DOE OSTI2025

Novel Zwitterionic Polyurethane-in-Salt Electrolytes with High Ion Conductivity, Elasticity, and Adhesion for High-Performance Solid-State Lithium Metal Batteries

This study presents a novel polymer-in-salt (PIS) zwitterionic polyurethane-based solid polymer electrolyte (zPU-SPE) that offers high ionic conductivity, strong interaction with electrodes, and excellent mechanical and electrochemical stabilities, making it promising for high-performance all solid-state lithium batteries (ASSLBs). The zPU-SPE exhibits remarkable lithium-ion (Li+) conductivity (3.7 × 10⁻⁴ S cm−1 at 25 °C), enabled by exceptionally high salt loading of up to 90 wt.% (12.6 molar ratio of Li salt to polymer unit) without phase separation. It addresses the limitations of conventional SPEs by combining high ionic conductivity with a Li+ transference number of 0.44, achieved through the incorporation of zwitterionic groups that enhance ion dissociation and transport. The high surface energy (338.4 J m−2) and elasticity ensure excellent adhesion to Li anodes, reducing interfacial resistance and ensuring uniform Li+ flux. When tested in Li||zPU||LiFePO₄ and Li||zPU||S/C cells, the zPU-SPE demonstrated remarkable cycling stability, retaining 76% capacity after 2000 cycles with the LiFePO4 cathode, and achieving 84% capacity retention after 300 cycles with the S/C cathode. Molecular simulations and a range of experimental characterizations confirm the superior structural organization of the zPU matrix, contributing to its outstanding electrochemical performance. The findings strongly suggest that zPU-SPE is a promising candidate for next-generation ASSLBs.

Wang, Kun↗

DOE OSTI2023

2,5‐Dimercapto‐1,3,4‐Thiadiazole (DMCT)‐Based Polymers for Rechargeable Metal–Sulfur Batteries

Organosulfur materials are a sustainable alternative to the present-day layered oxide cathodes in lithium-based batteries. One such organosulfur material that was intensely explored from the 1990s to early 2010s is 2,5-dimercapto-1,3,4-thiadiazole (DMCT). However, research interest declined as the electrode reactions with DMCT were assumed to be too sluggish to be practical. Armed with the advances in metal–sulfur batteries, we revisit DMCT-based materials in the form of poly[tetrathio-2,5-(1,3,4-thiadiazole)], referred to as pDMCT-S. With an appropriate choice of electrode design and electrolyte, pDMCT-S cathode paired with a Li-metal anode shows a capacity of 715 mA h g −1 and a Coulombic efficiency of 97.7% at a C/10 rate, thus quelling the concerns of sluggish reactions. Surprisingly, pDMCT-S shows significantly improved long-term cyclability compared to a sulfur cathode. Investigations into the origin of the stability reveals that the discharge product Li-DMCT in its mesomeric form can strongly bind to polysulfides, preventing their dissolution into the electrolyte and shuttling. This unique mechanism solves a critical problem faced by sulfur cathodes. Encouragingly, this mechanism results in a stable performance of pDMCT-S with Na-metal cells as well. In conclusion, this study opens the potential for exploring other organic materials that have inherent polysulfide sequestering capabilities, enabling long-life metal–sulfur batteries.

2,5-dimercapto-1,3,4-thiadiazole↗

DOE OSTI2024

Eliminating chemo-mechanical degradation of lithium solid-state battery cathodes during >4.5 V cycling using amorphous Nb2O5 coatings

Abstract Lithium solid-state batteries offer improved safety and energy density. However, the limited stability of solid electrolytes (SEs), as well as irreversible structural and chemical changes in the cathode active material, can result in inferior electrochemical performance, particularly during high-voltage cycling (>4.3 V vs Li/Li + ). Therefore, new materials and strategies are needed to stabilize the cathode/SE interface and preserve the cathode material structure during high-voltage cycling. Here, we introduce a thin (~5 nm) conformal coating of amorphous Nb 2 O 5 on single-crystal LiNi 0.5 Mn 0.3 Co 0.2 O 2 cathode particles using rotary-bed atomic layer deposition (ALD). Full cells with Li 4 Ti 5 O 12 anodes and Nb 2 O 5 -coated cathodes demonstrate a higher initial Coulombic efficiency of 91.6% ± 0.5% compared to 82.2% ± 0.3% for the uncoated samples, along with improved rate capability (10x higher accessible capacity at 2C rate) and remarkable capacity retention during extended cycling (99.4% after 500 cycles at 4.7 V vs Li/Li + ). These improvements are associated with reduced cell polarization and interfacial impedance for the coated samples. Post-cycling electron microscopy analysis reveals that the Nb 2 O 5 coating remains intact and prevents the formation of spinel and rock-salt phases, which eliminates intra-particle cracking of the single-crystal cathode material. These findings demonstrate a potential pathway towards stable and high-performance solid-state batteries during high-voltage operation.

Science & Technology - Other Topics↗

DOE OSTI2026

Liquified SO 2 induced solid/cathode electrolyte interphase for lithium ion batteries

Formation of robust solid/cathode electrolyte interphases (S/CEI) is vital for long-term stability and high-performance operation of lithium-ion batteries (LIBs), particularly under high voltage regimes. However, engineering electrochemically stable S/CEIs that effectively suppress interfacial side reactions remains a key challenge. Herein, we introduce a liquefied sulfur dioxide (SO 2 )– ionic liquid complex as a fluorine-free multifunctional electrolyte additive for the first time that significantly improves the formation of sulfate/sulfite-rich S/CEI layers at both graphite and NMC811 interfaces. The unique SO 2 -N coordination with a 1,2,4-triazolide-based ionic liquid enables homogeneous SO 2 dissolution, resulting in controlled SO 2 decomposition during the initial electrochemical cycle. This decomposition yields sulfur-rich interphase species that stabilize the electrolyte-electrode interface, reduce impedance growth, and lessen electrolyte decomposition. Electrochemical tests show significantly improved cycle life, reduced polarization, and increased Coulombic efficiency for both anodes and cathodes. XPS confirms the presence of SO 2 -derived surface species that contribute to interfacial stability. In conclusion, this approach highlights a new direction for interphase engineering using liquefied gas additives and opens pathways for sulfur-based S/CEI chemistry in advanced battery systems.

Graphite↗

DOE OSTI2024

Hydrogen Production and Li-Ion Battery Performance with MoS2-SiNWs-SWNTs@ZnONPs Nanocomposites

This study explores the hydrogen generation potential via water-splitting reactions under UV-vis radiation by using a synergistic assembly of ZnO nanoparticles integrated with MoS2, single-walled carbon nanotubes (SWNTs), and crystalline silicon nanowires (SiNWs) to create the MoS2-SiNWs-SWNTs@ZnONPs nanocomposites. A comparative analysis of MoS2 synthesized through chemical and physical exfoliation methods revealed that the chemically exfoliated MoS2 exhibited superior performance, thereby being selected for all subsequent measurements. The nanostructured materials demonstrated exceptional surface characteristics, with specific surface areas exceeding 300 m2 g−1. Notably, the hydrogen production rate achieved by a composite comprising 5% MoS2, 1.7% SiNWs, and 13.3% SWNTs at an 80% ZnONPs base was approximately 3909 µmol h−1g−1 under 500 nm wavelength radiation, marking a significant improvement of over 40-fold relative to pristine ZnONPs. This enhancement underscores the remarkable photocatalytic efficiency of the composites, maintaining high hydrogen production rates above 1500 µmol h−1g−1 even under radiation wavelengths exceeding 600 nm. Furthermore, the potential of these composites for energy storage and conversion applications, specifically within rechargeable lithium-ion batteries, was investigated. Composites, similar to those utilized for hydrogen production but excluding ZnONPs to address its limited theoretical capacity and electrical conductivity, were developed. The focus was on utilizing MoS2, SiNWs, and SWNTs as anode materials for Li-ion batteries. This strategic combination significantly improved the electronic conductivity and mechanical stability of the composite. Specifically, the composite with 56% MoS2, 24% SiNWs, and 20% SWNTs offered remarkable cyclic performance with high specific capacity values, achieving a complete stability of 1000 mA h g−1 after 100 cycles at 1 A g−1. These results illuminate the dual utility of the composites, not only as innovative catalysts for hydrogen production but also as advanced materials for energy storage technologies, showcasing their potential in contributing to sustainable energy solutions.

Chemistry↗

NASA NTRSDate not supplied

Performance of a Regenerative Fuel Cell System for the Lunar Surface

Regenerative fuel cells (RFCs) are an attractive energy storage solution for lunar missions as a technology capable of providing a higher specific energy (i.e., W∙h/kg) than state-of-the-art packaged Li-ion battery systems. An RFC consists of the (1 & 2) electrochemical stacks (chemical to electrical energy conversion to supply electricity to an external load, i.e. the fuel cell reaction, and electrical to chemical energy conversion of supplied electrical power to dissociate water into hydrogen and oxygen gases, i.e. water electrolysis), (3) fluidic conditioning, (4) reactant storage, (5) avionics, (6) power management and distribution (PMAD), and (7) thermal management. NASA’s Glenn Research Center has designed, assembled, and tested a breadboard RFC sys-tem capable of operating autonomously for multiple simulated lunar day/night cycles in a laboratory environment. The system is comprised of a non-flow through proton exchange membrane (PEM) fuel cell stack and a liquid-anode feed PEM electrolyzer (EZ) stack designed to electrochemically compress the reactants at balanced pressures up to 12.4 MPa (1800 psia). The fluidic conditioning, avionics, PMAD, and thermal management sub-systems are largely comprised of commercial-off-the-shelf components for this system-level development effort. The hardware is controlled by a CubeSat space processor running an operational program based on core flight architecture that can control the RFC hardware autonomously through a state machine with fault monitoring. The testing results highlighted here were completed with the system in an open-loop configuration such that reactants generated through water electrolysis were vented while gas cylinders supplied fuel cell operation. The breadboard operated autonomously, but there were five unplanned transitions to a safe state that required a manual restart after reviewing the data, determining a root cause, and implementing a solution. Four of the transitions were caused by the thermal management subsystem and the fifth was caused by a water management control issue in the EZ sub-system. The RFC system operated for over 550 hours with the final cycle being slightly abbreviated due to reasons unrelated to system performance.

Kerrigan Cain↗

NASA NTRSDate not supplied

Performance of a Regenerative Fuel Cell System for the Lunar Surface

Regenerative fuel cells (RFCs) are an attractive energy storage solution for lunar missions as a technology capable of providing a higher specific energy (i.e., W∙h/kg) than state-of-the-art packaged Li-ion battery systems. An RFC consists of the (1 & 2) electrochemical stacks (chemical to electrical energy conversion to supply electricity to an external load, i.e. the fuel cell reaction, and electrical to chemical energy conversion of supplied electrical power to dissociate water into hydrogen and oxygen gases, i.e. water electrolysis), (3) fluidic conditioning, (4) reactant storage, (5) avionics, (6) power management and distribution (PMAD), and (7) thermal management. NASA’s Glenn Research Center has designed, assembled, and tested a breadboard RFC sys-tem capable of operating autonomously for multiple simulated lunar day/night cycles in a laboratory environment. The system is comprised of a non-flow through proton exchange membrane (PEM) fuel cell stack and a liquid-anode feed PEM electrolyzer (EZ) stack designed to electrochemically compress the reactants at balanced pressures up to 12.4 MPa (1800 psia). The fluidic conditioning, avionics, PMAD, and thermal management sub-systems are largely comprised of commercial-off-the-shelf components for this system-level development effort. The hardware is controlled by a CubeSat space processor running an operational program based on core flight architecture that can control the RFC hardware autonomously through a state machine with fault monitoring. The testing results highlighted here were completed with the system in an open-loop configuration such that reactants generated through water electrolysis were vented while gas cylinders supplied fuel cell operation. The breadboard operated autonomously, but there were five unplanned transitions to a safe state that required a manual restart after reviewing the data, determining a root cause, and implementing a solution. Four of the transitions were caused by the thermal management subsystem and the fifth was caused by a water management control issue in the EZ sub-system. The RFC system operated for over 550 hours with the final cycle being slightly abbreviated due to reasons unrelated to system performance.

Kerrigan Cain↗

DOE OSTI2023

Interface Design for High‐Performance All‐Solid‐State Lithium Batteries

All‐solid‐state batteries suffer from high interface resistance and lithium dendrite growth leading to low Li plating/stripping Coulombic efficiency (CE) of <90% and low critical current density at high capacity. Here, in this work, both challenges are simultaneously addressed and the Li plating/stripping CE is significantly increased to 99.6% at 0.2 mA cm −2 /0.2 mAh cm −2 , and critical current density (CCD) of > 3.0 mA cm −2 /3.0 mAh cm −2 by inserting a mixed ionic‐electronic conductive (MIEC) and lithiophobic LiF‐C‐Li 3 N‐Bi nanocomposite interlayer between Li 6 PS 5 Cl electrolyte and Li anode. The highly lithiophobic LiF‐C‐Li 3 N‐Bi interlayer with high ionic conductivity (10 −5 S cm −1 ) and low electronic conductivity (3.4×10 −7 S cm −1 ) enables Li to plate on the current collector (CC) surface rather than on Li 6 PS 5 Cl surface avoiding Li 6 PS 5 Cl electrolyte reduction. During initial Li plating on CC, Li penetrates into porous LiF‐C‐Li 3 N‐Bi interlayer and lithiates Bi nanoparticles into Li 3 Bi. The lithiophilic Li 3 Bi and Li 3 N nanoparticles in LiF‐C‐Li 3 N‐Li 3 Bi sub‐interlayer will move to CC along with plated Li, forming LiF‐C/Li 3 N‐Li 3 Bi lithiophobic/lithiophilic sublayer during the following Li stripping. This interlayer enables Co 0.1 Fe 0.9 S 2 /Li 6 PS 5 Cl/Li cell with an areal capacity of 1.4 mAh cm −2 to achieve a cycle life of >850 cycles at 150 mA g −1 . The lithiophobic/lithiophilic interlayer enables solid‐state metal batteries to simultaneously achieve high energy and long cycle life.

25 ENERGY STORAGE↗

NASA NTRSDate not supplied

Thin-Film Embedded Sensors for Battery Health Monitoring

Hybrid or all-electric aircraft are being developed as the next generation of aircraft to both allow new forms of aviation and decrease environmental impact. Since these types of aircraft are based on high-capacity battery technology, safe operation of these batteries becomes increasingly important. In particular, the potential for battery failure due to uncontrolled chemical reactions resulting in thermal runaway, catastrophic failure, and battery fires must be addressed in order for such battery technology to have the level of safety needed for standard aviation implementation. Efforts to ensure battery safety often involve engineering solutions that seek to contain rather than prevent such events by early detection. Such approaches increase the system weight and decrease the power per unit mass provided by the battery system. Existing methods for measuring battery parameters to determine the battery state-of-health are limited. These methods include electrical measurements of the cell current and/or voltage output as well as temperature measurements taken externally on the cell surface. Such external temperature measurements are limited in their ability to provide early warning of impending battery failure. In response, an effort to develop sensors operating internal to battery for health monitoring has been ongoing in the NASA Sensor-based Prognostics to Avoid Runaway Reactions & Catastrophic Ignition (SPARRCI) project. The basic approach associated with this sensor work is the deposition of thin film sensors on the battery separator located between the anode and cathode of the battery. These thin film sensors are then monitored to determine changes in battery parameters and health. Microfabrication techniques are employed to minimize the overall impact of the sensors on battery operation through the implementation of sensors with minimal size, weight, and power consumption. The thickness of the films, which are fabricated through physical vapor deposition (sputtering), are on the order of thousands of angstroms and can have minimal surface area. Thin film sensors for system health management have been implemented for a many decades on complex components for aerospace applications. However, the application of thin films of this type on a battery separator for internal battery monitoring applications has not previously been demonstrated to our knowledge. This paper describes the development of sensors for the internal battery monitoring through the use of thin film sensor technology. Thin metal films were successfully deposited on a battery separator polymer material with good adherence and electrical continuity. Multiple types of sensors have been deposited, as well as lead connections from the sensor to the edge of the separator material. The ability of these thin film sensors immersed in electrolyte to perform multiple types of battery parameter measurements has been demonstrated. For example, a multiparameter sensor system measured multiple properties simultaneously inside of a pouch cell over a wide temperature range. Further, real time measurement of interior temperature changes in a battery pouch cell with an integrated interior temperature sensor was demonstrated. These changes include detecting a fault in the battery (shorting) in situ with rapid response time (less than a minute) corresponding to a more limited response by a temperature sensor mounted externally. Other aspects of monitoring battery health were also explored, such as real-time measurement of simulated dendrite growth/metal deposition by sensor on separator material demonstrated. Future efforts will include improvements in the durability of the sensor structure to allow introduction of the approach into standard battery fabrication techniques. Overall, this work is a step forward in providing a method to prevent catastrophic battery failures and provide a foundation for safer, lighter, and higher energy batteries for the electric aircraft industry.

thin film battery health↗