanent mechanical degradation, thus increasing the longevity of the insulation. Instead of relying on catalyst and monomer-filled microcapsules to crack, flow, and cure at the damaged sites described in well-published mechanisms, establishment of ionic crosslinks could allow for multiple healing events to occur with the added benefit of achieving full recovery strength under certain thermal environments. This could be possible if the operating temperature of the insulator is the same as or close to the temperature where ionic crosslinks are formed. Surlyn, a commercial material with ionic crosslinks, was investigated as a candidate self-healing insulator based off prior demonstrations of self-healing behavior. Thin films of varying thicknesses were investigated and the effects of thickness on the dielectric strength were evaluated and compared to representative polymer insulators. The effects of thermal conditioning on the recovery strength and healing were observed as a function of time following dielectric breakdown. Moisture absorption was also studied to determine if moisture absorption rates in Surlyn were lower than that of common polyimides.

electrical insulation↗

NASA NTRS2018

Nature-Inspired Motivation for Developing Self-Healable Electrical Insulation

Polymeric aircraft electrical insulation normally degrade by partial discharge with increasing voltage, which causes excessive localized Joule heating in the material and ultimately leads to dielectric failure of the insulator through thermal breakdown. Self-healing insulation may be a viable option to mitigate permanent mechanical degradation, thus increasing the longevity of the material. Instead of relying on catalyst and monomer-filled microcapsules to crack, flow, and cure at the damaged sites described in well-published mechanisms, self-healing through establishment of ionic crosslinks allows for multiple healing events to occur as well as achieving full recovery strength under certain thermal environments. Surlyn®, a commercial ionically-crosslinked material, was investigated as a self-healing insulation candidate based on prior demonstrations of self-healing behavior. Thin films of varying thicknesses were investigated and the effects of thickness on the dielectric strength were evaluated and compared to representative polymer insulators. The effects of thermal conditioning on the recovery strength and healing were observed as a function of time following dielectric breakdown. Moisture absorption was studied to determine if moisture absorption rates in Surlyn® were lower than that of common polyimide insulators. Preliminary data showed that when cut, Surlyn® films lost nearly 60 percent of its original dielectric strength. However, when Surlyn® was cut and subsequently annealed, the films not only re-mended, but also recouped approximately 93 percent of its original dielectric strength, along with 90-97 percent of its mechanical strength.

electrical↗

NASA NTRS2000

Development of Polymer Coatings for the ProSEDS Tether

The ProSEDS mission is designed to provide an on-orbit demonstration of the electrodynamic propulsion capabilities of tethers in space. The ProSEDS experiment will be a secondary payload on a Delta 11 unmanned, expendable booster. A 5 km conductive tether is attached to the deployer baseplate on the Delta 11 second stage and collects current from the low Earth orbit (LEO) plasma to facilitate de-orbit of the Delta II second stage. The conductive tether is attached to a 10-15 km non-conductive tether, which in turn is attached to an endmass. A bare metal tether would have the best conductivity but thermal concerns preclude this design. A conductive polymer developed by Triton Systems has been optimized for optimum conductivity and thermo-optical properties. The current design for the ProSEDS conductive tether is seven individually coated strands of 28 AWG aluminum wire, coated with 12.7 micrometers (0.5 mil) atomic oxygen-resistant conductive polymer composed of a mixture of COR and PANi, wrapped around a braided Kevlar 29 core. Extensive testing has been performed at the Marshall Space Flight Center to qualify this material for flight on ProSEDS. Atomic oxygen exposure has been performed, with solar absorptance and infrared emittance measured before and after exposure. Plasma chamber tests have been completed, as well as tether deployment tests. Also developed for the ProSEDS mission was the insulating polymer TOR-BP. Approximately 200 meters of the conductive tether closest to the Delta II second stage is insulated to prevent any electron reconnection to the tether from the plasma contactor. The insulating material is TOR-BP with a dielectric strength of TBD.

Vaughn, Jason A.↗

DOE OSTI2023

Enhanced through-thickness electrical conductivity and lightning strike damage response of interleaved vertically aligned short carbon fiber composites

Through-thickness electrical conductivity of carbon fiber reinforced polymers (CFRPs) is a key characteristic that determines the severity of lighting strike-induced damage. Carbon Fibers (CFs) are inherently electrically conductive and therefore provide high conductivity in the direction of the fiber orientation. However, electrical conductivities through the thickness and orthogonal to the CF orientation in CFRPs are governed by the insulating polymer matrix present between CFs. Here, in this work, through the thickness alignment of short CFs in between layers of CFRP laminates is demonstrated to improve the through-thickness electrical conductivity. Composites with interleaved vertically aligned short CF fibers (<150 μm) will be referred as V-fiber composites hereafter. The effect of the V-fiber on the lightning strike damage is evaluated against an artificial lightning strike of 100 kA (modified waveform A of SAE ARP-5412B standard). The improved through-thickness electrical conductivity of CFRP laminates (1.15 S/cm) through vertical alignment of short CFs was compared to reference CFRP laminates (0.13 S/cm) and was found to dissipate the artificial lightning strike current more efficiently. The surface damage after the artificial lightning strike in the V-fiber composites was reduced to 12.69 cm 2 compared to the reference CFRP surface damage of 57.67 cm 2 , a 78% reduction. It was also demonstrated that Joule heat generated due to lightning strike on the composites was significantly less than the reference sample using infrared (IR) thermography. A high retention (up to 78%) of flexural properties (modulus and strength) was observed in V-fiber composites post lightning strike impact as compared to only 47% retention in the reference panel.

42 ENGINEERING↗

NASA NTRSDate not supplied

Progresses in Developing Micro-Multilayer Multifunctional Electrical Insulation (MMEI) System for High Voltage Applications

Development of the novel patented high voltage insulation system, namely micro-multilayer multifunctional electrical insulation (MMEI) was continued particularly for the future hybrid or all electric aircraft applications. Initially, the concept and feasibility of the MMEI system were successfully demonstrated with its exceptionally high dielectric breakdown voltage via optimizing the multilayer structures of the Kapton® PI films and binder layers such as PFA in terms of individual film thickness and layer configuration. Overall, MMEI structures outperformed most of the state-of-the-art (SOA) polymer insulation materials or structures. Since then, further optimizations and improvement of the system were pursued with specific emphasis on multifunctionalities such as moisture blocking, partial discharge (PD) resistance, durability, etc. Efforts have been also continued to identify the controlling mechanisms for the major improvement in dielectric strength of the MMEI structures via 3-dimensional dielectric failure mode analysis. At the same time, significant progress has been made in scaling up the MMEI structures and assessing their commercial applicability and manufacturability by developing full-scale prototypes of electrical components, such as power cable and bus bar. Overall progresses on the MMEI development to date will be presented in this paper.

Novel Electrical Insulation↗

DOE OSTI2022

A Cable Condition Monitoring Strategy for Safe and Reliable Plant Operation

Electrical cables provide essential functions, such as delivery of power or instrumentation signals for monitoring systems. Most cables installed in industrial applications are constructed with organic polymer insulations that can become brittle, crack, or degrade over time from exposure to harsh environmental conditions, such as elevated temperatures, moisture, vibration, mechanical shock, and radiation. This paper describes an overall strategy for assessing the health and managing the aging of cables during the operating life of an industrial facility. This strategy involves performing condition assessments and monitoring of electrical cables using both in situ and laboratory testing techniques. It includes in situ testing to identify anomalies in the circuits, such as degraded terminations, splices, connections, and degraded sections of cable insulation, as well as as-found evaluations to determine the current condition of installed cables. Furthermore, these cable condition evaluations provide important information about the current state of the cable circuits. Moreover, the test results can be used to trend/monitor age-related degradation and estimate the remaining useful life of installed cables.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Development of Cable Aging Acceptance Criteria for Nuclear Facilities

The aging of nuclear power plant electrical cables has been the subject of substantial research and development (R&D) projects in the nuclear industry, national and international laboratories, universities, and vendor organizations for several years. More specifically, these R&D efforts were conducted to develop equipment and techniques for assessing age-related degradation of in-service cables in nuclear facilities including power plants, research reactors, waste facilities and fuel fabrication plants. In recent years, cable R&D efforts in the nuclear arena have also included work to develop new cables for the next generation of reactors. Over time, exposure to harsh environmental conditions such as elevated temperatures, radiation, and humidity in nuclear installations can result in age-related degradation and failure of cables. In the current fleet of nuclear reactors, there are thousands of miles of cabling installed in each plant and many of these cables are exposed to these harsh environmental conditions. For these cables, the jacket and insulation polymers harden and become brittle over time, making them more susceptible to crack formation and growth, moisture intrusion, and other mechanisms that can lead to cable failure. Moreover, the existing U.S. fleet of 98 nuclear reactors has an average operating age of 38 years. Many of these nuclear power plants have applied for and almost all have been granted regulatory approval for license renewals to operate for 60 years, 20 years beyond their original 40-year life. Further, subsequent license renewals (SLRs) are underway with a few commercial nuclear power sites already approved to operate up to 80 years. As these reactors pursue operating life extensions, utilities must find a way to address issues associated with age-related degradation of cables. Designers of small modular reactors are also in need of technologies to evaluate the performance of cables that will be installed in harsher environments (e.g. higher temperatures, radiation doses, dose rates, etc.) than those present in current-generation reactors. Today, a variety of cable condition monitoring (CM) techniques have been developed and successfully used in nuclear facilities. These techniques are used to identify age-related degradation and assess the condition of cables to determine if their performance characteristics have changed with age. However, objective criteria must be developed for these CM tests to help quantify cable condition and thereby develop repair and replacement schedules. With operating life extending to 80 years and more SLRs on the horizon, both nuclear facilities and regulators need an objective means to determine the aged condition of cables.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Development of Cable Aging Acceptance Criteria for Nuclear Facilities

The aging of nuclear power plant electrical cables has been the subject of substantial research and development (R&D) projects in the nuclear industry, national and international laboratories, universities, and vendor organizations for several years. More specifically, these R&D efforts were conducted to develop equipment and techniques for assessing age-related degradation of in-service cables in nuclear facilities including power plants, research reactors, waste facilities and fuel fabrication plants. In recent years, cable R&D efforts in the nuclear arena have also included work to develop new cables for the next generation of reactors. Over time, exposure to harsh environmental conditions such as elevated temperatures, radiation, and humidity in nuclear installations can result in age-related degradation and failure of cables. In the current fleet of nuclear reactors, there are thousands of miles of cabling installed in each plant and many of these cables are exposed to these harsh environmental conditions. For these cables, the jacket and insulation polymers harden and become brittle over time, making them more susceptible to crack formation and growth, moisture intrusion, and other mechanisms that can lead to cable failure. Moreover, the existing U.S. fleet of 98 nuclear reactors has an average operating age of 38 years. Many of these nuclear power plants have applied for and almost all have been granted regulatory approval for license renewals to operate for 60 years, 20 years beyond their original 40-year life. Further, subsequent license renewals (SLRs) are underway with a few commercial nuclear power sites already approved to operate up to 80 years. As these reactors pursue operating life extensions, utilities must find a way to address issues associated with age-related degradation of cables. Designers of small modular reactors are also in need of technologies to evaluate the performance of cables that will be installed in harsher environments (e.g. higher temperatures, radiation doses, dose rates, etc.) than those present in current-generation reactors. Today, a variety of cable condition monitoring (CM) techniques have been developed and successfully used in nuclear facilities. These techniques are used to identify age-related degradation and assess the condition of cables to determine if their performance characteristics have changed with age. However, objective criteria must be developed for these CM tests to help quantify cable condition and thereby develop repair and replacement schedules. With operating life extending to 80 years and more SLRs on the horizon, both nuclear facilities and regulators need an objective means to determine the aged condition of cables.

36 MATERIALS SCIENCE↗