DOE OSTI2024

Exploring the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

In this work, we present the performance and reliability of a fire-through copper (Cu) paste which has been screen printed on c-Si solar cell with passivated emitter rear contact (PERC). The Cu paste is fired through silicon nitride (SiN) anti-reflection coating at a peak temperature of 630 degrees C . SEM images of the Cu paste show a Cu core with ~200 nm oxide shell around the particles. This conductive oxide layer acts as a diffusion barrier between Cu and Si and prevents the degradation of cell performance during accelerated aging conditions. An efficiency of 19.250% has been achieved with Voc=654mV,FF= 76.68%, Jsc=38.40 m.A/cm 2 for champion PERC cells. Accelerated testing of the PERC mini-modules in damp heat chamber with 85 degrees C and 85% humidity have demonstrated that the devices are operational even after 1,500 hours. Devices with screen printed Ag contacts on the front side have been studied in parallel to the Cu contacts for comparison.

copper↗

DOE OSTI2024

Evaluating the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

A bifacial silicon heterojunction solar cell demands approximately 210 mg usage of silver paste (9 busbars, 24.5%, bifacial, M6 size wafer). Copper is an excellent alternative to silver: 100x cheaper, similar elecvtrical resistivities, and 1000x more abundant. Successful demonstration of large area selective emitter PERC solar cells using Cu fire-through paste with FF approximately 75% and approximately 19%. Paste chemistry results in oxide-based Cu diffusion barrier, leading to good reliability of the devices: 1000h DHT giving a 3.5% efficiency drop. The additional series resistance still needs to be lowered. Printed and fired cell performance is governed mostly by pFF, especially J02 ; same for DHT degradation. Further improvement in printing and firing optimization for lower series resistance and higher FF.

Ag↗

DOE OSTI2024

Exploring the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

For 40 TW of PV required to transition our planet to 100% renewables, the silver (Ag) should disappear from PV production. Advantages of copper (Cu) over silver (Ag) include 1) bulk Cu has a similar conductivity to Ag (1.7 mu O-cm for Cu, 1.6 mu O-cm for Ag) and 2) Cu is approximately 100 times cheaper than Ag, making it an excellent potential replacement. Problems associated with copper (Cu) contacts include 1) easy oxidation and 2) diffusion into the Si cell and recombination activity.

copper paste↗

DOE OSTI2024

Development and Reliability of Screen-Printable Fire-Through Cu Paste for Passivated Contact Solar Cells

We present the development of copper (Cu) paste which has been screen printed on Selective Emitter-Passivated Emitter Rear Contact (SE-PERC) solar cells. This paste can also be applied to Tunnel Oxide Passivated Contact (TOPCON) solar cells due to its fire-through nature. Champion PERC cells have achieved ....efficiency with ...parameters . Accelerated testing to investigate reliability performance of the SE- PERC mini-modules were carried out in damp heat chamber with 85oC and 85% humidity. The devices were found to be operational even after 1,500 hours. Devices with screen printed Ag contacts on the front side have been studied in parallel to the Cu contacts for comparison.

copper paste↗

DOE OSTI2023

Investigating Electric Field and Light Induced Degradation in Perovskite Solar Cells through Nanometer-Scale Potential Imaging

Electric field and light induced degradations in perovskite solar cells were evaluated through nanometer-scale potential imaging across the device by using in-situ Kelvin probe force microscopy (KPFM). We derived the electric field profile from potential profiles at different bias voltages to evaluate the locations and quality of junctions across the device. We found relative changes in electric field peak intensity at the HTL/perovskite and perovskite/ETL interfaces upon stressing devices separately under voltage or light. KPFM results during 12-hour stress/rest cycling under electrical bias show both reversible and irreversible changes in the device's interfacial fields. We also observed change in the electric field profile between control and degraded devices after 100 hours of stress/rest cycling under light. Our results demonstrate how nanometer-scale potential imaging can be used to understand the impacts of external electric fields and light soaking on both irreversible degradation and reversible metastability in perovskite solar cells.

Kelvin probe force microscopy↗

DOE OSTI2023

Microstructure-Property Relationships in Epitaxial Cu(In, Ga)Se2 Solar-Cell Absorbers

Epitaxially grown Cu(In,Ga)Se 2 (CIGS) absorber layers were analyzed by various techniques in scanning electron microscopy in order to reveal microstructure-property relationships in these thin films. Owing to their epitaxial nature, these CIGS absorber layers do not contain any grain boundaries, but only anti-phase domains (APDs) and dislocations. By combining electron channeling-contrast imaging, electron backscatter diffraction, and cathodoluminescence (CL), in some cases on identical specimen positions of polished cross-sections of CIGS/Mo/glass stacks, it was possible to correlate the presence and orientations of APDs and dislocations with the lateral distributions of the CL intensity and emission-peak energy. We studied CIGS layers with three different [Ga]/([Ga]+[In]) ratios as well as with and without NaF/KF treatments. Considerable differences between the CIGS layer properties in the microstructure-property relationships were found, depending on the growth parameters. Dislocations in the epitaxial CIGS layers do not tend to exhibit strong CL intensity decreases, which contrasts with the situation in numerous other semiconductor materials.

anti-phase domains↗

DOE OSTI2023

Understanding Hydrogen Passivation Mechanism in Poly-Si Passivating Contacts: Insights from Effusion Studies

Silicon PV is the dominant PV technology, and captures >95% world market share, supporting -100 GW/year. Diffused and passivated pn junctions along with other rear side passivation technologies are the mainstream technologies and will continue to remain so in the coming decades. Passivated contacts, using tunnel oxide passivation stacks at the rear side, will gain market share from about 10% in 2022 up to 58% within the next 10 years. Most mature approaches use passivating layers of hydrogenated Al2O3 and SiNx. LPCVD SiNx provides less hydrogen for passivation compared to PECVD SiNx but can retain the hydrogen up to higher temperatures which is beneficial for firing. Although SiNx provides large amount of hydrogen, this doesn't necessarily translate to good passivation. AlOx:H contributes to retaining H at higher temperatures. Water molecules are also detected during H-effusion and may play a role in passivation of the oxide/wafer interface.

effusion study↗

DOE OSTI2023

High-Performance Passivating Contacts for Si PV Based on Engineered, Doped Nanopinholes through Dielectric Layers

We present a novel, industrially relevant method to fabricate high-performance poly-Si passivating contacts for Si PV. Passivating contacts based on SiOx/poly-Si layer stacks have been implemented in record-efficiency homojunction Si solar cells. In this technology, the carrier transport through a surface-passivating SiOx is enabled either by quantum-tunneling or nanopinholes. The doped poly-Si layer provides charge-carrier selectivity. Previously, the ISFH research group demonstrated a record 26.1% efficient Si homojunction cell, where transport pinholes in ~2 nm SiOx were produced by thermal breakdown at > 1000 degrees C, which is hard to control and is surface morphology-dependent. At room temperature, our new process uses electroless plating of Ag nanoparticles, followed by metal-assisted chemical etching. Nanogalvanic corrosion yields < 20 nm-wide nanopinholes in an insulating > 2 nm SiOx layer. The nanopinholes are filled by a heavily doped a-Si:H overlayer. We drive in the dopants into the Si wafer with subsequent high-temperature annealing. Preferential incorporation of dopants at pinhole locations results in nanoscale p+/n or n+/n junctions near the wafer interface. Each heavily-doped nanoscale pinhole junction collects and transports photogenerated carriers to the cell metal contacts. The density of the engineered nanopinholes can be tuned over a wide range which is critical for optimization of device performance. The same nanogalvanic corrosion principles can be applied to produce doped transport pinholes in well-passivating thick dielectric SiOx/SiNy stacks. Importantly, our process does not rely on thermal breakdown of the dielectric layers and can be applied to textured wafers resulting in Si solar cells with > 20% conversion efficiency.

dielectric layer↗

DOE OSTI2023

Mechanism of Hydrogen Passivation in Passivated Contact Si Solar Cells

In this abstract, we discuss the mechanism of hydrogen passivation on symmetrical n-Si/ultra-thin SiO2/polySi structures. The hydrogen was introduced from different hydrogen-containing dielectric layers (AlOx:H and SiNx:H and their stacks), as well as by forming gas anneal (FGA). The effusion of hydrogen both from the dielectric layers and in the underlying poly-Si was explored using a quadrupole mass spectrometer (QMS) and FTIR spectroscopy. We show that the strength of hydrogen bonds depend on the deposition technique as well as hydrogenation mechanism. While a PECVD SiNx:H loses hydrogen at a peak temperature of ~450 degrees C, LPCVD SiNx:H, although having less hydrogen compared to PECVD, effuses at a peak temperature of ~850 degrees C. This becomes important to maintain passivation of passivated contacts after firing of metal contacts at high temperatures. On the other hand, it has been observed that SiNx:H provides larger amount of hydrogen to poly-Si after FGA compared to FGA treated AlOx:H, which acts as a capping layer and helps in retaining the hydrogen up to higher temperatures.

hydrogen bonding configuration↗

DOE OSTI2023

Metal-Complex Inks for Lower Cost and Improved Passivation for Silicon Photovoltaic Metallization

This contribution introduces the silicon PV community to screen-printable metal-complex inks that potentially will reduce Ag usage in Si PV metallization to one-quarter and costs to one-third that of traditional particle-based pastes while also improving passivation. Metal-complex inks are formulated using a Tollen's reaction to produce inks with a high percentage of diamminesilver (I) cations (22 wt %) in a solution of acetate and formate anions. When printed and dried labile ammonia ligands evaporate, leaving behind silver cations which, when reduced by formate anions and acetic acid, plate out silver and silver acetate. When annealed to just 300 degrees C a dense metallic silver film forms with excellent conductivity, and adhesion to silicon. When compared to traditional particle-based screen-printing pastes, the metal-complex inks are much denser, have higher conductivity, use less Ag, and are a fraction of the cost. Importantly, the inks anneal from 90 - 450 degrees C allowing for better passivation schemes than fired SiNx. This contribution highlights first experiments on the improved passivation of metallized poly-Si/SiO2 passivated contacts using metal-complex, Ag inks compared with particle-based, fired pastes.

metal-complex ink↗

DOE OSTI2023

Structure and Electronic Properties of Mesopores in Si PV Devices with PLEO Contacts

All current state-of-the-art silicon photovoltaic (PV) devices employ some flavor of passivating contact structure to minimize detrimental recombination while providing good conductivity. These properties are most often provided by a dielectric layer (SiNx, Al2O3, or SiOx) that is in contact with the crystalline silicon (c-Si) substrate. The effectiveness of these layers is heavily dependent on the nanoscale structure of both the dielectric layers and the crystalline silicon interface. As an example, the tunneling probability for charge carriers across thin SiOx layers, a process that is critical to maintain high conductivity, is extremely sensitive to the SiOx thickness. SiOx with a thickness below 2 nm readily allows charge carrier tunneling, whereas it is impeded for greater thicknesses. In the latter case it has been shown that modifications to the thermal processing schedule can induce disruptions, or pinholes, in thick SiOx layers that allow transport of charge carriers while maintaining excellent passivation. However, this requires higher temperatures processes that may inhibit widespread adoption by industry. Recently, another option has been presented that may circumvent the necessity for high temperature processing, namely metal assisted chemical etching (MACE). MACE relies on deposition of Ag nanoparticles onto the SiOx layers with subsequent electroless etching to form mesopores in the SiOx layers that are analogous to the pinholes created with high temperature processing. The size and density can be controlled based on the Ag nanoparticle deposition conditions. The resulting contact structure is known as polysilicon on locally etched oxide (PLEO) contacts. The nanoscale structure of the mesopores in PLEO contacts define the device level observables such as recombination current (Jo) and junction resistance. In this work we present atomic resolution transmission electron microscopy (TEM) analysis of mesopores in PLEO contacts formed with a different processing conditions to connect provide insight into how the nanoscale structure of the SiOx layer influences PV device properties. Additionally, we have previously used electron beam induced current (EBIC) to probe local transport properties in Si PV devices with a SiOx layer containing pinholes due to high temperature processing. Using EBIC we were able to directly show the enhance charge carrier transport through the pinholes. Here we also employ EBIC to study non-uniformities in charge carrier recombination and transport associated with mesopores in PLEO contacts and compare these results with our previous work on devices with pinholes in the SiOx formed through high temperature processes. The products of this work provide critical information that is required to both further optimize performance of Si PV devices with PLEO contact and to drive future adoption of this technology by industry.

ENGINEERING,SOLAR ENERGY↗

DOE OSTI2022

Characterization of Engineered Pinholes in Dielectric Stacks of High-Performance Poly-Silicon Passivating Contacts

Passivating contact structures are expected to be implemented in > 50 % of industrially manufactured silicon photovoltaics produced over the next decade. One type of passivating contact utilizes a c-Si/dielectric/doped poly-Si layer stack. In cases where the dielectric layer/s are thick enough to impede tunneling of charge carriers, it was shown that disruptions (pinholes) in the dielectric are required to facilitate transport.[1] Pinholes in SiOx layers have typically been formed via high temperature annealing that allows localized breakup of this layer. This approach has drawbacks; 1) high temperature annealing increases cost and 2) pinhole formation is sensitive to both the SiOx thickness and wafer surface morphology making control of density and dimensions difficult. Recently, an alternative method of pinhole formation relying on metal assisted chemical etching (MACE) was shown to allow control over pinhole areal densities.[2] Such control is critical as both the density and dimensions of the pinholes determine saturation current density and contact resistivity. The contacts formed with the MACE process are known as polysilicon on locally etched oxide or PLEO and also result in low saturation current densities and low contact resistivity due to SiOx passivation and engineered pinhole enabled charge carrier transport, respectively. Photovoltaic devices with efficiencies greater than 20 % have recently been produced with these contacts, demonstrating the viability of contacts with engineered pinholes. Experimentally, preferential local collection of excess charge carriers has been observed and definitively connected to thermally induced pinholes in thick SiOx layers within c-Si/SiOx/poly-Si contact structures.[3] Recent work has shown that enhanced local collection of excess carriers can result from enhanced diffusion of dopants through pinholes in SiOx layers.[4] This study was restricted to simulation and characterization of poly-Si with the same dopant type as the c-Si substrates. In this work we focus our analysis on boron doped poly-Si with different stacks of dielectric layers (PLEO and PLENO where the N refers to a SiNy layer on top of the SiOx) on n-type crystalline silicon. This provides insight into how engineered pinholes affect charge collection across the p-n junction. Like previous observations of locally enhanced carrier transport through thermally induced pinholes, the EBIC images in Figure 1 shows that engineered pinholes in PLENO (1a) and PLEO (1b) also exhibit locally enhanced carrier transport at pinhole locations (bright spots in the images). We will also present detailed correlative nanoscale structural and chemical analysis using TEM imaging and EELS analysis with sample preparation guided by EBIC imaging. This allows us to connect the density and dimensions of engineered pinholes with charge carrier transport and measured photovoltaic device parameters. Our findings will accelerate the adoption of PLEO and PLENO contacts in industrially manufactured photovoltaic devices.

EBIC↗

DOE OSTI2022

Nafion Passivation of c-Si Surface and Edge for Electron Paramagnetic Resonance

Effective surface passivation of crystalline silicon (c-Si) surface by reducing the carrier recombination rate has led to modern c-Si solar cells with efficiencies > 25% in both laboratory and industrial settings. Typical mainstream surface passivation techniques include high-temperature silicon oxide (SiOx), amorphous silicon (a-Si:H), hydrogen-rich silicon nitride (SiNx), and aluminum oxide (Al2O3) [1]. They have demonstrated excellent surface recombination velocity of < 1 cm/s owing to both chemical passivation (via the hydrogen saturation of Si dangling bonds at the c-Si surface), and field-effect passivation (via the band bending from the fixed charge of the dielectric layers). Recently, several groups have studied solution-based organic materials for c-Si passivation, including bis(trifluoromethane)sulfonimide (TFSI), polystyrenesulfonate, and Nafion [2, 3] via spin or dip coating. All films were processed at ambient room temperature, and a high lifetime of 12 ms, as well as a low saturation current density (J0) of 16 fA/cm2, have been demonstrated using Nafion passivation [2]. However, despite the air instability, Nafion has several advantages when introduced to PV applications: (a) Wafer quality can be measured at high throughput after several process stages. (b) It is compatible with PL mapping, compared to HF liquid passivation which cannot be performed in room ambient. (c) Nafion process is fast and poses fewer constraints on process complexity, and cleanness, compared to Al2O3 and a-Si:H passivation. (d) Nafion is the ideal room temperature passivation, which can be applied onto a small fragment of a degraded module to investigate microscopic mechanisms when studying degradation mechanisms. Edge passivation is needed for advanced characterization tests such as Electron Paramagnetic Resonance (EPR), Electrically Detected Magnetic Resonance (EDMR), Deep Level Transient Spectroscopy (DLTS), local cell current-voltage (J-V), and Suns-Voc. In such cases, the laser-damaged minicell edges will obscure the true degradation mechanisms, and Nafion can effectively passivate them without causing further degradation through elevated-temperature processes. In this contribution, we show the passivation results of Nafion on bare nCz and compare it with a Al2O3 witness. We highlight the importance of edge pre-treatment before Nafion to achieve good passivation. We show that Nafion can reach decent passivation without undergoing high-temperature processes. We also explore the temperature dependency of Nafion through photoluminescence (PL) study and demonstrate the application of Nafion under cryogenic temperature (~6 K) through EPR. Our results reveal that Nafion can reduce surface and edge Si dangling bonds at low temperatures. Thus, it can be used as an effective room temperature passivation technique for advanced characterization methods.

c-Si↗

DOE OSTI2022

Room Temperature, Dip Coating Organic Passivation for c-Si Surfaces

Surface passivation of crystalline Si (c-Si) to reduce recombination rate is crucial to obtain high-efficiency c-Si solar cells. A fast passivation technique that can be performed at room temperature is needed when studying the degradation behaviors using various characterization methods to not destroy the degraded states. In this contribution, we explore Nafion via dip coating on n-type Cz wafers. We show that both the Nafion concentration and the conditions of surface and edge affect the passivation quality, and we achieve excellent passivation quality of iVoc of 716 mV, with a saturation current density (J0) of 7 fA/cm2. Additionally, electron paramagnetic resonance (EPR) shows Nafion can be used under cryogenic temperature and reveals the reduction of Si dangling bond after Nafion treatment.

dielectric solar cell↗

DOE OSTI2022

Controlling Pinhole Radius and Areal Density in a-Si/SiOx Using Metal-Assisted Chemical Etching

Polysilicon on silicon oxide (poly-Si/SiOx) passivating contacts with predominant charge-carrier transport via pinholes are currently prepared via a>1000 degrees C thermal step to induce oxide break-up. Herein, we develop the precursor of a pinhole-enabled poly-Si/SiOx contact utilizing room temperature metal-assisted chemical etching (MACE) to form pinholes in the SiOx. The pinholes were created via electroless Ag nanoparticle (Ag NP) deposition followed by the MACE of intrinsic amorphous hydrogenated silicon (a-Si:H) on SiOx, creating isolated mesopores through the film stack. By varying the MACE etching solution (HF:H2O2) concentration, we were able to vary the pinhole areal density over four orders of magnitude (104-107 cm-2). We observed the Ostwald ripening of the Ag NP to enable control over the pinhole radii. Our work demonstrates proof-of-concept for a-Si:H/SiOx with mesopores across the film stack, which may serve as precursor for the development of poly-Si/SiOx passivating contacts of both polarities.

MATERIALS SCIENCE,SOLAR ENERGY↗

DOE OSTI2022

Non-Equilibrium Doping of Poly-Si:Ga/SiOx Passivating Contacts Solar Cells

In this contribution, we show that Ga-hyperdoped poly-Si/SiOx contacts are realized by pulsed laser annealing and post-hydrogenation. The motivation behind this work is to improve the inferior performance of boron-doped poly- Si/SiOx contacts when compared to the phosphorus-doped contacts. Here we used Ga as a novel p-type dopant to replace B, as B is known to accumulate at the interface between the oxide and the crystalline silicon and cause recombination. Due to a high diffusivity of Ga in oxide and a much higher segregation coefficient (Si:SiOx), Ga is shown to be immune to the oxide pileup phenomenon. However, Ga has a low solid solubility limit in Si (5x10^19 cm-3), which is not enough to form a low resistivity contact. To overcome this problem, we explored pulsed laser annealing via excimer laser by varying the laser energy densities and pulses. The passivation and electrical properties are studied systematically using photoluminescence (PL), secondary ion mass spectrometry (SIMS), and Van der Pauw-Hall measurements. We show an active Ga doping concentration above 1x10^20 cm^-3, which is above the solid solubility limit of Ga in Si. Good passivation quality is demonstrated with the highest implied Voc (iVoc) of 721 mV on single side polished samples. Furthermore, a low diode contact resistivity of ~22 m..omega.. cm^2 is obtained using Ti/Ag contacts, with minimal metal-to-semiconductor contact resistivity of 0.9 m..omega.. cm^2.

non-equilibrium doping↗

DOE OSTI2022

LeTID-Affected Cells from a Utility-Scale Photovoltaic System Characterized by Deep Level Transient Spectroscopy

Photovoltaic modules from a utility-scale field experienced power loss by light- and elevated temperature-induced degradation (LeTID). Samples of one of the affected monocrystalline silicon cells were cored and extracted from the module packaging and encapsulation. One of the cell fragments was processed using a regeneration cycle of applying short-circuit-rated current in forward bias at 85 degrees C for 2 weeks, while the other fragment was kept in its outdoor-degraded LeTID state. Both samples were scribed to form 2-mm diameter isolated areas using a femtosecond-pulse-width laser micromachining system. Both isolated areas contained front grid line segments which were wire bonded to larger contact pads, and the samples were probed in a cryostat linked to a deep-level transient spectroscopy (DLTS) system. Using DLTS, a majority-carrier, hole-trap defect was detected on each sample with an activation energy of 0.42 eV. The LeTID-degraded sample, however, had a larger signal corresponding to a trap density of 1.1x10^13 cm-3, which was about five times larger than the 2.1x10^12 cm-3 trap density of the regenerated sample.

charge carrier lifetime↗

DOE OSTI2022

Light- and Elevated-Temperature-Induced Degradation-Affected Silicon Cells From a Utility-Scale Photovoltaic System Characterized by Deep-Level Transient Spectroscopy

Photovoltaic modules from a utility-scale field experienced power loss by light- and elevated-temperature-induced degradation (LeTID). Samples from the affected monocrystalline silicon cells are cored and extracted from the module packaging and then laser-scribed to form 2-mm diameter isolated areas. Using deep-level transient spectroscopy, a majority-carrier, hole-trap defect with an activation energy of 0.42 eV is detected on degraded and regenerated samples. The LeTID-degraded sample, however, has a larger signal corresponding to a trap density of 1.1 x 10 13 cm -3 , which is about five times larger than the 2.1 x 10 12 cm -3 trap density of the regenerated sample. An increase in filling pulse time from 50 u s to 20 ms shows a slight decrease in activation energy from 0.42 to 0.36 eV suggesting that the defect level may consist of a band of energy states where shallower states continue to fill with long filling times. The capture rate of the defect is directly measured using an increasing series of filling pulsewidths in 15 to 125 ns range. This leads to a measured capture cross section of 5.1 x 10 -17 cm 2 , and using an approximate defect density of 10 13 cm -3 , the majority-carrier-hole lifetime related to this defect is approximately 100 u s when in the LeTID-degraded state.

charge carrier lifetime↗