Stradins, Paul

Publications and source records attributed to Stradins, Paul.

8 records

DOE OSTI2024

Passivation Mechanisms in Locally Etched P-Type Poly-Si on Silicon Nitride/Silicon Oxide Stack

Tunneling oxide passivated contacts are quickly becoming the industry standard for high-efficiency c-Si based photovoltaic cells. Further development of these structures is essential to enable higher efficiencies and better reliability of cells. By utilizing poly-Si/SixNy/SiOx stacks, very high efficiencies have been demonstrated on small area cells. In this work we investigate the cause of the excellent passivation seen by these structures and show that the primary reason of the excellent passivation seen is the blocking B diffusion to the SiOx/c -Si interface. We also show that the interface between the silicon nitride and polysilicon affects B diffusion through to the c-Si interface. Finally, we demonstrate that the composition of the nitride used is of great importance, and that an incorrect nitride composition leads to B diffusion, and is directly correlated to poor passivation performance.

industries↗

DOE OSTI2024

High Temperature Copper Metallization: Demand, Hurdles and Reliability

As newer cells structures come online, the pressing need to replace silver in the metallization pastes has renewed interest in alternative technologies employing base metals. Copper typically leads the charge with its abundance and lower cost but has faced numerous obstacles from relatively higher oxidation and diffusion rates which can damage the lifetime of the devices. In this study, a low-cost alternative to silver metallization pastes has been shown on PERC cells. The screen printable copper paste can be fired in air at temperatures >500 degrees C, and the impact of processing conditions and equipment on the performance and reliability of 274 cm2 cells have been evaluated. Through damp heat testing of micro-modules using 16 cm2 cells, routes that can lead to both the failure and success of durable contacts have been demonstrated.

copper↗

DOE OSTI2024

Exploring the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

In this work, we present the performance and reliability of a fire-through copper (Cu) paste which has been screen printed on c-Si solar cell with passivated emitter rear contact (PERC). The Cu paste is fired through silicon nitride (SiN) anti-reflection coating at a peak temperature of 630 degrees C . SEM images of the Cu paste show a Cu core with ~200 nm oxide shell around the particles. This conductive oxide layer acts as a diffusion barrier between Cu and Si and prevents the degradation of cell performance during accelerated aging conditions. An efficiency of 19.250% has been achieved with Voc=654mV,FF= 76.68%, Jsc=38.40 m.A/cm 2 for champion PERC cells. Accelerated testing of the PERC mini-modules in damp heat chamber with 85 degrees C and 85% humidity have demonstrated that the devices are operational even after 1,500 hours. Devices with screen printed Ag contacts on the front side have been studied in parallel to the Cu contacts for comparison.

copper↗

DOE OSTI2024

Evaluating the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

A bifacial silicon heterojunction solar cell demands approximately 210 mg usage of silver paste (9 busbars, 24.5%, bifacial, M6 size wafer). Copper is an excellent alternative to silver: 100x cheaper, similar elecvtrical resistivities, and 1000x more abundant. Successful demonstration of large area selective emitter PERC solar cells using Cu fire-through paste with FF approximately 75% and approximately 19%. Paste chemistry results in oxide-based Cu diffusion barrier, leading to good reliability of the devices: 1000h DHT giving a 3.5% efficiency drop. The additional series resistance still needs to be lowered. Printed and fired cell performance is governed mostly by pFF, especially J02 ; same for DHT degradation. Further improvement in printing and firing optimization for lower series resistance and higher FF.

Ag↗

DOE OSTI2024

Photovoltaics Based on Direct and Indirect Gap Semiconductors

Direct and thin, or indirect and thick absorbers can yield cells close to 30% but there are practical limits due to defects, cost, reliability. Tandems and new ideas are needed to minimize thermalization and entropy losses and to enable high absorptance in thin Si layers. Direct-gap absorbers have ~1000x higher recombination losses than Si, but being 100x thinner, the limiting 1-sun efficiencies are similar due to 100x higher G.

direct-gap↗

DOE OSTI2024

Exploring the Performance and Reliability of Screen-Printable Fire-Through Copper Paste on PERC Solar Cells

For 40 TW of PV required to transition our planet to 100% renewables, the silver (Ag) should disappear from PV production. Advantages of copper (Cu) over silver (Ag) include 1) bulk Cu has a similar conductivity to Ag (1.7 mu O-cm for Cu, 1.6 mu O-cm for Ag) and 2) Cu is approximately 100 times cheaper than Ag, making it an excellent potential replacement. Problems associated with copper (Cu) contacts include 1) easy oxidation and 2) diffusion into the Si cell and recombination activity.

copper paste↗

DOE OSTI2024

Screen-Printed Complex Ag Inks for Si HJT Metallization

Metallization using reactive metal inks has recently attracted significant research interest due to its advantages in cost of materials and manufacturing, while still achieving performance comparable to traditional fire-through particle pastes. Here, we present for the first time the use of reactive silver (Ag) inks via industrial screen-printing and inkjet printing methods for the metallization of different Si surfaces used in tunneling oxide passivating contacts (TOPCon) and Silicon heterojunction (SHJ) solar cells. Printed Ag lines exhibit a conductivity of ~5 Mu O·cm, which is approximately 3 times that of bulk Ag (1.59 µO·cm). The printed metal has a thickness of ~0.5-1.5 Mu m, an order of magnitude smaller than the current fire-through metal finger thickness (~15 Mu m). Contact resistivity measurements of the screen-printed and inkjet-printed samples on a transparent conducting oxide (TCO) surface show a very low value of ~0.2-12 mO·cm 2. Photoluminescence images of the metallized samples demonstrate minimal surface passivation degradation compared to the non-metallized areas (?iVoc <3.5 mV). Scanning electron microscopy images (SEM) reveal the structure of the printed metals on the Si surfaces as porous but much denser than fire-through Ag by nanoparticle paste. In the final presentation, we will showcase our results of printing these reactive Ag inks on high-efficiency heterojunction and TOPCon solar cells with full-area M6 wafers. Additionally, the adhesion of these reactive Ag inks on different Si surfaces according to ASTM D3359-17, as well as the performance of solar cells after standard IEC 61215 freeze/thaw and damp heat tests, will be presented. These new metal inks show promising potential as an alternative to the currently dominant particle-based pastes, offering lower Ag consumption and lower processing temperatures without compromising performance.

heterojunction solar cells↗

DOE OSTI2024

Development and Reliability of Screen-Printable Fire-Through Cu Paste for Passivated Contact Solar Cells

We present the development of copper (Cu) paste which has been screen printed on Selective Emitter-Passivated Emitter Rear Contact (SE-PERC) solar cells. This paste can also be applied to Tunnel Oxide Passivated Contact (TOPCON) solar cells due to its fire-through nature. Champion PERC cells have achieved ....efficiency with ...parameters . Accelerated testing to investigate reliability performance of the SE- PERC mini-modules were carried out in damp heat chamber with 85oC and 85% humidity. The devices were found to be operational even after 1,500 hours. Devices with screen printed Ag contacts on the front side have been studied in parallel to the Cu contacts for comparison.

copper paste↗