Strength, plasticity, and spin transition of Fe-N compounds in planetary cores
Elastic and plastic properties of Fe-light element alloys and compounds are needed to determine the compositions and dynamics of planetary cores. Elastic strength and plastic deformation mechanisms and their relationship to electronic properties of ε-Fe 7 N 3 and γ’-Fe 4 N mixture were investigated by x-ray diffraction and x-ray emission spectroscopy in the diamond anvil cell from 1 bar up to 60 GPa. X-ray diffraction shows that ε-Fe 7 N 3 reaches a pressure of 15–20 GPa before undergoing bulk plasticity at a differential stress of 4.4–10.4 GPa. ε-Fe 7 N 3 is stronger than γ’-Fe 4 N and hcp-Fe which achieve a flow stress of 1.5–3.6 GPa at 10–15 GPa and 2–3 GPa at ~20 GPa, respectively. X-ray emission spectroscopy shows that a decrease in electronic spin moment begins before and completes after plastic flow onset for each nitride, suggesting that pressure-driven changes in electronic arrangement do not trigger a plastic response although they may modify the strength and plastic behavior of Fe-N compounds. Plastic deformation in ε-Fe 7 N 3 and hcp-Fe results in a preferred orientation of (0001) normal to maximum compression, while γ’-Fe 4 N develops a maximum in the (110). Furthermore, these observations may be combined with measurements of elasticity to model seismic properties of cores of small planetary bodies such as Mars, Mercury, and the Moon.