DOE OSTI2023

Chemical contributions to silicon anode calendar aging are dominant over mechanical contributions

Silicon (Si) anodes are a promising candidate for increasing the energy density of lithium (Li)-ion batteries for electric vehicles. However, they have recently been identified as having poor calendar life that is insufficient for commercial needs, in addition to the well-known issue of their poor cycle life resulting from large volume expansion. Here, a specially designed protocol with variable rest periods between intermittent cycling is used to evaluate the impact of the mechanical disruption of Si and solid electrolyte interphase (SEI) from cycling on calendar aging measurements. Si was found to undergo more mechanical degradation during calendar aging with intermittent cycling than graphite. However, Si anode capacity fade was still dominated by time, especially for rest periods greater than or equal to 1 month between cycling. Postmortem dQ/dV half-cell analysis indicated this was mainly due to Li inventory loss and an increase in electrode resistance. Isothermal microcalorimetry further demonstrated that Si passivation is more disrupted than graphite passivation with intermittent cycling and suggested that there may be a chemical buildup of a detrimental species in the electrolyte, leading to a large spike in heat after the Si and SEI are disrupted by cycling.

25 ENERGY STORAGE↗
DOE OSTI2026

Mechanistic Understanding of Interphase-driven Aging in Silicon Anodes

Conventional solid electrolyte interphases (SEIs) strongly adhere to micro-silicon (µ-Si) and crack under volume changes, causing poor cycling performance. Nano-silicon improves cycling performance but remains costly with limited calendar life. Here potentiostatic ageing tests demonstrate that both calendar and cycle ageing are governed by SEI cracking and dissolution with different relative contributions. When the system is not dominated by SEI dissolution, the relative calendar life of Si anodes could correlates positively with their cycle life. LiF-rich SEI that enables long cycle life in µ-Si is therefore expected to enhance calendar life as well. Using this framework, we screened electrolytes, SEIs and electrodes and validated them with full-cell storage. LiF-rich SEI minimizes cracking and dissolution, enabling μ-Si to achieve excellent calendar life, whereas nano-silicon suffers from SEI dissolution and needs reduced electrolyte–electrode contact for better calendar life. This work clarifies calendar-ageing behaviour and accelerates electrolytes and SEI development for long-life Si anodes.

Johnson, Christopher S.↗
DOE OSTI2025

On the Efficacy of Repeat Voltage Holds for Conditioning and Calendar Life Testing of Graphite and Silicon Cells

Voltage-hold (V-hold) protocols have shown promise toward calendar lifetime analysis of cells with graphite (Gr) and silicon (Si) anodes. In this work, repeat V-holds are performed on Gr and Si cells paired with lithium iron phosphate cathodes to delineate their beneficial role in formation and conditioning. We find that V-hold at the top of charge supplements constant current cycling in conditioning the cell to higher capacities for both Gr and Si cells after the first V-hold. A reduced order model provides the irreversible capacity proportions of each V-hold. With each repeat V-hold, parasitic loss of lithium to the solid electrolyte interphase (SEI) decreases on both Gr and Si cells. Gr cells show the square-root-of-time capacity loss behavior within 200 h of V-hold, indicative of its fast relaxation and low impact of reference performance test cycles on the SEI growth. Lifetime estimates from repeat V-holds on Gr can reach years. Si exhibits longer transition times from kinetic to diffusion-limited SEI growth, evidenced by the 400 h and 200 h holds showing square-root-of-time and linear behavior, respectively. Lifetime predictions from repeat V-holds on Si only reach 1–2 months, highlighting its limitations. Recommended duration of V-holds for Si cells should be ≥400 h.

25 ENERGY STORAGE↗
DOE OSTI2023

Tin Metal Improves the Lithiation Kinetics of High-Capacity Silicon Anodes

Si-based anodes present a great promise for high energy density lithium-ion batteries. However, its commercialization is largely hindered by a grand challenge of a rapid capacity fade. Here, we demonstrate excellent cycling stability on a Si-Sn thin film electrode that outperforms pure Si or Sn counterpart under the similar conditions. Combined with the first-principles calculations, in situ transmission electron microscopy studies reveal a reduced volume expansion, increased conductivity, as well as dynamic rearrangement upon lithiation of the Si-Sn film. Here we attribute the improved lithiation kinetics to the formation of a conductive matrix that comprises a mosaic of nanostructured Sn, Li y Sn (specifically, Li 7 Sn 2 develops around the lithiation potential of Si), and Li x Si. This work provides an important advance in understanding the lithiation mechanism of Si-based anodes for next-generation lithium-ion batteries.

25 ENERGY STORAGE↗
DOE OSTI2021

A chemical switch enabled autonomous two-stage crosslinking polymeric binder for high performance silicon anodes

Silicon (Si) is a promising high-capacity anode material for high-energy-density lithium-ion batteries. However, the drastic volumetric changes of Si upon lithiation/delithiation hinder the practical use of Si anodes. Although adhesive polymeric binders, such as poly(acrylic acid) (PAA), mitigate this issue, the cycling performance of the fabricated Si anodes is still far from meeting the criteria of practical applications. In this study, we present a novel polymeric binder system for Si anodes consisting of PAA, a chemical switch (ammonia, NH 3 ), and a crosslinker (branched polyethylenimine, PEI). The crosslinking between PAA and PEI is switched off in the slurry, which can then be turned on during electrode drying. Interestingly, the crosslinking reaction consists of two stages: ionic cross-linking (PAA-PEI-i) and covalent crosslinking (PAA-PEI-c) at a higher temperature (e.g., 130 °C). In half-cells, Si anodes fabricated using the PAA-PEI-c binder show a 67% increase in capacity retention compared to PAA anodes over 150 cycles at C/3 rate. The PAA-PEI-c binder also outperforms PAA in full cells. In addition, the chemical switch controlled crosslinking binder system also facilitates the slurry making process by avoiding early crosslinking. This system requires no additional steps compared to the conventional electrode lamination process, showing enormous potential for direct adoption in large-scale manufacturing.

25 ENERGY STORAGE↗
DOE OSTI2021

Investigations on the effect of current density on SiO/Si composite electrodes

An oxide layer on the surface of silicon particles is inevitable and is necessary for their application as anode materials for lithium ion batteries with high capacity and durability. However, a thick surficial oxide layer could significantly reduce the capacity of a Si anode. Here, Si nanoparticles with a thick surficial oxide layer of ~20 nm (Si@SiO x ) were fabricated through thermal oxidation and investigated electrochemically. The results revealed that very low current density is needed to activate Si@SiO x anodes during the first formation cycle. Once activated, the Si@SiO x anode can deliver reversible capacity as high as ~1000 mAh/g with low current density. Then, the Si@SiO x can be cycled at higher current densities of >700 mAh/g. Electrochemical impedance spectroscopy (EIS) shows that the lower current density results in lower charge-transfer resistance of the Si@SiO x anode, suggesting a higher degree of lithiation of the surficial oxide layer during low-current activation. EIS analysis also reveals that the lithiation of the surficial oxide is irreversible. We believe that the surface silicon oxide layer is lithiated and forms lithium silicate during the initial activation process. Lithium silicate has high conductivity and allows the lithiation/delithiation of Si core under the oxide layer during following charge and discharge.

25 ENERGY STORAGE↗
DOE OSTI2026

Solid-state prealkylation of electrode architectures to tune solid electrolyte interphase composition

Efficient electrochemical cycling of certain Si anodes is limited by irreversible Li consumption to form and continually reform the solid electrolyte interface (SEI) due to Si expansion/contraction and fracture. Prelithiation can compensate for these losses; however, the starting open circuit potential (VOC) becomes highly reducing and, therefore, the electrolyte reduction chemistry that influences the SEI composition can change. Herein, we compare SEI formation for electrodes prelithiated using Solid State Prealkylation of Electrode Architectures (SPEAR) versus traditional electrochemically lithiated architectures (ECLAR), focusing on SEI compositional changes as a function of stoichiometry (0.28 ≤ x ≤ 1.38 in LixSi). Increasing SPEAR prelithiation decreased the initial VOC of Si anodes vs. Li/Li+ from ∼3 V (Li0.28Si) to < 0.5 V for Li1.38Si, enabling simultaneous competitive reduction of EC, EMC, and LiPF6 at low potentials. Ex situ7Li and 29Si cross-polarization NMR and XPS reveal that SPEAR drives thicker SEI formation with substantially increased P/F contributions and a predominantly inorganic insoluble SEI (71.4% inorganic for Li1.38Si), consistent with accelerated LiPF6-derived POx/LiPFx/LiF formation relative to ECLAR analogs which exhibit carbonate-rich organic SEI compositions. Symmetric-cell EIS further indicates SPEAR-specific impedance features consistent with pore reduction (filling) during LixSi formation. In full cells, SPEAR prelithiation increases the initial coulombic efficiency (ICE) and accelerates SEI formation and stabilization with Li1.38Si reaching 99.4% coulombic efficiency (CE) by cycle 2.

Musgrove, Amanda [ORNL] (ORCID:0009000220910389)↗
DOE OSTI2020

Nonpassivated Silicon Anode Surface

A stable solid electrolyte interphase (SEI) has been proven to be a key enabler to most advanced battery chemistries, where the reactivity between the electrolyte and the anode operating beyond the electrolyte stability limits must be kinetically suppressed by such SEIs. The graphite anode used in state-of-the-art Li-ion batteries presents the most representative SEI example. Because of similar operation potentials between graphite and silicon (Si), a similar passivation mechanism has been thought to apply on the Si anode when using the same carbonate-based electrolytes. Herein, we found that the chemical formation process of a proto-SEI on Si is closely entangled with incessant SEI decomposition, detachment, and reparation, which lead to continuous lithium consumption. Using a special galvanostatic protocol designed to observe the SEI formation prior to Si lithiation, we were able to deconvolute the electrochemical formation of such dynamic SEI from the morphology and mechanical complexities of Si and showed that a pristine Si anode could not be fully passivated in carbonate-based electrolytes.

25 ENERGY STORAGE↗
DOE OSTI2022

Failure analysis and design principles of silicon-based lithium-ion batteries using micron-sized porous silicon/carbon composite

Significant progresses have been made to overcome the fundamental challenges in silicon (Si)-based lithium-ion batteries (LIBs). However, much less work have been reported on the design and failure analysis these batteries for practical applications. In this work, we analyzed various cell design parameters affecting the performance of pouch cells using micron-sized porous Si with nano-pore structure and coated by pitch-carbon (p-Si/C). The correlation among particle level, electrode level, and cell level properties, especially the effect of electrode density on the volumetric capacity density of Si anode and full batteries have been systematically investigated. It is found that the corrosion of p-Si/C particle surface is the main failure mechanisms on the eventual capacity loss, while Li plating on anode electrode surface is the main reason for the fast capacity loss in later stage of cycling. The volumetric capacity of Si anode highly depends on both electrode density and the Si content. Moreover, the prelithiation of Si anodes is found to increase energy density while decreasing cycle life of Si-based full cells. Finally, the pathways and strategies for adoption of micron-sized p-Si/C anodes in LIBs have been proposed for their practical applications.

25 ENERGY STORAGE↗
DOE OSTI2025

Reactivity of Carbonate Solvent Electrolytes on Lithium Silicon Anodes

Silicon (Si) is promising for lithium-ion battery (LIB) anodes due to their high theoretical capacity and low electrochemical potential. However, significant challenges remain, including severe volumetric expansion during cycling and the electrochemical instability of electrolytes, which leads to the formation of a nonuniform solid electrolyte interphase (SEI). To investigate SEI formation mechanisms, computational molecular dynamics simulations offer valuable insights. In this work, we examine the trajectories and charge transfer behavior of lithium hexafluorophosphate (LiPF 6 ) salt with various solvent compositions using density functional theory (DFT) and ab initio molecular dynamics (AIMD). Among the tested electrolyte systems, LiPF 6 with vinylene carbonate (VC) added to ethyl methyl carbonate (EMC) exhibits the lowest reactivity with the Si anode. In contrast, the effects of fluoroethylene carbonate (FEC) and VC depend on whether the primary solvent is EMC alone or a mixture of ethylene carbonate (EC) and EMC. Moreover, we show that electrolyte reactivity varies with the degree of lithiation of the Si anode (LiSi vs Li 15 Si 4 ) and under different charge states. To decouple electrolyte reactivity from surface effects, we analyze the dissociation and formation energies of individual species from solvated configurations. Overall, these first-principles-based findings provide a strategic foundation for electrolyte design to improve cycling stability and extend calendar life in LIBs using Si anodes.

37 INORGANIC, ORGANIC, PHYSICAL, AND ANALYTICAL CH↗
DOE OSTI2022

Developing an In-situ Formed Dynamic Protection Layer to Mitigate Lithium Interface Shifting: Preventing Dendrite Formation on Metallic Lithium Surface to Facilitate Long Cycle Life of Lithium Solid-State Batteries

After extensive research on various system, a fully lithiated Si anode material (Li 3.75 Si) was synthesized. The high energy density, long cycle life anode demonstrated no apparent dendrite growth in an all-solid-state Li battery. A flexible solid-state electrolyte film with a thickness less than 50 μm was developed. All-solid-state Li full batteries were built and tested with NMC811, organic, organosulfide and sulfur cathode. Energy density of 1140 Wh/Kg at material level and 376 Wh/Kg at electrode level were demonstrated for over 500 cycles and with no apparent dendrite formation on the Li anode.

25 ENERGY STORAGE↗
DOE OSTI2022

Coal-derived graphene foam and micron-sized silicon composite anodes for lithium-ion batteries

Silicon-based materials demonstrate significant potential as lithium-ion batteries (LIBs) anode, but their expansion and degradation present engineering design challenges for commercial application. In this study, a porous three-dimensional (3D) graphene and micron-sized silicon composite anode (Si@G foam) was synthesized using humic acid (HA) derived from coal as a graphene precursor. In-situ formation of graphene structure through reducing HA was confirmed by Raman spectra. The reduced HA (rHA) shows similar electrical conductivity compared to the commercial conductive carbon. SEM images depict a 3D skeleton of coal-derived graphene, with silicon particles distributed on the 3D graphene foam's internal surface. The Si@G composite-anode displays a good reversible capacity of ~656 mAh/g at a current density of 50 mA/g, as well as a high-rate capability of ~433 mAh/g at a current density of 800 mA/g, and outstanding cycling stability –89.8% capacity retention after 300 cycles, which is significantly higher than that of other foam structures. During lithiation and de-lithiation, the graphene foam serves as a matrix of electrical conductors and a volume expansion support for silicon. This 3D graphene network will be beneficial for developing advanced silicon-based anodes for high-performance LIBs.

25 ENERGY STORAGE↗
DOE OSTI2025

End of (3rd) Month Progress Report - PhD Committee

For the months of (May-August), the focus has been to: ● Comply and attend all mandatory LLNL training(s). ● Practice & gain experience, using a 3D printer for direct-ink writing application. ● Construct & Test Cu-Si anodes for battery application: - Si nanoparticles (<100 nm) is alloyed within a Cu-based current collector, via direct-ink writing. - Tuning the overall architecture of the current collector (to accommodate the volume expansion of Si more efficiently/ stabilize its kinetics - of active Si loss). - Based on the following designed configurations: tape-casted, 2D (spiral-square), and 3D (spiral-square/ zig-zag) structures; utilizing commercial-based Cu paste. - Fabricated (half-cell) coin-cells are currently cycling long-term. ● Synthesize new Cu-Si paste, to further tune the rheology properties, for further comparison with commercial Cu-based paste.

99 GENERAL AND MISCELLANEOUS↗
DOE OSTI2023

Characterization of Annealing-Induced Phase Segregation in Composite Silicon Anodes for Li-ion Batteries

Silicon (Si) anodes present a promising alternative to graphite anodes for lithium-ion batteries (LIBs), as Si has a greater specific capacity. However, one major constraint is the volumetric change of Si during lithiation that results in an unstable solid-electrolyte interphase (SEI), so Si-containing electrodes require the use of various strategies to mitigate these effects and improve performance. One such solution is the use of Si nanoparticles (NPs) that maximize the surface area to volume ratio. Here, we discuss electrodes made with Si NPs treated with polyethylene oxide (PEO) (for improving dispersion during processing), conductive carbon NPs, and P84 polyimide binder which shows significant impacts of annealing treatment on improvements of active material utilization, first cycle efficiency, and capacity retention with extensive cycling . We used air-free argon ion polishing to create electrode cross sections and imaged through the electrode thickness using atomic force microscopy (AFM)-based nano-electrical characterization of scanning spreading resistance microscopy (SSRM), nano-mechanical characterizations of contact resonance and force volume (CR-FV), and scanning electron microscopy-based energy dispersive x-ray spectroscopy (SEM-EDS). Results show that the Si and conductive carbon segregate into phases with a distinctive carbon-rich banded morphology that surrounds the Si-rich phase during annealing. In pristine electrodes, the carbon- and SEI-rich bands exhibit a higher electronic conductivity and a lower elastic modulus than the Si active material phase. These structures, as well as distinct electronic and mechanical properties, remain during cycling, suggesting an improvement of electrical conduction pathways and a mechanical strain buffer for active Si material expansion during cycling. This phase separation may be a major factor in the improvement seen in electrochemical performance due to annealing. Additionally, our nm-scale and multi-mode characterizations provide a novel route for understanding and improving energy storage devices, which is advantageous due to the highly inhomogeneous of composite electrodes in nm-mm scales.

ENERGY STORAGE↗
DOE OSTI2021

Silicon-Based Anodes for Long-Cycle-Life Lithium-ion Batteries

CVD process has been studied and optimized to achieve 2x scale up of porous Si anode materials with a clean process. The roles of CVD temperature, duration, C 2 H 2 gas pressure, and carrier gas have been optimized. It is found that LHCE (LHCE-1 and LHCE-4) can lead to more than 50% increase in the cycling stability of Si||NMC622 cells. LHCE-4 can also lead to smaller impedance increase and longer calendar life when tested in single layer pouch cells. These results are very helpful in the understanding of the Si based anode and further development of Si based Li ion batteries.

25 ENERGY STORAGE↗
DOE OSTI2024

Surface and Bulk Stabilization of Silicon Anodes with Mixed-Multivalent Additives: Ca(TFSI) 2 and Mg(TFSI) 2

Here, silicon is drawing attention as the upcoming anode material for the next generation of lithium-ion batteries due to its higher capacity compared to commercial graphite. However, silicon anions formed during lithiation are highly reactive with binder and electrolyte components creating an unstable SEI layer and limiting the calendar life of silicon anodes. The reactivity of lithium silicide and the formation of an unstable SEI layer is mitigated by utilizing the use of a mixture of Ca and Mg multivalent cations as an electrolyte additive for Si anodes to improve their calendar life. The effect of mixed salts on the bulk and surface of silicon anodes was studied by multiple structural characterization techniques. Ca and Mg ions in the electrolyte formed relatively thermodynamically stable quaternary Li-Ca-Mg-Si Zintl phases in an in-situ fashion and more stable and denser SEI layer on the Si particles. These in turn protect silicon particles against side reactions with electrolytes in a coin cell. The full cell with the mixed cation electrolyte demonstrates enhanced calendar life performance with lower measured current and current leakage than that of the baseline electrolyte due to reduced side reactions. Electron Microscopy, HRXRD, and solid-state NMR results showed that electrodes with mixed cations tended to have less cracking on the electrode surface compared to Si electrodes with Gen2 + FEC and the presence of mixed cations enhances cation migration and formation of quaternary Zintl phases stabilizing bulk and forming a more stable SEI.

25 ENERGY STORAGE↗
DOE OSTI2022

Exploring the Promise of Multifunctional “Zintl-Phase-Forming” Electrolytes for Si-Based Full Cells

Li-M-Si ternary Zintl phases have gained attention recently due to their high structural stability, which can improve the cycling stability compared to a bulk Si electrode. Adding multivalent cation salts (such as Mg 2+ and Ca 2+ ) in the electrolyte was proven to be a simple way to form Li-M-Si ternary phases in situ in Si-based Li-ion cells. To explore the promise of Zintl-phaseforming electrolytes, we systematically investigated their application in pouch cells via electrochemical and multiscale postmortem analysis. The introduction of multivalent cations, such as Mg 2+ , during charging can form Li x M y Si ternary phases. They can stabilize Si anions and reduce side reactions with electrolyte, improving the bulk stability. More importantly, Mg 2+ and Ca 2+ incorporate into interfacial side reactions and generate inorganic-rich solid- electrolyte interphase, thus enhancing the interfacial stability. Therefore, the full cells with Zintl-phase-forming electrolytes achieve higher capacity retentions at the C/3 rate after 100 cycles, compared to a baseline electrolyte. Additionally, strategies for mitigating the electrode-level fractures of Si were evaluated to make the best use of Zintl-phase-forming electrolytes. In conclusion, this work highlights the significance of synergistic impact of multifunctional additives to stabilize both bulk and interface chemistry in high-energy Si anode materials for Li-ion batteries.

25 ENERGY STORAGE↗