DOE OSTI2023

Durable and Low-Cost Fractal Structured Multifunctional Coatings for Next-Generation CSP

Fractal coatings on various low-cost and high-temperature metallic substrates such as SS316, SS347, In800H, In740H, In625, Haynes 230, etc. were fabricated employing our patented novel electrodeposition process at various deposition potentials and deposition times, as well as chemical etching. The best combination of the materials and processing conditions were co-optimized for the reliable and repeatable fabrication of the multifunctional coatings. Surface morphologies were examined using SEM and AFM, and fractal characterization was done using a 3D optical surface profiler. Fractal dimension was used to identify successful fabrication and material parameters. The mechanical durability of the coatings was evaluated using several standardized tests, such as sand abrasion (ASTM D968) and adhesion (ASTM D3359), to fully characterize and demonstrate the mechanical durability of the fabricated surfaces. HTF immersion tests on the fractal multifunctional coatings were conducted based on a modification of the ASTM D870, which is established for static water immersion testing. To calculate the corrosion rates and descaled weight loss of the samples subjected to thermal exposure for different time durations (100 h, 300 h, 500 h, and optionally 750 h) to estimate the corrosion rate. While protecting the substrates from corrosion is an important goal, an allied goals is also to examine the post-corrosion temperature stability and properties of the molten salts themselves due to the dissolution of the constituents of the alloys and the corrosion products from the coatings that cause “fouling” of the molten salts. Fouling characteristics of the different molten salt HTFs exposed to coated and uncoated substrates were investigated. Finally, considering a prototype molten salt/sCO2 heat exchanger, cost/performance model is developed to demonstrate that the coatings on low-cost alloys such as stainless steel provide lower levelized cost of heat exchanger compared to high nickel content Ha230.

14 SOLAR ENERGY↗

DOE OSTI2025

Tailoring composition and deformation modes at the microstructural level for next generation low-cost high-strength austenitic stainless steels

The objective of this project is to enable deliberate development of cost-effective, hydrogen resistant alloys by establishing detailed relationships specific to the effects of alloy composition, short-range order (SRO), and microsegregation in the presence of hydrogen on the transition between homogeneous deformation and localized plasticity in shear bands. In collaboration with the International Institute for Carbon-Neutral Energy Research, I2CNER, at Kyushu University in Japan, we conceptualized, designed, and manufactured four austenitic alloys that maintain corrosion resistance and ensure lower cost relative to baseline commercial alloys. The mechanical properties and deformation modes of the novel alloys (KU alloys) were assessed in the presence of hydrogen (H). Correlations between composition and performance revealed that two of the KU alloys are suitable replacements for 316 steel, while another is a viable replacement for 304 steel at room temperature. We found that, in the presence of other austenite stabilizing elements namely Mn and N, replacing Ni with Cu does not lead to martensite formation as has been previously reported.1–3 Furthermore, we found that the addition of Cu leads to an earlier onset of multiple slip resulting in an relative earlier onset of a higher work hardening rate (WHR). Greater understanding of the relationships between alloy composition and SRO required the development of a novel advanced electron diffraction methodology to characterize SRO in complex FCC alloys. This innovative approach, which combines fluctuation and correlation analyses of diffuse-scattering signals, successfully differentiated between SRO and long-range ordering (LRO). Further investigations into annealed austenitic stainless steels could provide insights into manipulating SRO and its effects on material properties. Atomistic simulations provided understanding of SRO behavior that was difficult to capture experimentally. This project created the first spin cluster expansion model that is able to capture and describe SRO effects in Fe-Ni-Cr FCC alloys, accounting for the non-negligible effects of magnetism. An automated computational workflow was established to provide reliable predictions of SRO in Fe-Ni-Cr austenitic alloys, both with and without the presence of H atoms. Analysis of the propensity for SRO in Fe-Ni-Cr alloys revealed that H tends to cluster with specific, well-defined SRO domains. The computational framework is general purpose and can be extended to realistic stainless steels across diverse composition ranges. With confidence that SRO is possible in austenitic stainless steels, we developed a discrete dislocation finite element code to understand the interaction of dislocations with SRO in the presence of H. By incorporating H effects on the dislocation emission and SRO stress field we show that the critical stress for the dislocation pileup to breakthrough the SRO domain decreases in the presence of H, which directly contributes localized deformation at the macroscale. Through the simulation of a uniaxial tension test, we demonstrated that H-induced weakening of SRO stress field and H-enhanced dislocation emission can lead to the onset of shear localization at lower macroscopic strains. As a whole, this project identified three novel alloys that show improvements in performance and cost efficiency for H-facing applications by studying correlations between alloy chemistry and deformation behavior. We also made significant advancements to experimental and computational methodologies necessary to study the chemistry and distribution of SRO across a range of alloys, which in turn allowed us to demonstrate how deformation mechanisms change due to the contributions of SRO in austenitic alloys in the presence of H. The combined advancements in fundamental understanding with novel alloy development in this project has increased the viability of next generation H-technologies for the broader public through accessible low-cost alloys and accelerated development towards future H-infrastructure.

08 HYDROGEN↗

DOE OSTI2022

ZnCr and ZnNb Cold Spray Coatings

Novel cold spray zinc-based alloy coatings have been investigated for corrosion protection of API 5L low carbon steel pipelines used in transporting natural gas. These different zinc alloy coatings are designed for use to help prevent internal corrosion and improve the lifespan of steel pipelines via sacrificial anodic protection. The corrosion behavior of these cold deposited zinc alloy coatings was investigated in CO2 saturated 3.5 wt.% NaCl solutions under simulated natural gas pipeline conditions. Electrochemical tests were conducted at 25 and 40 °C to determine the polarization resistance and galvanic current between each coating and the steel substrate in the galvanic couple. Tests were conducted at atmospheric, 1 bar, pressure. The results indicate that use of these coatings has the potential to increase the lifespan of steel pipelines above what a zinc coating alone could provide.

Teeter, Lucas↗

DOE OSTI2023

Decoupling the effects of texture and composition on magnetic properties of Fe-Si sheet processed by shear deformation

Soft magnetic Fe-Si alloys (electrical steels) possess exceptional functional properties such as high permeability, low coercivity, and low core loss, which generally improve with increasing Si content in the alloy. However, Fe-Si alloys containing > 3.5 wt% Si are also characterized by prohibitively low workability and poor ductility that have prevented their efficient commercial production in sheet form by rolling. This has limited their use for improving efficiency of motors and transformers. In this study, hybrid cutting-extrusion (HCE) is used as a single-step thermomechanical processing method to produce continuous Fe-Si alloy sheet with high Si compositions of 4 wt% to 6.5 wt%. HCE sheet is shown to have a homogeneous annealed grain structure and simple-shear crystallographic textures. By controlling the HCE deformation path, varied crystallographic shear textures are created in the sheet. Quasi-static magnetic properties of the HCE sheet are evaluated to decouple the effects of sheet texture and Si composition on resultant permeability and coercivity properties. The results suggest that HCE, with suitable process scaling, is a viable route for production of high-Si content electrical steel sheet for next-generation motors and transformers.

36 MATERIALS SCIENCE↗

DOE OSTI2022

UK-US Collaboration on Fossil Energy R&D: Steam Side Oxidation

In recent years, interest in increasing the efficiency of power plants based on steam generation has led to the need to develop and qualify materials capable of operating at steam temperatures and pressures significantly higher than those employed in current power plants. The overall focus of this international program is on using ferritic-martensitic steels to the maximum possible temperature, before switching to austenitic steels and/or Ni-based alloys. The relatively low Cr content of these alloys raises concerns regarding their resistance to steam oxidation at these higher temperatures. Earlier work in this collaboration addressed the reliability of data from atmospheric pressure, laboratory-based steam oxidation tests. This raised issues regarding how representative the laboratory-grown oxides were compared to those formed on service-exposed material and how the tests could be made more reliable by introducing added complexity. In general laboratory-scale exposures are conducted under isothermal conditions at ambient or slightly elevated pressure, using a relatively low flow rate of steam. The coupons used in these tests are normally flat cuboids which have been ground to homogenise the surface and remove any pre-existing features. However, there is a concern that these samples and exposures are not representative of service conditions, and so it is necessary to quantify the influence of transient conditions, such as heat flux, pressure and sample geometry/surface conditions. To address such concerns a new collaborative program of work was initiated to determine the influence of these added features on oxidation kinetics and oxide scale morphology. The overall aim was to improve the understanding of alloy performance in ultrasupercritical (USC) steam conditions and qualify suitable test procedures.

20 FOSSIL-FUELED POWER PLANTS↗

DOE OSTI2025

Improved creep performance of CoCrFeNi high entropy alloys by Mo addition

The CoCrFeNi family of high entropy alloys has good mechanical and corrosion properties, performing like stainless steels with low yield stresses. They could, however, benefit from hardening methods for structural and high temperature applications. Here, this work investigates the potential for the CoCrFeNi alloy to be hardened with the addition of Mo. A series of CoCrFeNiMo alloys and their CoCrFeNi counterparts were subsequently manufactured at NETL and then mechanically creep tested at 650°C. The alloys were designed to possess a range of stacking fault energies which influence the mechanical properties of the alloys via the motion of their dislocations under stress. Results show that Mo-containing variants have creep rupture lives ranging from 4000 to 8000 hours, i.e., about two orders of magnitude longer than those for Mo-free variants. The significantly improved creep performance of the Mo-containing alloys is due to a combination of solid solution strengthening and precipitation strengthening from µ-phase and carbides.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Mechanical Property Measurements of HFIR-irradiated FM and ODS Alloys

This report provides a summary of the post-irradiation examination of the tensile properties of three ODS ferritic alloys, 14YWT-SM13, 9YWTV-PM2 and OFRAC, and two HT9 ferritic/martensitic steels, one with low N content and the other with high N content. The neutron irradiations were conducted in the flux trap of the High Flux Isotope Reactor as part of the Additive Manufacturing, Oxide Dispersion Strengthened Alloys and Wrought Steels (AMOW) irradiation campaign. Sub-sized tensile specimens fabricated from each material were exposed to nominal target temperatures and neutron doses of 300°C, 385°C, and 525°C and 8 dpa, 16 dpa, and 50 dpa, respectively.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Mechanical Property Measurements of HFIR-irradiated FM and ODS Alloys

This report provides a summary of the post-irradiation examination of the tensile properties of three ODS ferritic alloys, 14YWT-SM13, 9YWTV-PM2 and OFRAC, and two HT9 ferritic/martensitic steels, one with low N content and the other with high N content. The neutron irradiations were conducted in the flux trap of the High Flux Isotope Reactor as part of the A dditive M anufacturing, O xide Dispersion Strengthened Alloys and W rought Steels (AMOW) irradiation campaign. Sub-sized tensile specimens fabricated from each material were exposed to nominal target temperatures and neutron doses of 300°C, 385°C, and 525°C and 8 dpa, 16 dpa, and 50 dpa, respectively.

14YWT-SM13, 9YWTV-PM2, and OFRAC, and two HT9 ferr↗

DOE OSTI2022

Phase instabilities in austenitic steels during particle bombardment at high and low dose rates

Disruption of phase stability by energetic particle bombardment is a major challenge in designing advanced radiation-tolerant alloys and ion beam processing of nanocomposites. Particularly, ballistic dissolution susceptibility of different solute nanocluster species in alloys is poorly understood. Here, low dose rate neutron irradiations were conducted on a Fe-Cr-Ni based austenitic steel in the BOR-60 reactor (9.4 × 10 -7 dpa/s, 318 °C) followed by accelerated dose rate ion irradiations at multiple temperatures ( 10 -3 dpa/s, 380 – 420 °C). Using atom probe tomography, the stability of radiation-enhanced Cu-rich and radiation-induced Ni-Si-Mn-rich nanoclusters was evaluated. During neutron irradiation, Cu-rich clusters nucleated with their core concentrations progressively increasing with dose, while Ni-Si-Mn-rich clusters formed and evolved into G-phase precipitates. Ion irradiations dramatically altered the nanoclusters. Cu-rich clusters were ballistically dissolved, but Ni-Si-Mn-rich clusters remained stable and coarsened with dose at 400 and 420 °C, highlighting that different nanocluster species in a single microstructure can have innately distinct ballistic dissolution susceptibilities. Solute-specific recoil rates were incorporated into the Heinig precipitate stability model, which shows that in addition to radiation-enhanced diffusion, recovery from ballistic dissolution depends on solute concentration gradient near cluster interfaces. Finally, the combined experimental-modeling study quantified the critical temperatures and damage rates where ballistic dissolution dominates for each cluster species.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Si-Cr-Al-Mn Alloy for High Specific Resistivity

Laboratory material produced in budget period one met the target resistivity, mechanical and magnetic requirements for the Go/No-Go decision to move to industrial trials. The chosen chemistry settled on a high Cr strategy, with moderate Mn and Al additions, providing a good comprise on core loss and induction with minimal impact on mechanical properties, important to successful downstream processing. Industrial trials began in budget period two with the chosen chemistry, referred to as Alloy X. Difficulties occurred during initial hot rolling trials. Reheating the material using the standard NOES practice caused slab cracking from high thermal gradients in areas exposed to the roof burners, this was solved using a modified reheat practice. High Cr caused poor dynamic recrystallization during hot rolling, which was solved using a modified hot rolling practice. The high Cr content of the steel also caused poor decarburization during final annealing, which necessitated lowering the melt carbon aim for the final heat, together with a modified decarburization practice. Steel was finished to final thicknesses of 0.20 – 0.50 mm and evaluated for magnetic and mechanical properties. Although the target core loss for the 0.25 and 0.35 mm material was not achieved, significant reductions in high frequency core loss were measured, compared to equivalent commercially available material. Alloy X at 0.35 mm showed a 26 % and 23 % improvement at 400 HZ and 1000 Hz respectively, over Cliffs’ M-19 (0.35 mm) commercially available NOES. At 0.25 mm, Alloy X showed a 23 % and a 26 % improvement at 400 HZ and 1000 Hz respectively, over Cliffs’ HF-10 (0.25 mm) commercially available NOES. The 0.25 mm product was chosen for motor efficiency evaluation. ORNL collaborated with Cleveland-Cliffs (CC) to build, assemble, and test two 5HP motors: a baseline motor with M19 steel and a motor made with high efficiency steel (Alloy X) developed for the project. Overall, results were as expected with comparable performance at low speeds, and with more than 8% efficiency improvement for high speeds. Increased motor steel efficiency at high frequencies not only results in direct efficiency improvements but can yield reductions in motor size and cost by facilitating higher operation speeds, or by increasing the number of poles in the machine. This allows the production of more power-dense motors which are sometimes avoided with conventional material due to increased core losses. The material developed on this project provides more viable options for achieving improved motor efficiency or reduced motor size and cost.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Lifetime Energy Savings Via Advanced Manufacturing of Low Density Steels for Transportation Applications

The purpose of this “Low Density Steels for Transportation Applications” project was to develop an alloy composition and processing parameters that would result in a material suitable for use in automotive structural components at a reduced density over the current advanced high strength steel (AHSS) materials used. The project work successfully developed a robust alloy capable of exceeding project mechanical property targets at each stage of development, with an 8% density reduction over benchmark AHSS materials (7.8 g/cm3). The developed alloy has the potential to offer significant vehicle lightweighting and improved fuel economy, without sacrificing the increased passenger safety of more traditional AHSS. Through the three tasks of the project, (1) Alloy design and small-scale laboratory evaluation, (2) Laboratory development of hot rolled material and (3) Laboratory development of a cold rolled material, the laboratory work utilized advanced characterization and analytical methods on novel alloy compositions subjected to both conventional and non-conventional processing operations.

36 MATERIALS SCIENCE↗

DOE OSTI2021

Oxidation Behavior of Welded Fe-Based and Ni-Based Alloys in Supercritical CO 2

Next-generation supercritical CO 2 (sCO 2 ) power cycles will require different classes of alloy throughout the operational temperatures to optimize tradeoff of creep strength, oxidation performance and cost. This will necessitate joining methods such as welding, which might pose compatibility concerns at the joined interfaces. In this study, similar and dissimilar metal welds were generated from a variety of candidate alloys for sCO 2 systems including ferritic/martensitic steels, austenitic steels, and Ni-based superalloys. Samples were extracted from different regions of the welds and exposed to sCO 2 at 550 °C and 20 MPa for 2500 h, then characterized to understand their behavior in this environment. Unsurprisingly, the local oxidation behavior was largely dictated by the Cr content in the underlying metal. High-Cr austenitic steels and Ni alloys formed slow-growing Cr-rich oxide scales with minimal carburization of the underlying metal, while low-Cr ferritic/martensitic steels formed fast-growing Fe-rich oxide scales with significant carburization. Most welds did not show any unusual oxidation behavior at the interfaces, considering the local Cr content. The one exception was the 347H similar metal weld, where a larger grain size and complex grain structure in the fusion zone led to a significantly higher rate of Fe-rich oxide nodule formation compared to the base metal. This suggests that microstructural changes at joined interfaces can play an important role on the oxidation-limited lifetimes in future sCO 2 systems. The composition changes across the interfaces enabled study of the effect of Fe on the growth rate of Cr-rich oxides and of the origins of the sub-surface recrystallization zone that forms beneath them.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Understanding the effect of minor alloying elements on helium bubble formation in ferritic-martensitic steels

Ferritic-martensitic steels are promising structural materials for advanced nuclear reactors. To minimize long-term radioactivity, reduced-activation ferritic-martensitic steels have been developed by substituting high-activation elements like Ni and Mo with low-activation elements such as W. However, the impact of these alloying modifications on helium bubble formation, which plays a key role in material swelling, remains unclear. Here, in this study, we compared helium bubble formation in ferritic-martensitic steel T91 and reduced-activation ferritic-martensitic steel F82H. Both materials were irradiated with sequential 100 keV, 150 keV, and 200 keV helium ions to a dose of 0.5 dpa and a helium concentration of 9,000 appm at 500°C. The helium bubbles in F82H exhibited a larger average size and a lower density than those in T91, suggesting differences in minor alloying elements may influence the bubble growth. Here, to investigate the effects of these alloying elements, we characterized radiation-induced segregation near bubbles and grain boundaries. Prominent Ni-Mn-Si enriched clusters were found near bubbles in T91, while only Mn-Si enriched clusters were found near bubbles in F82H. In addition, the obvious Cr enrichment near grain boundaries was absent around bubbles in both steels. The different segregation trends among elements revealed the variations in element diffusion mechanisms and the different sink biases between bubbles and grain boundaries. Cr enrichment near grain boundaries is mostly driven by interstitial-mediated diffusion. However, since bubble growth relies on net vacancy flux, vacancy-mediated diffusion plays a dominant role in controlling element segregation near bubbles. Therefore, Cr enrichment was not found near bubbles. Because of preferential vacancy-drag diffusion for Ni, Si and Mn, these elements were enriched near bubbles. Due to the strong binding energies of vacancies with these solute atoms, the vacancy diffusivity can be reduced near these solutes. Therefore, the more prominent Ni-Si-Mn clustered near helium bubbles in T91 lead to stronger suppression of helium bubble growth compared to F82H.

36 MATERIALS SCIENCE↗

DOE OSTI2020

Effects of cryogenic temperature and grain size on fatigue-crack propagation in the medium-entropy CrCoNi alloy

CrCoNi-based high-entropy alloys have demonstrated outstanding mechanical properties, particularly at cryogenic temperatures. Here we investigate the fatigue-crack propagation properties of the equiatomic, single-phase, face-centered cubic, medium-entropy alloy (MEA), CrCoNi, that displays exceptional strength, ductility and toughness, all of which are enhanced at cryogenic temperatures. Fatigue-crack growth is examined, at a load ratio of 0.1 over a wide range of growth rates, from ~10 –11 to >10 –7 m/cycle, at room (293 K) and cryogenic (198 K, 77 K) temperatures for two grain sizes (~7 and 68 µm), with emphasis on near-threshold behavior. We find that the ΔK th fatigue thresholds are increased with decreasing temperature and increasing grain size: from 5.7 MPa√m at 293 K to 8 MPa√m at 77 K in the fine-grained alloy, and from 9.4 MPa√m at 293 K to 13.7 MPa√m at 77 K in the coarse-grained alloy. Mechanistically, transgranular cracking at 293 K transitions to a mixture of intergranular and transgranular at cryogenic temperatures, where the increased propensity of nano-twins appears to inhibit growth rates by deflecting the crack path. However, the main factor affecting near-threshold behavior is roughness-induced crack closure from interference between the crack flanks, which is enhanced by the rougher fracture surfaces at low temperatures, particularly in the coarser-grained microstructure. Here, fatigue-crack propagation behavior in CrCoNi is comparable to nickel-based superalloys but is superior to that of the high-entropy CrMnFeCoNi (Cantor) alloy and many high-strength steels, making the CrCoNi alloy an excellent candidate material for safety-critical applications, particularly involving low temperatures.

36 MATERIALS SCIENCE↗

DOE OSTI2025

Interpreting experimental measurements of helium bubbles using stochastic cluster dynamics models of heterogeneous nucleation and growth in irradiated ferritic alloys

Among a number of other advantageous features, ferritic/martensitic steels are being considered as fusion reactor structural materials due to their low intrinsic swelling under irradiation. However, under high-energy neutron irradiation, He produced through (n, α) reactions stabilizes vacancy clusters, which then act as seeds for bubble formation and growth, negating the intrinsic swelling resistance of these alloys. Standard models of irradiation damage accumulation and microstructural evolution consider homogeneous nucleation as the basis for bubble formation and growth. However, this generally does not explain the large bubble densities and sizes observed experimentally under a number of different conditions. Here, we propose a more realistic physical model of bubble nucleation, formation, and growth designed to capture recent experimental measurements of He-bubble formation and evolution during co-implantation of He and Fe ions in model ferritic alloys. We find that experimental results are explained only when the following three features are considered simultaneously: (i) heterogeneous nucleation of He-vacancy bubbles at defect sinks (e.g., dislocations, grain boundaries, and second-phase precipitates), (ii) nucleation and growth of bubbles via the ‘trap mutation’ mechanism (i.e., spontaneous production of Frenkel pairs due to absorption of He atoms), and (iii) transition from a growth-limited, He-stabilized bubble regime to a ‘runaway’ void-type growth scenario. The model is implemented into a stochastic cluster dynamics framework that takes advantage of cluster size grouping methods to accelerate the simulations, allowing us to reach 10 dpa of simulated irradiated dose, and to capture cluster sizes in excess of 20 nm. Further, a careful extrapolation exercise conducted assuming classical nucleation theory leads to excellent agreement with the experimental measurements at 50 dpa of irradiation.

36 MATERIALS SCIENCE↗

DOE OSTI2025

High-temperature nanoindentation creep studies on castable and sintered nanostructured low-activation ferritic-martensitic alloys

In this article, we present the creep characteristics of two reduced activation ferritic-martensitic steels of identical starting compositions formed by different fabrication routes: a nanostructured ferritic alloy commonly referred to as a castable nanostructured alloy (CNA) and a sintered nanostructured alloy (SNA) variant. Through a series of nanoindentation experiments spanning a temperature range of 25 °C to 650 °C, with a maximum load of 100 mN, we find creep behaviors in the cast and sintered materials to be remarkably similar. The creep stress exponent (n) for CNA and SNA were found to be in the range of 8–35 and the activation volume was ∼14–42b 3 , underscoring a dominance of dislocation-mediated mechanisms in both alloys. Notably, we observed a decline in the creep stress exponent with increasing temperature, attributable to the heightened influence of thermally activated dislocations. This phenomenon suggests a potential transition in the deformation mechanism towards a thermally activated dislocation climb process, significantly impacting the observed creep behavior.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Complete Optimization of LPBF Ni-Based Alloys Down-Selected from FY23 Candidate Materials Including, Thermodynamic Modeling, Sample Fabrication and Microstructure Characterization

The goal of the Advanced Materials and Manufacturing Technologies (AMMT) program is to accelerate the incorporation of new materials and manufacturing technologies into advanced nuclear-related systems. Although 316H stainless steel fabricated by laser powder bed fusion (LPBF) has already been identified as an alloy that could have a significant effect on various reactor technologies, many other materials and manufacturing techniques are being evaluated. Nickel-based alloys typically offer higher-temperature capabilities compared with advanced stainless steels, and previous reports looked at three Ni-based alloy categories: low-Co alloys with a potential use close to the reactor core; high-temperature, high-strength alloys; and molten salt–compatible alloys. In the first category, alloy 718 was studied in 2023, and creep testing at 600°C and 650°C revealed that the alloy exhibited great creep strength after the appropriate annealing but had low ductility. Advanced characterization was recently conducted to highlight the presence of strengthening γ' and γ" precipitates after creep testing and to show that brittle phases at grain boundaries might explain the low ductility of LPBF 718 compared with wrought 718. For the high-temperature, high-strength alloys, previously purchased powders of alloys 617, 230, and 625 were used to assess the printability of these three solution-strengthened alloys. Hot cracking could not be suppressed for alloy 617 and 230, and it was shown that these cracks, which were elongated along the build direction (BD), had a drastic effect on the ductility of alloy 230 at room temperature when specimens were machined perpendicular to the BD. On the contrary, LPBF printing of crack-free alloy 625 was achieved using similar printing parameters, and the alloy looked like a promising candidate for various reactor technologies. The fabrication of alloy 282 by LPBF, a γ'-strengthened alloy with great creep strength up to 800°C, was performed in 2023, and x-ray computed tomography (XCT) scans of the alloy before and after creep testing at 750°C were carried out to assess the effect of flaws on the alloy’s creep behavior. Correlation between the flaws’ volume fraction, creep ductility, and creep lifetime could be established, and future work on LPBF 625 will take full advantage of in situ printing data and ex situ XCT scans to accelerate the alloy qualification. Finally, single track experiments were performed on the two alloys previously identified as good molten salt–resistant, Ni-based candidates: Hastelloy N and 244. Various laser parameters were considered, and cracking was not observed for either of the two alloys. Wrought 244 offers better creep strength and molten salt compatibility than alloy 625, and future work will aim to establish the alloy LPBF processing window.

36 MATERIALS SCIENCE↗

DOE OSTI2024

Evaluation of Directed Energy Deposition and Laser Powder Bed Fusion Nickel-Based Alloys Process Application Envelopes Based on Performance, Process Economics, Supply Chain Risks, and Reactor-Specific Targeted Components

The goal of the Advanced Materials and Manufacturing Technologies (AMMT) program is to accelerate the deployment of new materials and manufacturing technologies into advanced nuclear-related systems. Although 316H stainless steel fabricated by laser powder bed fusion (LPBF) has already been identified as an alloy that could have a significant effect on various reactor technologies, many other materials and manufacturing techniques are being evaluated. Nickel-based alloys typically offer higher-temperature capabilities compared with advanced stainless steels, and previous reports looked at three Ni-based alloy categories: low-Co alloys with a potential use close to the reactor core; high-temperature, high-strength alloys; and molten salt–compatible alloys. Due to the increasing interest in the low Co 625 alloy for nuclear applications, the alloy was compared at the Oak Ridge National Laboratory (ORNL) with 617, 230, two high-temperature, high-strength solution-strengthened alloys. Hot cracking could not be suppressed for alloy 230, and it was shown that these cracks, which were elongated along the build direction (BD), had a drastic effect on the ductility of alloy 230 at room temperature when specimens were machined perpendicular to the BD. Cracking was not as significant for alloy 617, but still led to significant variation in ductility at room temperature along the build direction. On the contrary, LPBF printing of crack-free alloy 625 was achieved using similar printing parameters, and the alloy looks like a very promising candidate for various reactor technologies.

36 MATERIALS SCIENCE↗