DOE OSTI2021

Segregation behavior and phase instability of Eurofer97 after neutron irradiation to 72 dpa

Here, a reduced activation ferritic/martensitic steel, Eurofer97, was neutron irradiated in the vicinity of 300 °C in the High Flux Isotope Reactor (HFIR) up to 72 dpa. Advanced analytical scanning transmission electron microscopy and conventional transmission electron microscopy were applied to investigate the radiation-induced segregation and phase instability behavior after neutron irradiation. Amorphization was observed in M 23 C 6 carbides. Cr-rich clusters were seen within the matrix, near the lath boundaries and close to the M 23 C 6 carbides. Cr enrichment and Fe depletion were detected at both prior austenite grain boundaries and lath boundaries, despite different segregation magnitude. In addition, the enrichment of Ni, the depletion of V, and tiny cavities (presumably helium bubbles) are also found at lath boundaries. This work interrogates the evolution of microstructures after neutron irradiation, which provides detailed understanding on the microstructural aspects controlling the mechanical integrity of Eurofer97 under high-dose neutron damage.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Solute segregation and precipitation across damage rates in dual-ion–irradiated T91 steel

We report that dual-ion irradiations using 5.0 MeV defocused Fe 2+ ions and co-injected energy degraded 2.00 to 2.85 MeV He 2+ ions were conducted on a Fe9CrMo ferritic-martensitic steel T91 to 17 dpa at a damage rate range of 5 × 10 -5 dpa/s to 3 × 10 -3 dpa/s at 445°C, followed by characterization of the microstructure using conventional and scanning transmission electron microscopy. Radiation induced Ni/Si clusters and radiation induced segregation were quantified using energy dispersive X-ray spectroscopy at each condition and were compared with the same material irradiated in the BOR-60 reactor and in the as-received condition. No significant Cr segregation was found at lath boundaries after dual-ion irradiation, while Ni and Si enrichments both decreased with increasing damage rate leading to a sharp decrease in the density of Ni/Si clusters with damage rate. Increased point defect recombination at higher ion damage rates likely reduced the Ni/Si cluster density compared with BOR-60. Although the overall vacancy concentration and diffusion are enhanced by the irradiation damage rate, the lack of time for thermal diffusion and ballistic displacements of solutes are significant limiting factors for Ni/Si cluster formation. This work demonstrates the effect of irradiation damage rate on elemental segregation and clustering when using ion irradiation to simulate reactor irradiation.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Friction stir welding and self-ion irradiation effects on microstructure and mechanical properties changes within oxide dispersion strengthened steel $\mathrm{MA956}$

We report the joining process for oxide dispersion strengthened (ODS) alloys remains a key challenge facing the nuclear community. The microstructure and mechanical properties were characterized in the base material and friction stir welded ODS MA956 irradiated with 5 MeV Fe 2+ ions from 400 to 500°C up to 25 dpa. Nanoindentation was performed to assess changes in hardness and yield stress, and the dispersed barrier hardening (DBH) model was applied to described results. A combination of scanning transmission electron microscopy (STEM) and atom probe tomography (APT) were used to assess evolution of the microstructure including dispersoids, network dislocations and dislocation loops, nanoclusters, and solid solution concentrations. Overall, softening was observed as a result of increased dose, which was exacerbated at 500°C. The formation and coarsening of new dispersoids was noted while nanoclusters tended to dissolve in the base material, and were not observed in the stir zone. Solute nanocluster evolution was identified as a primary driver of the changes in mechanical properties.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Post-irradiation examination of commercial tantalum alloys following neutron irradiation

Post irradiation examination of two commercial tantalum alloys (based on Ta-8 %W) revealed significant irradiation hardening following neutron irradiation in the High Flux Isotope Reactor at Oak Ridge National Laboratory. Tensile samples of commercial Ta alloys T-111 and ASTAR-811C were irradiated to a total neutron fluence (E > 0.1 MeV) in the range (2–4)x10 21 n/cm 2 (0.39–0.75 dpa) at an irradiation temperature near 900 °C. Tensile testing conducted at room temperature and at 800 °C revealed significant irradiation hardening under all test conditions. Samples that were tensile tested at room temperature exhibited brittle failure, whereas ductility was maintained for elevated temperature testing. The irradiation hardening and embrittlement noted for both alloys was attributed to irradiation-induced dislocation loop formation as confirmed through scanning transmission electron microscopy analysis. Corresponding energy dispersive x-ray spectroscopy revealed radiation-induced segregation of Hf in these loop populations. This Hf enrichment is shown to result in eventual co-precipitation of elongated (Hf,O)-rich precipitates along the dislocation loops. Further, these results show that irradiation hardening is enhanced via irradiation-enhanced precipitation at elevated irradiation temperatures. Consequently, the minimum recommended operating temperature window for Ta alloys should be increased to account for observed hardening/embrittlement at irradiation temperatures as high as 900 °C (1,173 K).

36 MATERIALS SCIENCE↗
DOE OSTI2024

Microstructural and compositional evolutions in $γ$-LiAlO 2 pellets during ion irradiation at an elevated temperature

This study reports on the microstructural, phasic and compositional evolutions of γ-LiAlO 2 during ion irradiation. Polycrystalline γ-LiAlO 2 pellets were irradiated sequentially with He + and D 2 + ions to the same combined fluences of up to 3 × 10 17 (He + +D + )/cm 2 at 773 K. The irradiated pellets were characterized using scanning transmission electron microscopy and atom probe tomography. Surface amorphization likely due to radiolysis and planar defects as a possible precursor for formation of precipitates are created at 5 × 10 16 (He + +D + )/cm 2 , followed by the formation of nano-sized precipitates and fractures at higher doses. Spinel-like precipitates of non-stoichiometric LiAl 5 O 8 and gas-filled cavities are observed to grow with increasing dose. Faceted precipitates and rounded cavities appear at 2 × 10 17 (He + +D + )/cm 2 . With further increasing ion fluence to 3 × 10 17 (He + +D + )/cm 2 , amorphization of the precipitates takes place and micron-sized fractures appear. Surface exfoliation could occur at an extremely high ion fluence. There are compositional changes in the γ-LiAlO 2 pellets during the microstructural evolution. In the precipitate and amorphized regions, Li concentrations decrease to ~7 and 3.7 at.% from 25 at.% in γ-LiAlO 2 , respectively. This study reveals a full-cycle microstructural evolution with corresponding compositional changes in γ-LiAlO 2 pellets during ion irradiation at 773 K. In conclusion, the data could help model, assess, and predict the material performance during neutron irradiation in reactors.

73 NUCLEAR PHYSICS AND RADIATION PHYSICS↗
DOE OSTI2025

Characterization of the microstructure of yttrium hydride under proton irradiation

High moderation per unit volume solid moderator materials like yttrium hydride (YH x ) are necessary for compact nuclear microreactors. However, the phase stability and hydrogen transport processes of YH x under high-temperature irradiation are largely unknown. Proton irradiation was conducted on YH x at 300 °C and 580 °C to 0.2 dpa using 1 MeV or 2 MeV protons in a high-vacuum environment. The hydrogen concentration was determined before and after irradiation using elastic recoil detection analysis, and microstructural evolution was examined via post-irradiation scanning transmission electron microscopy and Raman spectroscopy. Dislocation loops and cavities were observed in all conditions; their distribution was correlated with the bombarding proton energy and ion irradiation temperature. This work revealed that hydrogen retention is proportional to the formation of traps for hydrogen gas atoms and identified pathways for hydrogen release. The relative contributions of bulk or fast diffusion paths, such as grain boundaries, delamination boundaries, and stacking faults are discussed; the primary mechanisms of hydrogen loss are likely based on diffusion, ruling out artefacts of the experimental design. In conclusion, the study suggests proton irradiation may be a strong surrogate to study hydrogen transport in hydride moderator materials under irradiation.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2025

In situ self-ion (Fe + ) irradiation of ODS-FeCrAl alloy fuel cladding materials with different Cr contents: The early stages of Cr-rich α’ phase precipitation

Oxide-dispersion-strengthened FeCrAl (ODS-FeCrAl) alloys are candidate accident-tolerant fuel cladding materials for light water reactors because they demonstrate satisfactory resistance to materials degradation effects such as high-temperature oxidation, radiation-induced swelling, and creep. Their perspective deployment to market is challenged, however, by their inherent susceptibility to irradiation embrittlement caused by the precipitation of the brittle Cr-rich α’ phase at relatively low temperatures (≤475 °C). This work used in situ self-ion irradiation (150 keV Fe + ) in a transmission electron microscope to elucidate the early stages of Cr-rich α’ phase precipitation in three candidate ODS-FeCrAl alloy fuel cladding materials with different Cr contents (10, 12, and 20 wt.%) and microstructures. The early stages of the process resulting in the precipitation of the Cr-rich α’ phase in these three ODS-FeCrAl alloys under Fe + irradiation were investigated at room temperature and 300 °C up to total fluences of 1.7 × 10 15 ions·cm -2 (2 dpa) and 3.4 × 10 15 ions·cm -2 (4 dpa), using three damage dose rates (5 × 10 –5 , 3.3 × 10 –4 , and 2 × 10 –3 dpa·s -1 ). Post-irradiation examination via scanning transmission electron microscopy, energy-dispersive X-ray spectroscopy and electron energy loss spectroscopy suggested that the precipitation of the Cr-rich α’ phase might be promoted by the phase separation of the alloy matrix into Cr-rich and Fe-rich regions. Interestingly, oxygen impurities segregated preferentially in the Cr-rich regions, possibly promoting the radiation-assisted formation of the Cr-rich α’ phase. α’ phase precipitation was more pronounced at room temperature when compared to 300 °C, and it was clearly promoted by the progressive increase in the Cr content of the ODS-FeCrAl alloy.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Microstructural features and deuterium diffusion in lithium penta-aluminate pellets under He + and D + ion irradiation

Lithium (Li) penta-aluminate (LiAl 5 O 8 ) is investigated as a potential tritium (T) breeding material, with a focus on microstructural response to ion irradiation and deuterium (D) diffusion behavior. Under high-fluence ion irradiation (2 x 10 17 (He + +D + )/cm 2 ) at 773 K, LiAl 5 O 8 exhibits significant disorder on the Li sublattice, as revealed by atomic-resolution scanning transmission electron microscopy, while the Al and O sublattices remain stable, demonstrating strong resistance to structural amorphization. Irradiation induces the formation of platelet-shaped antiphase boundaries (APBs), which may serve as effective D trapping sites. Atom probe tomography suggests the presence of 6 LiD clusters in the mass spectra, though definite conclusions regarding APB composition are hindered by signal overlap and limited data statistics. Time-of-flight secondary ion mass spectrometry reveals that D retention approaches to saturation at 3 x 10 17 (He + +D + )/cm 2 . Isothermal and isochronal annealing studies determine an average diffusivity of 1.6 x 10 -13 at 773 K and an effective activation energy of 0.8 ± 0.1 eV for D migration. Compared to γ-LiAlO 2 , LiAl 5 O 8 demonstrates superior irradiation resistance, minimal Li loss, and enhanced D retention, underscoring its potential as a durable breeder material for T production. In conclusion, these findings provide key insights into the microstructural evolution, defect dynamics, and D retention mechanisms in LiAl 5 O 8 under reactor-relevant conditions.

42 ENGINEERING↗
DOE OSTI2025

Microstructural evolution and hardness changes in ion irradiated nickel-based Haynes 282 superalloy

This study investigated the crucial aspects of thermal and irradiation stability in precipitation hardened Haynes 282 Ni-based superalloy. The Haynes 282 Ni-based alloy was irradiated by 8 MeV Ni 3+ ions to assess its resistance to phase instabilities and mechanical property alterations. The mid-range doses (at a depth of ∼1 µm) were 1 and 10 displacements per atom (dpa) at temperatures of 600°C and 750°C. Nanoindentation tests provided insights into bulk equivalent hardness of the irradiated and pristine regions, while scanning transmission electron microscopy (STEM) and energy dispersive X-ray spectroscopy (EDS) were used to examine the microstructural evolution of irradiation-induced defects and γ′ -Ni 3 (Al, Ti) precipitates and defect structure under irradiation. These precipitates, with an average diameter of 29 nm and a number density of 5 x 10 21 /m 3 , acted as robust dispersion strengthening agents with high radiation point defect sink strength. Remarkably, irradiation did not significantly alter the size or number density of the γ′ precipitates, indicating exceptional thermal stability and radiation resistance of these precipitates at the examined conditions. Radiation-induced dislocation loops were observed at 600°C, albeit without a substantial impact on mechanical properties due to the dominance of γ′ precipitates on the overall alloy strength. The superior stability of γ′ precipitates observed in this study contrasts with several previous research findings on Ni-based alloys that reported poor precipitate stability. Plausible reasons for this difference are discussed. Moreover, this work explicitly outlines a physically grounded approach to ensure accurate microstructure-hardness correlations and clarifies the hardening model by addressing common misapplications of superposition in prior studies.

36 MATERIALS SCIENCE↗
DOE OSTI2026

Growth of deuterium supersaturated surface layer with increasing ion flux and fluence in plasma-exposed tungsten

Deuterium supersaturated surface layer (DSSL) in tungsten, a few nm thick layer exhibiting extremely high deuterium content (> 5%), has been studied as a function of deuterium plasma ion flux and fluence. Tungsten samples were exposed at 400 K and deuterium ion energy of ∼ 60 eV. The deuterium ion flux spanned over an order of magnitude, being 7.3 × 10 20 , 4.2 × 10 21 , and 3.8 × 10 22 D/m 2 . The fluence ranged from 3.4 × 1024 to 3.4 × 1025 D/m2. The samples and their deuterium content were analyzed by nuclear reaction analysis (NRA), scanning transmission electron microscopy (STEM), and thermal desorption spectroscopy (TDS). The largest thickness of DSSL was found to be around 10.5 nm and was observed in the case of the highest exposure flux and fluence, whereas the layer was only about 3.8 nm thick in the case of the lowest value of the two parameters. The thickness of the DSSL was found to monotonically increase with both deuterium flux and fluence. Finally, similar to the thickness, the estimated D concentration seems to follow the same trend, increasing from the lowest value of around 3 at.% to the highest value of around 5 at.%.

Deuterium↗
DOE OSTI2026

Using X-ray spectrum imaging to quantify fission gas in high-burnup UO2 fuel

Analysis of fission gas bubbles (FGBs) in light-water reactor (LWR) fuel is needed to improve the understanding and predictive capability of fuel evolution under normal- and transient conditions. One of the most important parameters of a FGB is the pressure of the gas, primarily Xe, inside it. Bubble volume and location (inter- vs. intragranular) are important considerations as well. However, experimental analysis of such bubbles is challenging due to their small size and embedded nature, and usefulness of the data requires large numbers be analyzed. This paper proposes a method to measure the pressure of Xe bubbles using X-ray spectrum imaging (XSI) in scanning transmission electron microscopy (STEM). From X-ray generation and instrumental parameters, the number of Xe atoms yielding a given number of Xe L-series X-ray counts is estimated, and then from the estimated volume of the bubble the Xe density is estimated, which can then be converted to pressure via an equation-of-state. We apply the method to XSI datasets from high burnup (HBu) fuel from North Anna 1 reactor in as-irradiated and post-LOCA-test conditions and find Xe pressures in the FGBs clustered around 1 GPa.

Parish, Chad [ORNL] (ORCID:0000000312097439)↗
DOE OSTI2024

Fast ionic conduction achieved through the design and synthesis of ceramic heterointerfaces

Lithium (Li) chloride and iron oxychloride (FeOCl), typically nonconductive, were combined to form a [Li 1+δ Cl] δ+ /[FeOCl] δ- heterointerface composite material (LFH), achieving ionic conductivities of >1 mS cm -1 . Analysis techniques (scanning transmission electron microscopy [STEM] and electron energy-loss spectroscopy [EELS]) indicated that the microstructure of LFH consisted of an amorphous LiCl-based shell surrounding a crystalline FeOCl-based core. Electrochemical measurements alongside solid-state 6,7 Li nuclear magnetic resonance (NMR) and molecular dynamic simulations revealed Li+ as the sole conductive species, with a diffusion barrier of ~0.25 eV. X-ray photoelectron spectroscopy (XPS) and X-ray absorption fine structure (XAFS) results further supported interstitial Li + diffusion at the heterointerface and within the LiCl phase, made possible by the heterointerface. Despite susceptibility to electronic conductivity, iron’s defects and multivalency (Fe³⁺, Fe²⁺) enable the Fe–O–Cl framework to accept Cl - , facilitating Li⁺ ionic conduction. Finally, a prototype solid-state cell (showing 97% Coulombic efficiency) demonstrated the viability of this heterointerface design for applications in energy storage.

36 MATERIALS SCIENCE↗
DOE OSTI2026

The structure, composition, and performance impact of a YSZ-GDC interdiffusion layer in solid oxide electrolysis cells

This study provides a combined experimental and computational investigation into the structure and impact of the cation interdiffusion layer that appears at the gadolinium doped ceria (GDC)/yttria stabilized zirconia (YSZ) interface in solid oxide electrolysis cells (SOECs). Scanning transmission electron microscopy (STEM) illustrates that a ∼0.4 μm interdiffusion layer (IDL) with an intermixed cation distribution and fine grain size forms upon sintering. STEM identifies that the interdiffusion layer exists in the cubic fluorite structure despite changes in cation composition. The interdiffusion layer microstructure formed during sintering does not change during SOEC testing at either 1.3V or heightened voltage pulse testing. Modeling predicts that ionic conductivity may decrease in the interdiffusion layer due to Coulombic trapping between mobile oxygen vacancies and excess Gd 3+ acceptor dopants. Yet, the density and continuous nature of the layer should benefit cell stability by substantially reducing the formation of SrZrO 3 , which is corroborated by STEM and Synchrotron X-ray diffraction (XRD). We conclude that the interdiffusion layer acts as a beneficial barrier to Sr diffusion, when operating in a regime where electrolyte void formation is not observed.

organic↗
DOE OSTI2021

Creep properties of advanced austenitic steel 709 determined through short experiments under in-situ neutron diffraction followed by TEM characterization

Here in this study, the creep mechanisms at play in Alloy 709 (Fe-20Cr-25Ni) are investigated by performing short-term creep-type tests under in-situ neutron diffraction experiments. Short tests are performed in the temperature range of 500 to 900 °C under constant load with a load ranging from 50 to 150 MPa. The creep exponent and activation energy are determined using the Bird-Mukherjee-Dorn relation and compared to that obtained from conventional longer creep tests from the literature. Scanning transmission electron microscopy (S/TEM) of the post-creep microstructure indicates that interaction of dislocations with precipitates are a dominant mechanism at play. Furthermore, local elemental mapping indicated chemical segregation at grain boundaries and formation of complex precipitates.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Site-specific nanoscale characterization of zirconium hydrides in the hydride rim structure of hydrogen-charged zircaloy-4 cladding

Zircaloy-4 cladding tubes were hydrogen-charged using a static pressure hydrogen charging method to experimentally produce a zirconium-hydride rim structure similar to that observed in Zircaloy-4 cladding tubes after operation in commercial light-water nuclear reactors. Detailed characterization was performed using electron energy loss spectroscopy (EELS) and four-dimensional scanning transmission electron microscopy (4D-STEM). By mapping the position of the plasmon peak in the low-loss EELS spectrum, it was determined that the zirconium hydrides formed were predominantly solid δ-phase zirconium hydrides. 4D-STEM was used to generate phase and strain maps at nanoscale. The interactions between two zirconium hydride platelets less than 200 nm apart leads to the localized lattice rotations and possible phase change, revealing a potential hydride growth mechanism.

4D-STEM↗
DOE OSTI2025

Investigating Grain Structure and Microcracking in SiCf-SiCm Composites Using 4D-STEM

Silicon carbide (SiC) fiber-reinforced SiC matrix composites (SiCf-SiCm) are promising materials for accident-tolerant fuel (ATF) cladding in light water reactors. This paper, using four-dimensional scanning transmission electron microscopy (4D-STEM), studied the microstructure of SiCf-SiCm at nanoscale and provided grain statistics at the CVI/fiber region. Here, the results reveal that CVI region mainly contain irregular sub-micron grains (115 nm to 1800 nm) with a preferred orientation, while the fiber region has nano equiaxed grains (21 nm to 78 nm) with random orientations. Centered dark field imaging over the fiber regions verified the grain size measurement by 4D-STEM. Through 4D-STEM virtual dark field imaging and orientation mapping, intragranular propagation was identified as the fracture mechanism for a microcrack observed within the CVI region. The amorphous pyrolytic carbon layer was also shown to effectively arrest the microcrack.

4D-STEM↗
DOE OSTI2025

Mapping strain and structural heterogeneities around bubbles in amorphous ionically conductive Bi 2 O 3

While amorphous materials are often approximated to have a statistically homogeneous atomic structure, they frequently exhibit localized structural heterogeneity that challenges simplified models. This study uses 4D scanning transmission electron microscopy to investigate the strain and structural modifications around gas bubbles in amorphous Bi 2 O 3 induced by argon irradiation. We present a method for determining strain fields surrounding bubbles that can be used to measure the internal pressure of the gas. Compressive strain is observed around the cavities, with higher-order crystalline symmetries emerging near the cavity interfaces, suggesting paracrystalline ordering as a result of bubble coarsening. This ordering, along with a compressive strain gradient, indicates that gas bubbles induce significant localized changes in atomic packing. By analyzing strain fields with maximum compressive strains of 3%, we estimate a lower bound on the internal pressure of the bubbles at 2.5 GPa. These findings provide insight into the complex structural behavior of amorphous materials under stress, particularly in systems with gas inclusions, and offer new methods for probing the local atomic structure in disordered materials. Although considering structural heterogeneity in amorphous systems is non-trivial, these features have crucial impacts on material functionalities, such as mechanical strength, ionic conductivity, and electronic mobility.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Kinetics and mechanism of light-induced phase separation in a mixed-halide perovskite

Halide ion phase separation is a barrier to the application of mixed-halide perovskites, whereby the presence of large populations of photo-generated or injected carriers causes undesirable changes in the local band gap. Here, we investigate the mechanism of phase separation in CsPbI x Br 3-x perovskite single crystals driven by light. The phase separation process and its dynamics are visualized at the nanometer scale at cryogenic temperatures using in-situ scanning transmission electron microscopy and cathodoluminescence. Combined with phase field modeling that accounts for the coupling between electronic and chemical driving forces, our observations point to a spinodal decomposition mechanism in which both the amplitude of composition fluctuation and the characteristic length scale grow non-linearly with time. Our findings provide microscopic insights that can assist in further engineering mixed-halide perovskites either for stability or for intentional programming of the local halide ion composition, opening pathways to a wide range of applications.

36 MATERIALS SCIENCE↗