Results for “PV reliability” — Page 27

DOE OSTI2021

Fatigue-Like Behavior of Silver Metallization Gridlines and Proposed Damage Mechanics Model

In this work, we present a novel method to evaluate the fracture and fatigue-like behavior of crystalline silicon PV cell metallization. Initial results demonstrate that silver metal gridlines are capable of bridging a ~10–20 µm gap prior to becoming electrically open and do demonstrate fatigue-like behavior under cyclic straining conditions. This later phenomenon was well fit with a traditional power law equation for high cycle fatigue and enabled the development of a damage mechanics model for gridline failure.

41 EE - Solar Energy Technologies Office (EE-4S)↗

DOE OSTI2024

Development and Reliability of Screen-Printable Fire-Through Cu Paste for Passivated Contact Solar Cells

We present the development of copper (Cu) paste which has been screen printed on Selective Emitter-Passivated Emitter Rear Contact (SE-PERC) solar cells. This paste can also be applied to Tunnel Oxide Passivated Contact (TOPCON) solar cells due to its fire-through nature. Champion PERC cells have achieved ....efficiency with ...parameters . Accelerated testing to investigate reliability performance of the SE- PERC mini-modules were carried out in damp heat chamber with 85oC and 85% humidity. The devices were found to be operational even after 1,500 hours. Devices with screen printed Ag contacts on the front side have been studied in parallel to the Cu contacts for comparison.

copper paste↗

DOE OSTI2026

Powering Up Secure and Reliable Operations at the Port of Honolulu's Kapalama Container Terminal

The National Laboratory of the Rockies (NLR) is providing resilience planning support to the Pasha Group, the operator of Kapalama Container Terminal (KCT) at the Port of Honolulu, by exploring how distributed clean energy resources could help the terminal sustain a 36-hour outage and continue emergency operations. The Department of Energy's Energy Transitions Initiative (ETI) aims to advance self-reliant island and remote communities by promoting resilient, affordable, and sustainable clean energy resources.

25 ENERGY STORAGE↗

DOE OSTI2021

Standards development for modules in high temperature micro-environments

Photovoltaic (PV) module qualification standards, IEC 61215 and IEC 61730, were designed to apply to “general open-air climates” and IEC 61730 specifically indicated applicability of ambient air temperature of 40°C. Additionally, these standards provided allowances for so-called “open rack mounted PV modules” without a clear definition of “open-rack.” These implied restrictions and allowances meant that hotter climates or thermally restrictive installation methods may not be covered by these often customer-mandated certification standards. This is particularly salient for the significant growth regions of the Middle East and India that would be expected to operate at significantly higher temperatures. The applicability of these documents raised issues over the definition of “open rack” and the fact that the geographic location is just as important as the mounting configuration in assessing the impact of the micro-environment of a PV module. This work summarizes the scientific background for IEC Technical Specification 63126:2020 ED1, titled “Guidelines for qualifying PV modules components and materials for operation at high temperatures.” This standard was recently published by the IEC and is the first step in a systematic effort to rework these standards to address the question of temperature more directly. Instead of specifying a mounting condition, we specify different suites of tests suitable for a system (PV module, mounting style, and location) defined by the 98th percentile cell temperature. With a defined temperature regime to work from, this allowed us to use existing literature research combined with additional modeling work to determine, which tests would need to be modified. This resulted in suggested changes to material thermal indices, thermal cycling temperatures, hot spot testing, ultraviolet testing, and bypass diode testing among other tests and characteristics described in this study.

14 SOLAR ENERGY↗

DOE OSTI2021

Bridging Power System Protection Gaps with Data-driven Approaches

Protection is a critical function in power systems to avoid equipment damage, maintain personnel safety, and support system reliability. However, current protective relay technology cannot adequately protect equipment and personnel from effects of some events; these deficiencies are termed protection gaps. In this research, a data-driven approach is proposed to complement traditional protection technology and distinguish fault conditions from transients caused by normal operations. A convolutional neural network (CNN) based fault detection approach is implemented to achieve data translation invariance of the time-series input data. As a result, the data-driven method can accurately detect system faults despite variation and noise in the input data. In addition, using the CNN–based method avoids the complicated manual feature extraction procedure required by many traditional data-driven methods. The effectiveness of the proposed approach is tested on four kinds of protection gaps: high impedance faults, transformer/generator inter-turn faults, distribution system PV circuit faults, and the mis-operation situations of Zone 3 line protection relays operating under system stress. Finally, a transfer learning method is also proposed to address the common issue of data-driven methods for which real-world training data are scarce. Extensive study results demonstrate that the proposed approach can accurately bridge power system protection gaps.

24 POWER TRANSMISSION AND DISTRIBUTION↗

DOE OSTI2021

Representative Modules for Accelerated Thermal Cycling and Static Load Testing

In this work, we explore the influence of module size on the rate of interconnect solder bond thermomechanical fatigue (TMF) damage and the probability of cell fracture. For the solder bond TMF damage evaluation, structural mechanics models of crystalline silicon PV models are created to solve with the Finite Element Method. For the probability of cell fracture evaluation, Weibull analysis and weakest link theory are employed to resolve the probability of crystalline silicon PV cell fracture when measured as bare cells and when stressed in reduced- and full-sized modules. Results conclusively demonstrate that the rate of solder bond TMF damage is independent of module size, interconnect location across the cell and cell location across the module and that smaller, representative, modules must be loaded to a much higher level than their parent full-sized modules to achieve an equivalent driving force for cell fracture.

accelerated testing↗

DOE OSTI2021

Community-scale interaction of energy efficiency and demand flexibility in residential buildings

Demand-side management (DSM) strategies, including energy efficiency (EE) and demand flexibility (DF), contribute to cost-effective operation of the electricity grid. From a system-level perspective, such programs reduce costs, enhance reliability, and reduce network issues. Similarly, DSM programs help participating customers reduce utility bills while maintaining occupant comfort. Understanding the relationship between EE and DF is key to realizing the full potential of DSM programs. In this study, we modeled an all-electric residential community based on a 498-home community that is planned for construction in Fort Collins, Colorado in the United States. We used this community model to study the relationship between different EE measures, including building envelope upgrades and smart appliances, and DF enabled by a home energy management system (HEMS) responding to a time-varying tariff. Various EE levels in the homes – code-minimum, zero energy ready, and even higher levels of envelope efficiency – were simulated. DF is enabled by the HEMS, which coordinates behind-the-meter resources, including flexible building loads, PV, and home battery systems, to minimize utility bills while maintaining occupant comfort. When comparing to the code-minimum homes, EE upgrades alone reduce HVAC energy use during peak hours by up to 50% and the HVAC utility bill by up to $312/year. With the addition of HEMS, the average daily peak demand can be reduced by up to 0.58 MW or 1.2 kW/home in the higher envelope efficiency homes. The combination of EE upgrades, HEMS, and home battery systems is expected to save homeowners up to $590/year while increasing community load flexibility. However, HEMS and home battery systems are less effective in increasing the DF in the more efficient homes due to the lower load.

32 ENERGY CONSERVATION, CONSUMPTION, AND UTILIZATI↗

DOE OSTI2023

Extreme Weather Events and the Impact on PV Time Series Data

The impact of extreme weather events on PV performance was studied by comparing the National Oceanic and Atmospheric Administration database on severe weather with the PV Fleet database on continuous PV performance. We identified 170 systems that were immediately impacted by weather events. These severe weather events lead to a median loss of only 1% of annual production. However, flooding and high wind events were found to have an extremely long tail extending to 60 % loss showing that these discrete events can pose a substantial risk to PV systems. Besides the short-term impact of lost production due to outages, we also found a statistically significant increased performance loss rate (PLR) for high wind events comparing PLR before and after these weather events. In addition, hail events caused a higher PLR for 2 out of 3 systems. More data are required to better quantify the impact, but these first results illustrate the substantial risk these events pose short-and long-term.

degradation↗

DOE OSTI2025

Deployment Potential of Concentrating Solar Power Technologies in California

As states within the United States respond to future grid development goals, there is a growing demand for reliable and resilient nighttime generation that can be addressed by low-cost, long-duration energy storage solutions. This report studies the potential of including concentrating solar power (CSP) in the technology mix to support California’s goals as defined in Senate Bill 100. A joint agency report study that determined potential pathways to achieve the renewable portfolio standard set by the bill did not include CSP, and our work provides information that could be used as a follow-up. This study uses a capacity expansion model configured to have nodal spatial fidelity in California and balancing-area fidelity in the Western Interconnection outside of California. The authors discovered that by applying current technology cost projections CSP fulfills nearly 15% of the annual load while representing just 6% of total installed capacity in 2045, replacing approximately 30 GWe of wind, solar PV, and standalone batteries compared to a scenario without CSP included. The deployment of CSP in the results is sensitive to the technology’s cost, which highlights the importance of meeting cost targets in 2030 and beyond to enable the technology’s potential contribution to California’s carbon reduction goals.

14 SOLAR ENERGY↗

DOE OSTI2024

EVs@Scale Lab Consortium High-Power Charging Pillar Deep-Dive Technical Meeting

Managed under the the U.S. Department of Energy (DOE)-funded EVs@Scale Consortium, the High-Power Electric Vehicle Charging Hub Integration Platform (eCHIP) project aims to create an experimental platform for integration and control approaches in a direct current (DC), distribution-based high-power charging (HPC) system. The eCHIP project addresses the crucial need to design and validate efficient, low-cost, reliable, and interoperable solutions for a DC-coupled charging hub ("DC hub" for short). This report explains the design, development, and implementation process of an experimental platform for the DC hub. DC distribution holds significant potential for enhancing the operation of an HPC station architecture. However, there are challenges in establishing a DC hub, including interoperability, commoditization, distributed energy resource integration, stability, DC protection, and a lack of common system-level controllers. To address these challenges, a testing setup is required that accommodates commercial off-the-shelf (COTS) products, as well as novel, in-house designed solutions, to evaluate different use cases at rated power and voltage levels. The developed proof-of-concept charging platform and open-source SEMS allow the development and testing of various controllers and chargers from different vendors. The DC hub platform integrated EVs, an ESS, a PV system, and building load to demonstrate the flexibility of the platform. The open-source SEMS controlled the devices within the hub using a rule-based implementation, realizing available standards.

ADVANCED PROPULSION SYSTEMS↗

DOE OSTI2022

Degradation in Photovoltaic Encapsulant Transmittance: Results of the Second PVQAT TG5 Artificial Weathering Study

The optical degradation of encapsulants from ultraviolet (UV) radiation has historically resulted in a significant loss in performance throughout the life of a photovoltaic (PV) module. International Electrotechnical Commission (IEC) test methods have recently been developed to screen for PV encapsulants prone to loss in optical performance. The present study was performed to benchmark polymeric packaging materials relative to IEC 62788-1-4 (covering the measurement of optical transmittance) and IEC 62788-1-7 (on the durability of transmittance), provide feedback toward improvement of the methods, and develop insight regarding optical degradation. Contemporary materials were examined, including poly(ethylene-co-vinyl acetate) (EVA), thermoplastic polyolefin (TPO), polyolefin elastomer (POE), and polyvinyl butyral (PVB) encapsulants; a poly(ethene-co-tetrafluoroethene)/poly(ethylene terephthalate) (ETFE/PET) transparent backsheet; and a polystyrene (PS) working reference material. The use of silica-, specialty-, and rolled-glass was also compared in laminated coupons. Specimen size was separately examined from 2.5 to 12.5 cm. Weathering was performed with a xenon source, using IEC TS 62788-7-2 methods A2, A3, A4, and A5 (chamber temperature of 55 degrees C, 65 degrees C, 75 degrees C, or 85 degrees C), respectively. Characterizations were made using a UV-visible-near-infrared (UV-VIS-NIR) spectrophotometer (transmittance and reflectance, with and without an integrating sphere), a UV-VIS fluorescence spectrophotometer, a camera, and an optical microscope. Performance was analyzed, including solar weighted transmittance, yellowness index, UV cut-off wavelength, and haze (scattering). Separate Arrhenius analyses were performed to assess retention of transmittance and changes in yellowness index. The activation energy for both characteristics was found to range from 15-80 kJ mol-1, with an average of 48 kJ mol-1, similar to the average of 45 kJ mol-1 identified in the previous international PV Quality Assurance Task Force (PVQAT) Task Group 5 (TG5) study of more traditional encapsulants. The separate degradation modes of discoloration and scattering were distinguished in the encapsulants using a comprehensive spectral characterization. Based on these results, the IEC 62788-1-7 pass/fail criteria of 5% change in transmittance was confirmed to identify a known bad encapsulant.

durability↗

DOE OSTI2022

Correspondence: Bill of Materials Variation and Module Degradation in Utility-Scale PV Systems

We report photovoltaic (PV) modules of the same make and model are often assembled with different bills of materials (BOMs). In this correspondence, we revisit two case studies of utility-scale silicon PV systems in which these differing BOMs were associated with faster-than-expected degradation. In one of the sites, we found that different metallization paste had been used for grid lines in some cells leading to loss of contact to the cell and severe series resistance degradation. We provide details on the observation of this mechanism at two additional sites not described in the original article. In a second case study, we found that two different types of cell had been used, and that they could be distinguished by their back contact. Cells with uniform back contacts suffered from light and elevated temperature induced degradation (LeTID), while those with local back contacts did not. We also briefly describe BOM variations observed at other sites to illustrate the extent of the challenge. Our results from both sites underscore that variations in BOM, even among modules of the same make and model can lead to reliability challenges.

14 SOLAR ENERGY↗

DOE OSTI2024

Evaluating the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

A bifacial silicon heterojunction solar cell demands approximately 210 mg usage of silver paste (9 busbars, 24.5%, bifacial, M6 size wafer). Copper is an excellent alternative to silver: 100x cheaper, similar elecvtrical resistivities, and 1000x more abundant. Successful demonstration of large area selective emitter PERC solar cells using Cu fire-through paste with FF approximately 75% and approximately 19%. Paste chemistry results in oxide-based Cu diffusion barrier, leading to good reliability of the devices: 1000h DHT giving a 3.5% efficiency drop. The additional series resistance still needs to be lowered. Printed and fired cell performance is governed mostly by pFF, especially J02 ; same for DHT degradation. Further improvement in printing and firing optimization for lower series resistance and higher FF.

Ag↗

DOE OSTI2026

Multiple Hail Impact Testing

For resilient energy delivery PV modules and systems must withstand extreme weather events such as hailstorms, which are the leading cause of PV insurance claims. Currently, the industry testing is limited to one strike at a time, but in real hailstorms multiple hail strikes can occur within a fraction of a second. In this project we test if multiple simultaneous or near-simultaneous hail strikes cause more damage than with single hail strike testing.

14 SOLAR ENERGY↗

DOE OSTI2025

Characterization of Performance Degradation Mechanisms in Low-Cost High Throughput DI-O3 Layer for Passivated Contact Silicon Solar Cells

Characterization and mitigating performance limiting defects in Silicon (Si) PV is one of key areas to be addressed to improve PV hardware costs and energy yield in order to lower the levelized cost of energy (LCOE) of installed PV cost to $0.02/kWh. As Si PV cells efficiencies have surpassed 22% and approaching 23%, the recombination at the metal contacts have become the focus point to be addressed. Passivated contact technologies—having a heterojunction with a band-gap larger than silicon between the metal and silicon—have emerged as a great potential for future highand ultrahigh-efficiency solar cells, as it concurrently reduces recombination and increases carrier selectivity, by incorporating thin films within the contact structure. Passivated contact Si solar cell technologies use a wide variety of tunnel layers—playing a crucial role to passivate metal contacts and tunnel charge carriers—including stoichiometric silicon oxide (SiO 2 ) grown by thermal oxidation and Low-Pressure Chemical Vapor Deposition (LPCVD) technique and silicon oxide (SiO x ) by hot nitric acid. However, thorough investigations on understanding the failure and performance degradation mechanisms associated with tunnel layers are still limited to date. Unlocking those degradation characteristics in crucial tunnel layers could improve the reliability and energy yield of passivated contact Si solar cells. Besides, the technique of growing aforementioned tunneling layers are low throughput, and requires high temperature processes and/or a vacuum environment. In this project, we investigated the performance degradation mechanisms of a low-cost high-throughput ozonated oxide (DI-O 3 ) tunnel layer for the passivated contact Si solar cells.

14 SOLAR ENERGY↗

DOE OSTI2020

Energy Paths for the Yurok People

This Yurok Tribe energy strategic planning study examined electricity usage, costs and infrastructure, as well as electricity needs on the Reservation. It also assessed the Tribe’s energy resources. Equipped with this information, the project team conducted an energy options analysis that examined different project opportunities and identified key projects that are both feasible to implement and will help the Tribe reach its stated Energy Vision. A key finding of the energy needs assessment is that there are still numerous households that are without grid electric power, and it is likely that most of them will remain disconnected from the grid because of their remoteness. To provide these community members with reliable, affordable, modern energy services their homes will need to be electrified via a robust off-grid energy services program that installs and maintains off-grid energy systems. This is the key need that is explored and addressed in this plan. The approach taken is to establish a new business entity, a Tribal Energy Authority or Utility, that will operate a Tribal Energy Program. The Energy Strategic Plan identifies a number of potential funding sources that could be used to support both the On-grid and Off-grid Energy Programs. This plan also promotes continued efforts to reduce electricity consumption through the implementation of energy efficiency measures in existing facilities and the enforcement of a strong energy-efficient building code for all new construction on the Reservation. Finally, the plan promotes added resilience at critical Tribal facilities on the Reservation by recommending that battery energy storage systems and microgrid controls be coupled with rooftop solar PV systems to create cutting edge microgrid facilities that can provide critical power services to Tribal facilities when the main electric grid is shutdown.

29 ENERGY PLANNING, POLICY, AND ECONOMY↗

DOE OSTI2024

Is Clean Hydrogen Production a Good Fit for Questa? (Final Economic Impact Results) [Slides]

The Village of Questa, New Mexico is aiming to become a regional clean energy hub with robust and diverse employment opportunities for the local community supported by the energy sector and by other businesses inspired or attracted by abundant clean energy, outdoor recreation, and cultural opportunities. A coalition of stakeholders in the Village of Questa, comprising the Village, Kit Carson Electric Cooperative (KCEC), Questa Economic Development Fund, and Chevron, is exploring options to develop hydrogen production facilities as an opportunity to create jobs, provide reliable clean energy, and utilize former mine resources. Questa is home to a molybdenum mine owned by Chevron that closed in 2014. Several residents in Questa and surrounding communities lost their jobs when the mine closed and transitioned from active operations into environmental remediation. Although remediation efforts have been ongoing since 2014 and are expected to continue for at least 16 more years, the number of jobs with Chevron is much smaller now than it was before the closure. Between available workforce, brownfield land, and water rights formerly supporting mine operations but now in a transition period, there are considerable local resources that could be directed toward clean energy generation. Questa's electricity supply is already 100% solar during daylight hours thanks to Kit Carson Electric Cooperative's (KCEC's) strategic decision-making and partnering over the last decade. Now, Questa, KCEC, and Chevron are exploring the potential costs and benefits of siting an electrolytic hydrogen production facility and additional solar photovoltaic (PV) capacity in Questa to further advance the region's clean energy economy. In this report, we estimated the potential economic impacts (i.e., jobs, value added, gross output, tax revenue) of constructing and operating a combined hydrogen (32 MW polymer electrolyte membrane electrolizer + 7.5 MW fuel cell) and solar facility (22.5 MW) in the Village of Questa, as well as the resulting economic spillovers to Taos County and the state of New Mexico. We employ an input-output model that leverages IMPLAN's economic data for the region complemented by construction and operating expenses estimated by NREL and feedback from the local coalition to evaluate the direct, indirect and induced effects of the project construction (transient impacts) and operation (more permanent impacts). Based on the area's average trade profile, feedback from the coalition and current market conditions, these projects are expected to support 487 full-time equivalent jobs during construction, generating $\$24$ million in income for those workers and $\$82$ million in local economic activity in the state. Of those jobs, 106 are expected to be construction sector jobs. These investments are also estimated to add $\$36.5$ million to New Mexico's gross state product (GSP). In the Village of Questa, we estimate 16 jobs will be supported in construction and transportation industries, generating $\$0.9$ million in earnings. In Taos County, the construction phase is expected to support 285 jobs primarily in construction and professional services, while manufacturing jobs dominate the results for the Rest of New Mexico. The Village is also estimated to receive $\$0.9$ million in tax revenue from the construction phase alone. Once in operation, the project continues to impact the state and Questa. Around 20 jobs (full-time equivalent for each year of operation) are supported across New Mexico, with approximately 11 directly employed in Questa by both facilities. The total annual local economic activity supported by ongoing operations is just over $\$1.3$ million/yr, generating $\$1.6$ million/yr in additional income in the state. Annual operations are estimated to add $\$2.1$ million to the state's GSP. The Village is expected to receive around $\$43,000$/yr in tax revenue. Impacts vary significantly depending on which businesses are supplying materials, equipment and services, and where construction workers reside. Choosing local suppliers will most benefit Questa and the New Mexico economy, adding up to 500 jobs during construction and 13 long-term jobs. Local and state governments may consider ways to incentivize local businesses in order to maximize economic benefits.

08 HYDROGEN↗

DOE OSTI2024

Is Clean Hydrogen Production a Good Fit for Questa? Final Economic Impact Results

The Village of Questa, New Mexico is aiming to become a regional clean energy hub with robust and diverse employment opportunities for the local community supported by the energy sector and by other businesses inspired or attracted by abundant clean energy, outdoor recreation, and cultural opportunities. A coalition of stakeholders in the Village of Questa, comprising the Village, Kit Carson Electric Cooperative (KCEC), Questa Economic Development Fund, and Chevron, is exploring options to develop hydrogen production facilities as an opportunity to create jobs, provide reliable clean energy, and utilize former mine resources. Questa is home to a molybdenum mine owned by Chevron that closed in 2014. Several residents in Questa and surrounding communities lost their jobs when the mine closed and transitioned from active operations into environmental remediation. Although remediation efforts have been ongoing since 2014 and are expected to continue for at least 16 more years, the number of jobs with Chevron is much smaller now than it was before the closure. Between available workforce, brownfield land, and water rights formerly supporting mine operations but now in a transition period, there are considerable local resources that could be directed toward clean energy generation. Questa's electricity supply is already 100% solar during daylight hours thanks to Kit Carson Electric Cooperative's (KCEC's) strategic decision-making and partnering over the last decade. Now, Questa, KCEC, and Chevron are exploring the potential costs and benefits of siting an electrolytic hydrogen production facility and additional solar photovoltaic (PV) capacity in Questa to further advance the region's clean energy economy. In this report, we estimated the potential economic impacts (i.e., jobs, value added, gross output, tax revenue) of constructing and operating a combined hydrogen (32 MW polymer electrolyte membrane electrolizer + 7.5 MW fuel cell) and solar facility (22.5 MW) in the Village of Questa, as well as the resulting economic spillovers to Taos County and the state of New Mexico. We employ an input-output model that leverages IMPLAN's economic data for the region complemented by construction and operating expenses estimated by NREL and feedback from the local coalition to evaluate the direct, indirect and induced effects of the project construction (transient impacts) and operation (more permanent impacts). Based on the area's average trade profile, feedback from the coalition and current market conditions, these projects are expected to support 487 full-time equivalent jobs during construction, generating $\$24$ million in income for those workers and $\$82$ million in local economic activity in the state. Of those jobs, 106 are expected to be construction sector jobs. These investments are also estimated to add $\$36.5$ million to New Mexico's gross state product (GSP). In the Village of Questa, we estimate 16 jobs will be supported in construction and transportation industries, generating $\$0.9$ million in earnings. In Taos County, the construction phase is expected to support 285 jobs primarily in construction and professional services, while manufacturing jobs dominate the results for the Rest of New Mexico. The Village is also estimated to receive $\$0.9$ million in tax revenue from the construction phase alone. Once in operation, the project continues to impact the state and Questa. Around 20 jobs (full-time equivalent for each year of operation) are supported across New Mexico, with approximately 11 directly employed in Questa by both facilities. The total annual local economic activity supported by ongoing operations is just over $\$1.3$ million/yr, generating $\$1.6$ million/yr in additional income in the state. Annual operations are estimated to add $\$2.1$ million to the state's GSP. The Village is expected to receive around $\$43,000$/yr in tax revenue. Impacts vary significantly depending on which businesses are supplying materials, equipment and services, and where construction workers reside. Choosing local suppliers will most benefit Questa and the New Mexico economy, adding up to 500 jobs during construction and 13 long-term jobs. Local and state governments may consider ways to incentivize local businesses in order to maximize economic benefits.

08 HYDROGEN↗