Evaluating the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

Abstract

A bifacial silicon heterojunction solar cell demands approximately 210 mg usage of silver paste (9 busbars, 24.5%, bifacial, M6 size wafer). Copper is an excellent alternative to silver: 100x cheaper, similar elecvtrical resistivities, and 1000x more abundant. Successful demonstration of large area selective emitter PERC solar cells using Cu fire-through paste with FF approximately 75% and approximately 19%. Paste chemistry results in oxide-based Cu diffusion barrier, leading to good reliability of the devices: 1000h DHT giving a 3.5% efficiency drop. The additional series resistance still needs to be lowered. Printed and fired cell performance is governed mostly by pFF, especially J02 ; same for DHT degradation. Further improvement in printing and firing optimization for lower series resistance and higher FF.