Cast B-1900 with and without 1 weight percent Si was subjected to cyclic oxidation at 1000 and 1100 C in air for 700 and 200 hours, respectively. The results were judged by specific weight change, metallography and X-ray diffraction. Si was found to be of significant value in reducing oxidation attack, probably by increasing scale adherence.
The Florida Everglades formed from sawgrass and other aquatic plant remains that have accumulated over thousands of years and is a patterned peatland. The region was initially drained for agricultural and urban development in the late 1800s by the lowering of Lake Okeechobee water levels through canal drainage. Over the course of the past century, the Everglades has further been altered by the construction of canals and levees to provide control of Lake Okeechobee and Everglades water levels. The drainage has caused the loss of much of the peat of the Everglades by peat fires and microbial oxidation, much of it occurring between the 1880s and the 1950s. Plans for Everglades restoration are designed to provide additional water to flow through the remaining Everglades. Additional water into the Everglades would prevent further peat loss by reducing oxidation and encouraging the accretion of peat that has been lost. This potentially could result in the sequestration of significant quantities of atmospheric carbon. We used historic records to determine how much peat was there originally and how much has been lost. Over the past century and a half, approximately 50% of the original Everglades has been lost to agricultural and urban development. In addition, much of the peat in the remaining Everglades Protection Area has been lost. We used Geographic Information Systems technologies to determine the volume and mass of peat, the mass of carbon for each of the predrainage landscapes as well as the current Everglades regions. To do this, historical and current surveys within the Everglades were used to create elevation maps. With these maps, along with a bedrock contour map of south Florida, and soils data from the USEPA, we estimated Everglades peat characteristics. These calculations provide rough, quantitative estimates of the historical Everglades, its current condition, and the changes in the peat soil that have taken place since the 19th century. Given the uncertainties in the hindcasting of some of these data sets, this analysis provides rough estimates for the peat volumes and related constituents. Our calculations indicate that the current Everglades roughly contains less than 24% of theoriginal peat volume, 17% of its mass and 19% of its carbon. The work described was fully supported by the South Florida Water Management District, West Palm Beach, FL
A major health risk for human deep space exploration is central nervous system (CNS) damage by galactic cosmic ray radiation. Simulated galactic cosmic rays or their components, especially the high-linear energy transfer (LET) particles such as 56Fe ions, have been shown to cause CNS damage, neuroinflammation and cognitive dysfunction in rodent models, but their effects on human CNS remain to be investigated. CNS damage from any insult, including ionizing radiation, is partially mediated by the blood-brain barrier (BBB), which regulates interactions between CNS and the rest of the body. The main cellular regulators of BBB permeability are astrocytes, which also modulate neuroinflammation. However, there have been few studies on BBB and astrocyte functions in regulating CNS responses, especially in human tissue analogs. Therefore, we utilized a high-throughput 3D organ-on-a-chip system, seeded with human induced pluripotent stem cell-derived astrocytes and brain endothelial cells, or brain endothelial cells alone, to study human neurovascular responses to simulated deep space radiation. We investigated the permeability and morphology of vascular structures formed by endothelial cells, as well as oxidative stress and secreted cytokines and chemokine levels over 1-7 days after irradiation with 0.25 – 0.5 Gy 5-ion simplified simulated galactic cosmic rays or 0.3 – 0.8 Gy high-LET 600 MeV/n 56Fe particles, and compared the outcomes to low-LET X-ray irradiation. We observed that simulated deep space radiation caused delayed astrocyte activation in a pattern resembling CNS responses to brain injury, caused oxidative stress and the production of inflammatory cytokines, and compromised BBB integrity by damaging tight junctions, thus increasing vascular permeability. Furthermore, our results indicate that astrocytes have a dual role in regulating radiation responses: they exacerbate blood-brain barrier permeability early after irradiation, followed by switching to a more protective scar-like phenotype by reducing oxidative stress and pro-inflammatory cytokine and chemokine secretion. In a follow-up study using the same platform, we investigated the dose-rate effects of ionizing radiation, by exposing our model to chronic, low dose-rate, gamma radiation. Our model was significantly improved by adding additional cell types composing the BBB, modelling immune cell infiltration into the brain, and studying the effect of an antioxidant, to measure more complex outcomes and model more closely the effect of deep space radiation on the human BBB. In summary, our results present a human neurovascular model for space radiation studies and potential future automated payload adaptation, and suggest astrocyte regulatory mechanisms as targets for countermeasures to mitigate human neurovascular impairments during deep space exploration.
Hybrid-poplar tree plantations provide a source for biofuel and biomass, but they also increase forest isoprene emissions. The consequences of increased isoprene emissions include higher rates of tropospheric ozone production, increases in the lifetime of methane, and increases in atmospheric aerosol production, all of which affect the global energy budget and/or lead to the degradation of air quality. Using RNA interference (RNAi) to suppress isoprene emission, we show that this trait, which is thought to be required for the tolerance of abiotic stress, is not required for high rates of photosynthesis and woody biomass production in the agroforest plantation environment, even in areas with high levels of climatic stress. Biomass production over 4 y in plantations in Arizona and Oregon was similar among genetic lines that emitted or did not emit significant amounts of isoprene. Lines that had substantially reduced isoprene emission rates also showed decreases in flavonol pigments, which reduce oxidative damage during extremes of abiotic stress, a pattern that would be expected to amplify metabolic dysfunction in the absence of isoprene production in stress-prone climate regimes. However, compensatory increases in the expression of other proteomic components, especially those associated with the production of protective compounds, such as carotenoids and terpenoids, and the fact that most biomass is produced prior to the hottest and driest part of the growing season explain the observed pattern of high biomass production with low isoprene emission. Our results show that it is possible to reduce the deleterious influences of isoprene on the atmosphere, while sustaining woody biomass production in temperate agroforest plantations.
A shielded integrated complimentary MOS transistor structure is described which is used to prevent field inversion in the region not occupied by the gates and which permits the use of a thinner field oxide, reduces the chip area, and has provision for simplified multilayer connections. The structure is used in the design of a static shift register and results in a 20% reduction in area.
Nickel-plated device, with machined recesses matching the multipin pattern of particular circuit module, facilitates repairs to electronic systems and reduces chance of damage to adjacent components. Nickel-plating reduces oxidation and scaling. Recesses retain sufficient amount of molten solder to uniformly wet pins for simultaneous heating and extraction.
Experiments were performed in which meteoritic iron, iron ore and nickel-iron alloy were used to catalyze (in Fischer-Tropsch synthesis) the reaction of deuterium and carbon monoxide in a closed vessel. Normal alkanes and alkenes and their monomethyl substituted isomers and aromatic hydrocarbons were synthesized. Iron oxide and oxidized-reduced Canyon Diablo used as Fischer-Tropsch catalysts were found to produce aromatic hydrocarbons in distributions having many of the features of those observed in carbonaceous chondrites, but only at temperatures and reaction times well above 300 C and 6-8 h.
A new high pressure turbine shroud material has been developed from the consolidation of prealloyed powders of Ni, Cr, Al and Y. The new material, a filler for cast turbine shroud body segments, is called Genaseal. The development followed the identification of oxidation resistance as the primary cause of prior shroud deterioration, since conversion to oxides reduces erosion resistance and increases spalling under thermal cycled engine conditions. The NICrAlY composition was selected in preference to NIAL and FeCRALY alloys, and was formulated to a prescribed density range that offers suitable erosion resistance, thermal conductivity and elastic modulus for improved behavior as a shroud.
Water vapor in working fluid equilibrates with permeability-reducing oxides in metal parts. Report describes study of effects of water on permeation of heater-head tubes by hydrogen in Stirling engine. Experiments performed to determine minimum concentration of oxygen and/or oxygen-bearing gas maintaining oxide coverage adequate for low permeability. Tests showed 750 ppm or more of water effective in maintaining stable, low permeability.
Increasing interest in establishing a lunar base has generated considerable study on the utilization of lunar resources. Because of its importance in producing water, reducing oxides, and serving as a fuel for orbital tranfer vehicles, hydrogen is of prime importance as a resource. Lowman (1985) states that hydrogen would greatly facilitate the establishment of an autonomous permanent colony, and he calls hydrogen the most valuable lunar resource. Through the centuries, hydrogen has been embedded in lunar soil by the solar wind. The hydrogen can be extracted by heating the soil to 900 C (Carr et al, 1987). In order to obtain hydrogen on the lunar surface, an extraction method must be developed which will not only be reliable but also economically feasible. Three heating methods are examined for possible use in extracting hydrogen from lunar soil.
Some nickel based superalloys show reduced oxidation resistance from the lack of an adherent oxide layer during high temperature cyclic oxidation. The segregation of sulfur to the oxide-metal interface is believed to effect oxide adhesion, since low sulfur alloys exhibit enhanced adhesion. X ray Photoelectron Spectroscopy (XPS) was combined with an in situ sample heater to measure sulfur segregation in NiCrAl, PWA 1480, and NiAl alloys. The polished samples with a 1.5 to 2.5 nm (native) oxide were heated from 650 to 1100 C with hold times up to 6 hr. The sulfur concentration was plotted as a function of temperature versus time at temperature. One NiCrAl sulfur study was performed on the same casting used by Browning to establish a base line between previous Auger Electron Spectroscopy (AES) results and the XPS results of this study. Sulfur surface segregation was similar for PWA 1480 and NiCrAl and reached a maximum of 30 at% at 800 to 850 C. Above 900 C the sulfur surface concentration decreased to about 3 at% at 1100 C. These results are contrasted to the minimal segregation observed for low sulfur hydrogen annealed materials which exhibit improved scale adhesion.
Silicon carbide with a refractory oxide coating is potentially a very attractive ceramic system. It offers the desirable mechanical and physical properties of SiC and the environmental durability of a refractory oxide. The development of a thermal shock resistant plasma-sprayed mullite coating on SiC is discussed. The durability of the mullite/SiC in oxidizing, reducing, and molten salt environments is discussed. In general, this system exhibits better behavior than uncoated SiC. Areas for further developments are discussed.
We characterize ten chromatic chondrules, two spinelian chondrules andd one spinel-bearing chondrule and summarize data for 120 chromitic inclusions discovered in an extensive survey of ordinary chondrites. Compositional and petrographic evidence suggests that chromitic chondrules and inclusions are closely related. The Cr/(Cr + Al) ratios in the spinal of these objects range from 0.5 to 0.9 and bulk Al2O3 contents are uniformly high (greater than 10 wt%, except for one with 8 wt%). No other elements having comparable solar abundances are so stongly enriched, and alkali feldspar and merrillite are more common than in normal chondrules. The Cr/Mg ratios in chromitic chondrules are 180-750 times the ratios in the bulk chondrite. With the possible exception of magnetic clumping of chromite in the presolar cloud, mechanical processes cannot account for this enrichment. Examination of nebular equilibrium processes shows that 50%-condensation temperatures of Cr at pH2/pH2O of 1500 are several tens of degrees below those of Mg as Mg2SiO4; the condensation of Cr is primarily as MgCr2O4 dissolved in MgAl2O4 at nebular pressures of 10(exp -4) atm or below. At pH2 = 10(exp -3) atm condesation as Cr in Fe-Ni is favored. Making the nebula much more oxidizing reduces the difference in condensation temperatures but Mg remains more refractory. We conclude that nebular equilibrium processes are not responsible for the enhanced Cr/Mg ratios. We propose that both Cr and Al became enriched in residues formed by incomplete evaporation of presolar lumps. We suggest that spinals remained as solid phases when the bulk of the silicates were incorporated into the evaporating melt; vaporization of Al and Cr were inhibited by the slow kinetics of diffusion. Subsequent melting and crystallization of these residues fractionated Cr from Al. The resulting materials constituted major components in the precursors of chromitic chondrules. Our model implies that chromitic chondrules and inclusions preserve the Cr isotopic record of presolar sources.
The induced thermoluminescence (TL) properties of 16 CV and CV-related chondrites, four CK chondrites and Renazzo (CR2) have been measured in order to investigate their metamorphic history. The petrographic, mineralogical and bulk compositional differences among the CV chondrites indicate that the TL sensitivity of the approximately 130 C TL peak is reflecting the abundance of ordered feldspar, especially in chondrule mesostasis, which in turn reflects parent-body metamorphism. The TL properties of 18 samples of homogenized Allende powder heated at a variety of times and temperatures, and cathodoluminescence mosaics of Axtell and Coolidge, showed results consistent with this conclusion. Five refractory inclusions from Allende, and separates from those inclusions, were also examined and yielded trends reflecting variations in mineralogy indicative of high peak temperatures (either metamorphic or igneous) and fairly rapid cooling. The CK chondrites are unique among metamorphosed chondrites in showing no detectable induced TL, which is consistent with literature data that suggests very unusual feldspar in these meteorites. Using TL sensitivity and several mineral systems and allowing for the differences in the oxidized and reduced subgroups, the CV and CV-related meteorites can be divided into petrologic types analogous to those of the ordinary and CO type 3 chondrites. Axtell, Kaba, Leoville, Bali, Arch and ALHA81003 are type 3.0-3.1, while ALH84018, Efremovka, Grosnaja, Allende and Vigarano are type 3.2-3.3 and Coolidge and Loongana 001 are type 3.8. Mokoia is probably a breccia with regions ranging in petrologic type from 3.0 to 3.2. Renazzo often plots at the end of the reduced and oxidized CV chondrite trends, even when those trends diverge, suggesting that in many respects it resembles the unmetamorphosed precursors of the CV chondrites. The low-petrographic types and low-TL peak temperatures of all samples, including the CV3.8 chondrites, indicates metamorphism in the stability field of low feldspar (i.e., less than 800 C) and a metamorphic history similar to that of the CO chondrites but unlike that of the ordinary chondrites.
The single crystal superalloy Rene'N5 (with or without Y-doping and hydrogen annealing) was cyclically oxidized at 1150 C for 1000 hours. After considerable scale growth (>= 500 hours), even the adherent alumina scales formed on Y-doped samples exhibited delayed interfacial spallation during subsequent water immersion tests, performed up to one year after oxidation. Spallation was characterized by weight loss, the amount of spalled area, and acoustic emission response. Hydrogen annealing (prior to oxidation) reduced spallation both before and after immersion, but without measurably reducing the bulk sulfur content of the Y-doped alloys. The duration and frequency of sequential, co-located acoustic emission events implied an interfacial crack growth rate at least 10(exp -3) m/s, but possibly higher than 10(exp 2) m/s. This is much greater than classic moisture-assisted slow crack growth rates in bulk alumina (10(exp -6) to 10(exp -3) m/s), which may still have occurred undetected by acoustic emission. An alternative failure sequence is proposed: an incubation process for preferential moisture ingress leads to a local decrease in interfacial toughness, thus allowing fast fracture driven by stored strain energy.
Combustion in a variety of heterogeneous systems, leading to the synthesis of advanced materials, is characterized by high temperatures (2000-3500 K) and heating rates (up to 10(exp 6) K/s) at and ahead of the reaction front. These high temperatures generate liquids and gases which are subject to gravity-driven flow. The removal of such gravitational effects is likely to provide increased control of the reaction front, with a consequent improvement in control of the microstructure of the synthesized products. Thus, microgravity (mu-g) experiments lead to major advances in the understanding of fundamental aspects of combustion and structure formation under the extreme conditions of the combustion synthesis (CS) wave. In addition, the specific features of microgravity environment allow one to produce unique materials, which cannot be obtained under terrestrial conditions. The current research is a logic continuation of our previous work on investigations of the fundamental phenomena of combustion and structure formation that occur at the high temperatures achieved in a CS wave. Our research is being conducted in three main directions: 1) Microstructural Transformations during Combustion Synthesis of Metal-Ceramic Composites. The studies are devoted to the investigation of particle growth during CS of intermetallic-ceramic composites, synthesized from nickel, aluminum, titanium, and boron metal reactants. To determine the mechanisms of particle growth, the investigation varies the relative amount of components in the initial mixture to yield combustion wave products with different ratios of solid and liquid phases, under 1g and mu-g conditions; 2) Mechanisms of Heat Transfer during Reactions in Heterogeneous Media. Specifically, new phenomena of gasless combustion wave propagation in heterogeneous media with porosity higher than that achievable in normal gravity conditions, are being studied. Two types of mixtures are investigated: clad powders, where contact between reactants occurs within each particle, and mixtures of elemental powders, where interparticle contacts are important for the reaction; and 3) Mechanistic Studies of Phase Separation in Combustion of Thermite Systems. Studies are devoted to experiments on thermite systems (metal oxide-reducing metal) where phase separation processes occur to produce alloys with tailored compositions and properties. The separation may be either gravity-driven or due to surface forces, and systematic studies to elucidate the true mechanism are being conducted. The knowledge obtained will be used to find the most promising ways of controlling the microstructure and properties of combustion-synthesized materials. Low-gravity experiments are essential to create idealized an environment for insights into the physics and chemistry of advanced material synthesis processes.
STC Catalysts, Inc. (SCi) manufactures a noble metal reducible oxide catalyst consisting primarily of platinum and tin dioxide deposited on a ceramic substrate. It is an ambient temperature oxidation catalyst that was developed primarily for Carbon Dioxide Lasers.The catalyst was developed by the NASA Langley Research Center for the Laser Atmospheric Wind Sounder Program (LAWS) which was intended to measure wind velocity on a global basis. There are a number of NASA owned patents covering various aspects of the catalyst.
In the early 1980's, Lewis Research Center began a program to develop high-temperature lubricants for use on future aircraft flying at three or more times the speed of sound, which can result in vehicle skin temperatures as high as 1,600 degrees Fahrenheit. A material that emerged from this research is a plasma-sprayed, self-lubricating metal- glass-fluoride coating able to reduce oxidation at very high temperatures. Technology is now in commercial use under the trade name Surf-Kote C-800, marketed by Hohman Plating and Manufacturing Inc. and manufactured under a patent license from NASA. Among its uses are lubrication for sliding contact bearings, shaft seals for turbopumps, piston rings for high performance compressors and hot glass processing machinery; it is also widely used in missile and space applications.