Improving creep resistance of Al-0.27Zr-0.08Sn (wt%) via cold swaging while maintaining high electrical conductivity
This study investigates the effect of mechanical cold work (0, 50, and 90% cross-sectional area reduction via swaging) on the creep properties of cast aluminum alloys with high electrical conductivity including high-purity Al (HP-Al), Al-0.15Zr (Al-Zr), and Al-0.27Zr-0.08Sn (Al-Zr-Sn, wt%). The Al-Zr alloy is strengthened by Zr in solid solution while the Al-Zr-Sn alloy is additionally strengthened by Al3Zr nanoprecipitates (8 nm diameter). After 90% cold swaging, the alloys exhibit grains elongated along the swaging direction with their widths ranging between 8 and 152 μm perpendicular to the swaging direction. Creep testing at 200 °C shows that the minimum creep rate of all 90% swaged alloys shows high sensitivity to stress, which can be modeled via a threshold stress σth. Increasing swaging magnitude from 0 to 50 to 90% in Al-Zr-Sn improves the creep resistance without reducing electrical conductivity. The formation of subgrains, increased dislocation density, and columnar grain structure in swaged alloys all enhance creep resistance. HP-Al swaged to 90% exhibits much lower creep resistance (σth = 18 MPa) due to subgrain coarsening and the absence of precipitates compared to Al-Zr (σth = 40 MPa) and Al-Zr-Sn (σth = 40 MPa), which maintain stable subgrain structures and benefit from solid solution strengthening and Al3Zr nanoprecipitates, respectively. Although Al3Zr precipitates are known to stabilize the deformed microstructure by pinning grain-boundaries, this work demonstrates that Zr in solid solution alone can effectively stabilize the deformed microstructure resulting in enhanced creep resistance. This effect of Zr solute on stabilizing grain boundaries for creep performance was not previously well-defined in the literature. Despite similar creep performances of Al-Zr and Al-Zr-Sn, the latter shows 70% higher room-temperature microhardness and slightly improved electrical conductivity (56%IACS (International Annealed Copper Standard) vs. 57%IACS, respectively). This work provides new insights into creep mechanisms of cold-worked Al–Zr alloys that will guide the design of heat-resistant Al conductors for high-demand applications.