DOE OSTI2022

Effect of Cooling Rate on Nano-Eutectic Formation in Laser Surface Remelted and Rare Earth Modified Hypereutectic Al-20Si Alloys

Laser Surface Remelting (LSR) was applied to arc-melted Al-20Si-0.2Sr, Al-20Si-0.2Ce, and Al-20Si hypereutectic alloys to refine microstructures. Experiments revealed that microstructures in the melt pool varied from fully eutectic to a mixture of Al dendrites and inter-dendritic eutectic. We calculated cooling rates using the Eagar-Tsai model and correlated cooling rates with characteristic microstructures, revealing that a cooling rate on the order of 104 K/s could lead to maximized fully eutectic microstructure morphology. Due to rapid solidification, the Si composition in the LSR eutectic was measured at 18.2 wt.%, higher than the equilibrium eutectic composition of 12.6 wt.%Si. Compared to Al-20Si, Ce addition had no significant effect on the volume fraction of the fully eutectic structure but refined Si fibers to approximately 30 nm in diameter. Sr addition did not further refine the diameter of eutectic Si fibers compared to Al-20Si but increased the volume fraction of the fully eutectic microstructure morphology. The refinement ratio (φ) of the Si fiber diameter from the bottom of the melt pool to the surface for the three alloys was similar, at around 28%. The established correlation between the cooling rate and the size and morphology of the microstructure within the melt pool will enable tailoring of the microstructure in laser-processed as well as deposited alloys for high strength and plasticity.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Ultrafine-grained Fe-TiB 2 high-modulus nanocomposite steel with high strength and isotropic mechanical properties by laser powder bed fusion

Fe-TiB 2 metal matrix composite, also called high-modulus steels (HMSs), are of great interest for applications in fuel-efficient transportation infrastructure, aerospace, and wear industries due to their high specific stiffness and yield strength. However, conventional cast Fe-TiB 2 HMSs often contain coarse and sharp-edged TiB 2 particles which easily trigger premature cracking during loading. Here, we synthesized a Fe-TiB 2 nanocomposite HMS via laser powder bed fusion (LPBF) additive manufacturing of mixed micro-sized powders of Fe, Ti, and Fe 2 B. We investigated the microstructure formation and mechanical behavior of the Fe-TiB 2 HMS. We found that in situ chemical reaction of Ti and Fe 2 B enables the formation of TiB 2 particles at nanoscale during rapid solidification of LPBF. These nanoscale TiB 2 particles can serve as heterogeneous nucleation sites and promote the formation of ultrafine and equiaxed α-Fe grains with random crystallographic textures, which differ from many other additively manufactured (AM) metal alloys characteristic of strong crystallographic textures. As such, isotropic mechanical properties were achieved in the AM Fe-TiB 2 nanocomposite HMS with a high elastic modulus of ~ 240 GPa, an exceptional yield strength of ~ 1450 MPa, and a large plasticity of ~ 20% under compression. Quantitative analysis reveals that the high yield strength primarily originates from strengthening contributions of the ultrafine grains with an average grain size of ~450 nm, the nanoscale TiB 2 reinforcing particles of 20–180 nm, and a high density of printing-induced dislocations of the order of 10 15 m –2 . In situ synchrotron high-energy X-ray diffraction unveils the load partitioning from the softer α-Fe matrix to the stiffer and stronger TiB 2 nanoparticles, contributing to the sustained strain hardening during compression. Our work not only provides a general pathway for achieving high-performance metal matrix nanocomposites by in situ chemical reaction and precipitation of ceramic nanoparticles during additive manufacturing, but also offers mechanistic insights into the deformation mechanism of nanoparticle-reinforced HMS composites.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Multiscale hierarchical and heterogeneous mechanical response of additively manufactured novel Al alloy investigated by high-resolution nanoindentation mapping

Smart alloying and microstructural engineering mitigate challenges associated with laser-powder bed fusion additive manufacturing (L-PBFAM). A novel Al–Ni–Ti–Zr alloy utilized grain refinement by heterogeneous nucleation and eutectic solidification to achieve superior performance-printability synergy. Conventional mechanical testing cannot delineate complex micromechanics of such alloys. This study combined multiscale nanomechanical and microstructural mapping to illustrate mechanical signatures associated with hierarchical heat distribution and rapid solidification of L-PBFAM. The disproportionate hardening effect imparted by Al 3 (Ti,Zr) precipitates in the pool boundaries and the semi-solid zone was successfully demonstrated. Nanomechanical response associated with heterogeneity in particle volume fraction and coherency across melt pool was interpreted from nanoindentation force–displacement curves. The hardness map effectively delineated the weakest and strongest sections in the pool with microscopic accuracy. The presented approach serves as a high throughput methodology to establish the chemistry-processing-microstructure-properties correlation of newly designed alloys for L-PBFAM.

36 MATERIALS SCIENCE↗
DOE OSTI2023

Thermal Conductivity of AM Fabricated Stainless Steel 316L Part

Thermal properties are an integral part of many diverse engineering applications, and additive manufacturing (AM), particularly laser powder bed fusion (LPBF) is shown to affect thermal properties due to the laser processing parameters. For 316L stainless steel, there is little prior research to determine the effects of the process on thermal properties. In this work, the temperature gradient is shown to create uniform, chess board-like distributions of grains in the build direction. These zones create dislocations which were visualized with EBSD techniques. Processing parameters cause hierarchal grain size distribution, with localized concentrations of small grains and large grains. Thermomechanical stresses in the rapid solidification increases dislocation density during grain formation. Previous research shows a higher density of dislocations decreases local thermal conductivity. Local and bulk thermal conductivity are shown in this work to have statistically lowered values to an average of 10-12 W/m-K compared to 14 W/m-K for conventional 316L.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Strategies for Fabricating Molybdenum Structures Using Laser Powder Bed Fusion

Advances in manufacturing techniques are viewed as enabling technologies for development of high performance nuclear fuel forms that couple high uranium density with improvements to key properties such as thermal conductivity unattainable through conventional fabrication routes. Additive manufacturing (AM) enables the fabrication of complex fuel geometries that are difficult or impossible to achieve using conventional manufacturing methods. Melting-based AM processes, such as laser powder bed fusion (LPBF), provide high geometric resolution (>200 µm depending on the feature) across a variety of metal alloys, including those suitable for high-temperature fuel cladding applications, such as Nb, W, and Mo. Molybdenum is particularly attractive due to its high thermal conductivity, low thermal expansion, and excellent mechanical stability at elevated temperatures. However, its high melting temperature and brittle nature at low temperatures pose significant challenges during LPBF processing. Rapid solidification inherent to LPBF induces high residual stresses, often leading to post-solidification cracking, which limits the manufacturability of Mo components via this method.

11 NUCLEAR FUEL CYCLE AND FUEL MATERIALS↗
DOE OSTI2026

Which way does the dendrite grow? Competition among epitaxy, preferred growth direction, and thermal gradients in powder bed fusion additive manufacturing

The as-processed microstructure of metal alloy parts manufactured through laser powder bed fusion (LPBF) is heavily derived from the cellular dendritic solidification. The growth direction of dendrites within the melt pool is determined through competition among epitaxial growth, preferred growth directions, and maximum thermal gradients. However, the dominant factor and the specific role of each in developing melt pool microstructures remain unknown. Here, in this study, we performed single laser track scans on an SS316L single crystal substrate and combined experimental characterization of microstructure and crystal orientations with Computational Fluid Dynamics simulations of thermal gradients to evaluate the role of each factor in determining dendritic growth direction and evolution. Our results reveal that epitaxial growth dominates microstructure development by preferentially growing along a single 〈100〉 variant of the single crystal substrate adjacent to the melt pool boundary. Under LPBF’s highly curved and rapidly evolving thermal field, this preferential dendrite variant selection and its continued growth from the melt pool boundary to the centerline are governed by the local temperature gradient magnitude at the solid-liquid interface, rather than by the instantaneous maximum temperature gradient direction alone. Using these findings, we successfully predict changes in the dendrite growth direction with changing laser scan direction on a single crystal substrate, and show that the geometric melt pool centerline can deviate from the microstructural centerline because asymmetric local temperature gradient magnitudes transiently limit growth, resulting in different dendrite travel distances on each side of the melt pool.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Melting and solidification dynamics during laser melting of reaction-based metal matrix composites uncovered by in-situ synchrotron X-ray diffraction

Laser additive manufacturing (AM) of reaction-based metal matrix composites (MMCs) involves highly complex and non-equilibrium material transformation behavior, including melting, dissolution, precipitation, and solidification. Yet, the dynamics and interplay of these phase transformation processes remain poorly understood, posing substantial challenges in identifying the microstructure formation mechanism, and predicting and controlling the microstructure in the printed parts. Here, in this study, we performed the in-situ X-ray diffraction experiment to characterize the phase evolution dynamics of the 316L + 10 vol.%TiC system during laser melting, which provides direct and quantitative insights of the complex phase reaction and evolution dynamics under rapid heating and cooling conditions relevant to additive manufacturing of reaction-based MMCs. Further in-depth thermodynamic and kinetic calculations revealed that most of the phase evolution behavior observed in the in-situ X-ray diffraction experiment cannot be solely explained by widely used equilibrium thermodynamic models, and diffusion-controlled nonequilibrium dissolution and precipitation kinetics must be considered to elucidate the complex phase evolution behavior, including incomplete TiC dissolution, and three-step TiC precipitation. The three distinct types of precipitates generate unique hierarchical TiC micro- and nanostructures, which enhances the yield strength from 513 MPa to 877 MPa by 71 %, tensile strength from 628 MPa to 1054 MPa by 68 %, and Young's modulus from 193 GPa to 221 GPa by 14 %. The findings of our research provide the knowledge foundation for the design of unique microstructures and advanced MMC materials through laser AM.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Nanoscale interfacial melting enables bonding during high velocity microparticle impacts

Melting during high-velocity particle impact has been understood to be typically detrimental to bonding by lowering the strength at the interface and promoting rebound before solidification can occur. Here we establish a possible remedy to this challenge: by dramatically restricting the volume of molten material, its resolidification is accelerated, effectively forming a nanoscale, braze-type joint during impact. In-situ single particle impact imaging is combined with post-mortem structural and chemical analyses to reveal a regime where adhesion is governed not by extensive plastic deformation, but by the kinetics of melt layer resolidification. Furthermore, these findings redefine the role of melting in impact-based processes, establishing transient melting and rapid solidification as a viable strategy for engineering successful adhesion events.

Additive manufacturing↗
DOE OSTI2025

Quantification and prediction of solidification textures under additive manufacturing conditions

Crystallographic textures are a major determinant of the macroscale anisotropic properties of polycrystalline metallic alloys produced in a wide range of additive manufacturing (AM) processes. Here, we introduce a statistical method that can accurately quantify the degree of orientational order of textures despite the large random fluctuations in the orientation of individual grains inherent in AM processes. The method, demonstrated for laser and resolidification of AlSi thin films, extends Z-scoring to a dynamical regime to assess the statistical significance of observed textures compared to randomly generated ones at different stages of solidification. We further show that, combined with phase-field modeling, this method can be used to infer fundamental anisotropic properties of the solid-liquid interface that are essential for texture prediction, and are compared here to the results of atomistic simulations. In addition, phase-field modeling reveals that, even at rapid AM solidification rates, the observed 〈110〉-dominated textures in the AlSi thin films are controlled predominantly by the anisotropy of the interface free-energy and sheds light on the physical mechanism of grain competition. These results significantly enhance both the existing tools for the quantification and prediction of AM crystallographic textures and our basic understanding of their formation.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Laser Powder Directed Energy Deposition of Steels for Nuclear Applications

This comprehensive investigation examines the structure–property relationships in two nuclear alloy systems—Alloy 709 (A709) austenitic stainless steel and Grade 92 (G-92) ferritic/martensitic (F/M) steel—manufactured via directed energy deposition (DED) for sodium-cooled fast reactor applications. This study establishes the fundamental mechanisms for controlling microstructures for optimizing the mechanical performance of additively manufactured nuclear materials through systematic heat treatment optimization and multiscale characterization. As-deposited A709 steel develops a complex multiscale strengthening architecture consisting of a fine cellular solidification structure with diameter of 2-3 µm within10–50 µm grains, elevated dislocation densities from rapid thermal cycling, and grain boundary precipitates that activate concurrent Hall–Petch, dislocation, and precipitation hardening mechanisms to achieve exceptional properties [yield strength (YS): 603 MPa, ultimate tensile strength (UTS): 844 MPa, Vickers hardness: 220 HV] that achieve a 44% superior strength compared to that of the wrought material. Heat treatments produce different results. Solution annealing (SA) dissolves the cellular structure and reduces the hardness to 190 HV. Precipitation treatment (PT) keeps the cellular structure but adds carbides, allowing the hardness to reach 205 HV. The best approach combines both treatments (SA+PT) and creates uniform precipitate distributions with M 23 C 6 carbides at the grain boundaries and MX carbonitrides in the matrix, achieving a hardness of 195 HV. However, directional differences persist, with a 12%–15% strength variation between orientations due to the inherited layered microstructural architecture that survives aggressive heat treatment. While tensile testing at 550°C demonstrates 40%–50% thermal softening with dynamic strain aging, DED A709 steel still maintains a 71% higher YS than that of the wrought material. Ion irradiation studies (100–400 dpa) of DED A709 steel reveal progressive radiation damage with increasing void density and radiation-induced segregation causing nickel enrichment and chromium depletion, which will ultimately compromise mechanical properties. As-deposited G-92 exhibits exceptional strength (UTS: 1650–1700 MPa, 430 HV) through a complex microstructure containing both ferrite and martensite phases, a high geometrically necessary dislocation (GND) density (17.04×10 14 /m 2 ), and fine carbides. Heat treatments create distinct changes. Normalizing produces fresh martensite with the highest hardness (460 HV) and an increased GND density (20.23×10 14 /m 2 ). Tempering develops dual precipitation systems and reduces the hardness to 290 HV. The optimal approach uses sequential normalizing plus tempering, achieving balanced properties with the lowest hardness (250 HV) and a reduced GND density (11.01×10 14 /m 2 ). A processing-dependent anisotropy is observed: horizontal specimens achieve superior ductile behavior, while vertical specimens exhibit brittle failure. A tempering heat treatment successfully mitigates this anisotropic behavior by transforming the hard martensitic as-deposited structure into tempered martensite enabling both horizontal and vertical specimens to exhibit similar stress–strain characteristics with visible necking behavior. Remarkably, testing at 550°C reveals a reversal in the anisotropy, where as-deposited specimens achieve near isotropy with superior thermal stability (a 15%–20% strength reduction), while tempered specimens develop an orientation dependence with a 25%–30% strength reduction. Both alloy systems demonstrate that DED processing creates specimens with a superior strength through refined microstructural features, though with distinct strengthening mechanisms—austenitic through cellular structures and precipitates versus F/M through phase transformations and precipitates. Heat treatment optimization requires alloy-specific approaches, with A709 benefiting from controlled precipitation while G-92 requires careful phase transformation control. The results show that DED manufacturing can produce nuclear materials with exceptional performance, but directional effects and temperature-dependent behavior must be carefully considered for reactor component design and qualification.

22 GENERAL STUDIES OF NUCLEAR REACTORS↗
DOE OSTI2023

Freeform thermoelectrics in single-step manufacturing: additive manufacturing of bismuth-telluride thermoelectrics

The project succeeded in producing crack-free Bismuth Telluride thermoelectric parts with density exceeding 98% through laser powder bed fusion (LPBF) additive manufacturing (AM). This greatly exceeded the highest previously reported density of 88% and is the highest among all semiconducting materials processed by LPBF. The additively manufactured material shows comparable Seebeck coefficient as conventional form and can be made into complex geometries with reduced material loss. On the other hand, measured properties are dramatically sensitive to the AM process parameters used, such that with identical composition, the Seebeck coefficient can be controllably tuned from +120 µV/K to -207 µV/K, which means the material switches between an n-type to a p-type semiconductor depending on processing. These changes are accompanied by significant differences in the as-processed microstructure due to rapid solidification. A machine learning protocol was developed and greatly reduced the experimental burden of the project, reducing the typical process optimization period of 2 years to 6 months. The project was fully successful in the objective of producing defect-free, complex geometry of bismuth-telluride parts through LPBF, but only partially successful in achieving performance goals. First, cost reduction of manufacturing, as measured by material waste, was successfully reduced by up to 70% compared to conventional manufacturing methods. This exceeded the proposed 30% reduction in materials waste needed to reach the 20% cost reduction goal of the project. On the other hand, the device performance, as measured by Seebeck coefficient, failed to reach the 40% improvement in efficiency. Rather, we observe comparable Seebeck coefficient between AM samples and conventionally processed counterparts. The device-level efficiency improvement does exceed 40% for complex geometry samples due to shape-induced increase in temperature gradients, but this was not the originally proposed metric. The machine learning approach developed in this project greatly accelerated the process optimization and can be adopted for fast development of AM processing parameters for other brittle and otherwise difficult-to-print materials. For the public, we deliver an efficient and widely adoptable process for incorporating waste-heat harvesting thermoelectric devices in both industrial and commercial heat exchangers. The geometric flexibility allows the capturing device to conform to the shape of the heat source to improve the system-level conversion efficiency. The technique can be deployed on any commercial LBPF systems with zero modifications, thus poses minimal adoption barrier for any manufacturer that already employed AM technology. Beyond bismuth-telluride, the machine-learning guided optimization protocol can be used in the future to reduce both the time and cost of process development for AM of other energy conversion and harvesting materials.

36 MATERIALS SCIENCE↗
DOE OSTI2020

Microstructure and properties of a high temperature Al–Ce–Mn alloy produced by additive manufacturing

An Al–10Ce-8Mn (wt%) alloy was designed and fabricated by laser powder bed fusion additive manufacturing (AM). The rapid cooling rates of the AM process produced a refined microstructure with a large fraction of reinforcing intermetallic phases. The tensile properties of the alloy were characterized in the as-fabricated state and following thermal exposure. The properties of the as-fabricated microstructure showed exceptional high-temperature performance and strength retention at elevated temperatures up to 400 °C relative to benchmark wrought Al and AM Al alloy properties. Characterization of the microstructure and thermodynamic modeling of the ternary Al–Ce–Mn system rationalized the solidification and solid-state phase transformations. Finally, analysis of the relevant strengthening mechanisms for both the as-fabricated and thermally exposed conditions was performed.

36 MATERIALS SCIENCE↗
DOE OSTI2022

In Situ X-ray Radiography and Computational Modeling to Predict Grain Morphology in $\beta$-Titanium during Simulated Additive Manufacturing

The continued development of metal additive manufacturing (AM) has expanded the engineering metallic alloys for which these processes may be applied, including beta-titanium alloys with desirable strength-to-density ratios. To understand the response of beta-titanium alloys to AM processing, solidification and microstructure evolution needs to be investigated. In particular, thermal gradients (Gs) and solidification velocities (Vs) experienced during AM are needed to link processing to microstructure development, including the columnar-to-equiaxed transition (CET). In this work, in situ synchrotron X-ray radiography of the beta-titanium alloy Ti-10V-2Fe-3Al (wt.%) (Ti-1023) during simulated laser-powder bed fusion (L-PBF) was performed at the Advanced Photon Source at Argonne National Laboratory, allowing for direct determination of Vs. Two different computational modeling tools, SYSWELD and FLOW-3D, were utilized to investigate the solidification conditions of spot and raster melt scenarios. The predicted Vs obtained from both pieces of computational software exhibited good agreement with those obtained from in situ synchrotron X-ray radiography measurements. The model that accounted for fluid flow also showed the ability to predict trends unobservable in the in situ synchrotron X-ray radiography, but are known to occur during rapid solidification. A CET model for Ti-1023 was also developed using the Kurz–Giovanola–Trivedi model, which allowed modeled Gs and Vs to be compared in the context of predicted grain morphologies. Both pieces of software were in agreement for morphology predictions of spot-melts, but drastically differed for raster predictions. The discrepancy is attributable to the difference in accounting for fluid flow, resulting in magnitude-different values of Gs for similar Vs.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Microstructural evaluation of thin-wall sections of 316L stainless steel produced by laser powder-bed fusion processing

Laser powder bed fusion (LBPF) is a method of additive manufacturing (AM) that offers a means to fabricate complex components with features which rely upon the mechanical integrity of thin-wall (less than 0.4 mm thick) structures. The microstructure of a 316L AM thin wall is investigated as metallographically prepared from a cylindrical shell. Optimization is pursued through mechanical polishing and chemical etching to minimize the effects of surface roughness. Microanalysis measurements of the sectioned component reveal the sample has high microstructural fidelity, uniform composition and phase content across grain as well as powder layer boundaries within the thin wall. The results are attributed to a uniform thermal gradient at the part scale during rapid solidification.

36 MATERIALS SCIENCE↗
DOE OSTI2024

Critical role of slags in pitting corrosion of additively manufactured stainless steel in simulated seawater

Abstract Pitting corrosion in seawater is one of the most difficult forms of corrosion to identify and control. A workhorse material for marine applications, 316L stainless steel (316L SS) is known to balance resistance to pitting with good mechanical properties. The advent of additive manufacturing (AM), particularly laser powder bed fusion (LPBF), has prompted numerous microstructural and mechanical investigations of LPBF 316L SS; however, the origins of pitting corrosion on as-built surfaces is unknown, despite their utmost importance for certification of LPBF 316L SS prior to fielding. Here, we show that Mn-rich silicate slags are responsible for pitting of the as-built LPBF material in sodium chloride due to their introduction of deleterious defects such as cracks or surface oxide heterogeneities. In addition, we explain how slags are formed in the liquid metal and deposited at the as-built surfaces using high-fidelity melt pool simulations. Our work uncovers how LPBF changes surface oxides due to rapid solidification and high-temperature oxidation, leading to fundamentally different pitting corrosion mechanisms.

36 MATERIALS SCIENCE↗
DOE OSTI2022

Predictive Tools for Customizing Heat Treatment of Additively Manufactured Aerospace Components

Laser-bed powder fusion (LBPF) additive manufacturing is increasingly being used to produce components of complex geometries using the Ni-base superalloy Inconel 718. The composition and the microstructure of the alloy are currently well optimized for wrought components made using conventional manufacturing processes such as rolling, forging, extrusion, etc. The attractive mechanical properties of the alloy result from the underlying austenitic matrix with fine equiaxed grains, and a high density and uniform distribution of the precipitation hardening phase, γ". Heat treatment steps such as homogenization, solutioning and aging are well documented for the wrought alloy. However, when the same wrought alloy compositions are used for the additive manufacturing (AM) processes, the asprocessed microstructure is significantly different, because of the different thermal history associated with LBPF, including rapid solidification and multiple temperature excursions that lead to multiple re-melting and reheating in the solid state. Rapid solidification introduces potential non-equilibrium effects at the moving solid-liquid interfaces that impact the extent of solute segregation, as well as the morphology of the dendritic grains that form. In order to recover the target mechanical properties, AM components have to undergo post-process heat treatments. However, such heat treatments have to be custom designed for the AM process and the component geometry because of the expected vast differences in the microstructure at various locations of a component with complex geometry. The homogenization and precipitation steps should be optimized for the component so that target mechanical properties can be obtained throughout the part. The objective of this research is to utilize High Performance Computing in phase field simulations of microstructure evolution during post-processing of AM components. The physics-based modeling will be beneficial in reducing the experimental effort required for heat treatment process selection, optimization, and certification, thus leading to a significant reduction in energy consumption for AM and post-processing heat treatment. The optimization study will help identify heat treatments steps that are critical for development of a final desired microstructure with the minimum energy input. This combined with shortening of the production cycle (time-to-market) by reducing the number of failed parts (property targets), and reduction in the number of iterations for process optimization, will enable 30-40% savings in the energy costs. Phase field simulations of the degree of homogenization and the effect of local matrix composition on the nucleation and growth of competing precipitating phases were performed using the Microstructure Evolution Using Massively Parallel Phase Field Simulations code developed in-house at the Oak Ridge National Laboratory. The simulations were able to successfully capture the kinetics of nucleation and growth, and morphologies of various precipitating phases as a function of local matrix compositions and composition gradients characteristic of local microstructures arising from location-dependent variations in the thermal conditions. Future work will involve extending the simulations to a length scale consisting of multiple dendrites, so that the effect of homogenization on the coarsening of the dendrites can be simulated and used as an additional input to the optimization of the heat treatment process.

36 MATERIALS SCIENCE↗
DOE OSTI2025

Microstructural evolution and phase stability in Nb-containing interstitial Fe-Mn-Co-Cr-C high-entropy alloys: An in-situ synchrotron X-ray diffraction study during laser melting

The influence of Nb on phase stability and microstructural evolution in an interstitial Fe-Mn-Co-Cr-C high-entropy alloy was investigated using in-situ synchrotron X-ray diffraction (SXRD) during laser melting. Scheil-Gulliver simulations predict the formation of σ and γ-f.c.c. phases in all three alloys, along with NbC in Nb-containing compositions. SXRD confirmed the presence of most predicted phases, but the σ phase was absent. Nb promotes crystallite refinement and increases dislocation density, though excessive additions reduce refinement efficiency due to solubility limits and secondary phase formation. Furthermore, Nb addition also enhances ε-h.c.p. phase formation by reducing stacking fault energy through NbC-induced carbon depletion. Analysis of intensity peak evolution reveals that Nb alters preferred grain orientations, reducing {111} γ intensity while enhancing {220} γ , leading to a more isotropic grain distribution. Overall, Nb plays a key role in phase selection, microstructure refinement, and preferred orientation evolution, allowing the tailored microstructure of high-entropy alloys via rapid solidification.

Interstitial high entropy alloys↗
DOE OSTI2025

Massively parallel phase-field simulations targeting exascale

The interface thickness in the phase-field (PF) method limits its simulation scales. Consequently, large-scale PF simulations become prohibitively expensive for resolving the extremely fine microstructures that typically form during rapid solidification processing. This challenge is significant in predicting microstructure evolution in metal additive manufacturing and has been identified by the United States Department of Energy’s Exascale Computing Project. Here, to address this, we develop a multi-GPU and MPI-based massively parallel simulation code, utilizing state-of-the-art algorithms, software, and libraries, for large-scale three-dimensional (3D) PF simulations. We report the first GPU-parallel PF simulations on Frontier (currently the second TOP500 exascale cluster) and Summit machines, taking dendritic growth as an example problem. We evaluate the parallel performance of our implementation using scaling studies with more than 24 000 GPUs (among the largest known computations to date) and the acceleration performance using large-scale simulations of dendritic growth in 3D. Finally, massively parallel GPUs in these supercomputers enabled the first coupled multiscale simulations of laser melting and subsequent dendritic solidification on the scale of a full melt-pool, demonstrating the feasibility of performing PF simulations with a point total over 2 billion grid points within an acceptable time.

Exascale↗