A New Cathode Material for a Li–O 2 Battery Based on Lithium Superoxide

Abstract

Li–O 2 batteries suffer from large charge overpotentials due to the high charge transfer resistance of Li 2 O 2 discharge products. A potential solution to this problem is the development of LiO 2 -based batteries that possess low charge overpotentials due to the lower charge transfer resistance of LiO 2 . In this report, IrLi nanoparticles were synthesized and implemented for the first time as a LiO 2 battery cathode material. The IrLi nanoparticle synthesis was achieved by a temperature- and time-optimized thermal reaction between a precise ratio of iridium nanoparticles and lithium metal. Li–O 2 batteries employing the IrLi-rGO cathodes were cycled up to 100 cycles at moderate current densities with sustained low cell charge potentials (<3.5 V). Further, various characterization techniques, including SEM, DEMS, TEM, Raman, and titration, were used to demonstrate the LiO 2 discharge product and the absence of Li 2 O 2 . On the basis of first-principles calculations, it was concluded that the formation of crystalline LiO 2 can be stabilized by epitaxial growth on the (111) facets of IrLi nanoparticles present on the cathode surface. These findings demonstrate that, in addition to the previously studied Ir 3 Li intermetallic, the IrLi intermetallic also provides a means by which LiO 2 discharge products can be stabilized and confirms the importance of templating for the formation process.