DOE OSTI2025

Constructing Highly Durable Fuel Cell Catalysts Through Integrating Graphitic Shell‐Protected Composite Carbon Support with Gaseous Co Deposition‐Driven PtCo Intermetallics

Metal dissolution, nanoparticle agglomeration, and carbon support corrosion cause significant performance degradation of current PtCo catalysts under acidic and oxidative oxygen reduction reaction. Here, in this study, an integrated strategy is presented to design high-performance Pt 3 Co intermetallic catalysts by regulating gaseous Co deposition-driven diffusion into Pt nanoparticles supported on a composite carbon. The composite carbon is derived from ZIF-8/polyaniline, consisting of a high-surface-area (HSC) core and a protective graphitic shell (GS), which is employed to design 40 wt.% Pt/HSC@GS catalyst. The corresponding membrane electrode assemblies (MEAs) can maintain 1.09 A cm −2 at 0.7 V (20. 7% loss) after 10 000 cycles (1.0–1.5 V for carbon stability) and 1.15 A cm −2 (16.1% loss) after 150 000 cycles (0.60–0.95 V for catalyst stability). A ordered Pt 3 Co intermetallic is synthesized via a gaseous Co-deposition process, which yields a homogeneous Co-rich layer onto the Pt nanoparticles on the composite support, thereby facilitating Co diffusion into Pt crystal during subsequent ordering annealing to form the ordered intermetallic structure. This gaseous deposition leads to a thin carbon layer on PtCo nanoparticles, inhibiting particle growth during the annealing and mitigating Co dissolution under dynamic electrochemical conditions. The PtCo catalyst achieves impressive MEA performance and long-term durability (1.45 A cm −2 at 0.7 V after 120 000 cycles) under heavy-duty conditions.

30 DIRECT ENERGY CONVERSION↗

DOE OSTI2022

Preface for the special collection commemorating the career of Pat Thiel

This Special Collection in the Journal of Vacuum Science and Technology A (JVST A) has been compiled to commemorate the career of Professor Patricia (Pat) Thiel as a scientific leader in the international surface science community. Pat passed away in September 2020 due to breast cancer. This Collection includes 26 articles from colleagues, collaborators, and former Thiel group members. The topics overlap Pat’s scientific interests and advances in areas that include chemisorption, reconstruction, and complex formation on metal surfaces; submonolayer nucleation and growth and kinetic roughening of epitaxial thin films; coarsening of surface nanostructures; intercalation; surface phenomena for intermetallics including quasicrystals; and atomic-scale friction. We wish to thank the authors for their contributions towards producing this impressive Special Collection.

99 GENERAL AND MISCELLANEOUS↗

DOE OSTI2021

Disorder trapping and formation of antiphase nanodomains in Ni 3 Sn: in situ observation and high resolution characterization

Rapid solidification of the intermetallic Ni 3 Sn compound from an undercooled liquid was investigated using time-resolved synchrotron X-ray diffraction. Primary growth of an ordered and a disordered cubic solid was observed in situ at a low and a high undercooling, respectively. The disordered cubic solid was reordered after rapid solidification and experienced a solid-state transformation in cooling. A HRTEM study revealed high density of crystal defects and nanodomains in the transformed matrix. A HAADFSTEM study determined that the nanodomains are antiphase domains with chemical disorder. These observations indicated a possibility of online control of mechanical properties in additively manufactured intermetallics.

36 MATERIALS SCIENCE↗

DOE OSTI2024

La 4 Co 4 X ( X = Pb , Bi , Sb ) : A demonstration of antagonistic pairs as a route to quasi-low-dimensional ternary compounds

We outline how pairs of strongly immiscible elements, referred to here as antagonistic pairs, can be used to synthesize ternary compounds with low or quasi-reduced-dimensional motifs intrinsically built into their crystal structures. By identifying third elements that are mutually compatible with a given antagonistic pair, ternary compounds can be formed in which the third element segregates the immiscible atoms into spatially separated substructures. Quasi-low-dimensional structural units, such as sheets, chains, or clusters are a natural consequence of the immiscible atoms seeking to avoid close contact in the solid state. Further, as proof of principle, we present the discovery, crystal growth, and basic physical properties of La 4 ⁢Co 4 ⁢$\mathrm{X}$ (X = Pb, Bi, Sb), a family of intermetallic compounds based on the antagonistic pairs Co-Pb and Co-Bi. La 4 ⁢Co 4 ⁢$\mathrm{X}$ adopts an orthorhombic crystal structure (space group Pbam) containing quasi-two-dimensional Co slabs and La-X polyhedra that stack in an alternating manner along the α axis. Consistent with our proposal, the La atoms separate the Co and X substructures, ensuring there are no direct contacts between the members of the immiscible (antagonistic) pair. Within the Co slabs, the atoms occupy the vertices of corner sharing tetrahedra and triangles, and this bonding motif produces narrow electronic bands near the Fermi level that favor magnetism. The Co is moment bearing in each La 4 ⁢Co 4 $\mathrm{X}$ compound studied, and we show that whereas La 4 ⁢Co 4 ⁢Pb behaves as a three-dimensional antiferromagnet with T N =220K, La 4 ⁢Co 4 ⁢Bi and La 4⁢ Co 4 ⁢Sb have behavior consistent with low-dimensional magnetic coupling and ordering, with T N =153K and 143 K, respectively. In addition to the Pb-, Bi-, and Sb-based La 4 ⁢Co 4 ⁢$\mathrm{X}$ compounds, we also were likely able to produce an analogous La 4 ⁢Co 4 ⁢Sn in polycrystalline form, although we were unable to isolate single crystals. We anticipate that identifying and using mutually compatible third elements together with an antagonistic pair represents a generalizable design principle for discovering new materials and new structure types containing low-dimensional substructures.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Template Assisted Lithium Superoxide Growth for Lithium-Oxygen Batteries

Developing batteries with energy densities comparable to internal combustion technology is essential for a worldwide transition to electrified transportation. Li-O2 batteries are seen as the ‘holy grail’ of battery technologies since they have the highest theoretical energy density of all battery technologies. Current lithium-oxygen (Li-O2) batteries suffer from large charge overpotentials related to electronic resistivity of the insulating lithium peroxide (Li2O2) discharge product. One potential solution is the formation and stabilization of a lithium superoxide (LiO2) discharge intermediate that exhibits good electronic conductivity. However, LiO2 is reported to be unstable at ambient temperature despite its favorable formation energy at -1.0 eV/atom. In this paper, based on our recent work on the development of cathode materials for aprotic lithium oxygen batteries including two intermetallic compounds, LiIr3 and LiIr, that are found to form good template interfaces with LiO2, a simple goodness of fit R factor to gauge how well a template surface structure can support LiO2 growth is developed. The R factor is a quantitative measurement to calculate the geometric difference in the unit cells of specific Miller Index 2D planes of the template surface and LiO2. Using this as a guide, the R factors for LiIr3, LiIr, and La2NiO4+, are found to be good. This guide is attested by simple extension to other noble metal intermetallics with electrochemical cycling data including LiRh3, LiRh, and Li2Pd. Finally, the template concept is extended to main group elements and the R factors for LiO2 (111) and Li2Ca suggest that Li2Ca is a possible candidate for the template assisted LiO2 growth strategy.

Intermetallics↗

DOE OSTI2022

Interdiffusion and Formation of Intermetallic Compounds in High-Temperature Power Electronics Substrate Joints Fabricated by Transient Liquid Phase Bonding

Power electronics packages typically comprise a dielectric substrate bonded to a metal layer and attached to heat sinks using a low-thermal-conductivity solder. These multiple layers increase the effective thermal resistance of the package and are responsible for package failures under cyclic thermal loads. Bonding the aluminum nitride dielectric layer (AlN) directly to a low coefficient of thermal expansion (CTE) aluminum silicon carbide (AlSiC) cold plate using copper-aluminum (Cu-Al) transient liquid phase (TLP) bonding has been shown to improve the mechanical reliability of the power electronic packages while making the package more compact by bringing the cooling solutions closer to the devices. This study aims to characterize the Cu-Al bonds formed during the TLP bonding of AlSiC with three different power electronics substrates: pure aluminum nitride (AlN), aluminum (DBA), and copper (DBC). The material compositions and microstructures of the bonds were analyzed using scanning electron microscopy (SEM), x-ray spectroscopy (EDS), confocal scanning acoustic microscopy (C-SAM), and x-ray diffraction (XRD). ..alpha..-Al solid compound was identified as the dominant phase in AlN-AlSiC and Al-AlSiC, with a notable presence of SiC particles. In contrast, three intermetallic phases - ..theta..-CuAl2, ..eta..-CuAl, and ..gamma..'- Cu9Al4 - were observed in the Cu-AlSiC bond. A computational solid-state diffusion model was developed to predict the intermetallic compounds (IMCs) formed during Cu-Al TLP bonding in each system, which supported the observation that an initial Cu volume fraction of 20 % in the material layers produced a final bond composition of >95 % Al with minimal IMC growth. However, increased Cu concentrations produced higher concentration gradients, leading to increased growth of IMCs, Kirkendall voids, and interstitial cracks.

DIRECT ENERGY CONVERSION↗

DOE OSTI2022

Competition of magnetocrystalline anisotropy of uranium layers and zigzag chains in UNi 0.34 Ge 2 single crystals

Structural and thermodynamic properties of single-crystalline UNi 1-x Ge 2 with x = 0.66 have been investigated by measuring magnetization, specific heat, and thermal expansion over a wide range of temperatures and magnetic fields. The measurements revealed the emergence of a long-range antiferromagnetic ordering of uranium magnetic moments below the Néel temperature T N = 45.5 (1) K and the existence of two easy axes in the studied compound, namely b and c, which correspond to the planes of the uranium zig-zag chains. A magnetic field applied along these two crystallographic directions induces in the system a first-order metamagnetic phase transition (from antiferromagnetic to field-polarized paramagnetism), and the width of the magnetic hysteresis associated with that transition reaches as much as 40 kOe at the lowest temperatures. A magnetic phase diagram developed from the experimental data showed that the metastable region associated with that magnetic hysteresis forms a funnel that narrows toward the N´eel point in a zero magnetic field. The four-layer Ising model has successfully predicted the colinear antiferromagnetic structure in UNi 0.34 Ge 2 (known from earlier reports), its magnetic phase diagram, and temperature and field variations of its magnetization. Moreover, it suggests that the first-order phase transition extends down to zero magnetic field, although it is barely detectable in the experiments performed in low magnetic fields. According to this model, the second-order phase transition occurs in the compound only in zero field.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2024

Towards engineering the growth morphology of anisotropic bicrystals

Eutectic alloys, such as Pb-free Bi-Sn-Ag or Sn-Ag-Cu, are essential for their low melting points in solder joints but suffer from brittle intermetallic phases, reducing reliability. Traditional solder design relies on equilibrium phase diagrams, often neglecting the kinetic influence of crystalline anisotropy during solidification. This study hypothesizes that the energetics at the solid-solid-liquid trijunction dictate crystalline facet selection. Using the Al-Al 3 Ni alloy as a model, this project combines atomistic simulations and experimental methods to understand interfacial energies and develop predictive models. This approach aims to mitigate the negative effects of intermetallics, enhancing component reliability in electronic applications.

36 MATERIALS SCIENCE↗

DOE OSTI2022

A New Cathode Material for a Li–O 2 Battery Based on Lithium Superoxide

Li–O 2 batteries suffer from large charge overpotentials due to the high charge transfer resistance of Li 2 O 2 discharge products. A potential solution to this problem is the development of LiO 2 -based batteries that possess low charge overpotentials due to the lower charge transfer resistance of LiO 2 . In this report, IrLi nanoparticles were synthesized and implemented for the first time as a LiO 2 battery cathode material. The IrLi nanoparticle synthesis was achieved by a temperature- and time-optimized thermal reaction between a precise ratio of iridium nanoparticles and lithium metal. Li–O 2 batteries employing the IrLi-rGO cathodes were cycled up to 100 cycles at moderate current densities with sustained low cell charge potentials (<3.5 V). Further, various characterization techniques, including SEM, DEMS, TEM, Raman, and titration, were used to demonstrate the LiO 2 discharge product and the absence of Li 2 O 2 . On the basis of first-principles calculations, it was concluded that the formation of crystalline LiO 2 can be stabilized by epitaxial growth on the (111) facets of IrLi nanoparticles present on the cathode surface. These findings demonstrate that, in addition to the previously studied Ir 3 Li intermetallic, the IrLi intermetallic also provides a means by which LiO 2 discharge products can be stabilized and confirms the importance of templating for the formation process.

25 ENERGY STORAGE↗

DOE OSTI2021

In Situ Methods for Metal-Flux Synthesis in Inert Environments

Flux growth synthesis is an advantageous synthetic method as it allows for the growth of single crystals of both congruently melting and metastable phases. The determination of synthetic parameters for the flux growth of new crystalline phases is complex as many factors and parameters need to be considered, such as purity and morphology of starting material and heating profile variables including maximum temperature, dwell time, cooling rate and flux removal temperature. In situ monitoring of crystallite growth can lead to elucidation of reaction intermediates and growth mechanisms. The determination of pivotal reaction parameters can revolutionize the way growth parameters are selected. In this work, we report a new sample environment and furnace apparatus for synchrotron in situ synthesis of crystalline materials, including flux grown intermetallics.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗

DOE OSTI2020

Dynamic Observation of Dendritic Quasicrystal Growth upon Laser-Induced Solid-State Transformation

In this paper, we report the laser-induced solid-state transformation between a periodic “approximant” and quasicrystal in the Al-Cr system during rapid quenching. Dynamic transmission electron microscopy allows us to capture in situ the dendritic growth of the metastable quasicrystals. The formation of dendrites during solid-state transformation is a rare phenomenon, which we attribute to the structural similarity between the two intermetallics. Through ab initio molecular dynamics simulations, we identify the dominant structural motif to be a 13-atom icosahedral cluster transcending the phases of matter.

36 MATERIALS SCIENCE↗

DOE OSTI2021

2D Mg-Cu Intermetallic Compounds with Nontrivial Band Topology and Dirac Nodal Lines

Synthesis of vertical heterostructures that include atomically thin layers of materials with topologically nontrivial energy bands is desirable for exploring exotic quantum states. In this study, the authors report on atomic-layer-by-layer deposition of magnesium on copper(111) surface by molecular beam epitaxy, monitored in situ by low-energy electron microscopy and diffraction, and modeled by ab initio theory. It is found that a 2D MgCu 2 intermetallic compound forms during initial Mg deposition and persists till a full monolayer of Mg is formed. Deposition of additional Mg triggers a phase transition from the commensurate MgCu 2 to an incommensurate Mg 2 Cu layer and enables growth of the second layer of Mg. Ab initio calculations indicate non-trivial topology of the electron bands in the interfacial Mg 2 Cu layer and the existence of Dirac nodal lines near the Fermi level. The new 2D Mg 2 Cu material emerges as a promising platform to study new topological states of matter.

75 CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND↗

DOE OSTI2022

Charge Density Wave in Kagome Lattice Intermetallic ScV 6 Sn 6

Materials hosting kagome lattices have drawn interest for the diverse magnetic and electronic states generated by geometric frustration. In the AV 3 Sb 5 compounds (A=K, Rb, Cs), stacked vanadium kagome layers give rise to unusual charge density waves (CDW) and superconductivity. In this work, we report single-crystal growth and characterization of ScV 6 Sn 6 , a hexagonal HfFe 6 Ge 6 -type compound that shares this structural motif. We identify a first-order phase transition at 92 K. Single crystal x-ray and neutron diffraction reveal a charge density wave modulation of the atomic lattice below this temperature. This is a distinctly different structural mode than that observed in the AV 3 Sb 5 compounds, but both modes have been anticipated in kagome metals. The diverse HfFe 6 Ge 6 family offers more opportunities to tune ScV 6 Sn 6 and explore density wave order in kagome lattice materials.

36 MATERIALS SCIENCE↗

DOE OSTI2022

Understanding formation mechanisms of intermetallic compounds in dissimilar Al/steel joint processed by resistance spot welding

Here, this paper confirmed the formation mechanism of intermetallic compounds (IMCs) in Al/steel resistance spot welds with transmission electron microscopy, electron backscatter diffraction, nanoindentation and thermodynamic calculations. In particular, the formation of AlFe with BCC_B2 structure, which is not commonly seen in welds, was identified. The formation mechanism of IMCs at the high welding energy region is described as follows. Al 13 Fe 4 first nucleates from the Al side, followed by Al 5 Fe 2 growth with Fe atoms accumulating at the Al 13 Fe 4 grain boundaries. Then, Al 5 Fe 2 grains grow continuously to coarse columnar grains, and AlFe forms at the interface of Al 5 Fe 2 grains and the ferrite phase. Lastly, the needle-like Al 13 Fe 4 forms in the cooling process. At the middle welding energy region, only equiaxed Al 5 Fe 2 and small Al 13 Fe 4 grains are formed at the interface because of the lower diffusion rates of Al and Fe, hence postponing the growth of Al 5 Fe 2 and Al 13 Fe 4 . At the low welding energy region, only sporadic Al 5 Fe 2 and Al 13 Fe 4 grains are formed surrounded by the Al phase.

42 ENGINEERING↗

DOE OSTI2026

PIE-Enabled Study of Aqueous Corrosion & Zr Hydriding in Cr-Coated Cladding: M3GV-23PN0101132

Chromium-coated zirconium alloy cladding is under investigation as an accident-tolerant fuel (ATF) concept to extend performance to higher burnups via improved oxidation resistance and reduced hydrogen pickup. However, hydrothermal corrosion behavior and hydrogen transport mechanisms governing in-service hydriding of these coatings remain poorly understood. In a collaborative study between Pacific Northwest National Laboratory (PNNL), Idaho National Laboratory (INL), and the University of Huddersfield, cold spray (CS) and physical vapor deposition (PVD) Cr-coated Optimized ZIRLO™ cladding samples were characterized after exposure to PWR-simulated water chemistry under both in-core (neutron irradiation) and out-of-core (aqueous-only) conditions at the MIT Research Reactor. Multi-scale characterization was performed independently at PNNL and INL to evaluate coating integrity, microstructural evolution, Cr/Zr interface chemistry, and hydride formation. Both laboratories observed a consistent divergence in hydriding behavior: out-of-core CS Cr-coated cladding exhibited elevated hydride concentrations exceeding those of uncoated cladding, whereas in-core CS samples showed substantially suppressed hydriding. In-core specimens also displayed irradiation-specific features, including nanoscale voids within the Cr coating and radiation-induced segregation clusters in the Zr substrate. CS coatings retained an interdiffusion-free Cr/Zr bond with no intermetallic layer, whereas PVD coatings exhibited inferior quality with visible cracks and pores. An automated image-based hydride quantification method systematically overestimated bulk hydrogen content relative to inert gas fusion measurements, underscoring the need for standardized sample preparation and reference standards. Interpretation of hydride nucleation and growth is complicated by the open inner-diameter of the specimens, which provides additional hydrogen pathways. The results motivate further foundational studies to support predictive models of hydrothermal corrosion and hydrogen transport in unirradiated and irradiated Cr-coated cladding.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗

DOE OSTI2022

Stability, metallicity, and magnetism in niobium silicide nanofilms

Modern superconducting qubits based on two-dimensional (2D) transmons typically involve the growth of Nb thin films on high-resistivity Si substrates. Since imperfections at the Nb-Si heterointerface have been implicated as a source of two-level systems that limit quantum coherence times, detailed characterization and understanding of niobium silicide interfacial layers are critical to improving superconducting qubit technology. While bulk binary intermetallic niobium silicide phases are well understood, the thermodynamic phase stability and properties of ultrathin niobium silicides, such as those found at the Nb-Si heterointerface in 2D transmons, have not yet been explored. Here, we report finite-sized effects for ultrathin niobium silicide films using density functional theory calculations and predict nanoscale stabilization of Nb 6 Si 5 over the bulk α-Nb 5 Si 3 phase. This result is consistent with our experimental observations of a niobium silicide interfacial layer between a sputtered Nb thin film and the underlying Si substrate. Furthermore, our calculations show that Nb 6 Si 5 nanofilms are nonmagnetic, making them superior to nanofilms of α-Nb 5 Si 3 that exhibit antiferromagnetic correlations detrimental to long coherence times in superconducting qubits. Furthermore, by providing atomic-scale insight into niobium silicide nanofilms, this paper can help guide ongoing efforts to optimize Nb-Si heterointerfaces for long coherence times in superconducting qubits.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Fantastic n = 4: Ce5Co4+xGe13−ySny of the A n +1M n X3 n +1 homologous series

Ce-based intermetallics are of interest due to the potential to study the interplay of localized magnetic moments and conduction electrons. Our work on Ce-based germanides led to the identification of a new homologous series An+1MnX3n+1 (A = rare earth, M = transition metal, X = tetrels, and n = 1–6). This work presents the single-crystal growth, structure determination, and anisotropic magnetic properties of the n = 4 member of the Cen+1ConGe3n+1 homologous series. Ce5Co4+xGe13−ySny consists of three Ce sites, three Co sites, seven Ge sites, and two Sn sites, and the crystal structure is best modeled in the orthorhombic space group Cmmm where a = 4.3031(8) Å, b = 45.608(13) Å, and c = 4.3264(8) Å, which is in close agreement with the previously reported Sn-free analog where a = 4.265(1) Å, b = 45.175(9) Å, and c = 4.293(3) Å. Anisotropic magnetic measurements show Kondo-like behavior and three magnetic transitions at 6, 4.9, and 2.4 K for Ce5Co4+xGe13−ySny.

Weiland, Ashley (ORCID:0000000171983559)↗

DOE OSTI2024

Systematic discovery of new nano-scale metastable intermetallic eutectic phases in laser rapid solidified Aluminum-Germanium alloy

Laser surface remelting of as-cast Al-Ge eutectic alloy is shown to produce ultrafine lamellar eutectic morphology with interlamellar spacing refined up to ∼60 nm and composed of FCC Al solid solution and unusual Al x Ge y intermetallic phases that do not form during near-equilibrium solidification. The microstructures are characterized and analyzed using a combination of selected area electron diffraction, high-resolution scanning transmission electron microscopy, energy dispersive X-ray spectroscopy to obtain high-resolution elemental maps, and atomistic modeling using density functional theory followed by atomic-scale image simulation. Depending on the local solidification conditions, the crystallography of the Al x Ge y intermetallic phases in the eutectic microstructure is either monoclinic (C 2/c) or monoclinic (P 2 1 ), with high densities of defects in both cases. This is in sharp contrast to the as-cast alloys that showed nominally pure Al and Ge phases with significant solute partitioning and equilibrium FCC and diamond cubic crystal structures, respectively. Corresponding kinetic phase diagrams are proposed to interpret the evolution of nano-lamellar eutectic morphologies with equilibrium Al and metastable Al x Ge y phases, and to explain increased solid solubility in the Al phases manifested by precipitation of ultrafine clusters of Ge. Furthermore, the reasons for the formation of these metastable eutectics under laser rapid solidification are discussed from the perspective of the competitive growth criterion.

Al-Ge eutectic↗